CN106118397A - A kind of kitchen tubing anticorrosive paint - Google Patents

A kind of kitchen tubing anticorrosive paint Download PDF

Info

Publication number
CN106118397A
CN106118397A CN201610494991.2A CN201610494991A CN106118397A CN 106118397 A CN106118397 A CN 106118397A CN 201610494991 A CN201610494991 A CN 201610494991A CN 106118397 A CN106118397 A CN 106118397A
Authority
CN
China
Prior art keywords
parts
tubing
kitchen
anticorrosive paint
active charcoal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610494991.2A
Other languages
Chinese (zh)
Inventor
徐先锋
胡正才
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHENGSHI NEW BUILDING MATERIAL Co Ltd
Original Assignee
ANHUI ZHENGSHI NEW BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHENGSHI NEW BUILDING MATERIAL Co Ltd filed Critical ANHUI ZHENGSHI NEW BUILDING MATERIAL Co Ltd
Priority to CN201610494991.2A priority Critical patent/CN106118397A/en
Publication of CN106118397A publication Critical patent/CN106118397A/en
Pending legal-status Critical Current

Abstract

nullThe invention discloses a kind of kitchen tubing anticorrosive paint，Its raw material includes by weight: Epoxy Resin of Bisphenol A 20 30，Epoxy alkyd resin 10 18，Acrylic acid modified alkyd resin 40 80，N，N dimethylethanolamine 15，Styrene 15，Methylcellulose 5 10，Titanate coupling agent 12，Polydimethylsiloxane 13，Modified cocoanut active charcoal 5 20，Nano-glass microballon 5 10，Bentonite 28，Clay 6 10，Barium sulfate 28，Propylene glycol methyl ether acetate 24，2 amino 2 methyl 1 propanol 13，Pentyl acetate 5 20，Hydroxypropyl guar gum 12，Dodecylbenzene sodium sulfonate 12，Polyoxyethylene polyoxy propanol amidogen ether 12，Wetting agent 12，Preservative 0.5 1.5.Present invention oil smoke waterproof, resistance to, good toughness, excellent anti-corrosion performance, adhesive force is strong.

Description

A kind of kitchen tubing anticorrosive paint
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of kitchen tubing anticorrosive paint.
Background technology
At present, the pipe coatings used on the market is normally only used for decoration, and effect is preferable, but adhesive force, oil smoke waterproof, resistance to And corrosion resistance is poor, kitchen exterior wall tubing, owing to often passing rain drop erosion, fume pollution, cause tube surfaces paint film Easy to crack, peel off or overall peel off, rainwater, oil smoke just penetrate into inside tubing, corrode tubing, it would be highly desirable to solve.
Summary of the invention
The present invention proposes a kind of kitchen tubing anticorrosive paint, goods oil smoke waterproof, resistance to, good toughness, decay resistance Excellence, adhesive force is strong.
A kind of kitchen tubing anticorrosive paint that the present invention proposes, its raw material includes by weight: Epoxy Resin of Bisphenol A 20-30 part, epoxy alkyd resin 10-18 part, acrylic acid modified alkyd resin 40-80 part, N, N-dimethylethanolamine 1-5 Part, styrene 1-5 part, methylcellulose 5-10 part, titanate coupling agent 1-2 part, polydimethylsiloxane 1-3 part, modified coconut palm Shell activated carbon 5-20 part, nano-glass microballon 5-10 part, bentonite 2-8 part, clay 6-10 part, barium sulfate 2-8 part, propylene glycol first Ether acetate 2-4 part, 2-amino-2-methyl-1-propanol 1-3 part, pentyl acetate 5-20 part, hydroxypropyl guar gum 1-2 part, 12 Sodium alkyl benzene sulfonate 1-2 part, polyoxyethylene polyoxy propanol amidogen ether 1-2 part, wetting agent 1-2 part, preservative 0.5-1.5 part.
