CN106085066A - A kind of water-repellent paint used for building exterior wall - Google Patents

A kind of water-repellent paint used for building exterior wall Download PDF

Info

Publication number
CN106085066A
CN106085066A CN201610573652.3A CN201610573652A CN106085066A CN 106085066 A CN106085066 A CN 106085066A CN 201610573652 A CN201610573652 A CN 201610573652A CN 106085066 A CN106085066 A CN 106085066A
Authority
CN
China
Prior art keywords
parts
water
stirring
hydroxypropyl methylcellulose
exterior wall
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610573652.3A
Other languages
Chinese (zh)
Inventor
邱华岭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Original Assignee
ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd filed Critical ANHUI SHENGDE BUILDING MATERIAL TECHNOLOGY Co Ltd
Priority to CN201610573652.3A priority Critical patent/CN106085066A/en
Publication of CN106085066A publication Critical patent/CN106085066A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of water-repellent paint used for building exterior wall, it is characterised in that its raw material includes by weight: acrylic acid ester emulsion 40 80 parts, ethylene-vinyl acetate copolymer emulsion 25 30 parts, modified hydroxypropyl methylcellulose 36 parts, polydimethylsiloxane 0.5 2.2 parts, flocking 2 10 parts, winnofil 10 25 parts, 5 15 parts of asbestos powder, 46 parts of ethylene glycol ether, 2 hydroxypropyl celluloses 35 parts, antibacterial 12 parts, antisettling agent 12 parts, ammonia 12 parts, 50 100 parts of water.The water-repellent paint used for building exterior wall that the present invention proposes, not only water resistance is good, and excellent in mechanical performance, service life is long.

