CN106118366A - A kind of corrosion-resistant power transformation box based on composite coating - Google Patents
A kind of corrosion-resistant power transformation box based on composite coating Download PDFInfo
- Publication number
- CN106118366A CN106118366A CN201610576049.0A CN201610576049A CN106118366A CN 106118366 A CN106118366 A CN 106118366A CN 201610576049 A CN201610576049 A CN 201610576049A CN 106118366 A CN106118366 A CN 106118366A
- Authority
- CN
- China
- Prior art keywords
- composite coating
- corrosion
- power transformation
- composite
- transformation box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The application relates to a kind of corrosion-resistant power transformation box based on composite coating, including: a casing；At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；And at least one control device being located on described casing, this described control device includes temperature inductor and the relay being connected with temperature inductor, and described relay is also connected with described exhaust fan.
Description
Technical field
The application relates to power transformation box field, particularly relates to a kind of corrosion-resistant power transformation box based on composite coating.
Background technology
Power transformation box is the casing that in power system, voltage and current to electric energy converted, collected the place neutralizing distribution.
Power transformation box can produce substantial amounts of heat owing to working long hours, and it will be caused to burn if carrying out heat radiation not in time, thus cause
Bigger economic loss the most also brings many troubles to people's life.
Simultaneously as power transformation box working environment is complicated, it is easily corroded under humidity or corrosive atmosphere, thus right
Its safe operation produces hidden danger.
Summary of the invention
It is desirable to provide a kind of corrosion-resistant power transformation box based on composite coating, to solve problem set forth above.
Embodiments of the invention provide a kind of corrosion-resistant power transformation box based on composite coating, including:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
The technical scheme that embodiments of the invention provide can include following beneficial effect:
The present invention is provided with corrosion-resistant composite membrane in power transformation box interior and outer surface, and this composite membrane can effectively be protected
Power transformation box casing is not by the corrosion of gas, liquid etc. in environment, or corrosion is less on its impact, thus solves set forth above
Problem.
Aspect and advantage that the application adds will part be given in the following description, and part will become from the following description
Obtain substantially, or recognized by the practice of the application.It should be appreciated that above general description and details hereinafter only describe
It is exemplary and explanatory, the application can not be limited.
Accompanying drawing explanation
The invention will be further described to utilize accompanying drawing, but the embodiment in accompanying drawing does not constitute any limit to the present invention
System, for those of ordinary skill in the art, on the premise of not paying creative work, it is also possible to obtain according to the following drawings
Other accompanying drawing.
Fig. 1 is the structural representation of power transformation box of the present invention.
Fig. 2 is the Making programme figure of composite coating of the present invention.
Detailed description of the invention
Here will illustrate exemplary embodiment in detail, its example represents in the accompanying drawings.Explained below relates to
During accompanying drawing, unless otherwise indicated, the same numbers in different accompanying drawings represents same or analogous key element.Following exemplary embodiment
Described in embodiment do not represent all embodiments consistent with the present invention.On the contrary, they are only with the most appended
The example of the apparatus and method that some aspects that described in detail in claims, the present invention are consistent.
Metal, under the effect of surrounding medium, can occur corruption due to chemical reaction, electrochemical reaction or physical dissolution etc.
Erosion.Corrosion of metal problem is throughout economic every field, in life, the daily home appliance surface used can occur corrosion and
Reduce the life-span, in fields such as traffic, machinery, chemical industry, face the various problems that metal erosion brings equally, the anticorrosion to metal
Technology has become as the problem that Material Field is very important.
At present, the main method using surface to cover, metal material is kept apart with corrosive environment, and then avoids metal
Be corroded.According to the difference of covering material, surface covers and is divided into metal to cover and nonmetal covering.Using anticorrosive paint is to work as
One of front most widely used anticorrosion technique general, maximally effective.The key component of coating has film forming matter, solvent, color stuffing
And auxiliary agent.
Polyaniline has synthesis material low cost, scratch resistance, the advantage such as anticorrosive, is a kind of commonly used anticorrosive to have
Machine conducting polymer, research shows, polyaniline joins and can be obviously improved its mechanical performance and antiseptic property in epoxy resin,
But, current polyaniline compound anticorrosive paint still has the problem such as indissoluble, anticorrosion ability difference, therefore develops and expands polyaniline
Application in corrosion-resistant field has very important significance.
