CN106118553A - A kind of cracking reinforcing agent for wicker products - Google Patents
A kind of cracking reinforcing agent for wicker products Download PDFInfo
- Publication number
- CN106118553A CN106118553A CN201610551269.8A CN201610551269A CN106118553A CN 106118553 A CN106118553 A CN 106118553A CN 201610551269 A CN201610551269 A CN 201610551269A CN 106118553 A CN106118553 A CN 106118553A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid
- wicker products
- reinforcing agent
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of cracking reinforcing agent for wicker products, including A liquid and B liquid, described A liquid is made up of following material: wood vinegar, Mancozeb, Konjac glucomannan, sodium stearate, NPE, high-carbon fatty alcohol polyoxyethylene ether, positive silicic acid propyl ester, polydimethylsiloxane, ammonium polyacrylate, boric acid, water；Described B liquid is made up of following material: sodium hexameta phosphate, tartaric acid, sodium carboxymethyl cellulose, active carbon nanoparticles, nano silicon, propylene glycol methyl ether acetate, acrylic emulsion, Cortex Phellodendri extract, Camphora extract, water.The cracking reinforcing agent of present invention preparation is under the common effect of A liquid and B liquid, well it is filled with gap, avoid the erosion to it of the exogenous impurity composition, improve again its Vermins-proof mildew-proof performance and the intensity of entirety and wearability, the surface strength of final wicker products can improve about 40%, rupture strength can improve about 50%, and service life can extend 1 ~ 2 times, and use value is higher.
Description
Technical field
The invention belongs to wicker plaiting article manufacture field, be specifically related to a kind of cracking reinforcing agent for wicker products.
Background technology
Wicker plaiting article is China's one traditional technology, and present wicker products is commercially popular, and the kind of wicker products is numerous
Many, the polytypes such as seat, basket, basket, dustpan, round-bottomed basket, crate, shallow basket made of wicker or thin bamboo strips, the gaily decorated basket, bamboo strainer, food dish are had at domestic aspect.Export trade side
Face, has formed buck basket, flower pot coat, picnic tableware basket, hanging basket, lampshade, kennel, cat litter, Bird's Nest etc. through developing and design many
Kind, foreign trade is formed the appreciation effect that low-grade goods become high-grade, very popular.But wicker products preserve or
During improper use, tiny crack easily occurs, if things go on like this can develop into bigger deeper breach, not only can affect wicker plaiting article system
The antiseptic insect-repelling performance of product, can reduce again the intensity of wicker plaiting article, be deformed, and i.e. affecting attractive in appearance affects again practicality.People at present
Not yet paying attention to for problems, the quality that processes when usual wicker plaiting article finished product makes determines the length in service life, and in examination
It is not carried out maintenance maintenance with period, cause the shorter problem with the wasting of resources in service life.Groups of people use wooden use
Glue bonds, although can play certain effect in the short time, but can not solve question of substance.
Summary of the invention
In order to solve the problems referred to above, the invention provides a kind of cracking reinforcing agent for wicker products.
The present invention is achieved through the following technical solutions:
A kind of cracking reinforcing agent for wicker products, including A liquid and B liquid, described A liquid is made up of the material of following weight portion: 2
Part wood vinegar, 1 part of Mancozeb, 5 parts of Konjac glucomannan, 6 parts of sodium stearates, 3 parts of NPEs, 2 parts of high-carbon fatty alcohols
Polyoxyethylene ether, 4 parts of positive silicic acid propyl ester, 8 parts of polydimethylsiloxane, 5 parts of ammonium polyacrylates, 2 parts of boric acid, 100 parts of water；Described
B liquid is made up of the material of following weight portion: 4 parts of sodium hexameta phosphate, 3 parts of tartaric acid, 6 parts of sodium carboxymethyl cellulose, 5 parts of nanometers are lived
Property charcoal, 5 parts of nano silicons, 4 parts of propylene glycol methyl ether acetates, 15 parts of acrylic emulsions, 7 parts of Cortex Phellodendri extracts, 6 parts of Camphoras
Extract, 50 parts of water.
Further, the preparation method of described A liquid comprises the steps:
(1) by water temp. heating to 55 ~ 58 DEG C, then Konjac glucomannan and stearic acid sodium are added jointly, with 600 ~ 800 revs/min
Rotating speed is stirred continuously 15min, maintains 55 ~ 58 DEG C of condition insulation 30min standby the most again；
(2) by NPE, high-carbon fatty alcohol polyoxyethylene ether, positive silicic acid propyl ester, polydimethylsiloxane and poly-
Ammonium acrylate is common with the liquid mixing of step (1) gained, and heating holding temperature of liquid is 38 ~ 42 DEG C, with 1000 ~ 1200 turns/
Minute rotating speed be stirred continuously 20min, then naturally cool to room temperature standby；
(3) wood vinegar, Mancozeb and boric acid are joined jointly in the liquid of step (2) gained, with 350 ~ 400 revs/min
Rotating speed be stirred continuously 10min, then homogenizing 1h after i.e. obtain A liquid.