Description

A kind of water-repellent paint used for building exterior wall
Technical field
The present invention relates to exterior coating technical field, particularly relate to a kind of water-repellent paint used for building exterior wall.
Background technology
At present often can be at building exterior wall surface brushing paint, to improve, surface of wall is high temperature resistant, Corrosion Protection, extends it Service life, simple and effective, and low cost, building exterior wall surface is required higher by traditional acrylic coating, harsh at some Under environment, acrylic coating waterproof, mechanical property do not reach external wall use requirement, traditional acrylic coating cannot Meet the requirement in above-mentioned field, how to prepare a kind of water resistance good, excellent in mechanical performance, service life length used for building exterior wall Acrylic coating becomes to be presently required and solves the technical problem that.
Summary of the invention
The technical problem existed based on background technology, the present invention proposes a kind of water-repellent paint used for building exterior wall, not only prevents Aqueous can be good, and excellent in mechanical performance, service life is long.
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 40- 80 parts, ethylene-vinyl acetate copolymer emulsion 25-30 part, modified hydroxypropyl methylcellulose 3-6 part, polydimethylsiloxane 0.5-2.2 part, flocking 2-10 part, winnofil 10-25 part, asbestos powder 5-15 part, ethylene glycol ether 4-6 part, 2-hydroxypropyl Base cellulose 3-5 part, antibacterial 1-2 part, antisettling agent 1-2 part, ammonia 1-2 part, water 50-100 part.
Preferably, acrylic acid ester emulsion, ethylene-vinyl acetate copolymer emulsion, the weight of modified hydroxypropyl methylcellulose Ratio is 50-70:26-28:4-5.
Preferably, modified hydroxypropyl methylcellulose, ethylene glycol ether, 2-hydroxypropyl cellulose weight ratio be 4-5: 4.5-5.5:3.5-4.5.
Preferably, modified hydroxypropyl methylcellulose uses following technique to prepare: by hydroxypropyl methylcellulose, water mix and blend Uniformly, heat up, continue stirring, cooling, standing, add dalcium biphosphate stirring, send in baking oven and place, addition animal osseocolla, Activated carbon stirs, supersound process, then microwave treatment, adds sodium hydroxide solution stirring, places and obtain hydroxypropyl methylcellulose.
Preferably, modified hydroxypropyl methylcellulose uses following technique to prepare: by hydroxypropyl methylcellulose, water mix and blend Uniformly, it is warming up to 45-55 DEG C, continues stirring 55-105min, be cooled to 0-2 DEG C, stand 30-70min, add dalcium biphosphate Stirring 30-70min, sends into and places 2-4h in baking oven, and oven temperature is 45-55 DEG C, adds animal osseocolla, activated carbon stirring 8- 18min, mixing speed is 300-500r/min, supersound process 10-20min, then microwave treatment 5-8min, and microwave power is 180-200W, adds sodium hydroxide solution stirring 10-25min, places and obtain hydroxypropyl methylcellulose in 1.5-2.5 days.
Preferably, modified hydroxypropyl methylcellulose uses following technique to prepare: by weight by 3-8 part hydroxypropyl methylcellulose Element, 60-100 part water mixing and stirring, be warming up to 45-55 DEG C, continues stirring 55-105min, is cooled to 0-2 DEG C, stands 30- 70min, adds 1.5-2.5 part dalcium biphosphate stirring 30-70min, sends into and place 2-4h in baking oven, and oven temperature is 45-55 DEG C, adding 5-8 part animal osseocolla, 0.3-0.7 part activated carbon stirring 8-18min, mixing speed is 300-500r/min, ultrasonic place Reason 10-20min, then microwave treatment 5-8min, microwave power is 180-200W, adds 0.2-0.4 part sodium hydroxide solution and stirs Mix 10-25min, place and obtain hydroxypropyl methylcellulose in 1.5-2.5 days.
Preferably, its raw material includes by weight: acrylic acid ester emulsion 50-70 part, ethylene-vinyl acetate copolymer emulsion 26-28 part, modified hydroxypropyl methylcellulose 4-5 part, polydimethylsiloxane 1-2 part, flocking 4-8 part, winnofil 15-20 Part, asbestos powder 8-12 part, ethylene glycol ether 4.5-5.5 part, 2-hydroxypropyl cellulose 3.5-4.5 part, antibacterial 1.5-1.8 Part, antisettling agent 1.2-1.5 part, ammonia 1.4-1.6 part, water 60-80 part.
The present invention uses acrylic acid ester emulsion, ethylene-vinyl acetate copolymer emulsion to carry out synergism, not only water proofing property Can be good, and excellent in mechanical performance, service life is long, adds modified hydroxypropyl methylcellulose effect and can effectively promote acrylic acid Merging between ester emulsion, ethylene-vinyl acetate copolymer emulsion, mutual dispersing uniformity is fabulous；Modified hydroxypropyl methylcellulose Preparation process in, containing great amount of hydroxy group, ehter bond in hydroxypropyl methylcellulose molecule, make with dalcium biphosphate after pretreatment With, being formed and there is Bamboo-shaped rod structural material, and animal osseocolla, the good biocompatibility of activated carbon, through certain technique bar After part reaction, goods emulsifying activity is high, emulsion stability is good, and the S-S that induced animal osseocolla internal protein mounted molecule is formed Key, causes good waterproof performance；Modified hydroxypropyl methylcellulose, 2-hydroxypropyl cellulose and ethylene glycol ether synergism, goods Good film-forming property, film layer toughness is high, and film layer is the most excellent and the most easy to crack with the absorption property of exterior wall bottom, water resistance pole Good；Modified hydroxypropyl methylcellulose and winnofil, flocking, asbestos powder mixing uniformity fabulous, at polydimethylsiloxanes Under alkane effect, mutual adhesion is strong, and building bridge each other makes even film layer, completely, waterproof the most excellent with mechanical property, uses Life-span is the longest.