CN106182262A - A kind of preparation method of side's joggle W type bamboo lumber - Google Patents
A kind of preparation method of side's joggle W type bamboo lumber Download PDFInfo
- Publication number
- CN106182262A CN106182262A CN201610745545.4A CN201610745545A CN106182262A CN 106182262 A CN106182262 A CN 106182262A CN 201610745545 A CN201610745545 A CN 201610745545A CN 106182262 A CN106182262 A CN 106182262A
- Authority
- CN
- China
- Prior art keywords
- meng
- bamboo
- ancestor
- zongzhu
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The preparation method of a kind of side's joggle W type bamboo lumber, comprises the following steps: a, preparation ancestor bamboo abdomen material in the Meng;B, preparation ancestor bamboo wing material in the Meng;C, inside Meng ancestor bamboo wing material, place opens the groove inlaying ancestor bamboo abdomen material in above-mentioned Meng together, and gash depth is 0.8 cm, and width is approximately less than ancestor bamboo abdomen material thickness 0.1 mm in the Meng, and by adhesive coated in groove, moulding pressure, to hardening, pressurizes more than 8 hours.Described step a at room temperature carries out reacting 1~5 day in including Meng Zongzhu is soaked in this fixation liquid medicine.The present invention is so that the final square joggle W type bamboo lumber prepared presents natural green form, it is greatly enhanced the captivation to consumer, be conducive to improving the surcharge of product, for properly utilizing bamboo resource, promoting the green building of bamboo wood to have active influence.
Description
Technical field
The present invention relates to bamboo lumber production field, refer in particular to the preparation method of a kind of side's joggle W type bamboo lumber.
Background technology
Meng Zongzhu is the Phyllostachys pubescens Mazei ex H.de Lebaie abounding with south China.Bamboo is abounded with in the torrid zone, subtropical zone and temperate zone, and frigid zone is less, and with Asia
The monsoon zone in continent is distribution center, and the whole world has bamboo plant 60 to belong to, and more than 600 plant, and south China is that China's bamboo class abounds with district, meter 16 genus
Kind more than 100.Bamboo class is broadly divided into two big classes in China, and a class is grown on low altitude area or area by north, and property likes high temperature and humidity weather,
Its bar is grown thickly and is had the subterraneous stem of sympodium type, is generally called " Cluster Bamboo ".Another kind of High aititude or areas more by north of being grown on, more resistance to
Low temperature and like moistening environment, its bar is scattered and has the subterraneous stem of single-shaft variant, be generally called " Scattered bamboos ".Meng Zongzhu just belongs to " scattered
Bamboo ".The Meng the rhizomatous terminal bud of ancestor bamboo, be not unearthed excavate cry winter bamboo shoot, troat Radix Crotalariae szemoensis after being unearthed, be again Caulis Bambusae Germinatus, through 70 days left sides
Right bamboo sprout can basic well-thought-out plan.
The Meng, ancestor's Sinobambusa grass family, was the excellent cultivar of China, was also the maximum bamboo kind of economic worth.China is to bamboo wood
Utilization, prehistoric historical relic can be traced back to.Not having paper ancient times, word all writes on bamboo chip, then is connected into volume.Build as ancestor bamboo in the Meng
, also there is the history of more than thousand in house.In modern science and technology, Meng Zongzhu is the good raw material of paper industry, and 300 tons of bamboo woods can make one
Ton paper pulp.And Radix Crotalariae szemoensis are in addition to general eating, may also be fabricated which various dried bamboo shoots and canned food.
For now, the bamboo resource of China is the abundantest, and Meng Zongzhu can reach in short 3 to five years
Big net growth.Bamboo grove can give birth to decades-long continuously, if bamboo resource can be managed sustainably, and appropriate exploitation should
With, manufacture bamboo wood, then deficient to the demand of ARCHITECTURE TODAY material awkward situation, should be able to obtain and alleviate and improve.And bamboo class
The sustainable development of resource and utilization, should have front for current greenhouse effects of the earth and carbon dioxide isothermal chamber gas decrement problem
Benefit.
Bamboo flooring is a kind of bamboo product developed at the initial stage the 80's of 20th century.Owing to bamboo flooring appearance luster is simple and elegant
Like Dens Elephatis, ring is in picturesque disorder on plate face, forms natural decorative pattern, and material is hard, good springiness, and bamboo flooring symmetrical configuration is closed
Reason, good stability of the dimension, therefore product is just liked by consumer of China and foreign countries once coming out.Through the effort of more than ten years, bamboo ground
The manufacturing technology of plate becomes better and approaching perfection day by day.At present bamboo flooring has become as the floor decorative material of a kind of top grade, is popular in America and Europe, the southeast
The areas such as Asia, the Middle East, China is the major country of production of bamboo flooring, and yield is big, and product is sold to all over the world.