Preferably, modified cocoanut active charcoal uses following technique to prepare: Sanguis sus domestica, anticoagulant liquid is stirred, seals cold Hide, separate, obtain blood plasma liquid, concentrate, add cocoanut active charcoal stirring, ultrasonic, it is spray-dried, microwave treatment, adds absorbent cotton The seed dregs of rice, dehydrated alcohol, water, sodium hydroxide mixing and stirring, addition epoxy soybean oil, polypropylene glycol stir, and add three Ethanolamine, toluene di-isocyanate(TDI), '-diphenylmethane diisocyanate mix and blend, add starch, sodium metaperiodate, water mix and blend Uniformly, regulation system pH value, to 6-6.8, is warming up to 65-75 DEG C, adds tannic acid mix and blend, is cooled to 60-68 DEG C, adds Toluene di-isocyanate(TDI) mixing and stirring, is cooled to room temperature, obtains cocoanut active charcoal.
Preferably, modified cocoanut active charcoal uses following technique to prepare: by weight by 5-15 part Sanguis sus domestica, 0.1-0.5 part Anticoagulant liquid stirs, and seals cold preservation 1-5h, and refrigerated storage temperature is 2-6 DEG C；Separating, obtain blood plasma liquid, being concentrated into solid content is 20-28wt%, adds 5-10 part cocoanut active charcoal stirring 5-15min, and mixing speed is 40-80r/min, ultrasonic 10-30min, Being spray-dried, microwave treatment 2-6min, microwave power is 100-200W, adds 1-2 part degreased cottonseed meal, the anhydrous second of 5-15 part Alcohol, 5-15 part water, 0.1-0.7 part sodium hydroxide mixing and stirring, addition 1-2 part epoxy soybean oil, 1-2 part polypropylene glycol stir Mix uniformly, add 0.1-0.5 part triethanolamine, 1-2 part toluene di-isocyanate(TDI), 0.2-0.8 part '-diphenylmethane diisocyanate Mix and blend 10-20s, mixing speed is 600-800r/min, adds 1-4 part starch, 0.15-0.3 part sodium metaperiodate, 5-15 part Water mixing and stirring, regulation system pH value, to 6-6.8, is warming up to 65-75 DEG C, adds 1-2 part tannic acid mix and blend 10- 20min, is cooled to 60-68 DEG C, adds 0.1-0.7 part toluene di-isocyanate(TDI) mixing and stirring, is cooled to room temperature, obtains coconut palm Shell activated carbon.
Preferably, modified cocoanut active charcoal, nano-glass microballon, bentonite, clay, the weight ratio of barium sulfate are 10-15: 6-8:4-6:8-10:4-6.
Preferably, propylene glycol methyl ether acetate, 2-amino-2-methyl-1-propanol, the weight ratio of pentyl acetate are 3-3.6: 1.5-2.2:12-15.
Preferably, modified cocoanut active charcoal, methylcellulose, titanate coupling agent, the weight ratio of polydimethylsiloxane For 10-15:6-8:1.2-1.6:2-2.6.
Preferably, Epoxy Resin of Bisphenol A, epoxy alkyd resin, acrylic acid modified alkyd resin, modified coconut activated The weight ratio of charcoal is 22-26:12-14:50-60:10-15.
Preferably, N, N-dimethylethanolamine, cinnamic weight ratio are 2-3.5:2-2.8.
Preferably, described kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 22-26 Part, epoxy alkyd resin 12-14 part, acrylic acid modified alkyd resin 50-60 part, N, N-dimethylethanolamine 2-3.5 part, Styrene 2-2.8 part, methylcellulose 6-8 part, titanate coupling agent 1.2-1.6 part, polydimethylsiloxane 2-2.6 part, change Property cocoanut active charcoal 10-15 part, nano-glass microballon 6-8 part, bentonite 4-6 part, clay 8-10 part, barium sulfate 4-6 part, the third two Alcohol methyl ether acetate 3-3.6 part, 2-amino-2-methyl-1-propanol 1.5-2.2 part, pentyl acetate 12-15 part, hydroxypropyl guar Glue 1.4-1.8 part, dodecylbenzene sodium sulfonate 1.2-1.5 part, polyoxyethylene polyoxy propanol amidogen ether 1.2-1.5 part, wetting agent 1.2-1.5 part, preservative 1.2-1.4 part.
