CN106119975A - A kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen and preparation method thereof - Google Patents
A kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen and preparation method thereof Download PDFInfo
- Publication number
- CN106119975A CN106119975A CN201610531603.3A CN201610531603A CN106119975A CN 106119975 A CN106119975 A CN 106119975A CN 201610531603 A CN201610531603 A CN 201610531603A CN 106119975 A CN106119975 A CN 106119975A
- Authority
- CN
- China
- Prior art keywords
- hydrolytic collagen
- solar cell
- sodium
- sheet surface
- surface texture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, it is to be prepared by the raw material of following weight parts: hydrolytic collagen 0.3 0.5, sodium lauroyl sarcosine 0.1 0.15, styrene 1.5 2.5,5 10% ammonium persulfate solutions 12, sodium lauryl sulphate 0.1 0.2, ten difluoro heptyl propyl trimethoxy silicanes 0.1 0.15, sodium hydroxide 35, citric acid 0.3 0.5, hydroxypropyl urea 0.1 0.15, sodium gluconate 0.1 0.15, water 100 120.The silicon chip texture liquid response speed of the present invention is very fast, it is moderate to corrode, Reducing thickness is little, recycling rate of waterused is high, and the matte pyramid size prepared is uniform, and granule is less, and batch homogeneity is good, and repeatability is high, low cost, environmental protection, and usage safety performance is high.
Description
Technical field
The present invention relates to technical field of solar batteries, particularly relate to a kind of mono-crystalline silicon solar containing hydrolytic collagen
Cell piece surface texture liquid and preparation method thereof.
Background technology
Along with world energy sources crisis is more serious, solar energy has become most potential alternative energy source, and solaode
It it is i.e. a kind of electronic component that solar energy is converted directly into electric energy.The main problem hindering solar battery technology to develop is
Its high manufacturing cost.At present, for reducing the cost of monocrystaline silicon solar cell and improving electricity conversion, enter
Row silicon face texturing is the most easily to realize and the most efficient method.Texture, also known as making herbs into wool, i.e. utilizes and falls into light principle, make incident illumination carry out
Multiple reflections extends its propagation path at battery surface, thus improves the solaode absorption efficiency to light.Utilize silicon
The principle of anisotropic etch, monocrystalline silicon surface can form similar pyramidal structure, effectively reduces the reflectance of sunlight.
At present, monocrystalline silicon surface texture is most commonly used that chemical corrosion method, it is common to use texture liquid be NaOH/ isopropyl
Alcohol system, but isopropanol price is high, evaporation rate is fast, and cost is high and is unfavorable for environmental protection.Patent 201010161287.8 disclosure
A kind of velvet manufacturing solution of monocrystalline silicon additive, is made up of, without isopropanol alkaline corrosion liquid and surfactant and organic acid or salt
And rapidly and efficiently, but there is the problem of reaction lack of homogeneity in it, easily cause silicon face pyramid after texture bigger than normal and
Locally the situation such as excessive erosion, need to improve further in the quality make silicon chip.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of response speed is fast, uniformity good, corrosion
The monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen moderate, Reducing thickness is little, silicon chip surface quality is high and
Its preparation method.
The present invention is achieved by the following technical solutions:
A kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, it is by the raw material system of following weight parts
:
Hydrolytic collagen 0.3-0.5, sodium lauroyl sarcosine 0.1-0.15, styrene 1.5-2.5,5-10% Ammonium persulfate. is molten
Liquid 1-2, sodium lauryl sulphate 0.1-0.2, ten difluoro heptyl propyl trimethoxy silicane 0.1-0.15, sodium hydroxide 3-5, lemon
Lemon acid 0.3-0.5, hydroxypropyl urea 0.1-0.15, sodium gluconate 0.1-0.15, water 100-120.
The preparation method of a kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, including following step
Rapid:
(1) weigh raw material by weight, first sodium lauryl sulphate is added in the water of 1/3-1/2 weight and stir, then delay
Slowly add styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stir 0.5-1h, being finally slowly added dropwise over cure
Acid ammonium solution also stirs 2-4h in 70-80 DEG C, cools down, obtain complex emulsions after insulation 3-5h;
(2) first by hydrolytic collagen, citric acid add surplus water in 60-80 DEG C stirring 2-4h, be subsequently adding sodium hydroxide
With stirring 0.5-1h under sodium lauroyl sarcosine similarity condition, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60-80 DEG C, mistake
The monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen is i.e. obtained after filtering decontamination.
