CN106118503A - A kind of flame-retardant storage battery fluid sealant based on propane three ester and isobornyl thiocyanoacetate and manufacture method - Google Patents
A kind of flame-retardant storage battery fluid sealant based on propane three ester and isobornyl thiocyanoacetate and manufacture method Download PDFInfo
- Publication number
- CN106118503A CN106118503A CN201610487912.5A CN201610487912A CN106118503A CN 106118503 A CN106118503 A CN 106118503A CN 201610487912 A CN201610487912 A CN 201610487912A CN 106118503 A CN106118503 A CN 106118503A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- solvent
- ester
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of flame-retardant storage battery fluid sealant based on propane three ester and isobornyl thiocyanoacetate and manufacture method, including component A and B component;Described component A is made up of methacrylic acid trimethylolpropane triester, solvent, dioctyl phthalate, decabromodiphenyl oxide, reinforcing filler, antioxidant 1010, neoprene;B component is made up of isobornyl methacrylate, polyether rubber, trimethyl thiourea, Phosphonate Flame Retardant plasticizer, calcium carbonate, solvent, DEUCHEM2700, butyl titanate;The present invention by by the adhesive of two components of A, B by mixing in respectively vacuum kneading and reactor, make the adhesive of two different components.The present invention is by carrying out rational proportioning by the raw material in A, B component, make the bonding that two kinds of components in use can be good, and reduce the generation of air entrapment, decrease glue internal clearance, add good fire protecting performance and heat-proof quality simultaneously, ensure that the original mobility of adhesive, decrease the discharge of harmful substance.
Description
Technical field
The present invention relates to chemical technology field, particularly to accumulator being played the one of sealing function based on propane three ester
Flame-retardant storage battery fluid sealant and manufacture method with isobornyl thiocyanoacetate.
Background technology
Macromolecular material is increasingly extensive in building material industry application, but macromolecular material itself easily burns, when fire is sent out
Time raw, burning discharges substantial amounts of toxic gas, such as carbon monoxide, nitric oxide etc., people just can be made in very short time to be poisoned
Dead.Great mass of data shows, toxic smoke is the first of causing death the big killer in fire.Thus the fire resistance of construction material is direct
It is related to the people's lives and property safety.And the halogen flame that flame retardant sealant adds in a large number now can be given birth in combustion
Become the toxic gas such as substantial amounts of hydrogen halides, and bittern-free flame-proof material, magnesium hydroxide, aluminium hydroxide flame retardant effect poor, addition
Greatly, material property is had a strong impact on.Simultaneously because add substantial amounts of fire retardant, cause the mobility of fluid sealant to decline, be difficult to immerse
Narrow and small filleting, makes troubles to construction.
Summary of the invention
It is an object of the invention to provide one to have and decrease glue internal clearance, add simultaneously good fire protecting performance and every
Hot property, it is ensured that the original mobility of adhesive, decreases the one of discharge of harmful substance based on propane three ester and different ice
The flame-retardant storage battery fluid sealant of sheet ester and manufacture method, solve the use needs of problems of accumulator sealant.
In order to achieve the above object, the present invention provides following technical scheme:
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate, it is characterised in that: include component A and B component;
Described component A by methacrylic acid trimethylolpropane triester, solvent, dioctyl phthalate, decabromodiphenyl oxide, reinforcing
Filler, antioxidant 1010, neoprene forms;B component is by isobornyl methacrylate, polyether rubber, trimethyl thiourea, phosphine
Ester flame-proof plasticizing agent, calcium carbonate, solvent, DEUCHEM2700, butyl titanate forms;In wherein said component A, including: 40-
The methacrylic acid trimethylolpropane triester of 60 parts, the solvent of 20-30 part, the dioctyl phthalate of 4-8 part, 10-25
The decabromodiphenyl oxide of part, the reinforcing filler of 5-10 part, the antioxidant 1010 of 5-10 part, the neoprene composition of 20-35 part;Institute
State in B component, including: the isobornyl methacrylate of 60-80 part, the polyether rubber of 20-30 part, the trimethyl sulfur of 5-15 part
Urea, the Phosphonate Flame Retardant plasticizer of 5-15 part, the calcium carbonate of 5-10 part, 25-40 part solvent, the DEUCHEM2700 of 10-15 part,
The butyl titanate of 4-10 part.