Chinese invention patent (application number 201310748162.9) discloses the preparation technology of a kind of bamboo substrate material, and this is prepared
Bamboo wood is processed by technique according to following procedures: and saw cut → cuts open → discongests, flattens → and a fixed width calmly thickness → carbonization is dried
→ health preserving → secondary carbonization is dried → and applying glue → tri-time desiccant dehumidification → assembly, hot pressing → demoulding process, the bamboo substrate material obtained.
Although process above can decrease the loss of bamboo wood, improve the utilization rate of bamboo wood, but also deposit during actual use
There iing following weak point: 1, bamboo wood natural green on its surface after multiple working procedure processes is seriously damaged, the plate prepared
Material lacks green life, it is impossible to enough meet the demand that user is growing, is unfavorable for improving the value of product;2, more than using
Technique prepare bamboo wood do not possess antibacterial ability, life-time service easily occur mouldy, damage by worms, fade and deform.
Summary of the invention
The present invention provides the preparation method of a kind of side's joggle W type bamboo lumber, and its main purpose is to overcome existing bamboo matter
Sheet material exist without defect that is green, the most mouldy and that damage by worms.
For solving above-mentioned technical problem, the present invention adopts the following technical scheme that
The preparation method of a kind of side's joggle W type bamboo lumber, comprises the following steps: a, preparation ancestor bamboo abdomen material in the Meng;B, preparation Meng Zong
Bamboo wing material;C, inside Meng ancestor bamboo wing material, place opens the groove inlaying ancestor bamboo abdomen material in above-mentioned Meng together, and gash depth is 0.8
, width is approximately less than ancestor bamboo abdomen material thickness in the Meng 0.1, by adhesive coated in groove, and moulding pressure to hardening, pressurization 8
More than hour, described step a include following step by step: a1, select ancestor bamboo in fresh Meng and this Meng Zongzhu carried out fixed length;A2, edge
The axial vertical profile of Meng Zongzhu;A3, bamboo green grass or young crops of pruning;A4, Meng Zongzhu is soaked 80 minutes in the hot water of 80 DEG C~120 DEG C;A5, take chlorine
Change copper and configure fixation liquid medicine using methanol as solvent, at room temperature carry out reacting 1~5 in Meng Zongzhu is soaked in this fixation liquid medicine
My god;A6, taking-up Meng Zongzhu dry laggard pedestrian's work vapour seasoning;A7, Meng Zongzhu is carried out high-temperature low-oxygen carbonization process;A8, right
Meng Zongzhu carries out fixed thick fixed width, carries out jigsaw the most in the direction of the width;A9, the Meng Zongzhu after jigsaw is planished, and right
Its thickness direction is integrated, thus realizes ancestor bamboo abdomen material in integrated for bamboo Meng.
Further, described step b include following step by step: b1, select ancestor bamboo in fresh Meng and this Meng Zongzhu is carried out fixed
Long;B2, along the axial vertical profile of ancestor bamboo in the Meng;B3, bamboo green grass or young crops of pruning;B4, Meng Zongzhu is soaked 80 points in the hot water of 80 DEG C~120 DEG C
Clock;B5, take copper chloride using methanol as solvent configure fixation liquid medicine, at room temperature enter in Meng Zongzhu is soaked in this fixation liquid medicine
Row reaction 1~5 day;B6, taking-up Meng Zongzhu dry laggard pedestrian's work vapour seasoning;B7, Meng Zongzhu is carried out high-temperature low-oxygen carbonization
Process;B8, Meng Zongzhu is carried out fixed thick fixed width, carry out jigsaw the most in the direction of the width;B9, the Meng Zongzhu after jigsaw is carried out
Planing, and integrated to its thickness direction, thus realize ancestor bamboo wing material in integrated for bamboo Meng.
Further, in step c, binding agent is to be sprayed at described groove with the plural number spaced apart dotted line of bar.
