CN106121182A - A kind of high intensity solid wooden floor board and preparation method thereof - Google Patents
A kind of high intensity solid wooden floor board and preparation method thereof Download PDFInfo
- Publication number
- CN106121182A CN106121182A CN201610601692.4A CN201610601692A CN106121182A CN 106121182 A CN106121182 A CN 106121182A CN 201610601692 A CN201610601692 A CN 201610601692A CN 106121182 A CN106121182 A CN 106121182A
- Authority
- CN
- China
- Prior art keywords
- substrate
- rotary
- high intensity
- floor board
- wooden floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of high intensity solid wooden floor board, including substrate, it is separately positioned on two marine glue mucosas of the top and bottom of substrate, is separately positioned on the two marine glue mucosas, the two rotary-cut veneer away from the two sides of substrate, and is separately positioned on the two rotary-cut veneer, the two wear-resisting wood grain layers away from the two sides of substrate；Substrate is deep charring plank, and the grain direction of two rotary-cut veneer and substrate all staggers setting.The present invention, with deep charring plank as substrate, is respectively arranged rotary-cut veneer to both sides, and the grain direction of rotary-cut veneer staggers with the grain direction of substrate, and Direction of fibre distribution staggers, and effectively prevent the craze and transfiguration of substrate.Additionally, present invention also offers the manufacture method of above-mentioned high intensity solid wooden floor board.
Description
Technical field
The present invention relates to solid wooden floor board technical field, particularly to a kind of high intensity solid wooden floor board.
Background technology
At present, existing solid wooden floor board surface makes to paint front cover, benzene homologues can be caused to play, affect health, and
Due to dysplasia, yielding arch camber cracking and the moisture absorption such as are gone mouldy at the series of problems, and maintaining is relatively costly.
Summary of the invention
It is an object of the invention to provide a kind of high intensity solid wooden floor board, solve in above-mentioned technical problem or many
Individual.
On the one hand, the invention provides a kind of high intensity solid wooden floor board, including substrate；Two marine glue mucosas, are respectively provided with
Top and bottom at substrate；Two rotary-cut veneer, are separately positioned on the two marine glue mucosas two sides away from substrate；And two wear-resisting wood grains
Layer, be separately positioned on the two rotary-cut veneer two sides away from substrate；Substrate is deep charring plank, two rotary-cut veneer and the stricture of vagina of substrate
All stagger setting in reason direction.
The invention provides a kind of high intensity solid wooden floor board, with deep charring plank as substrate, be respectively arranged rotation to both sides
Cutting veneer, the grain direction of rotary-cut veneer staggers with the grain direction of substrate, and Direction of fibre distribution staggers, and effectively prevent substrate
Craze and transfiguration.
The present invention is with deep charring plank as substrate, and deep charring wood is in intercepting the oxidation environment with hydrolysis,
At a temperature of 185 DEG C～255 DEG C, timber is carried out the timber of short-term pyrolysis modification.Have antiseptic insect-repelling, do not stick up do not split, chi
Very little stable feature.
In some embodiments, two rotary-cut veneer are all vertically arranged with substrate grain direction.
On the other hand, the present invention provides the manufacture method of a kind of high intensity solid wooden floor board, comprises the steps:
S1, making deep charring plank, two marine glue mucosas, two rotary-cut veneer, two wear-resisting wood grain layers；
S2, from top to bottom, with a wear-resisting wood grain layer, a rotary-cut veneer, a marine glue mucosa, deep charring plank, another
High intensity solid wooden floor board is made in marine glue mucosa, another rotary-cut veneer, the order arrangement hot pressing of another wear-resisting wood grain layer；
In S2, the grain direction of two rotary-cut veneer and substrate all staggers setting.
In some embodiments, in S2, the grain direction of two rotary-cut veneer and substrate is all vertically arranged.
In some embodiments, in S1, the manufacture method of deep charring plank sequentially comprises the steps:
S1.a1, flitch is placed in 185 DEG C～255 DEG C anaerobic isoperibol process to complete carbonization, make carbonized wood
Side；
S1.a2, the thickness extremely needed by carbonization flitch plane, tooth punching is butted into strip, and after S4S, gluing split is plate
Body, sanding is smooth, saws Qi Sibian.
In some embodiments, in S1, the manufacture method of marine glue mucosa sequentially comprises the steps: mass fraction
Be 4% waterproofing agent, the dispersant of 1%, the formaldehyde catching agent of 1%, 94% melamine resin adehsive mixing and stirring after,
Uniformly gluing is in abrasion-proof paper, surface drying, makes marine glue mucosa.
