CN105196366A - Reinforced board - Google Patents

Reinforced board Download PDF

Info

Publication number
CN105196366A
CN105196366A CN201510521463.7A CN201510521463A CN105196366A CN 105196366 A CN105196366 A CN 105196366A CN 201510521463 A CN201510521463 A CN 201510521463A CN 105196366 A CN105196366 A CN 105196366A
Authority
CN
China
Prior art keywords
solid wood
wood board
paper
layer
board
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510521463.7A
Other languages
Chinese (zh)
Inventor
陈文芝
童霞
郭正
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI LONGHUA BAMBOO Co Ltd
Original Assignee
ANHUI LONGHUA BAMBOO Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI LONGHUA BAMBOO Co Ltd filed Critical ANHUI LONGHUA BAMBOO Co Ltd
Priority to CN201510521463.7A priority Critical patent/CN105196366A/en
Publication of CN105196366A publication Critical patent/CN105196366A/en
Pending legal-status Critical Current

Abstract

The invention relates to a reinforced board. A tree is sectioned in the radial direction to obtain solid wood sheets, the radial section is to cut the timber from tree bark via a heart center, a sectional surface is a radial sectional surface, and due to the existence of growth rings, a plurality of grain lines are formed on the radial sectional surface along the trunk direction. The reinforced board comprises a solid wood layer, a wear-resistant paper layer and a balanced paper layer, wherein the solid wood layer is formed by laminating a plurality of solid wood sheets, the grain lines of two adjacent solid wood sheets are intersected, two adjacent solid wood sheets are bonded by virtue ore resin adhesive, the uppermost layer of solid wood sheet is bonded with the wear-resistant paper layer in a hot pressing manner, and a lowermost layer of solid wood sheet is bonded with the balanced paper layer in a hot pressing manner. The process is simple, the cost is relatively low, and the strength of the board can be 17 times of that of an ordinary board, so that the board is durable, unlikely to deform and capable of guaranteeing the attractiveness and quality after being used for a long time.

Description

A kind of strengthening plank
Technical field
The invention belongs to rubber preparing device field, be specifically related to a kind of strengthening plank.
Background technology
Along with improving constantly of people's living standard, the healthy living of high-quality becomes the continuous pursuit of people.Increasing people pays close attention to the health of life staying idle at home environment, and especially more and more higher to the requirement of house ornamentation, the application of solid wooden floor board is more and more universal, but to wear no resistance and intensity is low due to timber floor, easily produces cut, volatile gloss.
Density board also claims fiberboard, for raw material with wood fibre or other plant fiber, the artificial board that applying Lauxite or other adhesive be suitable for are made, by the difference of its density, be divided into high-density plate, medium-density plate, low-density plank, density board due to matter soft shock-resistant, also easily reprocess, shortcoming is that water proofing property is poor, and this also limits its scope of application to a certain extent.
Summary of the invention
The invention provides a kind of strengthening plank, can effectively solve the problem.
The present invention is achieved through the following technical solutions:
A kind of strengthening plank, solid wood board is obtained by carrying out radial cutting to trees, described radial cutting timber is cut from bark by medulla, its section is radial longitudinal section, due to the existence of annual ring, radial longitudinal section forms many textures line along trunk direction, comprise solid wood layer, wear-resisting ply of paper peace weighing apparatus ply of paper, described solid wood layer is formed by stacking by polylith solid wood board, the solid wood board grain of adjacent two pieces is interlaced, resin glue is used to bond between described solid wood board, described the superiors solid wood board and wear-resisting ply of paper heat pressure adhesive, orlop solid wood board and balance ply of paper heat pressure adhesive.
Strengthen a processing and fabricating method for plank, procedure of processing is as follows:
(1) solid wood board cutting obtained carries out drying process, and solid wood board water content control is at 6-8%, and the thickness of top layer solid wood board is greater than the thickness of its underpart solid wood board, and solid wood board top and bottom evenly apply glue, interfolded;
(2) use resin glue to bond between solid wood board, described tack temperature is 100-120 DEG C, and pressure is 12-20MPa, and the time is 15 minutes, forms slab;
(3), on the lower bolster of hot press balance paper, slab and abrasion-proof paper placed successively, abrasion-proof paper, slab and balance paper hot pressing, with the pressure of 14-20MPa, temperature pressurize 40-50 second at 200-200 DEG C, link into an integrated entity, take out by bolster;
(4) after hot pressing completes, interlayer stacking is carried out to sheet material, puts that district keeps that air is smooth, temperature 20-25 DEG C and humidity 40-60%, put 1-2 days hours, then cutting edge, cut into required finished product.
Further, described solid wood layer is formed by stacking by 8 pieces of solid wood boards, and the thickness of solid wood board is 1.8-2.2mm, and described wear-resisting ply of paper uses abrasion-proof paper, described balance ply of paper balance paper.
Beneficial effect of the present invention: the inventive method technique is simple and cost is lower, utilizes plank of the present invention to be 17 times of common plank intensity, makes plank durable in use, and not yielding, ensures the attractive in appearance and quality of Long-Time Service.
Detailed description of the invention
A kind of strengthening plank, solid wood board is obtained by carrying out radial cutting to trees, described radial cutting timber is cut from bark by medulla, its section is radial longitudinal section, due to the existence of annual ring, radial longitudinal section forms many textures line along trunk direction, comprise solid wood layer, wear-resisting ply of paper peace weighing apparatus ply of paper, described solid wood layer is formed by stacking by polylith solid wood board, the solid wood board grain of adjacent two pieces is interlaced, resin glue is used to bond between described solid wood board, described the superiors solid wood board and wear-resisting ply of paper heat pressure adhesive, orlop solid wood board and balance ply of paper heat pressure adhesive.
Strengthen a processing and fabricating method for plank, procedure of processing is as follows:
(1) solid wood board cutting obtained carries out drying process, and solid wood board water content control is at 6-8%, and the thickness of top layer solid wood board is greater than the thickness of its underpart solid wood board, and solid wood board top and bottom evenly apply glue, interfolded;
(2) use resin glue to bond between solid wood board, described tack temperature is 100-120 DEG C, and pressure is 12-20MPa, and the time is 15 minutes, forms slab;
(3), on the lower bolster of hot press balance paper, slab and abrasion-proof paper placed successively, abrasion-proof paper, slab and balance paper hot pressing, with the pressure of 14-20MPa, temperature pressurize 40-50 second at 200-200 DEG C, link into an integrated entity, take out by bolster;
(4) after hot pressing completes, interlayer stacking is carried out to sheet material, puts that district keeps that air is smooth, temperature 20-25 DEG C and humidity 40-60%, put 1-2 days hours, then cutting edge, cut into required finished product.
Further, described solid wood layer is formed by stacking by 8 pieces of solid wood boards, and the thickness of solid wood board is 1.8-2.2mm, and described wear-resisting ply of paper uses abrasion-proof paper, described balance ply of paper balance paper.