Further, in step a7, described high-temperature low-oxygen carbonization processes and includes: by the Meng Zong after step a6 processes
Bamboo is placed in one and contains in steam vent, fan, the high temperature closed baking oven up to 250 DEG C, first with 40 DEG C, steam vent standard-sized sheet, processes about
Close steam vent after 20 hours, then after 120 DEG C, continue 5~6 hours with per hour 20 DEG C of heating rate homoiothermics, then with per hour
10 DEG C of heating rate homoiothermics, to 150 DEG C~180 DEG C, continue 24 hours.
Further, in step b7, described high-temperature low-oxygen carbonization processes and includes: by the Meng Zong after step b6 processes
Bamboo is placed in one and contains in steam vent, fan, the high temperature closed baking oven up to 250 DEG C, first with 40 DEG C, steam vent standard-sized sheet, processes about
Close steam vent after 20 hours, then after 120 DEG C, continue 5~6 hours with per hour 20 DEG C of heating rate homoiothermics, then with per hour
10 DEG C of heating rate homoiothermics, to 150 DEG C~180 DEG C, continue 24 hours.
Compared to the prior art, what the present invention produced has the beneficial effects that:
1, present invention process is simple, practical, and by configuring fixation liquid medicine, ancestor bamboo in the Meng only need to be immersed this fixation liquid medicine by user
Inside process, unstable chlorophyll form transformation can become stable green phosphor salt pigment combine organic pigment and group
The complex become, so that it may make it be maintained beautiful green appearance, and this green appearance keeps the most stable, at subsequent high temperature
The operation of reason all will not destroy the molecular structure of above-mentioned complex, thus so that the final square joggle W type bamboo scutum prepared
Material presents natural green form, is greatly enhanced the captivation to consumer, is conducive to improving the surcharge of product, for appropriate
It is apt to utilize bamboo resource, promote the green building of bamboo wood to have active influence.
2, in the present invention, by introducing copper ion as the main component of fixation liquid medicine, when the Meng ancestor bamboo immerse this fixation
In liquid medicine, upper part copper ion can be adsorbed, and final copper ion also will the side's of being stranded in joggle W type bamboo lumber, thus upper
During the side's of stating joggle W type bamboo lumber life-time service, its interior copper ion can suppress moth and antibacterial thereon effectively
Grow, so that the square joggle W type bamboo lumber that the present invention prepares has stronger anti-microbial property, be conducive to improving it
To ability that is anti-insect and that go mouldy.
3, in the present invention, by introducing high-temperature low-oxygen carbonization treatment process, not only material cost is inexpensively, Er Qieke
To reduce bamboo clappers cracking so that it is surface color and texture present preferable states, also are able to further prevent from going mouldy and worm simultaneously
Moth, improves product quality.
4, in the present invention, carry out gluing by dotted line spraying method, be possible not only to play saving glue, reduce environment
The effect polluted, and make the link position of ancestor bamboo abdomen material in the Meng and ancestor bamboo wing material in the Meng can be able to appropriateness buffering, it is to avoid because of length
Phase Exposure to Sunlight and cause link position swelling cracking.
Detailed description of the invention
The invention discloses the preparation method of a kind of side's joggle W type bamboo lumber, those skilled in the art can use for reference this
Literary composition content, is suitably modified technological parameter and realizes.Special needs to be pointed out is, all similar replacements and change are to art technology
Being apparent from for personnel, they are considered as being included in the present invention.Method and the application of the present invention have been passed through preferably
Embodiment is described, and related personnel substantially can be to side as herein described in without departing from present invention, spirit and scope
Method and application are modified or suitably change and combine, and realize and apply the technology of the present invention.
The preparation method of a kind of side's joggle W type bamboo lumber, comprises the following steps: a, preparation ancestor bamboo abdomen material in the Meng;B, preparation
The Meng ancestor bamboo wing material;C, inside Meng ancestor bamboo wing material, place opens the groove inlaying ancestor bamboo abdomen material in above-mentioned Meng together, and gash depth is
0.8, width is approximately less than ancestor bamboo abdomen material thickness in the Meng 0.1, and by adhesive coated in groove, moulding pressure, to hardening, adds
Press more than 8 hours.Wherein in step c, binding agent is to be sprayed at described groove with the plural number spaced apart dotted line of bar.
In the present embodiment, technique and the preparation ancestor bamboo abdomen material in the Meng of preparation ancestor bamboo wing material in the Meng are substantially the same, and its difference only exists
Otherwise varied in prepared wing material and abdomen material size, concrete, the cross dimensions of side's joggle W type bamboo lumber is 6 × 12
, described Meng, the thickness of ancestor bamboo abdomen material was 3, and described Meng, the thickness of ancestor bamboo wing material was 2.
Therefore, know from the above, described step a include following step by step:
A1, select ancestor bamboo in fresh Meng and this Meng Zongzhu is carried out fixed length.
A2, along the axial vertical profile of ancestor bamboo in the Meng.
A3, bamboo green grass or young crops of pruning.
A4, Meng Zongzhu is soaked 80 minutes in the hot water of 80 DEG C~120 DEG C.
