CN106187049B - The method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments - Google Patents
The method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments Download PDFInfo
- Publication number
- CN106187049B CN106187049B CN201610518652.3A CN201610518652A CN106187049B CN 106187049 B CN106187049 B CN 106187049B CN 201610518652 A CN201610518652 A CN 201610518652A CN 106187049 B CN106187049 B CN 106187049B
- Authority
- CN
- China
- Prior art keywords
- sierozem
- sponge brick
- medical stone
- catchments
- porous sponge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments, and comprises the following steps:The dispensing of the porous sponge brick that catchments:15~20wt% of cement, particle diameter is 100~250 μm of 50~75wt% of the hollow clay microballon of medical stone sierozem perforate, 5~15wt% of sodium metasilicate of modulus 3.2~3.5, 5~the 10wt% of flyash and polyvinyl alcohol high hydroscopic resin 1.5~5.0wt% of fiber proportion samples of loss on ignition 1.1% are simultaneously well mixed, compound is sized mixing with 0.5~0.7 ratio of mud, add the aluminium powder cream that compound gross weight is 0.2~1.0%, aluminium powder cream hydration reaction generates bubble, form porous expansion water suction slurries, the expansion water suction slurries of preparation are stirred and poured into the die trial of sponge brick press, through striking off, compacting, the demoulding, dry, the porous sponge brick that catchments is made.
Description
Technical field
The present invention relates to the method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments, belong to material
Technology is led.
Background technology
Due to EI Nino and La Nina Phenomenon, there is extreme change in the weather in China, and rainfall distributed pole is uneven, south
Northern drought and waterlogging are uneven, and rainfall is also extremely unequal in same area, 1 year, and water shortage has restricted expanding economy and the people
Life, rationally using existing precipitation, by cell road surface, road, the effective precipitation in public leisure square rationally collect, store,
Utilize, alleviate drought and water shortage season use water, the thermal capacity of water is big, can absorb heat also can heat release, improve miniclimate.
The content of the invention
The hollow clay microballon of medical stone sierozem perforate by the use of perforate is used as base-material, using sodium metasilicate as binding agent, water
Mud increases mechanical strength and cementation for the porous sponge brick that catchments, and the resin fibre of flyash and polyvinyl alcohol high water absorption is strong
Water absorbing agent, contain calcium carbonate in sierozem, compression strength is big after high-temperature firing, and the smaller specific surface area of medical stone particle diameter is bigger, inhales
Attached ability is stronger, and medical stone is to heavy metal ion adsorbed in water, the huge sum of money in cation and water substantially in medical stone
Category cation is swapped, and the heavy metal cation in water has been adsorbed by ion exchange medical stone, has adjusted the pH value of water, is used
Dilatant slurry, reduces the density of slurries, and a face of the manufactured porous sponge brick that catchments is in dovetail channel-shaped, the porous sponge brick that catchments
The moisture of absorption enters dovetail groove, is flowed into collector pipe again by the effect of gravity, the porous sponge brick that catchments is connected to one by collector pipe
Rise, rainwater catchment is into collecting-tank.
