CN1348852A - Bamboo comb and its making process

Info

Publication number: CN1348852A
Application number: CN 01130210
Authority: CN
Inventors: 熊晓洪; 熊晓晶
Original assignee: CHONGYI GUIZHU Co Ltd JIANGXI PROV
Current assignee: CHONGYI GUIZHU Co Ltd JIANGXI PROV
Priority date: 2001-11-11
Filing date: 2001-11-11
Publication date: 2002-05-15

Abstract

The present invention discloses bamboo comb using bamboo as raw material and its making method, it is made as follows: the green surface layers and internal layers of bamboo are alternately placed and coated with glue, then pressed to form bamboo single plate, the bamboo single plate and two horizontal bamboo sheets are joggle jointed, coated with glue and pressed to form bamboo comb plate material which is cross cut into four bamboo comb blank plate, then we use conventional method to process to bamboo comb blank plate into bamboo comb product. The invented product is good in elasticity, durable and beautiful.

Description

Bamboo comb and preparation method thereof

The invention discloses a kind of bamboo that with the bamboo is raw material make and comb and preparation method thereof, belong to bamboo product and small stores production technical field.

Sale and people's comb kind used in everyday mainly contain wooden comb, plastic comb, horn comb etc. on the existing market.Wooden comb, plastic comb are very crisp, easy tooth-breaking, and elasticity is relatively poor, and the horn comb cost is higher, the shortage of ox horn source, in addition, wooden comb will spend many wooden timber preferably, unsuitable large-scale production, plastic products can cause certain environmental pollution again.And so far, Shang Weijian has bamboo bamboo comb (Bamboo Comb).

The production cycle of bamboo is shorter, can become a useful person more than 4 years, and only be 1/5th of the wood grows phase.There are ten big bamboo townshiies in China, and bamboo resource is abundant.

Purpose of the present invention is exactly in order to make full use of China's bamboo resource, opens up the new purposes of bamboo, for filling a hole in the market, provides a kind of bamboo comb and preparation method thereof.

The objective of the invention is to be achieved through the following technical solutions.

The preparation method of bamboo comb comprises in the following order step and produces the bamboo monolithic: former bamboo felling

It is characterized in that making and continue in the following order step behind the bamboo monolithic and produce monolithic bamboo comb blanket:

1, with the bamboo strip 1 of monolithic and bamboo sac surface 2 alternate the putting of monolithic, the side brush coating adopts side pressure and malleation to carry out pressing plate simultaneously, and side pressure is 5-10MPa, and normal pressure is 8-12MPa, platen temperature 80-100 ℃, 5-8 minute pressing plate time, makes bamboo veneer 3.

2, open tenon at two ends perpendicular to the bamboo veneer 3 of each monolithic, choose two horizontal bamboo chips 4 simultaneously, and on every horizontal bamboo chip 4, open and make a groove, to tenon and groove applying glue and amalgamation, adopt hot press to be exerted pressure in its side and front then, press time 5-10 minute, press temperature 80-100 ℃, lateral pressure 5-10MPa, normal pressure 5-12MPa makes bamboo pecten material 5.

3, bamboo pecten material 5 is cross and cuts, get the bamboo comb blanket 6 of four monolithics.

Monolithic bamboo combed blanket 6 and make the bamboo comb, include the making comb shape, open broach, polish and wax, make as required true qualities finished product bamboo comb or carbonization finished product bamboo comb or true qualities carbonization parquets finished product bamboo comb by common comb processing technology thereafter.

The invention will be further described below in conjunction with accompanying drawing.

Fig. 1 is monolithic bamboo strip 1 and bamboo sac surface 2 alternate putting, the floor map of the bamboo veneer 3 that obtains after gluing is exerted pressure.

Fig. 2 is the arrangement method schematic diagram of bamboo veneer 3, horizontal bamboo chip 4.

Fig. 3 is the mortise and the fluting schematic diagram of bamboo veneer 3, horizontal bamboo chip 4.

Fig. 4 is to bamboo veneer 3 floor map with the bamboo pecten material 5 that makes after laterally bamboo chip 4 amalgamations are exerted pressure.

Fig. 5 is the schematic diagram that bamboo pecten material 5 is four blocks of veneer bamboo comb blankets 6 that obtain after cross is cut.

Fig. 6 is the schematic diagram of finished product bamboo comb 7.

Adopt bamboo comb (Bamboo Comb) that the inventive method makes because broach and bamboo veneer Bamboo grain direction is consistent, thereby elasticity is fine, and easy tooth-breaking not uses comfortablely, uses brighter and brighter, Production cost is low, and the production efficiency height is conducive to environmental protection, is in great demand, be loved by the people, Very high popularizing value is arranged, wide market prospects are arranged.

Claims

1, the preparation method of a kind of bamboo comb comprises in the following order step and produces the bamboo monolithic: be former

Monolithic is characterized in that: make and continue in the following order step behind the bamboo monolithic and produce monolithic bamboo comb blanket:

(1), with alternate the putting of bamboo sac surface (2) of bamboo strip (1) Yu the monolithic of monolithic, the side brush coating adopts side pressure and malleation to carry out pressing plate simultaneously, lateral pressure is 5-10MPa, and normal pressure is 8-12MPa, platen temperature 80-100 ℃, 5-8 minute pressing plate time, make bamboo veneer (3);

(2), open tenon at two ends perpendicular to the bamboo veneer (3) of each monolithic, choose two horizontal bamboo chips (4) simultaneously, and on every horizontal bamboo chip (4), open and make a groove, to tenon and groove applying glue and amalgamation, adopt hot press to be exerted pressure in its side and front then, press time 5-10 minute, press temperature 80-100 ℃, lateral pressure 5-10MPa, normal pressure 8-12MPa makes bamboo pecten material (5);

(3), bamboo pecten material (5) be cross cut, the bamboo comb blanket (6) of four monolithics;

Monolithic bamboo combed blanket (6) and make the bamboo comb, include the making comb shape, open broach, polish and wax, make as required true qualities finished product bamboo comb or carbonization finished product bamboo comb or true qualities carbonization parquets finished product bamboo comb by common comb processing technology thereafter.

2, a kind of bamboo comb is characterized in that with the bamboo being raw material, adopts the described method of claim 1 to make.