CN106118597A - The friction material of transmission braking and goods - Google Patents
The friction material of transmission braking and goods Download PDFInfo
- Publication number
- CN106118597A CN106118597A CN201610494593.0A CN201610494593A CN106118597A CN 106118597 A CN106118597 A CN 106118597A CN 201610494593 A CN201610494593 A CN 201610494593A CN 106118597 A CN106118597 A CN 106118597A
- Authority
- CN
- China
- Prior art keywords
- friction material
- friction
- braking
- transmission
- gross mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The friction material of a kind of transmission braking, including following material: bond material, fibrous material, damping material, antifriction material, increasing rub material, packing material, Acidity of Aikalinity regulation material, metal material and heat-resisting reinforcing material;It is good, little to the dish aggressivity of brake(-holder) block that this friction material has stable friction factor, anti-wear performance, and thermostability and the good feature of heat conductivity.
Description
Technical field
The present invention relates to friction material and the goods thereof of a kind of transmission braking, particularly relate to one and alleviate mating plate attack
Property transmission braking friction material and goods.
Background technology
Friction material is that one is applied on dynamic power machine, relies on rubbing action to perform the parts of braking and transmission agency
Material.It mainly includes brake facing (brake block) and clutch surface (clutch disc).Brake block is used for braking, clutch
Sheet is used for transmission.
The abrasion of existing friction material mating plate is the highest, and the renewal cost of the mating plate of brake(-holder) block is high, operation
Complicated.The service life extending mating plate is demand all the time.And the friction material of brake block is during braking
Owing to friction can produce substantial amounts of heat, the heat conduction of conventional friction material and heat-resisting be not the most fine, which results in needs
Brake block carrying out special handling or changes heat-resisting good material and prepare, this virtually adds the operation of production and becomes
This.
Summary of the invention
In order to solve above-mentioned technical problem, it is an object of the invention to provide one have stable friction factor, anti-wear performance good,
Little to the dish aggressivity of brake(-holder) block, and thermostability and wire-conducting performance good transmission braking friction material.
The friction material of a kind of transmission braking, it is characterised in that include following material: bond material, fibrous material, resistance
Damping material, antifriction material, increasing rub material, packing material, Acidity of Aikalinity regulation material, metal material and heat-resisting reinforcing material.
Preferably, described heat-resisting reinforcing material includes carborundum, carbon fibre, graphite oxide, Graphene, zirconium carbide, carbon
Change the one in boron, tungsten carbide or a combination thereof.
Preferably, this friction material is made up of following material mixture ratio:
Bond material accounts for the 3-11% of this friction material gross mass;
Fibrous material accounts for the 5-15% of this friction material gross mass;
Metal material accounts for the 12-25% of this friction material gross mass;
Damping material accounts for the 2-6% of this friction material gross mass;
Antifriction material accounts for the 7-12% of this friction material gross mass;
Increase the material that rubs and account for the 12-22% of this friction material gross mass;
Packing material accounts for the 24-32% of this friction material gross mass;
Acidity of Aikalinity regulation material accounts for the 3-5% of this friction material gross mass;
Heat-resisting reinforcing material accounts for the 3-6% of this friction material gross mass.
Preferably, described bond material includes phenolic resin, melmac, epoxy resin, melamine resin, modified phenol
One or more combinations in urea formaldehyde, Toxicodendron verniciflnum (Stokes) F. A. Barkley (Rhus verniciflua Stokes) resin, natural rubber and butadiene-styrene rubber etc..
Preferably, described fibrous material includes organic fiber and inorfil, and described organic fiber includes aramid fiber, fibre
One or more combinations in cellulose fiber and polyacrylic fibre;Described inorfil includes potassium titanate fibre, glass fibers
One or more combinations in dimension, ceramic fibre and aluminum series fiber.
Preferably, one or several groups during described antifriction material includes graphite, metal sulfide, molybdenum bisuphide etc.
Close, described increasing rub material include in zirconium oxide, aluminium oxide, ferrum oxide, Zirconium orthosilicate. one or several combination.
Preferably, described packing material is included organic filler material and inorganic filling material by packing material, described organic
Packing material includes nitrile rubber (NBR), butadiene-styrene rubber (SBR) and butadiene rubber (BR), rubber dust, organic dust and gathers
One or more combinations in tetrafluoroethene (PTFE), described inorganic filling material includes Vermiculitum, Muscovitum, calcium hydroxide, sulfur
One or more combinations in acid barium, calcium carbonate.
Preferably, described damping material includes organic Frication powder, described Acidity of Aikalinity regulation material include Calx, slaked lime,
Soda, Gypsum Fibrosum powder, sodium hydroxide, calcium hydroxide.
Present invention also offers a kind of brake block, including base material, tack coat and frictional layer, described frictional layer is by above-mentioned biography
The friction material of dynamic braking is made.
The friction material of the transmission braking of the present invention, has the advantages that the friction material pair that the present invention provides
The dish attack of brake(-holder) block mating plate is little, and by adding heat-resisting reinforcing material, can reach resistance on original raw material
The friction material that hot and heat conductivity is good, and production cost is low, it is possible to use and conventional production equipment produces.
Detailed description of the invention
Below with reference to embodiment, the present invention is explained in detail.But, the present invention should not be construed as limited to following
Embodiment.
Bond material includes phenolic resin, melmac, epoxy resin, melamine resin, phenol-formaldehyde resin modified, Toxicodendron verniciflnum (Stokes) F. A. Barkley (Rhus verniciflua Stokes)
One or more combinations in resin natural rubber and butadiene-styrene rubber etc..
Organic fiber include the one in aromatic polyamide (aramid fiber) fiber, cellulose fiber peacekeeping polyacrylic fibre or
Person's multiple combination.