Further, the preparation method of described B liquid comprises the steps:
(1) sodium hexameta phosphate, tartaric acid, sodium carboxymethyl cellulose, Cortex Phellodendri extract and Camphora extract are joined water jointly
In, and to heat holding aqueous temperature be 45 ~ 48 DEG C, is stirred continuously to the most standby after uniformly；
(2) active carbon nanoparticles, nano silicon and propylene glycol methyl ether acetate are joined in acrylic emulsion jointly, at frequency
Rate be 38KHz ultrasonic Treatment instrument in standby after stir process 15min；
(3) step (2) gained solution is mixed in the solution of step (1) gained with the speed of 15 ~ 20ml/s, simultaneously with 500
Rev/min rotating speed stir and i.e. obtain B liquid.
The using method of the cracking reinforcing agent of a kind of wicker products, comprises the steps:
(1) first it is rinsed roguing with clear water position pending to wicker products；
(2) position after rinsing step (1) is dried, and drying to its surface moisture is 20 ~ 30%；
(3) A liquid is sprayed at step (2) dry after wicker products on, then treat its naturally dry to surface tack-free；
(4) being uniformly sprayed at by B liquid on the wicker products after step (3) processes, putting it into temperature after completing is 35 ~ 38 DEG C
Under the conditions of dried 5 ~ 7min.
There is advantages that
(1) the A liquid of present invention preparation can well kill at wicker products cracking the impurity such as the antibacterial of residual, fungus, worm's ovum, anti-
Only it is further to the erosion within wicker plaiting article, has again preferable mobility simultaneously, relatively strong with cellulosic structure affinity, and
Tiny wooden burr can be softened to a certain extent, coat a hypoglyph in its surface, establish very well for follow-up operation
Basis.
(2) between the B liquid of present invention preparation and the counterdie of A liquid formation, adhesiveness is relatively strong, active carbon nanoparticles, nano silicon
Well it is filled with the gap of wicker products with acrylic emulsion, and enhances its wear resistence and intensity, Cortex Phellodendri extract and Camphor tree
The interpolation of brain extract enhances again the Vermins-proof mildew-proof performance of wicker products.
(3) the cracking reinforcing agent of present invention preparation is under the common effect of A liquid and B liquid, is well filled with gap, it is to avoid
The erosion to it of the exogenous impurity composition, improves again its Vermins-proof mildew-proof performance and the intensity of entirety and wearability, A liquid and B
The mixture that liquid is collectively forming not only has good cohesive force, has again certain elasticity, can improve its shock resistance, relatively
Pure glue bonds more practicality.The surface strength of final wicker products can improve about 40%, and it is left that rupture strength can improve 50%
The right side, is less susceptible to deformation, can extend 1 ~ 2 times service life, and use value is higher.
Detailed description of the invention
Embodiment 1
A kind of cracking reinforcing agent for wicker products, including A liquid and B liquid, described A liquid is made up of the material of following weight portion: 2
Part wood vinegar, 1 part of Mancozeb, 5 parts of Konjac glucomannan, 6 parts of sodium stearates, 3 parts of NPEs, 2 parts of high-carbon fatty alcohols
Polyoxyethylene ether, 4 parts of positive silicic acid propyl ester, 8 parts of polydimethylsiloxane, 5 parts of ammonium polyacrylates, 2 parts of boric acid, 100 parts of water；Described
B liquid is made up of the material of following weight portion: 4 parts of sodium hexameta phosphate, 3 parts of tartaric acid, 6 parts of sodium carboxymethyl cellulose, 5 parts of nanometers are lived
Property charcoal, 5 parts of nano silicons, 4 parts of propylene glycol methyl ether acetates, 15 parts of acrylic emulsions, 7 parts of Cortex Phellodendri extracts, 6 parts of Camphoras
Extract, 50 parts of water.
Further, the preparation method of described A liquid comprises the steps:
(1) by water temp. heating to 58 DEG C, then Konjac glucomannan and stearic acid sodium jointly being added, the rotating speed with 700 revs/min is continuous
Stirring 15min, maintains 56 DEG C of condition insulation 30min standby the most again；
(2) by NPE, high-carbon fatty alcohol polyoxyethylene ether, positive silicic acid propyl ester, polydimethylsiloxane and poly-
Ammonium acrylate is common with the liquid mixing of step (1) gained, and heating keeps temperature of liquid to be 39 DEG C, with 1100 revs/min turn
Speed is stirred continuously 20min, then naturally cools to room temperature standby；
(3) wood vinegar, Mancozeb and boric acid are joined jointly in the liquid of step (2) gained, with 390 revs/min turn
Speed i.e. obtains A liquid after being stirred continuously 10min, then homogenizing 1h.
Further, the preparation method of described B liquid comprises the steps:
(1) sodium hexameta phosphate, tartaric acid, sodium carboxymethyl cellulose, Cortex Phellodendri extract and Camphora extract are joined water jointly
In, and to heat holding aqueous temperature be 48 DEG C, is stirred continuously to the most standby after uniformly；
(2) active carbon nanoparticles, nano silicon and propylene glycol methyl ether acetate are joined in acrylic emulsion jointly, at frequency
Rate be 38KHz ultrasonic Treatment instrument in standby after stir process 15min；
(3) step (2) gained solution is mixed in the solution of step (1) gained with the speed of 18ml/s, simultaneously with 500 turns/
Minute rotating speed stir and i.e. obtain B liquid.