The invention have the advantage that
The present invention utilizes styrene and ten difluoro heptyl propyl trimethoxy silicane emulsions polymerization synthesis complex microsphere, can be good
Be attached to silicon chip surface, play certain etching mask effect, can reduce the excessive corrosion of silicon chip, promote reaction simultaneously
Uniformity, improves matte quality, is difficult to again remain at silicon chip surface, it is ensured that the spatter property of silicon chip;Meanwhile, by hydrolytic collagen egg
White wait raw material compounding with potentiation so as to get silicon chip texture liquid response speed very fast, corrode moderate, Reducing thickness is little, weight
Multiple utilization rate is high, and the matte pyramid size prepared is uniform, and granule is less, and batch homogeneity is good, and repeatability is high, cost
Low, environmental protection, usage safety performance is high.
Detailed description of the invention
A kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, by the component of following weight (kg)
Raw material is prepared from:
Hydrolytic collagen 0.3, sodium lauroyl sarcosine 0.1, styrene 1.5,5% ammonium persulfate solution 1, lauryl sulphate acid
Sodium 0.1, ten difluoro heptyl propyl trimethoxy silicanes 0.1, sodium hydroxide 3, citric acid 0.3, hydroxypropyl urea 0.1, gluconic acid
Sodium 0.1, water 100.
The preparation method of a kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, including following step
Rapid:
(1) weigh raw material by weight, first sodium lauryl sulphate is added in the water of 1/3 weight and stir, the most slowly add
Enter styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stir 0.5h, being finally slowly added dropwise Ammonium persulfate. molten
Liquid also stirs 2h in 70 DEG C, cools down, obtain complex emulsions after insulation 3h;
(2) first by hydrolytic collagen, citric acid add surplus water in 60 DEG C stirring 2h, be subsequently adding sodium hydroxide and Laurel
Stir 0.5h under acylsarcosine sodium similarity condition, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60 DEG C, filters
The monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen is i.e. obtained after removing impurity.
Through inspection, above-mentioned texture liquid 80 DEG C, uniform small size pyramid can be prepared at silicon chip surface under the conditions of 20min
Structure, its pyramid prepared is 9.8% at 0.5-1.5 μm, the average reflectance in the range of 300-1100nm, is corroded
Amount of silicon be about 4.7%.
Claims (2)
1. the monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen, it is characterised in that it is by following
The raw material of weight portion prepares:
Hydrolytic collagen 0.3-0.5, sodium lauroyl sarcosine 0.1-0.15, styrene 1.5-2.5,5-10% Ammonium persulfate. is molten
Liquid 1-2, sodium lauryl sulphate 0.1-0.2, ten difluoro heptyl propyl trimethoxy silicane 0.1-0.15, sodium hydroxide 3-5, lemon
Lemon acid 0.3-0.5, hydroxypropyl urea 0.1-0.15, sodium gluconate 0.1-0.15, water 100-120.
The system of a kind of monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen the most according to claim 1
Preparation Method, it is characterised in that comprise the following steps:
(1) weigh raw material by weight, first sodium lauryl sulphate is added in the water of 1/3-1/2 weight and stir, then delay
Slowly add styrene and the mixture of ten difluoro heptyl propyl trimethoxy silicanes and stir 0.5-1h, being finally slowly added dropwise over cure
Acid ammonium solution also stirs 2-4h in 70-80 DEG C, cools down, obtain complex emulsions after insulation 3-5h;
(2) first by hydrolytic collagen, citric acid add surplus water in 60-80 DEG C stirring 2-4h, be subsequently adding sodium hydroxide
With stirring 0.5-1h under sodium lauroyl sarcosine similarity condition, add remaining raw material stirring after cooling uniformly, obtain mixed liquor;
(3) it is slowly added to the complex emulsions in step (1) stir in the mixed liquor in step (2) and in 60-80 DEG C, mistake
The monocrystaline silicon solar cell sheet surface texture liquid containing hydrolytic collagen is i.e. obtained after filtering decontamination.