Its technical scheme is:The method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments, first
Step, the dispensing of the porous sponge brick that catchments:15~20wt% of cement, particle diameter are 100~250 μm of hollow potteries of medical stone sierozem perforate
Native 50~75wt% of microballon, 5~15wt% of sodium metasilicate of modulus 3.2~3.5,5~10wt% of flyash of loss on ignition 1.1% and poly-
Vinyl alcohol high hydroscopic resin 1.5~5.0wt% of fiber, the percentage by weight sum of above each component is 100%;
The preparation of second step, the porous sponge brick expansion water suction slurries that catchment:Sample by the percentage by weight of the first step, first will
Particle diameter is that 100~250 μm of hollow clay microballons of medical stone sierozem perforate are put into feed bin, and distributing device, cloth are sent into by elevator
The hollow clay microballon of medical stone sierozem perforate is evenly distributed on governing belt balance by glassware, and spray thrower is by modulus 3.2~3.5
Sodium metasilicate be uniformly sprayed at the outer surface of the hollow clay microballon of medical stone sierozem perforate, the hollow pottery of medical stone sierozem perforate
Native microballon enters inside spin drum agitation device with governing belt balance, makes the outer of the hollow clay microballon of each medical stone sierozem perforate
Sodium metasilicate is all uniformly adhered on surface, and sodium metasilicate is inorganic bond, is hydrophilic, and cohesive force is strong, intensity is higher, acid resistance,
Heat-resist, hydrophilicity does not influence caking property, and compound is 15~20wt% of cement, particle diameter is 100~250 μm of medical stone ashes
50~75wt% of the hollow clay microballon of calcium soil perforate, 5~15wt% of sodium metasilicate of modulus 3.2~3.5, the fine coal of loss on ignition 1.1%
5~10wt% of ash and polyvinyl alcohol high hydroscopic resin 1.5~5.0wt% of fiber, then compound is adjusted with 0.5~0.7 ratio of mud
Slurry, ash is compound, is eventually adding the aluminium powder cream that compound gross weight is 0.2~1.0%, hydration reaction generation bubble, is formed more
The slurries of hole expansion water suction, reduce the weight of sponge brick, and polyvinyl alcohol high hydroscopic resin fiber has extremely strong water imbibition, absorbed water
Sponge brick compression strength afterwards is constant;
The preparation of 3rd step, the porous sponge brick that catchments:Expansion water suction slurries prepared by second step, which stir, pours into sea
In the die trial of continuous brick press, by 1.2~2.0:1 volume ratio is suppressed, and ratio 1.2~2.0 is the volume before compacting, and ratio 1 is
Volume after compacting, through striking off, suppressing, being stripped, drying, the porous sponge brick that catchments, a face of the porous sponge brick that catchments is made
In dovetail channel-shaped, the porous moisture for catchmenting the absorption of sponge brick enters in dovetail groove, in collector pipe insertion dovetail groove, collector pipe insertion
A part of arc surface in dovetail groove is openning shape, and another part arc surface is closed, and rainwater passes through the porous sponge brick that catchments
Collect, into dovetail groove, flowed into collector pipe again by the effect of gravity, the single porous sponge brick that catchments is connected to by collector pipe
Together, the rainwater that collector pipe collects enters in collecting-tank.
The preparation of the hollow clay microballon of medical stone sierozem perforate:First by 80~200 μm of medical stones of particle diameter, 200~400 μm
Sierozem is by weight 20~30:70~85 compounds stir, and the percentage by weight sum of two kinds of components is 100%, mixing
Material is sized mixing by 0.5~0.7 ratio of mud, the compound that ash forms for two kinds of compositions of medical stone and sierozem, by centrifugal rotation
Injection forms microballon at a high speed, then through 800~950 DEG C of expansions, 1000~1500 DEG C of firings, quick cooling, forms wall thickness 50~100
μm, particle diameter is 100~250 μm of the hollow clay microballon of medical stone sierozem perforate, and two kinds of materials of medical stone and sierozem mix,
By high-temperature firing, modified medical stone and the compound clay resistance to compression microballon of sierozem are formd, the component of material is different, modified
The chemical property of material is also different, and calcium carbonate is contained in sierozem, and compression strength is big after high-temperature firing, and calcium carbonate forms oxidation
Calcium, calcium oxide hydration form calcium hydroxide, and into gelatinous material, the smaller specific surface area of medical stone particle diameter is bigger, absorption
Ability is stronger, and medical stone is to heavy metal ion adsorbed in water, the heavy metal in cation and water substantially in medical stone
Cation is swapped, and the heavy metal cation in water has been adsorbed by ion exchange medical stone, adjusts the pH value of water.
The modulus of sodium metasilicate is most important, and when modulus is more than 3.5, with the increase of modulus, sodium metasilicate, which is hardened, to become fragile, and glues
Knot property is deteriorated, and when modulus is less than 3.2, caking property declines.
Flyash is strong water absorbent, by high temperature sintering, there is higher activity.
