CN106150030A - A kind of double-layer wood floor and manufacture method - Google Patents
A kind of double-layer wood floor and manufacture method Download PDFInfo
- Publication number
- CN106150030A CN106150030A CN201610563725.0A CN201610563725A CN106150030A CN 106150030 A CN106150030 A CN 106150030A CN 201610563725 A CN201610563725 A CN 201610563725A CN 106150030 A CN106150030 A CN 106150030A
- Authority
- CN
- China
- Prior art keywords
- substrate
- groove
- lath
- veneer
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of double-layer wood floor, it is mainly composited by substrate and panel, and have, in four limits making, the tongue and groove installed, described substrate is by the lath of finger, the floor base plate being spliced after gluing in plate joggling apparatus, a surface of described substrate is horizontally arranged with a plurality of groove, and is inlaid with bamboo lath or hardwood strip in the trench, and arranging on fluted substrate surface with the compound thick china being made up of veneer, veneer of glue；Described manufacture method includes: a) raw material is selected and processes；B) finger lath makes；C) making of substrate；D) groove makes；E) parquet strip；F) veneer；It has simple in construction, high temperature resistant, is unlikely to deform, moisture resistant, anti-underground heat, the most easy to crack, be difficult to reflex action, has both possessed the natural sex of solid wooden floor board, comfortableness, ruggedness, has possessed again the features such as multi-layer floor weatherability, stability.
Description
Technical field
The present invention relates to be a kind of double-layer wood floor and manufacture method, belong to building decoration class formation floor skill
Art field.
Background technology
In prior art, the floor kind of building decoration is more, has solid wooden floor board, a bamboo-wood floor, plastic cement etc., and because of
Install and use occasion equal, produce differently plate structure, such as wear-resisting floor wearing floor, high temperature resistant floor etc., and the ground of different structure
The floor that plate or different materials are made, its cost is different, and application scenario is different.The reality for top grade the most generally occurred
Timber floor or Compossite solid-wood floor plate, or the relatively low plastic floor of class etc.；For Compossite solid-wood floor plate be generally three layers with
On sheet material be composited, because the number of plies is many, corresponding fastness is the poorest；And the solid wooden floor board of monolayer is because of waste timber resources, structure
Fastness is good, thus price is high；And using more composite floor board, because of compound effect, it is clear that using effect is not as good as single-layer solid wood
Floor, fastness is poor, of low grade.In prior art, seldom see two layers of compound floor.
Summary of the invention
It is an object of the invention to overcome the deficiency of above-mentioned existence, and a kind of simple in construction is provided, high temperature resistant, the most variable
Shape, moisture resistant, anti-underground heat, the most easy to crack, be difficult to reflex action, both possess the natural sex of solid wooden floor board, comfortableness, ruggedness, had again
For multi-layer floor weatherability, the double-layer wood floor of stability and manufacture method.
It is an object of the invention to complete by following technical solution, a kind of double-layer wood floor, it is mainly by substrate
Being composited with panel, and have, in four limits making, the tongue and groove installed, described substrate is by the lath of finger, at jigsaw
The floor base plate being spliced after gluing in machine, is horizontally arranged with a plurality of groove on a surface of described substrate, the most every 6cm
Place is provided with the expansion joint of 1mm, and is inlaid with bamboo lath or hardwood strip in the trench, and is arranging fluted substrate
With the compound thick china being made up of veneer, veneer of glue on surface.
As preferably: laterally homogeneous on a surface of described substrate be provided with a plurality of groove, and the two ends of every groove are divided
It is not positioned at inside substrate dual-side, and after being compounded with described thick china on this surface of substrate, described groove and interior edge
Do not expose in embedding bamboo lath or hardwood strip are hidden in substrate.
As preferably: laterally homogeneous on a surface of described substrate be provided with a plurality of groove, and the two ends of every groove are divided
The both sides of other through substrate, and after being compounded with described thick china on this surface of substrate, described groove and in inlay
Bamboo lath or hardwood strip are exposed to two avris of substrate.
As preferably: two long sides of described substrate are also shaped with the whole piece avris lath consistent with substrate thickness by glue envelope,
And the thick china both sides width of described substrate surface covers the avris lath on described substrate and two avris.
