CN106145797A - 一种混凝土水泥砂浆及其制备方法 - Google Patents
一种混凝土水泥砂浆及其制备方法 Download PDFInfo
- Publication number
- CN106145797A CN106145797A CN201610511230.3A CN201610511230A CN106145797A CN 106145797 A CN106145797 A CN 106145797A CN 201610511230 A CN201610511230 A CN 201610511230A CN 106145797 A CN106145797 A CN 106145797A
- Authority
- CN
- China
- Prior art keywords
- cement mortar
- water
- cement
- titanium dioxide
- sodium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种混凝土水泥砂浆,其配比如下:水泥28‑32%、石英砂15‑20%、滑石粉12‑14%、乙烯‑醋酸乙烯共聚乳液13‑15%、有机硅聚醚消泡剂0.1‑0.2%、聚羧酸减水剂1.2‑1.5%、钛白粉1‑1.5%、碳酸钠0.15‑0.2%、聚丙烯纤维0.2‑0.3%、余量为水;该混凝土水泥砂浆的制备方法为:将乙烯‑醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合8‑12min,得混凝土水泥砂浆。本发明制备工艺简单,制得的聚合物水泥砂浆适用于钢筋混凝土结构的修复;通过水泥与其他原料的配伍,可以显著提高聚合物水泥砂浆的水化速率,从而提高其早期强度,缩短工程工期。
Description
技术领域
本发明属于建筑材料技术领域,涉及一种混凝土水泥砂浆及其制备方法,具有早强及施工作业时间短的特点。
背景技术
聚合物水泥砂浆是由水泥、骨料和可以分散在水中的有机聚合物搅拌而成的。聚合物可以是有一种单体聚合而成的均聚物,也可以由两种或更多的单聚体聚合而成的共聚物。聚合物必须在环境条件下成膜覆盖在水泥颗粒子上,并使水泥机体与骨料形成强有力的粘接。聚合物网络必须具有阻止微裂缝发生的能力,而且能阻止裂缝的扩展。
聚合物水泥砂浆作为一种广泛应用的水泥基修复材料,具有保水性好、与原有基层的黏结力强、抗弯拉强度高等特点,较为广泛的应用于混凝土结构的修复领域。但是聚合物砂浆存在着凝结时间长、早期粘结强度低、早期抗折强度低等问题,如授权公告号CN101580369B公开的一种混凝土结构修补用纤维增强高强砂浆。针对这些问题,必须采取有效的方式提高聚合物水泥砂浆的水化速率、早期粘结强度、早期抗折强度等,尤其是提高聚合物水泥砂浆的力学和耐久性能,不仅有利于工期的缩短和快速抢修工程的进行,也有利于聚合物修复砂浆工程质量的改善。
发明内容
本发明的目的在于提供一种具有早强及施工作业时间短特点的混凝土水泥砂浆及其制备方法。
本发明的目的可以通过以下技术方案实现:
一种混凝土水泥砂浆,所述的水泥砂浆组分及质量分数配比如下:水泥28-32%、石英砂15-20%、滑石粉12-14%、乙烯-醋酸乙烯共聚乳液13-15%、有机硅聚醚消泡剂0.1-0.2%、聚羧酸减水剂1.2-1.5%、钛白粉1-1.5%、碳酸钠0.15-0.2%、聚丙烯纤维0.2-0.3%、余量为水。
一种制备混凝土快速修复用聚合物水泥砂浆的方法,该方法包括以下步骤:
(1)将乙烯-醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;
(2)将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合8-12min,得混凝土水泥砂浆。
本发明的有益效果:本发明制备工艺简单,制得的聚合物水泥砂浆适用于钢筋混凝土结构的修复;通过水泥与其他原料的配伍,可以显著提高聚合物水泥砂浆的水化速率,从而提高其早期强度,缩短工程工期;
本发明利用碳酸钠可调节聚合物水泥砂浆的凝结时间;钛白粉可以明显提高聚合物水泥砂浆与旧混凝土的粘结强度;聚丙烯纤维可显著降低聚合物水泥砂浆的收缩率和增加其抗折强度;乳液可显著提高其低温环境下的力学和耐久性能。
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。
实施例1
一种混凝土水泥砂浆,水泥砂浆组分及质量分数配比如下:水泥30%、石英砂18%、滑石粉13%、乙烯-醋酸乙烯共聚乳液14%、有机硅聚醚消泡剂0.15%、聚羧酸减水剂1.3%、钛白粉1.3%、碳酸钠0.18%、聚丙烯纤维0.5%、余量为水。
(1)将乙烯-醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;
(2)将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合10min,得混凝土水泥砂浆。
上述制备工艺简单,制得的聚合物水泥砂浆适用于钢筋混凝土结构的修复;
通过水泥与其他原料的配伍,可以显著提高聚合物水泥砂浆的水化速率,从而提高其早期强度,缩短工程工期;
碳酸钠可调节聚合物水泥砂浆的凝结时间;
钛白粉可以明显提高聚合物水泥砂浆与旧混凝土的粘结强度;
聚丙烯纤维可显著降低聚合物水泥砂浆的收缩率和增加其抗折强度;
乳液可显著提高其低温环境下的力学和耐久性能。
实施例2
一种混凝土水泥砂浆,水泥砂浆组分及质量分数配比如下:水泥32%、石英砂15%、滑石粉14%、乙烯-醋酸乙烯共聚乳液13%、有机硅聚醚消泡剂0.2%、聚羧酸减水剂1.2%、钛白粉1.5%、碳酸钠0.15%、聚丙烯纤维0.3%、余量为水。
(1)将乙烯-醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;
(2)将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合3min,得混凝土水泥砂浆。
实施例3
一种混凝土水泥砂浆,水泥砂浆组分及质量分数配比如下:水泥28%、石英砂20%、滑石粉12%、乙烯-醋酸乙烯共聚乳液15%、有机硅聚醚消泡剂0.1%、聚羧酸减水剂1.5%、钛白粉1%、碳酸钠0.2%、聚丙烯纤维0.2%、余量为水。
(1)将乙烯-醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;
(2)将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合5min,得混凝土水泥砂浆。
以上内容仅仅是对本发明所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
Claims (2)
1.一种混凝土水泥砂浆,其特征在于,所述的水泥砂浆组分及质量分数配比如下:水泥28-32%、石英砂15-20%、滑石粉12-14%、乙烯-醋酸乙烯共聚乳液13-15%、有机硅聚醚消泡剂0.1-0.2%、聚羧酸减水剂1.2-1.5%、钛白粉1-1.5%、碳酸钠0.15-0.2%、聚丙烯纤维0.2-0.3%、余量为水。
2.一种制备如权利要求1所述混凝土水泥砂浆的方法,其特征在于,该方法包括以下步骤:
(1)将乙烯-醋酸乙烯共聚乳液、有机硅聚醚消泡剂和水按照配比搅拌混合均匀,得混合物待用;
(2)将水泥、石英砂、滑石粉、聚羧酸减水剂、钛白粉、碳酸钠、聚丙烯纤维与上述所得混合物一起拌合8-12min,得混凝土水泥砂浆。