Described solvent is in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene
One or more;Reinforcing filler be fume colloidal silica, precipitated silica and surface process the one in white carbon or
Several.
In described component A, including: the methacrylic acid trimethylolpropane triester of 40-55 part, the solvent of 20-28 part, 4-
The dioctyl phthalate of 7 parts, the decabromodiphenyl oxide of 10-22 part, the reinforcing filler of 5-8 part, the antioxidant of 5-9 part
The neoprene composition of 1010,20-33 parts;In described B component, including: the isobornyl methacrylate of 60-78 part, 20-25
The polyether rubber of part, the trimethyl thiourea of 5-12 part, the Phosphonate Flame Retardant plasticizer of 5-13 part, the calcium carbonate of 5-8 part, 25-35
The solvent of part, the butyl titanate of the DEUCHEM2700 of 10-14 part, 4-8 part.
In described component A, including: the methacrylic acid trimethylolpropane triester of 50 parts, the solvent of 25 parts, the neighbour of 6 parts
Dioctyl phthalate, the decabromodiphenyl oxide of 22 parts, the reinforcing filler of 8 parts, the antioxidant 1010 of 8 parts, the neoprene rubber of 28 parts
Glue forms;In described B component, including: the isobornyl methacrylate of 70 parts, the polyether rubber of 25 parts, the trimethyl of 10 parts
Thiourea, the Phosphonate Flame Retardant plasticizer of 10 parts, the calcium carbonate of 8 parts, the solvent of 35 parts, the DEUCHEM2700 of 13 parts, the titanium of 8 parts
Acid butyl ester.
Concretely comprise the following steps:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, de-
Water is blended 60~300 minutes, prepares A group compound, moves in high speed dispersion stirred tank, standby;By methacrylic acid in B component
Isobornyl thiocyanoacetate, polyether rubber, Phosphonate Flame Retardant plasticizer, solvent adds vacuum kneader according to above-mentioned parts by weight proportioning mode
In, in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, dehydration is blended 60~300 minutes, prepares B group compound, shifting
Enter in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares A group and is thoroughly mixed
Material;To add trimethyl thiourea in above-mentioned B group compound, calcium carbonate, DEUCHEM2700, butyl titanate is placed in stirred tank, very
Reciprocal of duty cycle is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares B group and is thoroughly mixed material.
Beneficial effects of the present invention: the present invention, by the raw material in A, B component is carried out rational proportioning, makes two kinds of components
Bonding that in use can be good, and reduce the generation of air entrapment, decrease glue internal clearance, add simultaneously
Good fire protecting performance and heat-proof quality, it is ensured that the original mobility of adhesive, decrease the discharge of harmful substance.
Detailed description of the invention
Below in conjunction with embodiment, technical scheme is clearly and completely described, it is clear that described
Embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under not making creative work premise, broadly falls into present invention protection
Scope.
Embodiment 1:
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate, it is characterised in that: include component A and B component;
Described component A by methacrylic acid trimethylolpropane triester, solvent, dioctyl phthalate, decabromodiphenyl oxide, reinforcing
Filler, antioxidant 1010, neoprene forms;B component is by isobornyl methacrylate, polyether rubber, trimethyl thiourea, phosphine
Ester flame-proof plasticizing agent, calcium carbonate, solvent, DEUCHEM2700, butyl titanate forms;In wherein said component A, including: 40-
The methacrylic acid trimethylolpropane triester of 60 parts, the solvent of 20-30 part, the dioctyl phthalate of 4-8 part, 10-25
The decabromodiphenyl oxide of part, the reinforcing filler of 5-10 part, the antioxidant 1010 of 5-10 part, the neoprene composition of 20-35 part;Institute
State in B component, including: the isobornyl methacrylate of 60-80 part, the polyether rubber of 20-30 part, the trimethyl sulfur of 5-15 part
Urea, the Phosphonate Flame Retardant plasticizer of 5-15 part, the calcium carbonate of 5-10 part, 25-40 part solvent, the DEUCHEM2700 of 10-15 part,
The butyl titanate of 4-10 part.
Described solvent is in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene
One or more;Reinforcing filler be fume colloidal silica, precipitated silica and surface process the one in white carbon or
Several.