In the present invention, epoxy alkyd resin and Epoxy Resin of Bisphenol A, acrylic acid modified alkyd resin synergism, Goods dryness, oil smoke strong to substrate adhesion and waterproof, resistance to, resistance to chemical corrosion is excellent.At Epoxy Resin of Bisphenol A, epoxy Containing a large amount of conjugated alkene chains, epoxy resin chain, amino, hydroxyl, epoxy in modified alkyd resin, acrylic acid modified alkyd resin Base, ester group and carboxyl isoreactivity group, can produce net macromolecular, film compactness, corrosion resistant with modified cocoanut active charcoal effect Erosion, adhesion performance further enhance.
In modified cocoanut active charcoal, Sanguis sus domestica is through pretreatment, and emulsifying activity is fabulous with emulsion stability, and albumen in it Matter mounted molecule, acts under certain condition with degreased cottonseed meal further, and protein activation is thorough, the active group of protein molecule After group is grafted with epoxy soybean oil, residual activity group and the toluene di-isocyanate(TDI) of follow-up addition, diphenylmethane diisocyanates Ester reacts, and forms cross-linked network structure, and goods are water-fast and oil resistant smoke performance is fabulous, and additionally surface residual hydroxyl can be with starch, height Sodium iodate, tannic acid, toluene di-isocyanate(TDI) react, and goods toughness is fabulous, the most easy to crack；N, N-dimethylethanolamine and benzene second Alkene is as cross-linking agent, and coordinates work with modified cocoanut active charcoal, methylcellulose, titanate coupling agent, polydimethylsiloxane With, coating film forming postadhesion power is good, excellent anti-corrosion performance, and wet-heat resisting, temp. variation resistant, even if under the adverse circumstances of pole, also will not Produce speckle, blackout phenomenon.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
A kind of kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 20 parts, epoxide modified Alkyd resin 18 parts, acrylic acid modified alkyd resin 40 parts, N, N-dimethylethanolamine 5 parts, styrene 1 part, methylcellulose 10 parts, titanate coupling agent 1 part, polydimethylsiloxane 3 parts, modified cocoanut active charcoal 5 parts, nano-glass microballon 10 parts, swollen 2 parts of profit soil, clay 10 parts, 2 parts of barium sulfate, propylene glycol methyl ether acetate 4 parts, 2-amino-2-methyl-1-propanol 1 part, acetic acid penta Ester 20 parts, hydroxypropyl guar gum 1 part, dodecylbenzene sodium sulfonate 2 parts, polyoxyethylene polyoxy propanol amidogen ether 1 part, wetting agent 2 parts, Preservative 0.5 part.
Embodiment 2
A kind of kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 30 parts, epoxide modified Alkyd resin 10 parts, acrylic acid modified alkyd resin 80 parts, N, N-dimethylethanolamine 1 part, styrene 5 parts, methylcellulose 5 Part, titanate coupling agent 2 parts, polydimethylsiloxane 1 part, modified cocoanut active charcoal 20 parts, nano-glass microballon 5 parts, swelling 8 parts of soil, clay 6 parts, 8 parts of barium sulfate, propylene glycol methyl ether acetate 2 parts, 2-amino-2-methyl-1-propanol 3 parts, pentyl acetate 5 Part, hydroxypropyl guar gum 2 parts, dodecylbenzene sodium sulfonate 1 part, polyoxyethylene polyoxy propanol amidogen ether 2 parts, wetting agent 1 part, anticorrosion Agent 1.5 parts.