Claims (3)

1. a strengthening plank, solid wood board is obtained by carrying out radial cutting to trees, described radial cutting timber is cut from bark by medulla, its section is radial longitudinal section, due to the existence of annual ring, radial longitudinal section forms many textures line along trunk direction, it is characterized in that: comprise solid wood layer, wear-resisting ply of paper peace weighing apparatus ply of paper, described solid wood layer is formed by stacking by polylith solid wood board, the solid wood board grain of adjacent two pieces is interlaced, resin glue is used to bond between described solid wood board, described the superiors solid wood board and wear-resisting ply of paper heat pressure adhesive, orlop solid wood board and balance ply of paper heat pressure adhesive.
2. strengthen a processing and fabricating method for plank, it is characterized in that procedure of processing is as follows:
(1) solid wood board cutting obtained carries out drying process, and solid wood board water content control is at 6-8%, and the thickness of top layer solid wood board is greater than the thickness of its underpart solid wood board, and solid wood board top and bottom evenly apply glue, interfolded;
(2) use resin glue to bond between solid wood board, described tack temperature is 100-120 DEG C, and pressure is 12-20MPa, and the time is 15 minutes, forms slab;
(3), on the lower bolster of hot press balance paper, slab and abrasion-proof paper placed successively, abrasion-proof paper, slab and balance paper hot pressing, with the pressure of 14-20MPa, temperature pressurize 40-50 second at 200-200 DEG C, link into an integrated entity, take out by bolster;
(4) after hot pressing completes, interlayer stacking is carried out to sheet material, puts that district keeps that air is smooth, temperature 20-25 DEG C and humidity 40-60%, put 1-2 days hours, then cutting edge, cut into required finished product.
3. strengthening plank according to claim 1, is characterized in that: described solid wood layer is formed by stacking by 8 pieces of solid wood boards, and the thickness of solid wood board is 1.8-2.2mm, and described wear-resisting ply of paper uses abrasion-proof paper, described balance ply of paper balance paper.
CN201510521463.7A 2015-08-24 2015-08-24 Reinforced board Pending CN105196366A (en)