CN106188863A - A kind of high tenacity flame retardant plastics thin film and preparation method thereof - Google Patents
A kind of high tenacity flame retardant plastics thin film and preparation method thereof Download PDFInfo
- Publication number
- CN106188863A CN106188863A CN201610643524.1A CN201610643524A CN106188863A CN 106188863 A CN106188863 A CN 106188863A CN 201610643524 A CN201610643524 A CN 201610643524A CN 106188863 A CN106188863 A CN 106188863A
- Authority
- CN
- China
- Prior art keywords
- parts
- thin film
- high tenacity
- flame retardant
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high tenacity flame retardant plastics thin film and preparation method thereof, described high tenacity flame retardant plastics thin film is made up of the raw material of following parts by weight: acrylic resin 80 100 parts, Kaolin 5 12 parts, polyacrylamide 15 30 parts, cumyl peroxide 26 parts, fire retardant 14 parts, 13 parts of antioxidant, compatilizer 13 parts, phosphorous acid lipid stabilizer 25 parts, magnesium stearate 0.8 1.8 parts, Tissuemat E 0.8 2.5 parts, 15 parts of kieselguhr, silicon dioxide 26 parts, oleamide 15 parts, polyoxyethylene carboxylate 8 16 parts, flax fiber 25 parts, tributyl 2-acetylcitrate 37 parts, poly(ethylene oxide) glycerin mono-fatty acid ester 7 15 parts.High tenacity flame retardant plastics thin film in the present invention has the advantages such as high tenacity, fire resistance be good, thus makes its using effect be greatly enhanced.
Description
Technical field
The invention belongs to thin film materials art, particularly to a kind of high tenacity flame retardant plastics thin film and preparation method thereof.
Background technology
Plastic sheeting may be used for packaging, coating layer, and in recent years, plastics package and plastic packet product are commercially shared
Share increasing, particularly composite plastic flexible package, have been widely used for the fields such as food, medicine, chemical industry, wherein
Maximum with packaging for foodstuff proportion again, such as beverage packaging, quick frozen food packaging, cooking food packaging, fast food packaging
Deng, these products all bring great convenience to people's life.But, generally there is resistance to elevated temperatures in existing plastic sheeting
And fire resistance is poor, toughness is also required to improve further simultaneously, thus makes its application and range of application by greatly
Limit.
Summary of the invention
It is an object of the invention to provide a kind of high tenacity flame retardant plastics thin film and preparation method thereof, this plastic sheeting has height
The advantages such as toughness, fire resistance are good.
For achieving the above object, the present invention provides following technical scheme:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 80-100 part,
Kaolin 5-12 part, polyacrylamide 15-30 part, cumyl peroxide 2-6 part, fire retardant 1-4 part, antioxidant 1-3 part, compatible
Agent 1-3 part, phosphorous acid lipid stabilizer 2-5 part, magnesium stearate 0.8-1.8 part, Tissuemat E 0.8-2.5 part, kieselguhr 1-5
Part, silicon dioxide 2-6 part, oleamide 1-5 part, polyoxyethylene carboxylate 8-16 part, flax fiber 2-5 part, acetyl Fructus Citri Limoniae
Acid tributyl 3-7 part, poly(ethylene oxide) glycerin mono-fatty acid ester 7-15 part.
Preferably, described high tenacity flame retardant plastics thin film is made up of the raw material of following parts by weight: acrylic resin 85 parts,
Kaolin 7 parts, polyacrylamide 16 parts, cumyl peroxide 3.5 parts, fire retardant 2 parts, 1.5 parts of antioxidant, compatilizer 1 part, sub-
Phosphoric acid lipid stabilizer 3 parts, magnesium stearate 1 part, Tissuemat E 1.6 parts, 3 parts of kieselguhr, silicon dioxide 4 parts, oleamide 2.8
Part, polyoxyethylene carboxylate 13 parts, flax fiber 2.6 parts, tributyl 2-acetylcitrate 6 parts, poly(ethylene oxide) glycerol list oil
Acid esters 10 parts.
Preferably, described high tenacity flame retardant plastics thin film is made up of the raw material of following parts by weight: acrylic resin 90 parts,
Kaolin 8 parts, polyacrylamide 20 parts, cumyl peroxide 4.5 parts, fire retardant 2.6 parts, 1.7 parts of antioxidant, compatilizer 1.5
Part, phosphorous acid lipid stabilizer 3.5 parts, magnesium stearate 0.9 part, Tissuemat E 1.4 parts, 2.8 parts of kieselguhr, silicon dioxide 4.8
Part, oleamide 2.3 parts, polyoxyethylene carboxylate 13 parts, flax fiber 3.6 parts, tributyl 2-acetylcitrate 3.5 parts, poly-
Oxirane glycerin mono-fatty acid ester 8 parts.