A rainwater part for accumulation is pooled in collecting-tank by the porous sponge brick that catchments by collector pipe, and another part penetrates into
Into soil, increase soil water content, in summer high-temperature season, the heat on surface can also be transmitted to by the porous sponge brick that catchments
In soil, the temperature on sponge tile floor surface is reduced, the thermal capacity of water is big, and can absorb heat also can heat release.
The present invention has advantages below.
1st, the Materials Inorganic environment-friendly materials used in sponge brick are prepared, environment will not be damaged, the recyclable energy of sponge brick
Secondary use.
2nd, it is strong water absorbent to prepare sponge brick flyash and the resin fibre of polyvinyl alcohol high water absorption, can absorb sponge brick table
The moisture in face enters inside, when reaching certain amount, is dropped into the presence of by gravity in collector pipe.
3rd, aluminium powder cream is added in compound, forms the slurries of porous expansion, reduces the density of slurries.
4th, the heavy metal cation in the cation and water in medical stone swaps, and is adsorbed by ion exchange medical stone
Heavy metal cation in water, adjust the pH value of water.
Brief description of the drawings
Fig. 1 is the axle geodesic structure schematic diagram of the sea brick of the embodiment of the present invention.
Fig. 2 is that the bottom of the sea brick of the embodiment of the present invention regards structural representation.
Fig. 3 is the structural representation that the monolithic sponge brick of the embodiment of the present invention is linked together by collector pipe.
Wherein 1 in figure, sponge brick 2, dovetail groove 3, collector pipe.
Embodiment
Embodiment 1.
In embodiment as shown in Figures 1 to 3, absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments
Method, the preparation of the first step, the hollow clay microballon of medical stone sierozem perforate:First by 100 μm of medical stones of particle diameter, 300 μm of ashes
Calcium soil is by weight 30:70 compounds are stirred, and compound is sized mixing by 0.6 ratio of mud, are sprayed at a high speed by centrifugal rotation
Microballon is formed, then through 820 DEG C of expansions, 1150 DEG C of high-temperature firings, quick cooling, forms 80 μm of wall thickness, particle diameter is 250 μm of wheat meal
The hollow clay microballon of stone sierozem perforate.
The dispensing of second step, the porous sponge brick that catchments:It is 250 μm of medical stone sierozem perforates to take cement 20wt%, particle diameter
Hollow clay microballon 58wt%, the sodium metasilicate 12wt% of modulus 3.3, the flyash 6wt% of loss on ignition 1.1% and polyvinyl alcohol are high to be inhaled
Water-resin fiber 4.0wt%.
The preparation of 3rd step, the porous sponge brick expansion water suction slurries that catchment:Sample by the percentage by weight of the first step, first will
Particle diameter is that 250 μm of hollow clay microballons of medical stone sierozem perforate are put into feed bin, is sent into distributing device by elevator, distributing device will
The hollow clay microballon of medical stone sierozem perforate is evenly distributed on governing belt balance, and spray thrower is equal by the sodium metasilicate of modulus 3.3
The even outer surface for being sprayed at the hollow clay microballon of medical stone sierozem perforate, enter inside spin drum agitation with governing belt balance
Device, compound is sized mixing with 0.6 ratio of mud, add the aluminium powder cream that compound gross weight is 0.5%, hydration reaction generation gas
Bubble, the slurries of porous expansion water suction are formed, reduce the weight of sponge brick, polyvinyl alcohol high hydroscopic resin fiber has extremely strong suction
Water-based, the sponge brick compression strength after water suction is constant, and medical stone is to heavy metal ion adsorbed in water, substantially in medical stone
Cation and water in heavy metal cation carry out ion exchange, the heavy metal in water has been adsorbed by ion exchange medical stone
Cation, adjust the pH value of water.
