CN101391431A - Process method of large breadth wood composite floor - Google Patents
Process method of large breadth wood composite floor Download PDFInfo
- Publication number
- CN101391431A CN101391431A CNA2008100689269A CN200810068926A CN101391431A CN 101391431 A CN101391431 A CN 101391431A CN A2008100689269 A CNA2008100689269 A CN A2008100689269A CN 200810068926 A CN200810068926 A CN 200810068926A CN 101391431 A CN101391431 A CN 101391431A
- Authority
- CN
- China
- Prior art keywords
- base material
- processing method
- wooden
- sanding
- compound floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing method of a big width wood multi-layer floor, the processing method includes the steps such as a substrate sanding, a wood skin sanding, a substrate drying and a wood skin drying, a wood skin widening, a substrate sizing, an assembling, a cold pressing, a material cutting, a sanding, an orifice opening and a painting and the like. The invention solves the deficiencies in the producing process of the traditional floor that the floor is easily deformed, the low quality product is easily produced, the production efficiency is low, a plurality of sites need to be occupied, and the production cost is high; the invention has the advantages that the equipment investment is low, the occupied site is few, the production efficiency is high, the production cost is low, and the quality of the products is high and the like.
Description
Technical field
The present invention relates to a kind of production technology of timber floor, particularly a kind of processing method of large format solid wooden compound floor.
Background technology
The specification of tradition timber floor is generally less, and the third dimension of overall appearance and visual effect are not enough outstanding.At present, many overlength, super wide large format solid wooden compound floor have appearred on the market, the plate face nature of this large format solid wooden compound floor, coherent and long, the back integral body of mating formation is generous naturally, of tremendous momentum, greatly strengthen the associative perception on floor, be particularly suitable for the finishing in large-scale places such as large-scale palace, auditorium or meeting room.
The production technology of traditional large format solid wooden compound floor is that base material and wooden skin is dry respectively when drying, cause the moisture of base material and wooden skin not match, there is bigger internal stress after making base material and wooden skin pressing, thereby causes the large format composite floor board easy deformation of production, influence product quality.And traditional handicraft is to drive locating slot earlier on base material when pasting wooden skin, and then along the locating slot of base material wooden skin sticked on the base material, and this quadrat method causes wooden skin to slide on base material easily, and wooden skin and base material are misplaced, and is easy to produce defective products.In addition, traditional floor producing technology needs health after the pressing of floor, not only causes production efficiency low, and need take a large amount of places, has increased the weight of the production cost of enterprise.
Summary of the invention
Technical problem to be solved by this invention is, provides that a kind of place takies less, the processing method of production efficiency height, production cost is low, product quality is high large format solid wooden compound floor.
For solving the problems of the technologies described above technical scheme of the present invention: a kind of processing method of large format solid wooden compound floor.This processing method may further comprise the steps,
A, base material sanding, wooden skin sanding;
B, carry out drying after base material and wooden skin stacked;
C, base material sanding, wooden skin sanding;
D, wooden skin are pieced together wide;
E, base material applying glue;
F, assembly;
G, cold pressing;
H, open material;
I, sanding;
J, open tongue and groove;
K, paint.
In the processing method of above-mentioned large format solid wooden compound floor, described base material sanding of step a, step c and wooden skin sanding are respectively base material and wooden skin to be carried out the sanding processing with sander.
In the processing method of aforesaid large format solid wooden compound floor, step b is that to be dried to moisture content after base material and wooden skin are stacked be 6～12%.
In the processing method of aforesaid large format solid wooden compound floor, it is with PUR wooden skin to be pieced together widely that the described wooden skin of steps d is pieced together wide, makes wooden skin become a whole plate.
In the processing method of aforesaid large format solid wooden compound floor, the described base material applying glue of step e is with sizing applicator base material to be carried out applying glue, and the adhesive of employing is anhydrous adhesive, and resin added is 80～90g/m
2
In the processing method of aforesaid large format solid wooden compound floor, described anhydrous adhesive is anhydrous mono component wet solidifying liquid polyurethane adhesive.
In the processing method of aforesaid large format solid wooden compound floor, the described assembly of step f is that the wooden skin of piecing together after wide is sticked on the base material.
In the processing method of aforesaid large format solid wooden compound floor, step g is described colds pressing is the wooden skin behind the assembly and base material to be sent into carry out pressing in the cold press, and pressing pressure is 0.8～1.2Mpa, and pressing time is 10～30 minutes.
In the processing method of aforesaid large format solid wooden compound floor, the described material of opening of step h is along the edge joint position of wooden skin monoblock blanket saw to be separated into solid wooden compound floor base sheet with multiple blade saw.
In the processing method of aforesaid large format solid wooden compound floor, the thickness of wooden skin is 2～5mm.