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 40 Part, ethylene-vinyl acetate copolymer emulsion 30 parts, modified hydroxypropyl methylcellulose 3 parts, polydimethylsiloxane 2.2 parts, flocking 2 parts, winnofil 25 parts, 5 parts of asbestos powder, 6 parts of ethylene glycol ether, 2-hydroxypropyl cellulose 3 parts, antibacterial 2 parts, anti-settling Shallow lake agent 1 part, ammonia 2 parts, 50 parts of water.
Embodiment 2
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 80 Part, ethylene-vinyl acetate copolymer emulsion 25 parts, modified hydroxypropyl methylcellulose 6 parts, polydimethylsiloxane 0.5 part, flocking 10 parts, winnofil 10 parts, 15 parts of asbestos powder, 4 parts of ethylene glycol ether, 2-hydroxypropyl cellulose 5 parts, antibacterial 1 part, anti- Precipitant 2 parts, ammonia 1 part, 100 parts of water.
Modified hydroxypropyl methylcellulose uses following technique to prepare: by hydroxypropyl methylcellulose, water mixing and stirring, rises Temperature, continues stirring, cooling, standing, adds dalcium biphosphate stirring, sends in baking oven and place, and addition animal osseocolla, activated carbon stir Mix, supersound process, then microwave treatment, add sodium hydroxide solution stirring, place and obtain hydroxypropyl methylcellulose.
Embodiment 3
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 60 Part, ethylene-vinyl acetate copolymer emulsion 27 parts, modified hydroxypropyl methylcellulose 4.5 parts, polydimethylsiloxane 1.5 parts, cotton Consider 6 parts to be worth doing, winnofil 18 parts, 10 parts of asbestos powder, 5 parts of ethylene glycol ether, 2-hydroxypropyl cellulose 4 parts, antibacterial 1.6 Part, antisettling agent 1.3 parts, ammonia 1.5 parts, 70 parts of water.
Modified hydroxypropyl methylcellulose uses following technique to prepare: by hydroxypropyl methylcellulose, water mixing and stirring, rises Temperature, to 50 DEG C, continues stirring 75min, is cooled to 1 DEG C, stand 50min, adds dalcium biphosphate stirring 50min, sends in baking oven Placing 3h, oven temperature is 50 DEG C, adds animal osseocolla, activated carbon stirring 13min, and mixing speed is 400r/min, ultrasonic place Reason 15min, then microwave treatment 6min, microwave power is 190W, adds sodium hydroxide solution stirring 17min, places and obtain for 2 days Hydroxypropyl methylcellulose.
Embodiment 4
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 50 Part, ethylene-vinyl acetate copolymer emulsion 28 parts, modified hydroxypropyl methylcellulose 4 parts, polydimethylsiloxane 2 parts, flocking 4 Part, winnofil 20 parts, 8 parts of asbestos powder, 5.5 parts of ethylene glycol ether, 2-hydroxypropyl cellulose 3.5 parts, antibacterial 1.8 Part, antisettling agent 1.2 parts, ammonia 1.6 parts, 60 parts of water.
Modified hydroxypropyl methylcellulose uses following technique to prepare: by weight by 8 parts of hydroxypropyl methylcellulose, 60 parts of water Mixing and stirring, is warming up to 55 DEG C, continues stirring 55min, is cooled to 2 DEG C, stands 30min, add 2.5 parts of dalcium biphosphates Stirring 30min, sends into and places 4h in baking oven, and oven temperature is 45 DEG C, adds 8 parts of animal osseocolla, 0.3 part of activated carbon stirring 18min, mixing speed is 300r/min, supersound process 20min, then microwave treatment 5min, and microwave power is 200W, adds 0.2 part of sodium hydroxide solution stirring 25min, places and obtains hydroxypropyl methylcellulose in 1.5 days.
Embodiment 5
The one water-repellent paint used for building exterior wall that the present invention proposes, its raw material includes by weight: acrylic acid ester emulsion 70 Part, ethylene-vinyl acetate copolymer emulsion 26 parts, modified hydroxypropyl methylcellulose 5 parts, polydimethylsiloxane 1 part, flocking 8 Part, winnofil 15 parts, 12 parts of asbestos powder, 4.5 parts of ethylene glycol ether, 2-hydroxypropyl cellulose 4.5 parts, antibacterial 1.5 Part, antisettling agent 1.5 parts, ammonia 1.4 parts, 80 parts of water.
Modified hydroxypropyl methylcellulose uses following technique to prepare: by weight by 3 parts of hydroxypropyl methylcellulose, 100 parts Water mixing and stirring, is warming up to 45 DEG C, continues stirring 105min, is cooled to 0 DEG C, stands 70min, add 1.5 parts of di(2-ethylhexyl)phosphates Hydrogen calcium stirring 70min, sends into and places 2h in baking oven, and oven temperature is 55 DEG C, adds 5 parts of animal osseocolla, 0.7 part of activated carbon stirring 8min, mixing speed is 500r/min, supersound process 10min, then microwave treatment 8min, and microwave power is 180W, adds 0.4 Part sodium hydroxide solution stirring 10min, places and obtains hydroxypropyl methylcellulose in 2.5 days.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto, Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.

