CN106147478A - 一种用于外墙的隔热保温仿石漆及其制备方法 - Google Patents
一种用于外墙的隔热保温仿石漆及其制备方法 Download PDFInfo
- Publication number
- CN106147478A CN106147478A CN201610524947.1A CN201610524947A CN106147478A CN 106147478 A CN106147478 A CN 106147478A CN 201610524947 A CN201610524947 A CN 201610524947A CN 106147478 A CN106147478 A CN 106147478A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- reflection
- agent
- insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种用于外墙的隔热保温仿石漆，其按重量份的组分为：去离子水5‑9份、纤维素增稠剂0.1‑0.2份、矿物油消泡剂0.05‑0.15份、润湿剂0.05‑0.15份、丙二醇0.05‑0.15份、纳米银抗菌剂0.1‑0.5份、硅氧烷防水剂0.3‑0.7份、十二醇酯0.05‑0.15份、纳米TiO2光触媒胶体2‑6份、纳米二氧化锆分散体1‑3份、硅丙乳液10‑14份、聚氨酯改性弹性乳液2‑5份、无机硅酸钾1‑5份、PU增稠剂2‑5份、反射型烧结彩色石英砂45‑55份、反射型烧结彩色陶瓷空心微球10‑20份。本发明具有逼真的仿天然石材效果，高效的近红外线反射性能，隔热性好、色彩丰富、自洁性好、隔热性持久、防水性好、抗裂性好、重量轻、涂层寿命长、适用性广，具有极好的经济性。
Description
技术领域
本发明涉及一种漆，具体是一种用于外墙的隔热保温仿石漆及其制备方法。
背景技术
隔热仿石漆(也称隔热真石漆)是近年来流行的一种新型高档节能材料，属厚浆型产品，采用喷涂或批刮施工工艺，达到天然真石材逼真的效果。适用于不用的基面和造型，用途十分广泛，既符合国家节能标准要求，又符合环保、安全，装饰效果强，性价比极高，在外墙装饰中呈快速上升的趋势。而传统隔热真石漆一般采用普通真石漆中添加陶瓷空心微珠等低导热系数轻质材料作为隔热填料，涂层具有一定的隔热效果，但必须配合其他保温板或保温层或在施工完的真石漆面上施工一层半透明反射隔热功能的涂料，本质是通过底层保温层或面层隔热漆达到效果。传统产品中通过陶瓷空心微珠的加入量来降低导热系数，加入量大，隔热效果会明显，但会影响颜色的展色性，只适合选择白色或浅色。普遍彩砂采用的天然彩砂或人工染色砂或烧结彩砂不具备红外线反射功能，会吸收大部分的红外线，反而影响隔热效果。为达到隔热效果，很多彩色无法选择，真石漆表面本身是粗糙面，又极易受外界污染，从而影响隔热寿命。
发明内容
本发明的目的在于提供一种用于外墙的隔热保温仿石漆，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种用于外墙的隔热保温仿石漆，其按重量份的组分为：去离子水5-9份、纤维素增稠剂0.1-0.2份、矿物油消泡剂0.05-0.15份、润湿剂0.05-0.15份、丙二醇0.05-0.15份、纳米银抗菌剂0.1-0.5份、硅氧烷防水剂0.3-0.7份、十二醇酯0.05-0.15份、纳米TiO2光触媒胶体2-6份、纳米二氧化锆分散体1-3份、硅丙乳液10-14份、聚氨酯改性弹性乳液2-5份、无机硅酸钾1-5份、PU增稠剂2-5份、反射型烧结彩色石英砂45-55份、反射型烧结彩色陶瓷空心微球10-20份。
作为本发明进一步的方案：其按重量份的组分优选为：去离子水7份、纤维素增稠剂0.15份、矿物油消泡剂0.1份、润湿剂0.1份、丙二醇1份、纳米银抗菌剂0.3份、硅氧烷防水剂0.5份、十二醇酯1份、纳米TiO2光触媒胶体4份、纳米二氧化锆分散体2份、硅丙乳液12份、聚氨酯改性弹性乳液3.5份、无机硅酸钾3份、PU增稠剂0.35份、反射型烧结彩色石英砂50份、反射型烧结彩色陶瓷空心微球15份。
作为本发明进一步的方案：所述反射型烧结彩色石英砂的粒径为40-80目。
作为本发明进一步的方案：所述反射型烧结彩色陶瓷空心微球的粒径为80-150目。