Beneficial effect of the present invention: compared with prior art, it is few that the present invention has an equipment investment, and the place takies few, the production efficiency height, and production cost is low, the characteristics that product quality is high.The present invention stacks drying with base material and wooden skin, with traditional handicraft base material is compared with wooden skin separate drying, the moisture of base material and wooden skin is mated more, reduce the internal stress of base material and wooden skin after the pressing, thereby solved the technical problem of large format solid wooden compound floor easy deformation.The present invention is when assembly, earlier wooden skin assembly is become a whole plate after wide with PUR, and then the wooden skin that will piece together after wide sticks on the base material, this method has solved prior art and has pasted wooden Pi Shiyin wood skin and slide on base material easily and cause wooden skin and base material to misplace, thereby the technical problem that defective products occurs, the product quality height.In addition, compare with traditional technology, the present invention makes the moisture content of base material and wooden skin finish coupling owing to adopt base material and the folded drying synchronously of wooden tare weight, and after adopting anhydrous adhesive pressing, no moisture content difference between base material and the wooden skin, so also internal stress free is can be without health, thereby improved production efficiency, reduce equipment investment and production site takies, reduced the production cost of enterprise, had favorable economic benefit.
The specific embodiment
The present invention is further illustrated below in conjunction with embodiment.
Embodiment.Produce the large format solid wooden compound floor according to following step:
A, respectively base material and wooden skin are carried out sanding with sander and handle, can closely contact when wooden skin is stacked with base material, when drying, reach moisture and mate thereby help wooden skin and base material; The thickness of wood skin is 2～5mm.
B, base material and wooden skin are stacked, carry out drying then, dried moisture content is controlled at 6～12%, deforms to avoid the floor;
C, with sander dried base material and wooden skin are carried out sanding once more and handle;
D, wooden skin is pieced together wide processing, promptly wooden skin is pieced together widely, make wooden skin become a whole plate with PUR;
E, to the base material applying glue, promptly base material is carried out applying glue with sizing applicator, the adhesive of employing is anhydrous mono component wet solidifying liquid polyurethane adhesive, resin added is controlled at 80～90g/m
2
F, assembly.The wooden skin of piecing together after wide is sticked on the base material;
G, cold pressing.Wooden skin behind the assembly and base material sent into carry out pressing in the cold press, pressing pressure is 0.8～1.2Mpa, and pressing time is 10～30 minutes (relevant with environment temperature, temperature is high more, and pressing time is short more).
H, open material.Along the edge joint position of wooden skin monoblock blanket saw is separated into solid wooden compound floor base sheet with multiple blade saw;
The solid wooden compound floor base sheet of saw being separated according to common process carries out sanding, opens tongue and groove and the processing of painting then, promptly gets large format solid wooden compound floor finished product.
Embodiments of the present invention are not limited to the foregoing description, and the various variations of making under the prerequisite that does not break away from aim of the present invention all belong within protection scope of the present invention.
Claims (10)
1, a kind of processing method of large format solid wooden compound floor is characterized in that: may further comprise the steps,
A, base material sanding, wooden skin sanding;
B, carry out drying after base material and wooden skin stacked;
C, base material sanding, wooden skin sanding;
D, wooden skin are pieced together wide;
E, base material applying glue;
F, assembly;
G, cold pressing;
H, open material;
I, sanding;
J, open tongue and groove;
K, paint.
2, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: described base material sanding of step a, step c and wooden skin sanding are respectively base material and wooden skin to be carried out the sanding processing with sander.
3, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: step b is that to be dried to moisture content after base material and wooden skin are stacked be 6～12%.
4, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: it is with PUR wooden skin to be pieced together widely that the described wooden skin of steps d is pieced together wide, makes wooden skin become a whole plate.
5, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: the described base material applying glue of step e is with sizing applicator base material to be carried out applying glue, and the adhesive of employing is anhydrous adhesive, and resin added is 80～90g/m
2
6, the processing method of large format solid wooden compound floor according to claim 5 is characterized in that: described anhydrous adhesive is anhydrous mono component wet solidifying liquid polyurethane adhesive.
7, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: the described assembly of step f is that the wooden skin of piecing together after wide is sticked on the base material.
8, the processing method of large format solid wooden compound floor according to claim 1, it is characterized in that: step g is described colds pressing is the wooden skin behind the assembly and base material to be sent into carry out pressing in the cold press, pressing pressure is 0.8～1.2Mpa, and pressing time is 10～30 minutes.
9, the processing method of large format solid wooden compound floor according to claim 1 is characterized in that: the described material of opening of step h is along the edge joint position of wooden skin monoblock blanket saw to be separated into solid wooden compound floor base sheet with multiple blade saw.
10, according to the processing method of any described large format solid wooden compound floor in the claim 1～9, it is characterized in that: the thickness of described wooden skin is 2～5mm.