Claims (7)

1. a water-repellent paint used for building exterior wall, it is characterised in that its raw material includes by weight: acrylic acid ester emulsion 40-80 Part, ethylene-vinyl acetate copolymer emulsion 25-30 part, modified hydroxypropyl methylcellulose 3-6 part, polydimethylsiloxane 0.5- 2.2 parts, flocking 2-10 part, winnofil 10-25 part, asbestos powder 5-15 part, ethylene glycol ether 4-6 part, 2-hydroxypropyl is fine Dimension element 3-5 part, antibacterial 1-2 part, antisettling agent 1-2 part, ammonia 1-2 part, water 50-100 part.
Water-repellent paint the most used for building exterior wall, it is characterised in that acrylic acid ester emulsion, ethyl vinyl acetate second Alkene copolymer emulsion, the weight ratio of modified hydroxypropyl methylcellulose are 50-70:26-28:4-5.
Water-repellent paint used for building exterior wall the most according to claim 1 or claim 2, it is characterised in that modified hydroxypropyl methylcellulose, second Allyl diglycol ether, 2-hydroxypropyl cellulose weight ratio be 4-5:4.5-5.5:3.5-4.5.
4. according to water-repellent paint used for building exterior wall described in any one of claim 1-3, it is characterised in that modified hydroxypropyl methylcellulose Element uses following technique to prepare: by hydroxypropyl methylcellulose, water mixing and stirring, heats up, and continues stirring, cooling, stands, add Entering dalcium biphosphate stirring, send in baking oven and place, add animal osseocolla, activated carbon stirring, supersound process, then at microwave Reason, adds sodium hydroxide solution stirring, places and obtain hydroxypropyl methylcellulose.
5. according to water-repellent paint used for building exterior wall described in any one of claim 1-4, it is characterised in that modified hydroxypropyl methylcellulose Element uses following technique to prepare: by hydroxypropyl methylcellulose, water mixing and stirring, be warming up to 45-55 DEG C, continues stirring 55- 105min, is cooled to 0-2 DEG C, stands 30-70min, adds dalcium biphosphate stirring 30-70min, sends into and place 2-in baking oven 4h, oven temperature is 45-55 DEG C, adds animal osseocolla, activated carbon stirring 8-18min, and mixing speed is 300-500r/min, super Sonication 10-20min, then microwave treatment 5-8min, microwave power is 180-200W, adds sodium hydroxide solution stirring 10- 25min, places and obtains hydroxypropyl methylcellulose in 1.5-2.5 days.
6. according to water-repellent paint used for building exterior wall described in any one of claim 1-5, it is characterised in that modified hydroxypropyl methylcellulose Element uses following technique to prepare: by weight by 3-8 part hydroxypropyl methylcellulose, 60-100 part water mixing and stirring, heats up To 45-55 DEG C, continue stirring 55-105min, be cooled to 0-2 DEG C, stand 30-70min, add 1.5-2.5 part dalcium biphosphate Stirring 30-70min, sends into and places 2-4h in baking oven, and oven temperature is 45-55 DEG C, adds 5-8 part animal osseocolla, 0.3-0.7 part Activated carbon stirring 8-18min, mixing speed is 300-500r/min, supersound process 10-20min, then microwave treatment 5-8min, Microwave power is 180-200W, adds 0.2-0.4 part sodium hydroxide solution stirring 10-25min, places and obtain hydroxyl in 1.5-2.5 days Third methylcellulose.
7. according to water-repellent paint used for building exterior wall described in any one of claim 1-5, it is characterised in that its raw material wraps by weight Include: acrylic acid ester emulsion 50-70 part, ethylene-vinyl acetate copolymer emulsion 26-28 part, modified hydroxypropyl methylcellulose 4-5 Part, polydimethylsiloxane 1-2 part, flocking 4-8 part, winnofil 15-20 part, asbestos powder 8-12 part, ethylene glycol ether 4.5-5.5 part, 2-hydroxypropyl cellulose 3.5-4.5 part, antibacterial 1.5-1.8 part, antisettling agent 1.2-1.5 part, ammonia 1.4- 1.6 parts, water 60-80 part.
CN201610573652.3A 2016-07-19 2016-07-19 A kind of water-repellent paint used for building exterior wall Pending CN106085066A (en)