Preferably, described high tenacity flame retardant plastics thin film is made up of the raw material of following parts by weight: acrylic resin 100
Part, Kaolin 8 parts, polyacrylamide 26 parts, cumyl peroxide 3 parts, fire retardant 1.5 parts, 2.2 parts of antioxidant, compatilizer 2
Part, phosphorous acid lipid stabilizer 5 parts, magnesium stearate 1 part, Tissuemat E 2 parts, 4 parts of kieselguhr, silicon dioxide 3.8 parts, oleic acid acyl
Amine 2.5 parts, polyoxyethylene carboxylate 15 parts, flax fiber 3 parts, tributyl 2-acetylcitrate 5 parts, poly(ethylene oxide) glycerol list
Oleate 14 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Compared with prior art, the invention has the beneficial effects as follows:
Plastic sheeting in the present invention be mainly added with acrylic resin, Kaolin, cumyl peroxide, fire retardant,
The raw materials such as phosphorous acid lipid stabilizer, magnesium stearate and kieselguhr, make these plastics thin by rational proportion between each raw material components
Film has the advantages such as high tenacity, fire resistance be good, is greatly improved its using effect.
Detailed description of the invention
Describe technical scheme in detail below in conjunction with embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 90 parts, kaolinite
6 parts of soil, polyacrylamide 22 parts, cumyl peroxide 3.5 parts, fire retardant 2.7 parts, 2 parts of antioxidant, compatilizer 1.6 parts, phosphorous
Acid lipid stabilizer 3 parts, magnesium stearate 1.2 parts, Tissuemat E 1.6 parts, 4 parts of kieselguhr, silicon dioxide 3 parts, oleamide 4
Part, polyoxyethylene carboxylate 13 parts, flax fiber 2 parts, tributyl 2-acetylcitrate 5 parts, poly(ethylene oxide) glycerol list oleic acid
Ester 11 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment two:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 100 parts, high
10 parts of ridge soil, polyacrylamide 17 parts, cumyl peroxide 3.8 parts, fire retardant 2.6 parts, 1.7 parts of antioxidant, compatilizer 2.4
Part, phosphorous acid lipid stabilizer 3.6 parts, magnesium stearate 1.2 parts, Tissuemat E 2.5 parts, 2 parts of kieselguhr, silicon dioxide 4.5 parts,
Oleamide 5 parts, polyoxyethylene carboxylate 9 parts, flax fiber 5 parts, tributyl 2-acetylcitrate 7 parts, poly(ethylene oxide) is sweet
Oil monoleate 8 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment three:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 85 parts, kaolinite
7 parts of soil, polyacrylamide 16 parts, cumyl peroxide 3.5 parts, fire retardant 2 parts, 1.5 parts of antioxidant, compatilizer 1 part, phosphorous acid
Lipid stabilizer 3 parts, magnesium stearate 1 part, Tissuemat E 1.6 parts, 3 parts of kieselguhr, silicon dioxide 4 parts, oleamide 2.8 parts,
Polyoxyethylene carboxylate 13 parts, flax fiber 2.6 parts, tributyl 2-acetylcitrate 6 parts, poly(ethylene oxide) glycerin mono-fatty acid ester
10 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment four:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 90 parts, kaolinite
8 parts of soil, polyacrylamide 20 parts, cumyl peroxide 4.5 parts, fire retardant 2.6 parts, 1.7 parts of antioxidant, compatilizer 1.5 parts, sub-
Phosphoric acid lipid stabilizer 3.5 parts, magnesium stearate 0.9 part, Tissuemat E 1.4 parts, 2.8 parts of kieselguhr, silicon dioxide 4.8 parts, oil
Acid amide 2.3 parts, polyoxyethylene carboxylate 13 parts, flax fiber 3.6 parts, tributyl 2-acetylcitrate 3.5 parts, polycyclic oxygen second
Alkane glycerin mono-fatty acid ester 8 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment five:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 100 parts, high
8 parts of ridge soil, polyacrylamide 26 parts, cumyl peroxide 3 parts, fire retardant 1.5 parts, 2.2 parts of antioxidant, compatilizer 2 parts, phosphorous
Acid lipid stabilizer 5 parts, magnesium stearate 1 part, Tissuemat E 2 parts, 4 parts of kieselguhr, silicon dioxide 3.8 parts, oleamide 2.5
Part, polyoxyethylene carboxylate 15 parts, flax fiber 3 parts, tributyl 2-acetylcitrate 5 parts, poly(ethylene oxide) glycerol list oleic acid
Ester 14 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment six:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 90 parts, kaolinite
10 parts of soil, polyacrylamide 24 parts, cumyl peroxide 5 parts, fire retardant 3 parts, 1.3 parts of antioxidant, compatilizer 2.6 parts, phosphorous
Acid lipid stabilizer 3.4 parts, magnesium stearate 1.5 parts, Tissuemat E 1.6 parts, 2.8 parts of kieselguhr, silicon dioxide 3.5 parts, oleic acid
Amide 4 parts, polyoxyethylene carboxylate 11 parts, flax fiber 2.6 parts, tributyl 2-acetylcitrate 6.5 parts, poly(ethylene oxide) is sweet
Oil monoleate 9 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment seven:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 95 parts, kaolinite
7 parts of soil, polyacrylamide 30 parts, cumyl peroxide 3 parts, fire retardant 1.4 parts, 2 parts of antioxidant, compatilizer 2.2 parts, phosphorous acid
Lipid stabilizer 3 parts, magnesium stearate 1 part, Tissuemat E 2.5 parts, 4.2 parts of kieselguhr, silicon dioxide 3 parts, oleamide 4 parts,
Polyoxyethylene carboxylate 12 parts, flax fiber 5 parts, tributyl 2-acetylcitrate 7 parts, poly(ethylene oxide) glycerin mono-fatty acid ester 7
Part.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Embodiment eight:
A kind of high tenacity flame retardant plastics thin film, it is made up of the raw material of following parts by weight: acrylic resin 80 parts, kaolinite
9 parts of soil, polyacrylamide 18 parts, cumyl peroxide 5.5 parts, fire retardant 2 parts, 2 parts of antioxidant, compatilizer 3 parts, phosphite
Class stabilizer 3.8 parts, magnesium stearate 1.6 parts, Tissuemat E 1.6 parts, 5 parts of kieselguhr, silicon dioxide 3.4 parts, oleamide 5
Part, polyoxyethylene carboxylate 15 parts, flax fiber 2.5 parts, tributyl 2-acetylcitrate 6 parts, poly(ethylene oxide) glycerol list oil
Acid esters 11 parts.