Application scenarios one:
Fig. 1 shows a kind of based on composite coating the corrosion-resistant power transformation box that embodiments herein relates to, by Fig. 1, institute
State power transformation box to include:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
Preferably, it is additionally provided with illuminator in described casing.
Preferably, described illuminator is sound control lighting device.
Preferably, described interior and outer surface are provided with corrosion-resistant composite membrane, and described corrosion-resistant composite film thickness is
400～600 μm.
Preferably, described corrosion-resistant composite membrane is coated in described interior and outer surface through being dried by composite coating
Rear solidification 12h is formed.
Embodiments of the invention by having corrosion-resistant composite membrane at the inner surface of described power transformation box casing and outer surface,
The Corrosion Protection making this power transformation box significantly improves, and in combination with the exhaust fan on casing, can mention protection against the tide, anticorrosion effect
Really.
Preferably, described composite coating is with epoxy resin as film forming matter, and polyaniline/Al nanoparticle is as filler, plating
The composite fibre of copper carbon fiber and polyaniline fiber composition is as Internet.
In the composite coating of the application, the composite fibre formed using copper carbon fiber and polyaniline fiber as Internet,
On the one hand, copper carbon fiber has the transmission of excellent pliability and electric conductivity, beneficially conductive ion；Simultaneously copper carbon fiber with
Polyaniline fiber is used in mixed way, and both form network structure alternately so that the application composite coating, in mechanical properties, strengthens
The suppleness of coating, impact resistance, this composite network structure enhances the wearability of composite coating simultaneously, increases and uses the longevity
Life；In terms of electrochemistry, corynebacterium copper carbon fiber mutually splices, and forms conductive network, for conducting electricity in corrosion electrolytic solution
Ion possesses electric screening action, strengthens the corrosion resistance of coating；On the other hand, in the application composite coating Internet effectively every
From matrix and contacting of corroding electrolyte, there is physical shielding effect, hinder the corrosive ion diffusion to matrix, improve matrix
Corrosion resistance.
Preferably, described composite coating is using normal propyl alcohol as antifreeze.
In the application composite coating, add normal propyl alcohol as antifreeze so that at low temperatures, this composite coating thin film still has
There are suitable corrosion resistance, meanwhile, frost resistance and composite fibre synergism, the at low temperatures mechanical performance of composite coating thin film
Decline relatively low, create good effect.
It is further preferred that the preparation process of described composite coating is as follows:
Step one, prepares copper carbon fiber:
Taking carbon fiber, a diameter of 50～100 μm, carbon fiber, as electrode, uses electrochemical method its plated surface one layer
Copper film, copper film thickness is 5 μm, is then cut to 1～5mm length；
Step 2, prepares polyaniline fiber:
Take aniline and distilled water that volume ratio is 1:60, under the effect of mineral acid, aniline is dissolved in distilled water, super
Under sound, mix homogeneously, form solution A, then take FeCl3 6H2O and distilled water that mass ratio is 1:50, by FeCl3 6H2O
Being dissolved in distilled water, form solution B, then by A, B mix homogeneously, wherein A, B volume ratio is 2:3, is existed by A, B mixed solution
Standing and reacting 10h under the conditions of ice-water bath, obtains bottle green product, is filtered by reaction gained solution, be first washed with deionized water in
Property, then it is colourless to be washed till filtrate with ethanol, by product dried 30h in drying baker, obtains polyaniline fiber；
Then, take copper carbon fiber and polyaniline fiber, mass ratio 1:1, put it in dilute hydrochloric acid solution, constantly stir
Mix, simultaneously acidification 2h, be then washed with deionized water to neutrality, dried 5h in drying baker, obtain composite fibre；
Step 3, prepares polyaniline/Al nanoparticle:
First the dodecylbenzene sodium sulfonate taking 3g is dissolved in 200ml deionized water, is added by the aniline of 3ml, at water
In bath, 78 DEG C process 30min, are subsequently adding 0.5g Al nanoparticle, magnetic agitation 1h, obtain the homogeneous suspension of Al particle；
The Ammonium persulfate. of 10g is dissolved in 100ml hydrochloric acid solution, magnetic agitation 1h, then utilizes separatory funnel by ammonium persulfate solution
It is added drop-wise in aniline solution, is stirred continuously and makes it react 4h, then stand filtration, filtrate washing is pulverized after drying
