CN106187191A - A kind of durable ceramic material - Google Patents

A kind of durable ceramic material Download PDF

Info

Publication number
CN106187191A
CN106187191A CN201610531224.4A CN201610531224A CN106187191A CN 106187191 A CN106187191 A CN 106187191A CN 201610531224 A CN201610531224 A CN 201610531224A CN 106187191 A CN106187191 A CN 106187191A
Authority
CN
China
Prior art keywords
parts
ceramic material
oxide
titanium
durable ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610531224.4A
Other languages
Chinese (zh)
Inventor
徐茂航
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Baiqianchuan Marine Ecological Technology Co Ltd
Original Assignee
Qingdao Baiqianchuan Marine Ecological Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Baiqianchuan Marine Ecological Technology Co Ltd filed Critical Qingdao Baiqianchuan Marine Ecological Technology Co Ltd
Priority to CN201610531224.4A priority Critical patent/CN106187191A/en
Publication of CN106187191A publication Critical patent/CN106187191A/en
Pending legal-status Critical Current

Abstract

A kind of durable ceramic material, it is made up of the raw material of following parts by weight: silica flour 15 24 parts, titanium diboride 6 11 parts, boron nitride 46 parts, water-base resin polyacrylamide 5 10 parts, Kaolin 9 13 parts, titanium oxide 26 parts, aluminium nitride 8 14 parts, 69 parts of black hard rock abrasive material, natrium carbonicum calcinatum 9 13 parts, potassium oxide 7 10 parts, white clouds 25 parts, magnesium oxide 47 parts, 7 10 parts of manganese, OPE 68 parts.The invention has the beneficial effects as follows: the ceramic material of the present invention that there is good durability and stability, and intensity, wearability are higher；And there is self-cleaning.

Description

A kind of durable ceramic material
Technical field
The present invention relates to a kind of durable ceramic material.
Background technology
Traditional ceramic material is primarily referred to as aluminosilicate.Time incipient, people are less demanding to the selection of aluminosilicate, Purity is little, and the granularity of granule also heterogeneity, typed pressure is the highest.At this moment obtain pottery and be referred to as traditional ceramics.Developed into later Purity is high, and granularity is little and homogeneous, and typed pressure is high, and the sintered body being sintered obtaining is called fine ceramics.Along with entering of society Step, the performance of ceramic material also becomes better and better, and existing ceramic material has good mechanical characteristic, thermal characteristics, electrical characteristics etc. Performance, but along with people are more and more higher for the requirement of pottery, existing ceramic material can not well meet use Demand, needs further to improve.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of ceramic material, has good resistance to For a long time property and stability, and intensity, wearability are higher；There is self-cleaning simultaneously.
For solving prior art problem, the technical scheme that the present invention provides is that a kind of durable ceramic material, it is by following The raw material of parts by weight is made:
Silica flour 15-24 part, titanium diboride 6-11 part, boron nitride 4-6 part, water-base resin polyacrylamide 5-10 part, Kaolin 9- 13 parts, titanium oxide 2-6 part, aluminium nitride 8-14 part, black hard rock abrasive material 6-9 part, natrium carbonicum calcinatum 9-13 part, potassium oxide 7-10 part, White clouds 2-5 part, magnesium oxide 4-7 part, manganese 7-10 part, OPE 6-8 part.
The invention has the beneficial effects as follows: the ceramic material of the present invention that there is good durability and stability, and intensity, Wearability is higher；And there is self-cleaning.
Detailed description of the invention
Embodiment 1
A kind of durable ceramic material, it is made up of the raw material of following parts by weight:
Silica flour 15 parts, titanium diboride 6 parts, boron nitride 4 parts, water-base resin polyacrylamide 5 parts, Kaolin 9 parts, titanium oxide 2 parts, Aluminium nitride 8 parts, 6 parts of black hard rock abrasive material, natrium carbonicum calcinatum 9 parts, potassium oxide 7 parts, white clouds 2 parts, magnesium oxide 4 parts, 7 parts of manganese, oxidation Tissuemat E 6 parts.
Embodiment 2
A kind of durable ceramic material, it is made up of the raw material of following parts by weight:
Silica flour 24 parts, titanium diboride 11 parts, boron nitride 6 parts, water-base resin polyacrylamide 10 parts, Kaolin 13 parts, titanium oxide 6 Part, aluminium nitride 14 parts, 9 parts of black hard rock abrasive material, natrium carbonicum calcinatum 13 parts, potassium oxide 10 parts, white clouds 5 parts, magnesium oxide 7 parts, manganese 10 Part, OPE 8 parts.

Claims (1)

1. a durable ceramic material, it is characterised in that: it is made up of the raw material of following parts by weight:
Silica flour 15-24 part, titanium diboride 6-11 part, boron nitride 4-6 part, water-base resin polyacrylamide 5-10 part, Kaolin 9- 13 parts, titanium oxide 2-6 part, aluminium nitride 8-14 part, black hard rock abrasive material 6-9 part, natrium carbonicum calcinatum 9-13 part, potassium oxide 7-10 part, White clouds 2-5 part, magnesium oxide 4-7 part, manganese 7-10 part, OPE 6-8 part.
CN201610531224.4A 2016-07-07 2016-07-07 A kind of durable ceramic material Pending CN106187191A (en)