The preparation of the porous sponge brick that catchments of 4th step, absorbent-type:Expansion water suction slurries prepared by second step stir
Pour into the die trial of sponge brick press, by 1.5:1 volume ratio compacting, through striking off, suppressing, being stripped, drying, is made porous
Catchment sponge brick 1, and a face of the porous sponge brick 1 that catchments is in the shape of dovetail groove 2, and the porous moisture for catchmenting the absorption of sponge brick 1 enters
In dovetail groove 2, collector pipe 3 is installed in dovetail groove 2, rainwater collects by the porous sponge brick 1 that catchments, into dovetail groove 2
It is interior, collector pipe 3 is flowed into again by the effect of gravity, and collector pipe 3 links together the single porous sponge brick 1 that catchments, and collector pipe 3 converges
The rainwater of collection enters in collecting-tank, by precipitating, filtering, reuses.
The above described is only a preferred embodiment of the present invention, being not the limitation for making other forms to the present invention, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Embodiment is imitated, every without departing from technical solution of the present invention content, the technical spirit according to type of the present invention is made to above example
Any simple modification, equivalent variations and remodeling, still fall within the protection domain of type technical scheme of the present invention.
Claims (1)
1. the method that absorbent-type medical stone sierozem clay microballon prepares the porous sponge brick that catchments, comprises the following steps:The first step,
The dispensing of the porous sponge brick that catchments:15~20wt% of cement, particle diameter are that 100~250 μm of hollow clay of medical stone sierozem perforate are micro-
50~75wt% of pearl, 5~15wt% of sodium metasilicate of modulus 3.2~3.5, the 5~10wt% of flyash and polyethylene of loss on ignition 1.1%
Alcohol high hydroscopic resin 1.5~5.0wt% of fiber, the percentage by weight sum of above each component is 100%, medical stone sierozem perforate
The preparation of hollow clay microballon:First by 80~200 μm of medical stones of particle diameter, 200~400 μm of sierozem by weight 20~30:70
~85 compounds stir, and the percentage by weight sum of two kinds of components is 100%, and compound is adjusted by 0.5~0.7 ratio of mud
Slurry, ash are the compound of two kinds of composition compositions of medical stone and sierozem, and by centrifugal rotation, injection forms microballon at a high speed, then passes through
800~950 DEG C of expansions, 1000~1500 DEG C of firings, quick cooling, form 50~100 μm of wall thickness, and particle diameter is 100~250 μm
The hollow clay microballon of medical stone sierozem perforate;
The preparation of second step, the porous sponge brick expansion water suction slurries that catchment:Sampled by the percentage by weight of the first step, first by particle diameter
It is put into for 100~250 μm of hollow clay microballons of medical stone sierozem perforate in feed bin, distributing device, distributing device is sent into by elevator
The hollow clay microballon of medical stone sierozem perforate is evenly distributed on governing belt balance, spray thrower is by the silicon of modulus 3.2~3.5
Sour sodium is uniformly sprayed at the outer surface of the hollow clay microballon of medical stone sierozem perforate, and the hollow clay of medical stone sierozem perforate is micro-
Pearl enters inside spin drum agitation device with governing belt balance, then compound is sized mixing with 0.5~0.7 ratio of mud, is eventually adding
The aluminium powder cream that compound gross weight is 0.2~1.0% stirs, and aluminium powder cream hydration reaction generation bubble, forms porous expansion and inhales
Aqueous slurry;
The preparation of 3rd step, the porous sponge brick that catchments:Expansion water suction slurries prepared by second step, which stir, pours into sponge brick
In the die trial of press, through striking off, suppressing, being stripped, drying, the porous sponge brick that catchments is made(1), the porous sponge brick that catchments(1)
A face be in dovetail groove(2)Shape, collector pipe(3)Embedded dovetail groove(2)It is interior, collector pipe(3)Embedded dovetail groove(2)Interior one
Cyclotomy cambered surface is openning shape, and another part arc surface is closed, and rainwater passes through the porous sponge brick that catchments(1)Collect, enter
Dovetail groove(2)It is interior, entered collector pipe by the effect of gravity(3), collector pipe(3)By the single porous sponge brick that catchments(1)It is connected to
Together, collector pipe(3)The rainwater collected enters in collecting-tank.