In some embodiments, the manufacture method of wear-resisting wood grain layer comprises the steps:
S1.b1, anion powder by weight fraction is 3%, the titanium dioxide powder of 4%, the nano-silica powder of 1%,
The dispersant of 2%, the melamine resin adehsive mix homogeneously of 90%, make compound adhesive；
S1.b2, by wear-resisting woodgrained paper immerse compound adhesive, take out, film surface sprays aluminium sesquioxide after drying, prepare leaching
Stain top layer film.
In some embodiments, in S2, hot pressing temperature is 120 DEG C～230 DEG C.
Accompanying drawing explanation
Fig. 1 is the structural representation of a kind of embodiment that the invention provides a kind of high intensity solid wooden floor board.
Detailed description of the invention
Below in conjunction with Figure of description, the present invention is described in more detail.
As shown in Figure 1, on the one hand, the invention provides a kind of high intensity solid wooden floor board, including substrate 1；
Two marine glue mucosas 2, are separately positioned on the top and bottom of substrate 1；
Two rotary-cut veneer 3, are separately positioned on the two marine glue mucosas 2 two sides away from substrate 1；And
Two wear-resisting wood grain layers 4, it is separately positioned on the two rotary-cut veneer 3 two sides away from substrate 1；
Substrate 1 is deep charring plank, and the grain direction of two rotary-cut veneer 3 and substrate 1 all staggers setting.
The invention provides a kind of high intensity solid wooden floor board, with deep charring plank for substrate 1, be respectively arranged rotation to both sides
Cutting veneer 3, the grain direction of rotary-cut veneer 3 staggers with the grain direction of substrate 1, and Direction of fibre distribution staggers, and effectively prevent
The craze and transfiguration of substrate 1.
The present invention is with deep charring plank for substrate 1.Deep charring wood is in intercepting the oxidation environment with hydrolysis,
At a temperature of 185 DEG C～255 DEG C, timber is carried out the timber of short-term pyrolysis modification.Have antiseptic insect-repelling, do not stick up do not split, chi
Very little stable feature.
Further, two rotary-cut veneer 3 are all vertically arranged with substrate 1 grain direction.
On the other hand, the invention provides the manufacture method of above-mentioned a kind of high intensity solid wooden floor board, comprise the steps:
S1, making deep charring plank, the two wear-resisting wood grain layers 4 of marine glue mucosa 2, two rotary-cut veneer 3, two；
S2, from top to bottom, with wear-resisting wood grain layer 4, rotary-cut veneer 3, marine glue mucosa 2, deep charring plank, another
High intensity solid wooden floor board is made in one marine glue mucosa 2, another rotary-cut veneer 3, the order arrangement hot pressing of another wear-resisting wood grain layer 4；
In S2, the grain direction of two rotary-cut veneer 3 and substrate 1 all staggers setting.
The manufacture method of the above-mentioned high intensity solid wooden floor board that the present invention provides.
Wherein, described S1 makes deep charring plank, the two wear-resisting wood grain layers 4 of marine glue mucosa 2, two rotary-cut veneer 3, two
Step in no particular order.
Further, in S2, the grain direction of two rotary-cut veneer 3 and substrate 1 is all vertically arranged.
Farthest prevent the craze and transfiguration of substrate 1.
Wherein, in S1, the manufacture method of deep charring plank sequentially comprises the steps:
S1.a1, flitch is placed in 185 DEG C～255 DEG C anaerobic isoperibol process to complete carbonization, make carbonized wood
Side；
S1.a2, the thickness extremely needed by carbonization flitch plane, tooth punching is butted into strip, and after S4S, gluing split is plate
Body, sanding is smooth, saws Qi Sibian.
During gluing split, it is preferred to use double-component isocyanate glue.There is the function of environmental protection.
Wherein, in S1 the manufacture method of marine glue mucosa 2 sequentially comprise the steps: by mass fraction be 4% waterproof
Agent, the dispersant of 1%, the formaldehyde catching agent of 1%, 94% melamine resin adehsive mixing and stirring after, uniform gluing in
Abrasion-proof paper, surface drying, make marine glue mucosa.Above-mentioned mass fraction refers to that each raw materials quality accounts for the percentage ratio of total raw material quality.