Inorfil includes one or more combinations in potassium titanate fibre, glass fibre, ceramic fibre and aluminum series fiber.
Fiber base material can use with chopped fiber or powder type.
Packing material includes organic filler material and inorganic filling material, organic filler material include nitrile rubber (NBR),
Butadiene-styrene rubber (SBR) and the various rubber of butadiene rubber (BR), rubber dust, organic dust such as Fructus anacardii dust and polytetrafluoro
One or more combinations in ethylene (PTFE) etc.;Inorganic filling material includes Vermiculitum, Muscovitum, calcium hydroxide, barium sulfate, carbon
One or more combinations in acid calcium etc..
Antifriction material includes one or several combinations in graphite, metal sulfide, molybdenum bisuphide etc..
Increase one or several combinations that the material that rubs includes in zirconium oxide, aluminium oxide, ferrum oxide, Zirconium orthosilicate. etc..
Damping material includes organic Frication powder.
Metal material includes one or several combinations in the metal dust of copper, aluminum, stannum, ferrum and zinc etc..
Acidity of Aikalinity regulation material includes Calx, slaked lime, soda, Gypsum Fibrosum powder, sodium hydroxide, calcium hydroxide.
Heat-resisting reinforcing material includes carborundum, carbon fibre, graphite oxide, Graphene, zirconium carbide, boron carbide, tungsten carbide
In one or a combination thereof.
By each formula (mass percent) shown in table 1, table 2, utilize blender will to be used for each of friction material
Component mixing 15min, it is thus achieved that the friction material mixture of mix homogeneously.Subsequently by friction material mixture the temperature of 150 DEG C
Down and pressurize 6 seconds under the pressure of 14Mpa, then aerofluxus 3 seconds, circulates 5 times, obtains compressing product, then will be pressed into
The product of type is heat treatment 3 hours at a temperature of 180 DEG C, finally by the product sprayed protection paint after heat treatment, the temperature of 150 DEG C
30min is solidified under degree.
[table 1]
[table 2]
From table 1, table 2 it can be seen that the thermostability become reconciled of the anti-wear performance that this friction material has had and good dish are attacked
Property.
Present invention also offers a kind of brake block, including base material, tack coat and frictional layer, described frictional layer is by above-mentioned biography
The friction material of dynamic braking is made, and frictional layer is bonded on base material by tack coat.
The above disclosed present pre-ferred embodiments that is only, can not limit the right model of the present invention with this certainly
Enclose, the equivalent variations therefore made according to the claims in the present invention, still belong to the scope that the present invention is contained.
Claims (9)
1. the friction material of transmission braking, it is characterised in that include following material: bond material, fibrous material, damping
Material, antifriction material, increasing rub material, packing material, Acidity of Aikalinity regulation material, metal material and heat-resisting reinforcing material.
The friction material of transmission the most according to claim 1 braking, it is characterised in that described heat-resisting reinforcing material includes
One in carborundum, carbon fibre, graphite oxide, Graphene, zirconium carbide, boron carbide, tungsten carbide or a combination thereof.
The friction material of transmission the most according to claim 2 braking, it is characterised in that this friction material is by following material
Proportioning forms:
Bond material accounts for the 3-11% of this friction material gross mass;
Fibrous material accounts for the 5-15% of this friction material gross mass;
Metal material accounts for the 12-25% of this friction material gross mass;
Damping material accounts for the 2-6% of this friction material gross mass;
Antifriction material accounts for the 7-12% of this friction material gross mass;
Increase the material that rubs and account for the 12-22% of this friction material gross mass;
Packing material accounts for the 24-32% of this friction material gross mass;
Acidity of Aikalinity regulation material accounts for the 3-5% of this friction material gross mass;
Heat-resisting reinforcing material accounts for the 3-6% of this friction material gross mass.
The friction material of transmission the most according to claim 3 braking, it is characterised in that described bond material includes phenolic aldehyde
Resin, melmac, epoxy resin, melamine resin, phenol-formaldehyde resin modified, Toxicodendron verniciflnum (Stokes) F. A. Barkley (Rhus verniciflua Stokes) resin, natural rubber and butadiene-styrene rubber
One or more combinations in Deng.
The friction material of transmission the most according to claim 3 braking, it is characterised in that described fibrous material includes organic
Fiber and inorfil, described organic fiber include the one in aramid fiber, cellulose fiber peacekeeping polyacrylic fibre or
Multiple combination;Described inorfil includes in potassium titanate fibre, glass fibre, copper fiber, ceramic fibre and aluminum series fiber a kind of
Or multiple combination.
The friction material of transmission the most according to claim 3 braking, it is characterised in that described antifriction material includes stone
One or several combinations in ink, metal sulfide, molybdenum bisuphide etc., the described increasing material that rubs includes zirconium oxide, aluminium oxide, oxygen
Change one or several combinations in ferrum, Zirconium orthosilicate..
The friction material of transmission the most according to claim 3 braking, it is characterised in that described packing material is by filling material
Material includes that organic filler material and inorganic filling material, described organic filler material include nitrile rubber (NBR), butadiene-styrene rubber
(SBR) one or more groups and in butadiene rubber (BR), rubber dust, organic dust and politef (PTFE)
Closing, described inorganic filling material includes one or more combinations in Vermiculitum, Muscovitum, calcium hydroxide, barium sulfate, calcium carbonate.
The friction material of transmission the most according to claim 3 braking, it is characterised in that described damping material includes organic
Frication powder, described Acidity of Aikalinity regulation material includes in Calx, slaked lime, soda, Gypsum Fibrosum powder, sodium hydroxide, calcium hydroxide
Plant or several combination.
9. a brake block, including base material, tack coat and frictional layer, it is characterised in that described frictional layer is appointed by claim 1-8
The friction material of the transmission braking described in is made.