The using method of the cracking reinforcing agent of a kind of wicker products, comprises the steps:
(1) first it is rinsed roguing with clear water position pending to wicker products；
(2) position after rinsing step (1) is dried, and drying to its surface moisture is 27 ~ 30%；
(3) A liquid is sprayed at step (2) dry after wicker products on, then treat its naturally dry to surface tack-free；
(4) B liquid is uniformly sprayed on the wicker products after step (3) processes, after completing, puts it into the bar that temperature is 37 DEG C
Dried 5min under part.
Comparative example 1
Compared with Example 1, described A liquid is the most identical with each composition proportion in B liquid, but the most straight for this comparative example 1
Connecing the mixed liquor that A liquid and B liquid composition carry out be mixed and made into one, both weight ratios are 1:1.5, are the most also direct
Spray mixed liquor.
Matched group
Plank class adhesive.
In order to contrast effect of the present invention, with solvent corresponding to above-mentioned three kinds of modes respectively to same batch, cracking degree phase
As wicker products process, and its performance of test statistics, find that the rupture strength of the wicker products of embodiment 1 correspondence is right
Ratio 1.2 times of embodiment 1, is 1.1 times of matched group；Its service life is 1.3 times of comparative example 1, is the 1.7 of matched group
Times, it is 2.5 times of the unprocessed wicker products life-span.
Claims (4)
1. the cracking reinforcing agent for wicker products, it is characterised in that including A liquid and B liquid, described A liquid is by following weight
Part material make: 2 parts of wood vinegar, 1 part of Mancozeb, 5 parts of Konjac glucomannan, 6 parts of sodium stearates, 3 parts of NPEs,
2 parts of high-carbon fatty alcohol polyoxyethylene ethers, 4 parts of positive silicic acid propyl ester, 8 parts of polydimethylsiloxane, 5 parts of ammonium polyacrylates, 2 parts of boron
Acid, 100 parts of water；Described B liquid is made up of the material of following weight portion: 4 parts of sodium hexameta phosphate, 3 parts of tartaric acid, 6 parts of carboxymethyl fibres
Dimension element sodium, 5 parts of active carbon nanoparticles, 5 parts of nano silicons, 4 parts of propylene glycol methyl ether acetates, 15 parts of acrylic emulsions, 7 parts of Huangs
Cypress extract, 6 parts of Camphora extracts, 50 parts of water.
A kind of cracking reinforcing agent for wicker products the most according to claim 1, it is characterised in that the system of described A liquid
Preparation Method comprises the steps:
(1) by water temp. heating to 55 ~ 58 DEG C, then Konjac glucomannan and stearic acid sodium are added jointly, with 600 ~ 800 revs/min
Rotating speed is stirred continuously 15min, maintains 55 ~ 58 DEG C of condition insulation 30min standby the most again；
(2) by NPE, high-carbon fatty alcohol polyoxyethylene ether, positive silicic acid propyl ester, polydimethylsiloxane and poly-
Ammonium acrylate is common with the liquid mixing of step (1) gained, and heating holding temperature of liquid is 38 ~ 42 DEG C, with 1000 ~ 1200 turns/
Minute rotating speed be stirred continuously 20min, then naturally cool to room temperature standby；
(3) wood vinegar, Mancozeb and boric acid are joined jointly in the liquid of step (2) gained, with 350 ~ 400 revs/min
Rotating speed be stirred continuously 10min, then homogenizing 1h after i.e. obtain A liquid.
A kind of cracking reinforcing agent for wicker products the most according to claim 1, it is characterised in that the system of described B liquid
Preparation Method comprises the steps:
(1) sodium hexameta phosphate, tartaric acid, sodium carboxymethyl cellulose, Cortex Phellodendri extract and Camphora extract are joined water jointly
In, and to heat holding aqueous temperature be 45 ~ 48 DEG C, is stirred continuously to the most standby after uniformly；
(2) active carbon nanoparticles, nano silicon and propylene glycol methyl ether acetate are joined in acrylic emulsion jointly, at frequency
Rate be 38KHz ultrasonic Treatment instrument in standby after stir process 15min；
(3) step (2) gained solution is mixed in the solution of step (1) gained with the speed of 15 ~ 20ml/s, simultaneously with 500
Rev/min rotating speed stir and i.e. obtain B liquid.
4. the wicker products as described in claim 1 ~ 3 cracking reinforcing agent using method, it is characterised in that include as
Lower step:
(1) first it is rinsed roguing with clear water position pending to wicker products；
(2) position after rinsing step (1) is dried, and drying to its surface moisture is 20 ~ 30%；
(3) A liquid is sprayed at step (2) dry after wicker products on, then treat its naturally dry to surface tack-free；
(4) being uniformly sprayed at by B liquid on the wicker products after step (3) processes, putting it into temperature after completing is 35 ~ 38 DEG C
Under the conditions of dried 5 ~ 7min.