The preparation method of described high tenacity flame retardant plastics thin film, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is
250-260 rev/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting
Product.
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to relatively
The present invention has been described in detail by good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent, and without deviating from objective and the scope of the technical program, it all should be contained in the present invention
Right in the middle of.
Claims (5)
1. a high tenacity flame retardant plastics thin film, it is characterised in that be made up of the raw material of following parts by weight: acrylic resin
80-100 part, Kaolin 5-12 part, polyacrylamide 15-30 part, cumyl peroxide 2-6 part, fire retardant 1-4 part, antioxidant
1-3 part, compatilizer 1-3 part, phosphorous acid lipid stabilizer 2-5 part, magnesium stearate 0.8-1.8 part, Tissuemat E 0.8-2.5 part,
Kieselguhr 1-5 part, silicon dioxide 2-6 part, oleamide 1-5 part, polyoxyethylene carboxylate 8-16 part, flax fiber 2-5 part,
Tributyl 2-acetylcitrate 3-7 part, poly(ethylene oxide) glycerin mono-fatty acid ester 7-15 part.
High tenacity flame retardant plastics thin film the most according to claim 1, it is characterised in that by the raw material system of following parts by weight
Become: acrylic resin 85 parts, Kaolin 7 parts, polyacrylamide 16 parts, cumyl peroxide 3.5 parts, fire retardant 2 parts, antioxidant
1.5 parts, compatilizer 1 part, phosphorous acid lipid stabilizer 3 parts, magnesium stearate 1 part, Tissuemat E 1.6 parts, 3 parts of kieselguhr, dioxy
SiClx 4 parts, oleamide 2.8 parts, polyoxyethylene carboxylate 13 parts, flax fiber 2.6 parts, tributyl 2-acetylcitrate 6 parts,
Poly(ethylene oxide) glycerin mono-fatty acid ester 10 parts.
High tenacity flame retardant plastics thin film the most according to claim 1, it is characterised in that by the raw material system of following parts by weight
Become: acrylic resin 90 parts, Kaolin 8 parts, polyacrylamide 20 parts, cumyl peroxide 4.5 parts, fire retardant 2.6 parts, antioxygen
Agent 1.7 parts, compatilizer 1.5 parts, phosphorous acid lipid stabilizer 3.5 parts, magnesium stearate 0.9 part, Tissuemat E 1.4 parts, kieselguhr
2.8 parts, silicon dioxide 4.8 parts, oleamide 2.3 parts, polyoxyethylene carboxylate 13 parts, flax fiber 3.6 parts, acetyl Fructus Citri Limoniae
Acid tributyl 3.5 parts, poly(ethylene oxide) glycerin mono-fatty acid ester 8 parts.
High tenacity flame retardant plastics thin film the most according to claim 1, it is characterised in that by the raw material system of following parts by weight
Become: acrylic resin 100 parts, Kaolin 8 parts, polyacrylamide 26 parts, cumyl peroxide 3 parts, fire retardant 1.5 parts, antioxygen
Agent 2.2 parts, compatilizer 2 parts, phosphorous acid lipid stabilizer 5 parts, magnesium stearate 1 part, Tissuemat E 2 parts, 4 parts of kieselguhr, dioxy
SiClx 3.8 parts, oleamide 2.5 parts, polyoxyethylene carboxylate 15 parts, flax fiber 3 parts, tributyl 2-acetylcitrate 5 parts,
Poly(ethylene oxide) glycerin mono-fatty acid ester 14 parts.
5. according to the preparation method of the high tenacity flame retardant plastics thin film according to any one of claim 1-4, it is characterised in that bag
Include following steps:
(1) each raw material components is weighed according to ratio of weight and number;
(2) will stir in off-the-shelf each raw material components addition mixing roll in step (1), mixing speed is 250-
260 revs/min, mixing time is 20-25 minute, and temperature controls, for 88-92 DEG C, to obtain raw mixture;
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting finished product.