The manufacture method on a kind of double-layer wood floor as above, described manufacture method comprises the steps:
A) raw material is selected and processes: select carpenter to roll off the production line the weedtree such as waste wood, short timber, concentrates and sends into balance kiln together and do
Dry, control moisture content within 10%；
B) finger lath make: the raw material after dried is sawn into 20mm, 30mm, 40mm, 50mm, 60mm, 70mm or
The lath of 80mm, then the lath finger sub-electing above width become a length of 930mm, 1230mm, 1930mm, 2200mm or
The lath of 2500mm；
C) making of substrate: be up to the lath of standard by being combined into required ground board size with plate joggling apparatus after gluing two-by-two, rule
Lattice are respectively the floor base plate within 910*90mm, 910*125mm, 1210*165mm, 1900*190mm；
D) groove makes: be sawn into by a surface professional equipment of substrate or milling becomes the lateral trench of a plurality of following size:
Width A:3mm, 4mm, 5mm, 6mm, 7mm, 8mm, 9mm or 10mm of groove；
The depth B of groove: 5mm, 6mm, 7mm, 8mm, 9mm, 10mm, 11mm or 12mm；
E) parquet strip: according to the specification needs on width, the degree of depth and the floor of above groove, uses stretching resistance bamboo lath or hardwood
Lath is embedded in described groove；
F) veneer: will after sorting, thickness as veneer dash board, i.e. panel, use glue table at the veneer of 2-6mm or veneer
After topcoating is covered, be compounded in the surface of substrate, by colding pressing, hot pressing, after receipts plate and health preserving described double-layer wood floor.
As preferably: before described step f) veneer, first carry out health preserving process, the floor base plate inlayed and veneer are used
After dash board sorting, uniformly put neatly with standard aluminum alloy parting bead, send into the balance dry health preserving of kiln drying, make floor base plate and veneer use
The moisture content of dash board is within 6-8；
Described step d) groove makes, and is sawn into by a surface professional equipment of substrate or milling becomes a plurality of lateral trench, wherein
Described lateral trench is lateral direction penetrating formula groove or the concealed groove extending in dual-side；
Described step e) parquet strip, after being mounted in the groove of upper surface of base plate by lath, needs before veneer step
Surfacing processing is carried out, with the veneer operation of applicable upper surface at upper surface of base plate.
As preferably: described substrate is after step e) parquet strip, and two long sides of substrate are also fixed with width with glue
Degree not less than the whole piece avris lath of substrate thickness, and hot pressing through both sides, cold pressing after carry out the flatness of substrate surface and repair
Multiple, form the floor base plate of one piece of surfacing；The glue of described coating is environment-friendlyformaldehyde-free formaldehyde-free glue.
Present invention mainly solves internal stress in timber and produce the disaster of the deformation on all floors, warpage and instability
Topic, has simple in construction, high temperature resistant, is unlikely to deform, moisture resistant, anti-underground heat, the most easy to crack, be difficult to reflex action, has both possessed solid wood ground
The natural sex of plate, comfortableness, ruggedness, possessed again the features such as multi-layer floor weatherability, stability.
Accompanying drawing explanation
Fig. 1 is the structural representation of finger lath of the present invention.
Fig. 2 is the structural representation of floor base plate of the present invention.
Fig. 3 is the structural representation of veneer on floor base plate of the present invention.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention will be described in detail: shown in Fig. 3, a kind of double-layer wood ground of the present invention
Plate, it is mainly composited by substrate 1 and thick china 2, and makes according to existing conventional floor on four limits and have the tongue and groove installed,
Described substrate 1 is that the floor base plate being spliced after gluing in plate joggling apparatus, at described substrate by the lath 11 of finger
It is horizontally arranged with a plurality of groove 12 on one surface of 1, at the most every 6cm, is provided with the expansion joint 13 of 1mm, and at described groove 12
In be inlaid with bamboo lath or hardwood strip 3, and compound by veneer, veneer structure with glue on the substrate surface being provided with groove 12
The thick china 2 become.