Modified cocoanut active charcoal uses following technique to prepare: Sanguis sus domestica, anticoagulant liquid are stirred, and seals cold preservation, separates, Obtain blood plasma liquid, concentrate, add cocoanut active charcoal stirring, ultrasonic, it is spray-dried, microwave treatment, adds degreased cottonseed meal, anhydrous Ethanol, water, sodium hydroxide mixing and stirring, addition epoxy soybean oil, polypropylene glycol stir, and add triethanolamine, first Phenylene diisocyanate, '-diphenylmethane diisocyanate mix and blend, add starch, sodium metaperiodate, water mixing and stirring, regulation System pH, to 6-6.8, is warming up to 65 DEG C, adds tannic acid mix and blend, is cooled to 68 DEG C, adds toluene di-isocyanate(TDI) and mixes Conjunction stirs, and is cooled to room temperature, obtains cocoanut active charcoal.
Embodiment 3
A kind of kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 22 parts, epoxide modified Alkyd resin 14 parts, acrylic acid modified alkyd resin 50 parts, N, N-dimethylethanolamine 3.5 parts, styrene 2 parts, Methyl cellulose Element 8 parts, titanate coupling agent 1.2 parts, polydimethylsiloxane 2.6 parts, modified cocoanut active charcoal 10 parts, nano-glass microballon 8 Part, bentonite 4 parts, clay 10 parts, 4 parts of barium sulfate, propylene glycol methyl ether acetate 3.6 parts, 2-amino-2-methyl-1-propanol 1.5 Part, pentyl acetate 15 parts, hydroxypropyl guar gum 1.4 parts, dodecylbenzene sodium sulfonate 1.5 parts, polyoxyethylene polyoxy propanol amidogen ether 1.2 parts, wetting agent 1.5 parts, preservative 1.2 parts.
Modified cocoanut active charcoal uses following technique to prepare: by weight by equal to 5 parts of Sanguis sus domestica, 0.5 part of anticoagulant liquid agitation Even, seal cold preservation 1h, refrigerated storage temperature is 6 DEG C；Separating, obtain blood plasma liquid, being concentrated into solid content is 20wt%, adds 10 parts of coconut husks Activated carbon stirring 5min, mixing speed is 80r/min, ultrasonic 10min, is spray-dried, and microwave treatment 6min, microwave power is 100W, adds 2 parts of degreased cottonseed meals, 5 parts of dehydrated alcohol, 15 parts of water, 0.1 part of sodium hydroxide mixing and stirring, adds 2 parts of rings Oxygen soybean oil, 1 part of polypropylene glycol stir, and add 0.5 part of triethanolamine, 1 part of toluene di-isocyanate(TDI), 0.8 part of hexichol first Alkane diisocyanate mix and blend 10s, mixing speed is 800r/min, adds 1 part of starch, 0.3 part of sodium metaperiodate, 5 parts of water mix Conjunction stirs, regulation system pH value to 6.8, is warming up to 65 DEG C, adds 2 parts of tannic acid mix and blend 10min, is cooled to 68 DEG C, add 0.1 part of toluene di-isocyanate(TDI) mixing and stirring, be cooled to room temperature, obtain cocoanut active charcoal.
Embodiment 4
A kind of kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 26 parts, epoxide modified Alkyd resin 12 parts, acrylic acid modified alkyd resin 60 parts, N, N-dimethylethanolamine 2 parts, styrene 2.8 parts, Methyl cellulose Element 6 parts, titanate coupling agent 1.6 parts, polydimethylsiloxane 2 parts, modified cocoanut active charcoal 15 parts, nano-glass microballon 6 parts, Bentonite 6 parts, clay 8 parts, 6 parts of barium sulfate, propylene glycol methyl ether acetate 3 parts, 2-amino-2-methyl-1-propanol 2.2 parts, second Acid pentyl ester 12 parts, hydroxypropyl guar gum 1.8 parts, dodecylbenzene sodium sulfonate 1.2 parts, polyoxyethylene polyoxy propanol amidogen ether 1.5 parts, Wetting agent 1.2 parts, preservative 1.4 parts.