Wherein, the manufacture method of wear-resisting wood grain layer 4 comprises the steps:
S1.b1, anion powder by weight fraction is 3%, the titanium dioxide powder of 4%, the nano-silica powder of 1%,
The dispersant of 2%, the melamine resin adehsive mix homogeneously of 90%, make compound adhesive；
S1.b2, by wear-resisting woodgrained paper immerse compound adhesive, take out, film surface sprays aluminium sesquioxide after drying, prepare leaching
Stain top layer film.
The thickness preferably spraying aluminium sesquioxide is 0.2mm.
Wherein, in S2, hot pressing temperature is 120 DEG C～230 DEG C.
Waterproofing agent in the present invention can select fat with aluminium salt water-repellent or silicone waterproofing agent, dispersant
Acids, aliphatic amide type, esters, the metallic salt of higher fatty acids.
Wear-resisting woodgrained paper in the present invention includes half wear-resisting woodgrained paper.
The optimal way being only the present invention presented above, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, it is also possible to making some deformation and improvement, these also should be regarded as the protection of the present invention
Within the scope of.
Claims (8)
1. a high intensity solid wooden floor board, it is characterised in that include
Substrate (1)；
Two marine glue mucosas (2), are separately positioned on the top and bottom of described substrate (1)；
Two rotary-cut veneer (3), are separately positioned on marine glue mucosa (2) described in two away from the two sides of described substrate (1)；And
Two wear-resisting wood grain layers (4), it is separately positioned on rotary-cut veneer (3) described in two away from the two sides of described substrate (1)；
Described substrate (1) is deep charring plank, and described in two, rotary-cut veneer (3) all staggers with the grain direction of described substrate (1)
Arrange.
A kind of high intensity solid wooden floor board the most according to claim 1, it is characterised in that rotary-cut veneer (3) and institute described in two
State substrate (1) grain direction to be all vertically arranged.
3. the manufacture method of a high intensity solid wooden floor board, it is characterised in that comprise the steps:
S1, making deep charring plank, two marine glue mucosas (2), two rotary-cut veneer (3), two wear-resisting wood grain layers (4)；
S2, from top to bottom, with a wear-resisting wood grain layer (4), a rotary-cut veneer (3), a marine glue mucosa (2), deep charring plank,
High intensity solid wood is made in another marine glue mucosa (2), another rotary-cut veneer (3), the order arrangement hot pressing of another wear-resisting wood grain layer (4)
Floor；
In S2, the grain direction of rotary-cut veneer (3) described in two and described substrate (1) all staggers setting.
The manufacture method of a kind of high intensity solid wooden floor board the most according to claim 3, it is characterised in that revolve described in two in S2
The grain direction cutting veneer (3) and described substrate (1) is all vertically arranged.
The manufacture method of a kind of high intensity solid wooden floor board the most according to claim 3, it is characterised in that the degree of depth described in S1
The manufacture method of carbonization plank sequentially comprises the steps:
S1.a1, flitch is placed in 185 DEG C～255 DEG C anaerobic isoperibol process to complete carbonization, make carbonization flitch；
S1.a2, the thickness extremely needed by described carbonization flitch plane, tooth punching is butted into strip, and after S4S, gluing split is plate
Body, sanding is smooth, saws Qi Sibian.
The manufacture method of a kind of high intensity solid wooden floor board the most according to claim 3, it is characterised in that waterproof gluing in S1
The manufacture method of film (4) sequentially comprises the steps: waterproofing agent that mass fraction is 4%, the dispersant of 1%, the formaldehyde of 1%
Agent for capturing, 94% melamine resin adehsive mixing and stirring after, uniform gluing, in abrasion-proof paper, surface drying, is made waterproof gluing
Film.
The manufacture method of a kind of high intensity solid wooden floor board the most according to claim 3, it is characterised in that described wear-resisting wood grain
The manufacture method of layer (4) comprises the steps:
S1.b1, anion powder by weight fraction is 3%, the titanium dioxide powder of 4%, the nano-silica powder of 1%, 2%
Dispersant, the melamine resin adehsive mix homogeneously of 90%, make compound adhesive；
S1.b2, by wear-resisting woodgrained paper immerse described compound adhesive, take out, film surface sprays aluminium sesquioxide after drying, prepare leaching
Stain top layer film.
The manufacture method of a kind of high intensity solid wooden floor board the most according to claim 3, it is characterised in that hot pressing in described S2
Temperature is 120 DEG C～230 DEG C.