A5, take copper chloride and configure fixation liquid medicine using methanol as solvent, Meng Zongzhu is soaked in this fixation liquid medicine in room
Carry out under temperature reacting 1~5 day.
A6, taking-up Meng Zongzhu dry laggard pedestrian's work vapour seasoning.
A7, Meng Zongzhu is carried out high-temperature low-oxygen carbonization process.Described high-temperature low-oxygen carbonization processes and includes: will be through step a6
Meng Zongzhu after process is placed in one and contains in steam vent, fan, the high temperature closed baking oven up to 250 DEG C, first with 40 DEG C, steam vent
Standard-sized sheet, closes steam vent after processing about 20 hours, less to continuing 5~6 after 120 DEG C with per hour 20 DEG C of heating rate homoiothermics
Time, then with per hour 10 DEG C of heating rate homoiothermics to 150 DEG C~180 DEG C, continue 24 hours.
A8, Meng Zongzhu is carried out fixed thick fixed width, carry out jigsaw the most in the direction of the width.
A9, the Meng Zongzhu after jigsaw is planished, and integrated to its thickness direction, thus realize ancestor bamboo in integrated for bamboo Meng
Abdomen material.
It addition, know from the above, described step b include following step by step:
B1, select ancestor bamboo in fresh Meng and this Meng Zongzhu is carried out fixed length.
B2, along the axial vertical profile of ancestor bamboo in the Meng.
B3, bamboo green grass or young crops of pruning.
B4, Meng Zongzhu is soaked 80 minutes in the hot water of 80 DEG C~120 DEG C.
B5, take copper chloride and configure fixation liquid medicine using methanol as solvent, Meng Zongzhu is soaked in this fixation liquid medicine in room
Carry out under temperature reacting 1~5 day.
B6, taking-up Meng Zongzhu dry laggard pedestrian's work vapour seasoning.
B7, Meng Zongzhu carrying out high-temperature low-oxygen carbonization process, described high-temperature low-oxygen carbonization processes and includes: will be through step a6
Meng Zongzhu after process is placed in one and contains in steam vent, fan, the high temperature closed baking oven up to 250 DEG C, first with 40 DEG C, steam vent
Standard-sized sheet, closes steam vent after processing about 20 hours, less to continuing 5~6 after 120 DEG C with per hour 20 DEG C of heating rate homoiothermics
Time, then with per hour 10 DEG C of heating rate homoiothermics to 150 DEG C~180 DEG C, continue 24 hours.
B8, Meng Zongzhu is carried out fixed thick fixed width, carry out jigsaw the most in the direction of the width.
B9, the Meng Zongzhu after jigsaw is planished, and integrated to its thickness direction, thus realize ancestor bamboo in integrated for bamboo Meng
Wing material.
Compared to the prior art, what the present invention produced has the beneficial effects that:
1, present invention process is simple, practical, and by configuring fixation liquid medicine, ancestor bamboo in the Meng only need to be immersed this fixation liquid medicine by user
Inside process, unstable chlorophyll form transformation can become stable green phosphor salt pigment combine organic pigment and group
The complex become, so that it may make it be maintained beautiful green appearance, and this green appearance keeps the most stable, at subsequent high temperature
The operation of reason all will not destroy the molecular structure of above-mentioned complex, thus so that the final square joggle W type bamboo scutum prepared
Material presents natural green form, is greatly enhanced the captivation to consumer, is conducive to improving the surcharge of product, for appropriate
It is apt to utilize bamboo resource, promote the green building of bamboo wood to have active influence.
2, in the present invention, by introducing copper ion as the main component of fixation liquid medicine, when the Meng ancestor bamboo immerse this fixation
In liquid medicine, upper part copper ion can be adsorbed, and final copper ion also will the side's of being stranded in joggle W type bamboo lumber, thus upper
During the side's of stating joggle W type bamboo lumber life-time service, its interior copper ion can suppress moth and antibacterial thereon effectively
Grow, so that the square joggle W type bamboo lumber that the present invention prepares has stronger anti-microbial property, be conducive to improving it
To ability that is anti-insect and that go mouldy.
3, in the present invention, by introducing high-temperature low-oxygen carbonization treatment process, not only material cost is inexpensively, Er Qieke
To reduce bamboo clappers cracking so that it is surface color and texture present preferable states, also are able to further prevent from going mouldy and worm simultaneously
Moth, improves product quality.