Modified cocoanut active charcoal uses following technique to prepare: by weight by equal to 15 parts of Sanguis sus domestica, 0.1 part of anticoagulant liquid agitation Even, seal cold preservation 5h, refrigerated storage temperature is 2 DEG C；Separating, obtain blood plasma liquid, being concentrated into solid content is 28wt%, adds 5 parts of coconut husks Activated carbon stirring 15min, mixing speed is 40r/min, ultrasonic 30min, is spray-dried, and microwave treatment 2min, microwave power is 200W, adds 1 part of degreased cottonseed meal, 15 parts of dehydrated alcohol, 5 parts of water, 0.7 part of sodium hydroxide mixing and stirring, adds 1 part of ring Oxygen soybean oil, 2 parts of polypropylene glycols stir, and add 0.1 part of triethanolamine, 2 parts of toluene di-isocyanate(TDI)s, 0.2 part of hexichol first Alkane diisocyanate mix and blend 20s, mixing speed is 600r/min, adds 4 parts of starch, 0.15 part of sodium metaperiodate, 15 parts of water Mixing and stirring, regulation system pH value, to 6-6.8, is warming up to 65 DEG C, adds 2 parts of tannic acid mix and blend 10min, is cooled to 68 DEG C, add 0.1 part of toluene di-isocyanate(TDI) mixing and stirring, be cooled to room temperature, obtain cocoanut active charcoal.
Embodiment 5
A kind of kitchen tubing anticorrosive paint, its raw material includes by weight: Epoxy Resin of Bisphenol A 24 parts, epoxide modified Alkyd resin 13 parts, acrylic acid modified alkyd resin 55 parts, N, N-dimethylethanolamine 3 parts, styrene 2.4 parts, Methyl cellulose Element 7 parts, titanate coupling agent 1.4 parts, polydimethylsiloxane 2.3 parts, modified cocoanut active charcoal 12 parts, nano-glass microballon 7 Part, bentonite 5 parts, clay 9 parts, 5 parts of barium sulfate, propylene glycol methyl ether acetate 3.3 parts, 2-amino-2-methyl-1-propanol 2 parts, Pentyl acetate 14 parts, hydroxypropyl guar gum 1.6 parts, dodecylbenzene sodium sulfonate 1.3 parts, polyoxyethylene polyoxy propanol amidogen ether 1.4 Part, wetting agent 1.4 parts, preservative 1.3 parts.
Modified cocoanut active charcoal uses following technique to prepare: by weight by equal to 10 parts of Sanguis sus domestica, 0.2 part of anticoagulant liquid agitation Even, seal cold preservation 3h, refrigerated storage temperature is 4 DEG C；Separating, obtain blood plasma liquid, being concentrated into solid content is 24wt%, adds 12.5 portions of coconut palms Shell activated carbon stirring 10min, mixing speed is 60r/min, ultrasonic 20min, is spray-dried, microwave treatment 4min, microwave power For 150W, add 1.5 parts of degreased cottonseed meals, 10 parts of dehydrated alcohol, 10 parts of water, 0.4 part of sodium hydroxide mixing and stirring, add 1.2 parts of epoxy soybean oils, 1.6 parts of polypropylene glycols stir, add 0.3 part of triethanolamine, 1.5 parts of toluene di-isocyanate(TDI)s, 0.5 part of '-diphenylmethane diisocyanate mix and blend 15s, mixing speed is 700r/min, adds 2.5 parts of starch, 0.2 part of high iodine Acid sodium, 10 parts of water mixing and stirring, regulation system pH value, to 6-6.8, is warming up to 70 DEG C, adds 1.5 parts of tannic acid mixing and stirs Mix 15min, be cooled to 64 DEG C, add 0.4 part of toluene di-isocyanate(TDI) mixing and stirring, be cooled to room temperature, obtain coconut husk and live Property charcoal.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto, Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.

Claims (8)

1. a kitchen tubing anticorrosive paint, it is characterised in that its raw material includes by weight: Epoxy Resin of Bisphenol A 20-30 Part, epoxy alkyd resin 10-18 part, acrylic acid modified alkyd resin 40-80 part, N, N-dimethylethanolamine 1-5 part, benzene Ethylene 1-5 part, methylcellulose 5-10 part, titanate coupling agent 1-2 part, polydimethylsiloxane 1-3 part is modified coconut activated Charcoal 5-20 part, nano-glass microballon 5-10 part, bentonite 2-8 part, clay 6-10 part, barium sulfate 2-8 part, propylene glycol monomethyl ether acetic acid Ester 2-4 part, 2-amino-2-methyl-1-propanol 1-3 part, pentyl acetate 5-20 part, hydroxypropyl guar gum 1-2 part, detergent alkylate Sodium sulfonate 1-2 part, polyoxyethylene polyoxy propanol amidogen ether 1-2 part, wetting agent 1-2 part, preservative 0.5-1.5 part.