In described component A, including: the methacrylic acid trimethylolpropane triester of 40-55 part, the solvent of 20-28 part, 4-
The dioctyl phthalate of 7 parts, the decabromodiphenyl oxide of 10-22 part, the reinforcing filler of 5-8 part, the antioxidant of 5-9 part
The neoprene composition of 1010,20-33 parts;In described B component, including: the isobornyl methacrylate of 60-78 part, 20-25
The polyether rubber of part, the trimethyl thiourea of 5-12 part, the Phosphonate Flame Retardant plasticizer of 5-13 part, the calcium carbonate of 5-8 part, 25-35
The solvent of part, the butyl titanate of the DEUCHEM2700 of 10-14 part, 4-8 part.
In described component A, including: the methacrylic acid trimethylolpropane triester of 50 parts, the solvent of 25 parts, the neighbour of 6 parts
Dioctyl phthalate, the decabromodiphenyl oxide of 22 parts, the reinforcing filler of 8 parts, the antioxidant 1010 of 8 parts, the neoprene rubber of 28 parts
Glue forms;In described B component, including: the isobornyl methacrylate of 70 parts, the polyether rubber of 25 parts, the trimethyl of 10 parts
Thiourea, the Phosphonate Flame Retardant plasticizer of 10 parts, the calcium carbonate of 8 parts, the solvent of 35 parts, the DEUCHEM2700 of 13 parts, the titanium of 8 parts
Acid butyl ester.
Concretely comprise the following steps:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, de-
Water is blended 60~300 minutes, prepares A group compound, moves in high speed dispersion stirred tank, standby;By methacrylic acid in B component
Isobornyl thiocyanoacetate, polyether rubber, Phosphonate Flame Retardant plasticizer, solvent adds vacuum kneader according to above-mentioned parts by weight proportioning mode
In, in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, dehydration is blended 60~300 minutes, prepares B group compound, shifting
Enter in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares A group and is thoroughly mixed
Material;To add trimethyl thiourea in above-mentioned B group compound, calcium carbonate, DEUCHEM2700, butyl titanate is placed in stirred tank, very
Reciprocal of duty cycle is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares B group and is thoroughly mixed material.
Embodiment 2:
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate, it is characterised in that: include component A and B component;
Described component A by methacrylic acid trimethylolpropane triester, solvent, dioctyl phthalate, decabromodiphenyl oxide, reinforcing
Filler, antioxidant 1010, neoprene forms;B component is by isobornyl methacrylate, polyether rubber, trimethyl thiourea, phosphine
Ester flame-proof plasticizing agent, calcium carbonate, solvent, DEUCHEM2700, butyl titanate forms;In wherein said component A, including: 40-
The methacrylic acid trimethylolpropane triester of 60 parts, the solvent of 20-30 part, the dioctyl phthalate of 4-8 part, 10-25
The decabromodiphenyl oxide of part, the reinforcing filler of 5-10 part, the antioxidant 1010 of 5-10 part, the neoprene composition of 20-35 part;Institute
State in B component, including: the isobornyl methacrylate of 60-80 part, the polyether rubber of 20-30 part, the trimethyl sulfur of 5-15 part
Urea, the Phosphonate Flame Retardant plasticizer of 5-15 part, the calcium carbonate of 5-10 part, 25-40 part solvent, the DEUCHEM2700 of 10-15 part,
The butyl titanate of 4-10 part.
Following manufacture method is utilized to make the proportioning in above-mentioned component:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, de-
Water is blended 60~300 minutes, prepares A group compound, moves in high speed dispersion stirred tank, standby;By methacrylic acid in B component
Isobornyl thiocyanoacetate, polyether rubber, Phosphonate Flame Retardant plasticizer, solvent adds vacuum kneader according to above-mentioned parts by weight proportioning mode
In, in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, dehydration is blended 60~300 minutes, prepares B group compound, shifting
Enter in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares A group and is thoroughly mixed
Material;To add trimethyl thiourea in above-mentioned B group compound, calcium carbonate, DEUCHEM2700, butyl titanate is placed in stirred tank, very
Reciprocal of duty cycle is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares B group and is thoroughly mixed material.
Component A and B component stand subpackage respectively, during use directly by component A, B component according to weight ratio mix homogeneously after
Potting operation can be carried out.
Following table is the Data Comparison of the present invention and other series products:
Upper table shows that the properties of the present invention is better than like product, can meet the process requirements that accumulator seals.