作为本发明再进一步的方案：用于外墙的隔热保温仿石漆的制备方法，其具体步骤如下：
(1)浆料制备：先投下去离子水到分散缸中，将分散机调至800-1000转/分，然后投下纤维素增稠剂，溶解分散4-6分钟，再依次投下消泡剂、润湿剂、丙二醇、纳米银抗菌剂、硅氧烷防水剂和十二醇酯，分散均匀12-16分钟后，再依次投下纳米Tio2光触媒胶体和纳米二氧化锆分散体，分散均匀4-6分钟后，投下硅丙乳液、聚氨酯改性弹性乳液、无机硅酸钾和PU增稠剂，分散14-16分钟至均匀状态，检验合格后进行下道工序。
(2)调漆制备：将合格的浆料投入卧式搅拌机中，根据颜色和质感的要求加入不同粒径的反射型烧结彩色石英砂和反射型烧结彩色陶瓷空心微球，搅拌均匀14-16分钟后，检测粘度、施工性以及外观指标。
与现有技术相比，本发明的有益效果是：
1、高效近红外线反射：产品引进高反射型烧结彩色石英砂、反射型烧结彩色陶瓷空心微球，并引进透明纳米二氧化锆分散体，红外线反射高达92％以上。
2、色彩丰富：反射型烧结彩色石英砂、反射型烧结彩色陶瓷空心微球，是采用高耐候高反射颜料、无机粘合剂，通过高温煅烧结方式，将颜色固定在石英砂、陶瓷空心微球面上，达到既能反射红外线又能隔热，并能提供丰富的色彩选择，避免天然彩砂颜色不丰富的局限性，并且吸收红外线缺点。
3、隔热性能好：引进高反射彩色陶瓷空心微球，精选不同粒径微球的复合，涂层极低导热系数，低于0.04w/m·k，对热的反射性、阻隔热性非常明显。
4、涂层自洁性优异：引进纳米Tio2光触媒胶体，利用光触媒净化环境技术，经紫外线照射后产生的“分解力”及“亲水性”两者作用下产生自洁效果，经污染10次后太阳光反射的变化率小于10％，长期保持涂层干净，不受外界污染，色彩明度不会下降，从而长期保持热反射效果。
5、防水性好：引进硅氧烷防水剂，采用无机和有机复合技术，涂层具有优异的防水性能、抗开裂性。
6、质量轻：引进反射型彩色陶瓷空心微球，涂层质量轻，只有普通真石漆的2/3，减少建筑物的重量，减少安全隐患。
7、隔热持久性优异：人工老化1200h后，太阳光反射比变化率小于5％。
8、装饰性好：色彩丰富，具有逼真的仿天然石材效果，通过喷涂或批刮方式，能创造出客户喜欢的仿石效果。
9、经济性好：施工到合适的厚度可以取代保温板及其他隔热材料，提高施工进度。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明实施例中，一种用于外墙的隔热保温仿石漆，其按重量份的组分为：去离子水5份、纤维素增稠剂0.1份、矿物油消泡剂0.05份、润湿剂0.05份、丙二醇0.05份、纳米银抗菌剂0.1份、硅氧烷防水剂0.3份、十二醇酯0.05份、纳米TiO2光触媒胶体2份、纳米二氧化锆分散体1份、硅丙乳液10份、聚氨酯改性弹性乳液2份、无机硅酸钾1份、PU增稠剂2份、反射型烧结彩色石英砂45份、反射型烧结彩色陶瓷空心微球10份。
所述反射型烧结彩色石英砂的粒径为40目。
所述反射型烧结彩色陶瓷空心微球的粒径为80目。
用于外墙的隔热保温仿石漆的制备方法：
(1)浆料制备：先投下去离子水到分散缸中，将分散机调至800转/分，然后投下纤维素增稠剂，溶解分散4分钟，再依次投下消泡剂、润湿剂、丙二醇、纳米银抗菌剂、硅氧烷防水剂和十二醇酯，分散均匀12分钟后，再依次投下纳米Tio2光触媒胶体和纳米二氧化锆分散体，分散均匀4分钟后，投下硅丙乳液、聚氨酯改性弹性乳液、无机硅酸钾和PU增稠剂，分散14分钟至均匀状态，检验合格后进行下道工序。
(2)调漆制备：将合格的浆料投入卧式搅拌机中，根据颜色和质感的要求加入不同粒径的反射型烧结彩色石英砂和反射型烧结彩色陶瓷空心微球，搅拌均匀14分钟后，检测粘度、施工性以及外观指标。
实施例2
本发明实施例中，一种用于外墙的隔热保温仿石漆，其按重量份的组分为：去离子水7份、纤维素增稠剂0.15份、矿物油消泡剂0.1份、润湿剂0.1份、丙二醇1份、纳米银抗菌剂0.3份、硅氧烷防水剂0.5份、十二醇酯1份、纳米TiO2光触媒胶体4份、纳米二氧化锆分散体2份、硅丙乳液12份、聚氨酯改性弹性乳液3.5份、无机硅酸钾3份、PU增稠剂0.35份、反射型烧结彩色石英砂50份、反射型烧结彩色陶瓷空心微球15份。
所述反射型烧结彩色石英砂的粒径为60目。
所述反射型烧结彩色陶瓷空心微球的粒径为115目。