Laterally homogeneous on one surface of substrate 1 of the present invention it is provided with a plurality of groove 12, and the two ends of every groove 12
Lay respectively at inside substrate 1 dual-side, and after being compounded with described thick china 2 on this surface of substrate 1, described groove 12
Do not expose in the bamboo lath inlayed in and or hardwood strip 3 are hidden in substrate 1, in substrate 1, be i.e. formed with dark filler rod.
Shown in figure is the another kind of bright inlay strip structure form of the present invention, i.e. laterally homogeneous on a surface of described substrate 1
It is provided with a plurality of groove 12, and the both sides of the two ends of every groove 12 through substrate 1 respectively, and multiple on this surface of substrate 1
Close after having described thick china 2, described groove 12 and in the bamboo lath inlayed or hardwood strip 3 be exposed to the both sides of substrate 1
Side.The degree of depth of above-mentioned groove 12 with
Another embodiment of the present invention is on the basis of said structure, improves as follows, i.e. two long sides of described substrate 1
Also it is shaped with the whole piece avris lath with substrate 1 consistency of thickness by glue envelope, and the thick china 2 both sides width on described substrate 1 surface covers
Cover the avris lath on described substrate 1 and two avris.
The manufacture method on a kind of double-layer wood floor as above, described manufacture method comprises the steps:
A) raw material is selected and processes: select carpenter to roll off the production line the weedtree such as waste wood, short timber, concentrates and sends into balance kiln together and (be dried
Kiln) it is dried, control moisture content within 10%；
B) finger lath make: the raw material after dried is sawn into 20mm, 30mm, 40mm, 50mm, 60mm, 70mm or
The lath of 80mm, then the lath finger sub-electing above width become a length of 930mm, 1230mm, 1930mm, 2200mm or
The lath of 2500mm；
C) making of substrate: be up to the lath of standard by being combined into required ground board size with plate joggling apparatus after gluing two-by-two, rule
Lattice are respectively the floor base plate within 910*90mm, 910*125mm, 1210*165mm, 1900*190mm；
D) groove makes: be sawn into by a surface professional equipment of substrate or milling becomes the lateral trench of a plurality of following size:
Width A:3mm, 4mm, 5mm, 6mm, 7mm, 8mm, 9mm or 10mm of groove；
The depth B of groove: 5mm, 6mm, 7mm, 8mm, 9mm, 10mm, 11mm or 12mm；
E) parquet strip: according to the specification needs on width, the degree of depth and the floor of above groove, uses stretching resistance bamboo lath or hardwood
Lath is embedded in described groove；
F) veneer: will after sorting, thickness as veneer dash board, use glue surface-coated at the veneer of 2-6mm or veneer
Afterwards, be compounded in the surface of substrate, by colding pressing, hot pressing, after receipts plate and health preserving described double-layer wood floor.
Before step f) veneer of the present invention, first carry out health preserving process, by the floor base plate inlayed and veneer table
After plate sorting, uniformly put neatly with standard aluminum alloy parting bead, send into the balance dry health preserving of kiln drying, make floor base plate and veneer table
The moisture content of plate is within 6-8；
Described step d) groove makes, and is sawn into by a surface professional equipment of substrate or milling becomes a plurality of lateral trench, wherein
Described lateral trench is lateral direction penetrating formula groove or the concealed groove extending in dual-side；
Described step e) parquet strip, after being mounted in the groove of upper surface of base plate by lath, needs before veneer step
Surfacing processing is carried out, with the veneer operation of applicable upper surface at upper surface of base plate.
Substrate of the present invention is after step e) parquet strip, and two long sides of substrate are also fixed with width not with glue
Less than the whole piece avris lath of substrate thickness, and hot pressing through both sides, cold pressing after carry out the flatness reparation of substrate surface, shape
Become the floor base plate of one piece of surfacing；The glue of described coating is environment-friendlyformaldehyde-free formaldehyde-free glue.
Claims (7)
1. a double-layer wood floor, it is mainly composited by substrate and panel, and makes on four limits and have the tongue and groove installed,
It is characterized in that described substrate is by the lath of finger, the floor base plate being spliced after gluing in plate joggling apparatus,
It is horizontally arranged with a plurality of groove on one surface of described substrate, at the most every 6cm, is provided with the expansion joint of 1mm, and at described ditch
Groove is inlaid with bamboo lath or hardwood strip, and compound by veneer, veneer structure with glue arranging on fluted substrate surface
The thick china become.