Embodiment 3:
In described component A, including: the methacrylic acid trimethylolpropane triester of 40-55 part, the solvent of 20-28 part, 4-7 part
Dioctyl phthalate, the decabromodiphenyl oxide of 10-22 part, the reinforcing filler of 5-8 part, the antioxidant 1010 of 5-9 part,
The neoprene composition of 20-33 part;In described B component, including: the isobornyl methacrylate of 60-78 part, 20-25 part
Polyether rubber, the trimethyl thiourea of 5-12 part, the Phosphonate Flame Retardant plasticizer of 5-13 part, the calcium carbonate of 5-8 part, 25-35 part
Solvent, the butyl titanate of the DEUCHEM2700 of 10-14 part, 4-8 part.
Following manufacture method is utilized to make the proportioning in above-mentioned component:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 100 DEG C, vacuum is 0.12MPa, dehydration is blended 300
Minute, prepare A group compound, move in high speed dispersion stirred tank, standby;By isobornyl methacrylate in B component, polyethers
Rubber, Phosphonate Flame Retardant plasticizer, solvent adds in vacuum kneader, in temperature 100 according to above-mentioned parts by weight proportioning mode
DEG C, vacuum is 0.12MPa, dehydration is blended 300 minutes, prepares B group compound, moves in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.12MPa, rotating speed 600rpm, is sufficiently mixed 5 hours, prepares A group and is thoroughly mixed material;Above-mentioned B group is mixed
Adding trimethyl thiourea, calcium carbonate, DEUCHEM2700 in material, butyl titanate is placed in stirred tank, and vacuum is 0.12MPa, turns
Speed 600rpm, is sufficiently mixed 5 hours, prepares B group and is thoroughly mixed material.
Component A and B component stand subpackage respectively, during use directly by component A, B component according to weight ratio mix homogeneously after
Potting operation can be carried out.
Embodiment 4:
In described component A, including: the methacrylic acid trimethylolpropane triester of 50 parts, the solvent of 25 parts, the adjacent benzene two of 6 parts
Formic acid dioctyl ester, the decabromodiphenyl oxide of 22 parts, the reinforcing filler of 8 parts, the antioxidant 1010 of 8 parts, the neoprene group of 28 parts
Become;In described B component, including: the isobornyl methacrylate of 70 parts, the polyether rubber of 25 parts, the trimethyl thiourea of 10 parts,
The Phosphonate Flame Retardant plasticizer of 10 parts, the calcium carbonate of 8 parts, the solvent of 35 parts, the DEUCHEM2700 of 13 parts, the metatitanic acid fourth of 8 parts
Ester.
Following manufacture method is utilized to make the proportioning in above-mentioned component:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 70 C, vacuum is 0.08MPa, dehydration is blended 60 points
Clock, prepares A group compound, moves in high speed dispersion stirred tank, standby;By isobornyl methacrylate in B component, polyethers rubber
Glue, Phosphonate Flame Retardant plasticizer, solvent adds in vacuum kneader according to above-mentioned parts by weight proportioning mode, in temperature 70 C,
Vacuum is 0.08MPa, dehydration is blended 60 minutes, prepares B group compound, moves in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.08MPa, rotating speed 100rpm, is sufficiently mixed 5 hours, prepares A group and is thoroughly mixed material;Above-mentioned B group is mixed
Adding trimethyl thiourea, calcium carbonate, DEUCHEM2700 in material, butyl titanate is placed in stirred tank, and vacuum is 0.08MPa, turns
Speed 100rpm, is sufficiently mixed 5 hours, prepares B group and is thoroughly mixed material.
Component A and B component stand subpackage respectively, during use directly by component A, B component according to weight ratio mix homogeneously after
Potting operation can be carried out.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
Those familiar with the art, in the technical scope that the invention discloses, can readily occur in change or replace, should contain
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should described be as the criterion with scope of the claims.