Kitchen the most according to claim 1 tubing anticorrosive paint, it is characterised in that modified cocoanut active charcoal uses as follows Prepared by technique: Sanguis sus domestica, anticoagulant liquid are stirred, and seals cold preservation, separates, obtains blood plasma liquid, concentrates, and adds cocoanut active charcoal Stirring, ultrasonic, it is spray-dried, microwave treatment, adds degreased cottonseed meal, dehydrated alcohol, water, sodium hydroxide mixing and stirring, Add epoxy soybean oil, polypropylene glycol stirs, and adds triethanolamine, toluene di-isocyanate(TDI), diphenylmethane diisocyanates Ester mix and blend, adds starch, sodium metaperiodate, water mixing and stirring, and regulation system pH value, to 6-6.8, is warming up to 65-75 DEG C, add tannic acid mix and blend, be cooled to 60-68 DEG C, add toluene di-isocyanate(TDI) mixing and stirring, be cooled to room Temperature, obtains cocoanut active charcoal.
Kitchen the most according to claim 1 and 2 tubing anticorrosive paint, it is characterised in that modified cocoanut active charcoal, nanometer Glass microballoon, bentonite, clay, the weight ratio of barium sulfate are 10-15:6-8:4-6:8-10:4-6.
Kitchen the most according to claim 1 and 2 tubing anticorrosive paint, it is characterised in that propylene glycol methyl ether acetate, 2- Amino-2-methyl-1-propanol, the weight ratio of pentyl acetate are 3-3.6:1.5-2.2:12-15.
Kitchen the most according to claim 1 and 2 tubing anticorrosive paint, it is characterised in that modified cocoanut active charcoal, methyl Cellulose, titanate coupling agent, the weight ratio of polydimethylsiloxane are 10-15:6-8:1.2-1.6:2-2.6.
Kitchen the most according to claim 1 and 2 tubing anticorrosive paint, it is characterised in that Epoxy Resin of Bisphenol A, epoxy Modified alkyd resin, acrylic acid modified alkyd resin, the weight ratio of modified cocoanut active charcoal are 22-26:12-14:50-60:10- 15。
Kitchen the most according to claim 1 and 2 tubing anticorrosive paint, it is characterised in that N, N-dimethylethanolamine, benzene The weight ratio of ethylene is 2-3.5:2-2.8.
8. according to the kitchen tubing anticorrosive paint described in any one of claim 1-7, it is characterised in that its raw material is by weight Including: Epoxy Resin of Bisphenol A 22-26 part, epoxy alkyd resin 12-14 part, acrylic acid modified alkyd resin 50-60 part, N, N-dimethylethanolamine 2-3.5 part, styrene 2-2.8 part, methylcellulose 6-8 part, titanate coupling agent 1.2-1.6 part, Polydimethylsiloxane 2-2.6 part, modified cocoanut active charcoal 10-15 part, nano-glass microballon 6-8 part, bentonite 4-6 part is viscous Soil 8-10 part, barium sulfate 4-6 part, propylene glycol methyl ether acetate 3-3.6 part, 2-amino-2-methyl-1-propanol 1.5-2.2 part, second Acid pentyl ester 12-15 part, hydroxypropyl guar gum 1.4-1.8 part, dodecylbenzene sodium sulfonate 1.2-1.5 part, polyoxyethylene polyoxy third Alcohol amidogen ether 1.2-1.5 part, wetting agent 1.2-1.5 part, preservative 1.2-1.4 part.
CN201610494991.2A 2016-06-29 2016-06-29 A kind of kitchen tubing anticorrosive paint Pending CN106118397A (en)