Double-layer wood floor the most according to claim 1, it is characterised in that laterally homogeneous on a surface of described substrate set
It is equipped with a plurality of groove, and the two ends of every groove lay respectively at inside substrate dual-side, and be compounded with on this surface of substrate
After described thick china, described groove and in the bamboo lath inlayed or hardwood strip be hidden in substrate in and do not expose.
Double-layer wood floor the most according to claim 1, it is characterised in that laterally homogeneous on a surface of described substrate set
It is equipped with a plurality of groove, and the both sides of the two ends of every groove through substrate respectively, and is compounded with described on this surface of substrate
Thick china after, described groove and in the bamboo lath inlayed or hardwood strip be exposed to two avris of substrate.
4. according to the double-layer wood floor described in claim 1 or 2 or 3, it is characterised in that two long sides of described substrate are also used
Glue envelope is shaped with the whole piece avris lath consistent with substrate thickness, and the thick china both sides width of described substrate surface covers described base
Avris lath on plate and two avris.
5. the manufacture method on a double-layer wood floor as claimed in claim 1 or 2 or 3 or 4, it is characterised in that described system
Comprise the steps: as method
A) raw material is selected and processes: select carpenter to roll off the production line the weedtree such as waste wood, short timber, concentrates and sends into balance kiln together and do
Dry, control moisture content within 10%；
B) finger lath make: the raw material after dried is sawn into 20mm, 30mm, 40mm, 50mm, 60mm, 70mm or
The lath of 80mm, then the lath finger sub-electing above width become a length of 930mm, 1230mm, 1930mm, 2200mm or
The lath of 2500mm；
C) making of substrate: be up to the lath of standard by being combined into required ground board size with plate joggling apparatus after gluing two-by-two, rule
Lattice are respectively the floor base plate within 910*90mm, 910*125mm, 1210*165mm, 1900*190mm；
D) groove makes: be sawn into by a surface professional equipment of substrate or milling becomes the lateral trench of a plurality of following size:
Width A:3mm, 4mm, 5mm, 6mm, 7mm, 8mm, 9mm or 10mm of groove；
The depth B of groove: 5mm, 6mm, 7mm, 8mm, 9mm, 10mm, 11mm or 12mm；
E) parquet strip: according to the specification needs on width, the degree of depth and the floor of above groove, uses stretching resistance bamboo lath or hardwood
Lath is embedded in described groove；
F) veneer: will after sorting, thickness as veneer dash board, use glue surface-coated at the veneer of 2-6mm or veneer
Afterwards, be compounded in the surface of substrate, by colding pressing, hot pressing, after receipts plate and health preserving described double-layer wood floor.
The manufacture method on double-layer wood floor the most according to claim 5, it is characterised in that before described step f) veneer,
First carry out health preserving process, after the floor base plate inlayed and veneer dash board are sorted, uniformly put with standard aluminum alloy parting bead
Neatly, send into the balance dry health preserving of kiln drying, make the moisture content of floor base plate and veneer dash board within 6-8；
Described step d) groove makes, and is sawn into by a surface professional equipment of substrate or milling becomes a plurality of lateral trench, wherein
Described lateral trench is lateral direction penetrating formula groove or the concealed groove extending in dual-side；
Described step e) parquet strip, after being mounted in the groove of upper surface of base plate by lath, needs before veneer step
Surfacing processing is carried out, with the veneer operation of applicable upper surface at upper surface of base plate.
The manufacture method on double-layer wood floor the most according to claim 6, it is characterised in that described substrate is in step e)
After parquet strip, two long sides of substrate are also fixed with the width whole piece avris lath not less than substrate thickness, and warp with glue
Cross both sides hot pressing, cold pressing after carry out the flatness reparation of substrate surface, form the floor base plate of one piece of surfacing；Described
The glue of coating is environment-friendlyformaldehyde-free formaldehyde-free glue.