4, in the present invention, carry out gluing by dotted line spraying method, be possible not only to play saving glue, reduce environment
The effect polluted, and make the link position of ancestor bamboo abdomen material in the Meng and ancestor bamboo wing material in the Meng can be able to appropriateness buffering, it is to avoid because of length
Phase Exposure to Sunlight and cause link position swelling cracking.
Above are only the detailed description of the invention of the present invention, but the design concept of the present invention is not limited thereto, all utilize this
Design carries out the change of unsubstantiality to the present invention, all should belong to the behavior invading scope.
Claims (5)
1. the preparation method of a square joggle W type bamboo lumber, it is characterised in that comprise the following steps: a, preparation ancestor bamboo abdomen in the Meng
Material;B, preparation ancestor bamboo wing material in the Meng;C, inside Meng ancestor bamboo wing material, place opens the groove inlaying ancestor bamboo abdomen material in above-mentioned Meng together, groove
The degree of depth is 0.8, and width is approximately less than ancestor bamboo abdomen material thickness in the Meng 0.1, and by adhesive coated in groove, moulding pressure is extremely
Hardening, pressurizes more than 8 hours, described step a include following step by step: a1, select ancestor bamboo in fresh Meng and this Meng Zongzhu carried out
Fixed length;A2, along the axial vertical profile of ancestor bamboo in the Meng;A3, bamboo green grass or young crops of pruning;A4, Meng Zongzhu is soaked 80 points in the hot water of 80 DEG C~120 DEG C
Clock;A5, take copper chloride using methanol as solvent configure fixation liquid medicine, at room temperature enter in Meng Zongzhu is soaked in this fixation liquid medicine
Row reaction 1~5 day;A6, taking-up Meng Zongzhu dry laggard pedestrian's work vapour seasoning;A7, Meng Zongzhu is carried out high-temperature low-oxygen carbonization
Process;A8, Meng Zongzhu is carried out fixed thick fixed width, carry out jigsaw the most in the direction of the width;A9, the Meng Zongzhu after jigsaw is carried out
Planing, and integrated to its thickness direction, thus realize ancestor bamboo abdomen material in integrated for bamboo Meng.
The preparation method of a kind of side's joggle W type bamboo lumber the most as claimed in claim 1, it is characterised in that described step b bag
Include following step by step: b1, select ancestor bamboo in fresh Meng and this Meng Zongzhu carried out fixed length;B2, along the axial vertical profile of ancestor bamboo in the Meng;B3, cut
Go bamboo blue or green;B4, Meng Zongzhu is soaked 80 minutes in the hot water of 80 DEG C~120 DEG C;B5, take copper chloride and join as solvent using methanol
Put fixation liquid medicine, at room temperature carry out reacting 1~5 day in Meng Zongzhu is soaked in this fixation liquid medicine;B6, taking-up Meng Zongzhu dry
Laggard pedestrian's work vapour seasoning;B7, Meng Zongzhu is carried out high-temperature low-oxygen carbonization process;B8, Meng Zongzhu is carried out fixed thick fixed width, so
After carry out jigsaw in the direction of the width;B9, the Meng Zongzhu after jigsaw is planished, and integrated to its thickness direction, thus real
Now by ancestor bamboo wing material in integrated for bamboo Meng.
The preparation method of a kind of side's joggle W type bamboo lumber the most as claimed in claim 2, it is characterised in that: in step c,
Binding agent is to be sprayed at described groove with the plural number spaced apart dotted line of bar.
The preparation method of a kind of side's joggle W type bamboo lumber the most as claimed in claim 3, it is characterised in that: in step a7,
Described high-temperature low-oxygen carbonization process include: by through step a6 process after Meng Zongzhu be placed in one containing steam vent, fan, high temperature can
Reach in the closed baking oven of 250 DEG C, first with 40 DEG C, steam vent standard-sized sheet, after processing about 20 hours, close steam vent, then with per hour
20 DEG C of heating rate homoiothermics continue 5~6 hours after 120 DEG C, then with per hour 10 DEG C of heating rate homoiothermics to 150 DEG C~180
DEG C, continue 24 hours.
The preparation method of a kind of side's joggle W type bamboo lumber the most as claimed in claim 4, it is characterised in that: in step b7,
Described high-temperature low-oxygen carbonization process include: by through step b6 process after Meng Zongzhu be placed in one containing steam vent, fan, high temperature can
Reach in the closed baking oven of 250 DEG C, first with 40 DEG C, steam vent standard-sized sheet, after processing about 20 hours, close steam vent, then with per hour
20 DEG C of heating rate homoiothermics continue 5~6 hours after 120 DEG C, then with per hour 10 DEG C of heating rate homoiothermics to 150 DEG C~180
DEG C, continue 24 hours.