CN106148860A - A kind of high-hardness ceramic material - Google Patents
A kind of high-hardness ceramic material Download PDFInfo
- Publication number
- CN106148860A CN106148860A CN201610531228.2A CN201610531228A CN106148860A CN 106148860 A CN106148860 A CN 106148860A CN 201610531228 A CN201610531228 A CN 201610531228A CN 106148860 A CN106148860 A CN 106148860A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic material
- oxide
- hardness
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high-hardness ceramic material, it is made up of the raw material of following parts by weight: boron carbide powder 12 22 parts, silicon nitride 9 11 parts, Pulvis Talci 8 12 parts, silicon dioxide 8 11 parts, 59 parts of Muscovitum, yittrium oxide 46 parts, aluminium oxide 9 14 parts, calcium carbonate 69 parts, instrument comminuted steel shot 7 12 parts, dehydrated alcohol 9 13 parts, boric acid 24 parts, 14 16 parts of carbon fiber, ferrum oxide 7 10 parts, OPEO 26 parts, copper nanoparticle 7 12 parts, 9 12 parts of carbonization technetium powder.The invention has the beneficial effects as follows: the ceramic material of the present invention that there is higher hardness and intensity, simultaneously wearability and having excellent weather resistance；Service life is long.
Description
Technical field
The present invention relates to a kind of high-hardness ceramic material.
Background technology
Traditional ceramic material is primarily referred to as aluminosilicate.Time incipient, people are less demanding to the selection of aluminosilicate,
Purity is little, and the granularity of granule also heterogeneity, typed pressure is the highest.At this moment obtain pottery and be referred to as traditional ceramics.Developed into later
Purity is high, and granularity is little and homogeneous, and typed pressure is high, and the sintered body being sintered obtaining is called fine ceramics.Along with entering of society
Step, the performance of ceramic material also becomes better and better, and existing ceramic material has good mechanical characteristic, thermal characteristics, electrical characteristics etc.
Performance, but along with people are more and more higher for the requirement of pottery, existing ceramic material can not well meet use
Demand, needs further to improve.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of ceramic material, has higher hard
Degree and intensity, simultaneously wearability and having excellent weather resistance；Service life is long.
For solving prior art problem, the technical scheme that the present invention provides is, a kind of high-hardness ceramic material, it is by following
The raw material of parts by weight is made:
Boron carbide powder 12-22 part, silicon nitride 9-11 part, Pulvis Talci 8-12 part, silicon dioxide 8-11 part, Muscovitum 5-9 part, yittrium oxide
4-6 part, aluminium oxide 9-14 part, calcium carbonate 6-9 part, instrument comminuted steel shot 7-12 part, dehydrated alcohol 9-13 part, boric acid 2-4 part, carbon fiber
14-16 part, ferrum oxide 7-10 part, OPEO 2-6 part, copper nanoparticle 7-12 part, carbonization technetium powder 9-12 part.
The invention has the beneficial effects as follows: the ceramic material of the present invention that there is higher hardness and intensity, simultaneously wearability and
Have excellent weather resistance；Service life is long.
Detailed description of the invention
Embodiment 1
A kind of high-hardness ceramic material, it is made up of the raw material of following parts by weight:
Boron carbide powder 12 parts, silicon nitride 9 parts, Pulvis Talci 8 parts, silicon dioxide 8 parts, 5 parts of Muscovitum, yittrium oxide 4 parts, aluminium oxide 9 parts,
Calcium carbonate 6 parts, instrument comminuted steel shot 7 parts, dehydrated alcohol 9 parts, boric acid 2 parts, 14 parts of carbon fiber, ferrum oxide 7 parts, octyl phenol polyoxyethylene
2 parts of ether, copper nanoparticle 7 parts, 9 parts of carbonization technetium powder.
Embodiment 2
A kind of high-hardness ceramic material, it is made up of the raw material of following parts by weight:
Boron carbide powder 22 parts, silicon nitride 11 parts, Pulvis Talci 12 parts, silica 11 part, 9 parts of Muscovitum, yittrium oxide 6 parts, aluminium oxide
14 parts, calcium carbonate 9 parts, instrument comminuted steel shot 12 parts, dehydrated alcohol 13 parts, boric acid 4 parts, 16 parts of carbon fiber, ferrum oxide 10 parts, octyl phenol
Polyoxyethylene ether 6 parts, copper nanoparticle 12 parts, 12 parts of carbonization technetium powder.
Claims (1)
1. a high-hardness ceramic material, it is characterised in that: it is made up of the raw material of following parts by weight:
Boron carbide powder 12-22 part, silicon nitride 9-11 part, Pulvis Talci 8-12 part, silicon dioxide 8-11 part, Muscovitum 5-9 part, yittrium oxide
4-6 part, aluminium oxide 9-14 part, calcium carbonate 6-9 part, instrument comminuted steel shot 7-12 part, dehydrated alcohol 9-13 part, boric acid 2-4 part, carbon fiber
14-16 part, ferrum oxide 7-10 part, OPEO 2-6 part, copper nanoparticle 7-12 part, carbonization technetium powder 9-12 part.