End, obtains polyaniline/Al nanoparticle powder body；
Step 4, prepares composite coating:
The application composite coating with epoxy resin as film forming matter, polyaniline/Al nanoparticle as filler, zinc phosphate,
Aluminium triphosphate, Pulvis Talci and barium sulfate are as color stuffing, copper carbon fiber and the composite fibre conduct of polyaniline fiber composition
Internet, n-butyl alcohol and N-Methyl pyrrolidone are as mixed solvent, and silane coupler is as auxiliary agent, and polyamide 6 50 is as solid
Agent, normal propyl alcohol is as antifreeze；
Take 5 parts of polyanilines/Al nanoparticle and 9 parts of composite fibre be placed in beaker, add 60 parts of N-Methyl pyrrolidone,
Magnetic agitation 30min, is then sonicated 2h；
Then putting in another beaker by 10 parts of epoxy resin and 6 parts of n-butyl alcohol, magnetic agitation 1h, by solution in two beakers
Mixing, stirs 2h, is sequentially added into normal propyl alcohol 4 parts, zinc phosphate 1 part, aluminium triphosphate 2 parts, Pulvis Talci 1 part and 3 parts of barium sulfate, then
Add 2 parts of polyamide 6 50 firming agent after stirring 1h, after mechanical agitation 2h, obtain the composite coating of the application；
Described composite coating is coated in target object surface, solidifies 12h after drying, after solidification, coating layer thickness be 400～
600μm。
Preferably, the experiment effect aspect of the application composite coating, the corrosion resistance of the application composite coating: anticorrosive
Performance is evaluated by electrochemical means, by molten for the Na2S that the matrix coating different-thickness composite coating of the present invention is placed on 4wt%
In liquid, stand 300h, test resistance rate of change, it is found that the corrosion of the application composite coating is less from electric current, it is possible to effectively prevent corruption
The erosion electrolyte corrosion to matrix, and the anti-freezing property of described composite coating is good.
Application scenarios two:
Fig. 1 shows a kind of based on composite coating the corrosion-resistant power transformation box that embodiments herein relates to, by Fig. 1, institute
State power transformation box to include:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
Preferably, it is additionally provided with illuminator in described casing.
Preferably, described illuminator is sound control lighting device.
Preferably, described interior and outer surface are provided with corrosion-resistant composite membrane, and described corrosion-resistant composite film thickness is 0
～200 μm.
Preferably, described corrosion-resistant composite membrane is coated in described interior and outer surface through being dried by composite coating
Rear solidification 12h is formed.
Embodiments of the invention by having corrosion-resistant composite membrane at the inner surface of described power transformation box casing and outer surface,
The Corrosion Protection making this power transformation box significantly improves, and in combination with the exhaust fan on casing, can mention protection against the tide, anticorrosion effect
Really.
Preferably, described composite coating is with epoxy resin as film forming matter, and polyaniline/Al nanoparticle is as filler, plating
The composite fibre of copper carbon fiber and polyaniline fiber composition is as Internet.
In the composite coating of the application, the composite fibre formed using copper carbon fiber and polyaniline fiber as Internet,
On the one hand, copper carbon fiber has the transmission of excellent pliability and electric conductivity, beneficially conductive ion；Simultaneously copper carbon fiber with
Polyaniline fiber is used in mixed way, and both form network structure alternately so that the application composite coating, in mechanical properties, strengthens
The suppleness of coating, impact resistance, this composite network structure enhances the wearability of composite coating simultaneously, increases and uses the longevity
Life；In terms of electrochemistry, corynebacterium copper carbon fiber mutually splices, and forms conductive network, for conducting electricity in corrosion electrolytic solution
Ion possesses electric screening action, strengthens the corrosion resistance of coating；On the other hand, in the application composite coating Internet effectively every
From matrix and contacting of corroding electrolyte, there is physical shielding effect, hinder the corrosive ion diffusion to matrix, improve matrix
Corrosion resistance.
Preferably, described composite coating is using normal propyl alcohol as antifreeze.
In the application composite coating, add normal propyl alcohol as antifreeze so that at low temperatures, this composite coating thin film still has
There are suitable corrosion resistance, meanwhile, frost resistance and composite fibre synergism, the at low temperatures mechanical performance of composite coating thin film
Decline relatively low, create good effect.