用于外墙的隔热保温仿石漆的制备方法：
(1)浆料制备：先投下去离子水到分散缸中，将分散机调至900转/分，然后投下纤维素增稠剂，溶解分散5分钟，再依次投下消泡剂、润湿剂、丙二醇、纳米银抗菌剂、硅氧烷防水剂和十二醇酯，分散均匀14分钟后，再依次投下纳米Tio2光触媒胶体和纳米二氧化锆分散体，分散均匀5分钟后，投下硅丙乳液、聚氨酯改性弹性乳液、无机硅酸钾和PU增稠剂，分散15分钟至均匀状态，检验合格后进行下道工序。
(2)调漆制备：将合格的浆料投入卧式搅拌机中，根据颜色和质感的要求加入不同粒径的反射型烧结彩色石英砂和反射型烧结彩色陶瓷空心微球，搅拌均匀15分钟后，检测粘度、施工性以及外观指标。
实施例3
本发明实施例中，一种用于外墙的隔热保温仿石漆，其按重量份的组分为：去离子水9份、纤维素增稠剂0.2份、矿物油消泡剂0.15份、润湿剂0.15份、丙二醇0.15份、纳米银抗菌剂0.5份、硅氧烷防水剂0.7份、十二醇酯0.15份、纳米TiO2光触媒胶体6份、纳米二氧化锆分散体3份、硅丙乳液14份、聚氨酯改性弹性乳液5份、无机硅酸钾5份、PU增稠剂5份、反射型烧结彩色石英砂55份、反射型烧结彩色陶瓷空心微球20份。
所述反射型烧结彩色石英砂的粒径为80目。
所述反射型烧结彩色陶瓷空心微球的粒径为150目。
用于外墙的隔热保温仿石漆的制备方法：
(1)浆料制备：先投下去离子水到分散缸中，将分散机调至1000转/分，然后投下纤维素增稠剂，溶解分散6分钟，再依次投下消泡剂、润湿剂、丙二醇、纳米银抗菌剂、硅氧烷防水剂和十二醇酯，分散均匀16分钟后，再依次投下纳米Tio2光触媒胶体和纳米二氧化锆分散体，分散均匀6分钟后，投下硅丙乳液、聚氨酯改性弹性乳液、无机硅酸钾和PU增稠剂，分散16分钟至均匀状态，检验合格后进行下道工序。
(2)调漆制备：将合格的浆料投入卧式搅拌机中，根据颜色和质感的要求加入不同粒径的反射型烧结彩色石英砂和反射型烧结彩色陶瓷空心微球，搅拌均匀16分钟后，检测粘度、施工性以及外观指标。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (5)
1.一种用于外墙的隔热保温仿石漆，其特征在于，其按重量份的组分为：去离子水5-9份、纤维素增稠剂0.1-0.2份、矿物油消泡剂0.05-0.15份、润湿剂0.05-0.15份、丙二醇0.05-0.15份、纳米银抗菌剂0.1-0.5份、硅氧烷防水剂0.3-0.7份、十二醇酯0.05-0.15份、纳米TiO2光触媒胶体2-6份、纳米二氧化锆分散体1-3份、硅丙乳液10-14份、聚氨酯改性弹性乳液2-5份、无机硅酸钾1-5份、PU增稠剂2-5份、反射型烧结彩色石英砂45-55份、反射型烧结彩色陶瓷空心微球10-20份。
2.根据权利要求1所述的一种用于外墙的隔热保温仿石漆，其特征在于，其按重量份的组分为：去离子水7份、纤维素增稠剂0.15份、矿物油消泡剂0.1份、润湿剂0.1份、丙二醇1份、纳米银抗菌剂0.3份、硅氧烷防水剂0.5份、十二醇酯1份、纳米TiO2光触媒胶体4份、纳米二氧化锆分散体2份、硅丙乳液12份、聚氨酯改性弹性乳液3.5份、无机硅酸钾3份、PU增稠剂0.35份、反射型烧结彩色石英砂50份、反射型烧结彩色陶瓷空心微球15份。
3.一种如权利要求1-2任一所述的用于外墙的隔热保温仿石漆的制备方法，其特征在于，其具体步骤如下：
(1)浆料制备：先投下去离子水到分散缸中，将分散机调至800-1000转/分，然后投下纤维素增稠剂，溶解分散4-6分钟，再依次投下消泡剂、润湿剂、丙二醇、纳米银抗菌剂、硅氧烷防水剂和十二醇酯，分散均匀12-16分钟后，再依次投下纳米Tio2光触媒胶体和纳米二氧化锆分散体，分散均匀4-6分钟后，投下硅丙乳液、聚氨酯改性弹性乳液、无机硅酸钾和PU增稠剂，分散14-16分钟至均匀状态，检验合格后进行下道工序。
(2)调漆制备：将合格的浆料投入卧式搅拌机中，根据颜色和质感的要求加入不同粒径的反射型烧结彩色石英砂和反射型烧结彩色陶瓷空心微球，搅拌均匀14-16分钟后，检测粘度、施工性以及外观指标。
4.根据权利要求1所述的一种用于外墙的隔热保温仿石漆，其特征在于，所述反射型烧结彩色石英砂的粒径为40-80目。
5.根据权利要求1所述的一种用于外墙的隔热保温仿石漆，其特征在于，所述反射型烧结彩色陶瓷空心微球的粒径为80-150目。