Claims (5)
1. a flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate, it is characterised in that: include component A and B group
Point;Described component A, by methacrylic acid trimethylolpropane triester, solvent, dioctyl phthalate, decabromodiphenyl oxide, is mended
Epistasis filler, antioxidant 1010, neoprene forms;B component is by isobornyl methacrylate, polyether rubber, trimethyl sulfur
Urea, Phosphonate Flame Retardant plasticizer, calcium carbonate, solvent, DEUCHEM2700, butyl titanate forms;In wherein said component A, bag
Include: the methacrylic acid trimethylolpropane triester of 40-60 part, the solvent of 20-30 part, the dioctyl phthalate of 4-8 part,
The decabromodiphenyl oxide of 10-25 part, the reinforcing filler of 5-10 part, the antioxidant 1010 of 5-10 part, the neoprene group of 20-35 part
Become;In described B component, including: the isobornyl methacrylate of 60-80 part, the polyether rubber of 20-30 part, the three of 5-15 part
Methylthiourea, the Phosphonate Flame Retardant plasticizer of 5-15 part, the calcium carbonate of 5-10 part, 25-40 part solvent, 10-15 part
The butyl titanate of DEUCHEM2700,4-10 part.
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate the most according to claim 1, its feature
It is: described solvent is in acetone, chloroform, dichloroethanes, nylon acid dimethyl ester, ethyl acetate, toluene or dimethylbenzene
One or more;Reinforcing filler is the one or several that fume colloidal silica, precipitated silica and surface process in white carbon
Kind.
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate the most according to claim 1, its feature
It is: in described component A, including: the methacrylic acid trimethylolpropane triester of 40-55 part, the solvent of 20-28 part, 4-7 part
Dioctyl phthalate, the decabromodiphenyl oxide of 10-22 part, the reinforcing filler of 5-8 part, the antioxidant 1010 of 5-9 part,
The neoprene composition of 20-33 part;In described B component, including: the isobornyl methacrylate of 60-78 part, 20-25 part
Polyether rubber, the trimethyl thiourea of 5-12 part, the Phosphonate Flame Retardant plasticizer of 5-13 part, the calcium carbonate of 5-8 part, 25-35 part
Solvent, the butyl titanate of the DEUCHEM2700 of 10-14 part, 4-8 part.
A kind of flame-retardant storage battery fluid sealant based on propane three ester Yu isobornyl thiocyanoacetate the most according to claim 1, its feature
It is: in described component A, including: the methacrylic acid trimethylolpropane triester of 50 parts, the solvent of 25 parts, the adjacent benzene two of 6 parts
Formic acid dioctyl ester, the decabromodiphenyl oxide of 22 parts, the reinforcing filler of 8 parts, the antioxidant 1010 of 8 parts, the neoprene group of 28 parts
Become;In described B component, including: the isobornyl methacrylate of 70 parts, the polyether rubber of 25 parts, the trimethyl thiourea of 10 parts,
The Phosphonate Flame Retardant plasticizer of 10 parts, the calcium carbonate of 8 parts, the solvent of 35 parts, the DEUCHEM2700 of 13 parts, the metatitanic acid fourth of 8 parts
Ester.
5. seal according to a kind of based on propane three ester with isobornyl thiocyanoacetate the flame-retardant storage battery according to any one of claim 1-4
The manufacture method of glue, it is characterised in that: concretely comprise the following steps:
1, by methacrylic acid trimethylolpropane triester in component A, solvent, dioctyl phthalate, neoprene according to
Above-mentioned parts by weight proportioning mode adds in vacuum kneader, and in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, de-
Water is blended 60~300 minutes, prepares A group compound, moves in high speed dispersion stirred tank, standby;By methacrylic acid in B component
Isobornyl thiocyanoacetate, polyether rubber, Phosphonate Flame Retardant plasticizer, solvent adds vacuum kneader according to above-mentioned parts by weight proportioning mode
In, in temperature 70~100 DEG C, vacuum is 0.08~0.12MPa, dehydration is blended 60~300 minutes, prepares B group compound, shifting
Enter in high speed dispersion stirred tank, standby;
2, at room temperature, will add decabromodiphenyl oxide in above-mentioned A group compound, reinforcing filler, antioxidant 1010 is placed in stirring
In still, vacuum is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares A group and is thoroughly mixed
Material;To add trimethyl thiourea in above-mentioned B group compound, calcium carbonate, DEUCHEM2700, butyl titanate is placed in stirred tank, very
Reciprocal of duty cycle is 0.08~0.12MPa, rotating speed 100~600rpm, is sufficiently mixed 1~5 hour, prepares B group and is thoroughly mixed material.