It is further preferred that the preparation process of described composite coating is as follows:
Step one, prepares copper carbon fiber:
Taking carbon fiber, a diameter of 50～100 μm, carbon fiber, as electrode, uses electrochemical method its plated surface one layer
Copper film, copper film thickness is 5 μm, is then cut to 1～5mm length；
Step 2, prepares polyaniline fiber:
Take aniline and distilled water that volume ratio is 1:60, under the effect of mineral acid, aniline is dissolved in distilled water, super
Under sound, mix homogeneously, form solution A, then take FeCl3 6H2O and distilled water that mass ratio is 1:50, by FeCl3 6H2O
Being dissolved in distilled water, form solution B, then by A, B mix homogeneously, wherein A, B volume ratio is 2:3, is existed by A, B mixed solution
Standing and reacting 10h under the conditions of ice-water bath, obtains bottle green product, is filtered by reaction gained solution, be first washed with deionized water in
Property, then it is colourless to be washed till filtrate with ethanol, by product dried 30h in drying baker, obtains polyaniline fiber；
Then, take copper carbon fiber and polyaniline fiber, mass ratio 1:1, put it in dilute hydrochloric acid solution, constantly stir
Mix, simultaneously acidification 2h, be then washed with deionized water to neutrality, dried 5h in drying baker, obtain composite fibre；
Step 3, prepares polyaniline/Al nanoparticle:
First the dodecylbenzene sodium sulfonate taking 3g is dissolved in 200ml deionized water, is added by the aniline of 3ml, at water
In bath, 78 DEG C process 30min, are subsequently adding 0.5g Al nanoparticle, magnetic agitation 1h, obtain the homogeneous suspension of Al particle；
The Ammonium persulfate. of 10g is dissolved in 100ml hydrochloric acid solution, magnetic agitation 1h, then utilizes separatory funnel by ammonium persulfate solution
It is added drop-wise in aniline solution, is stirred continuously and makes it react 4h, then stand filtration, filtrate washing is pulverized after drying
End, obtains polyaniline/Al nanoparticle powder body；
Step 4, prepares composite coating:
The application composite coating with epoxy resin as film forming matter, polyaniline/Al nanoparticle as filler, zinc phosphate,
Aluminium triphosphate, Pulvis Talci and barium sulfate are as color stuffing, copper carbon fiber and the composite fibre conduct of polyaniline fiber composition
Internet, n-butyl alcohol and N-Methyl pyrrolidone are as mixed solvent, and silane coupler is as auxiliary agent, and polyamide 6 50 is as solid
Agent, normal propyl alcohol is as antifreeze；
Take 5 parts of polyanilines/Al nanoparticle and 9 parts of composite fibre be placed in beaker, add 60 parts of N-Methyl pyrrolidone,
Magnetic agitation 30min, is then sonicated 2h；
Then putting in another beaker by 10 parts of epoxy resin and 6 parts of n-butyl alcohol, magnetic agitation 1h, by solution in two beakers
Mixing, stirs 2h, is sequentially added into normal propyl alcohol 4 parts, zinc phosphate 1 part, aluminium triphosphate 2 parts, Pulvis Talci 1 part and 3 parts of barium sulfate, then
Add 2 parts of polyamide 6 50 firming agent after stirring 1h, after mechanical agitation 2h, obtain the composite coating of the application；
Described composite coating is coated in target object surface, solidifies 12h after drying, and after solidification, coating layer thickness is 0～200 μ
m。
Preferably, the experiment effect aspect of the application composite coating, the corrosion resistance of the application composite coating: anticorrosive
Performance is evaluated by electrochemical means, by molten for the Na2S that the matrix coating different-thickness composite coating of the present invention is placed on 4wt%
In liquid, stand 300h, test resistance rate of change, it is found that the corrosion of the application composite coating is less from electric current, it is possible to effectively prevent corruption
The erosion electrolyte corrosion to matrix, and the anti-freezing property of described composite coating is good.
Application scenarios three:
Fig. 1 shows a kind of based on composite coating the corrosion-resistant power transformation box that embodiments herein relates to, by Fig. 1, institute
State power transformation box to include:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
Preferably, it is additionally provided with illuminator in described casing.
Preferably, described illuminator is sound control lighting device.
Preferably, described interior and outer surface are provided with corrosion-resistant composite membrane, and described corrosion-resistant composite film thickness is
200～400 μm.
Preferably, described corrosion-resistant composite membrane is coated in described interior and outer surface through being dried by composite coating
Rear solidification 12h is formed.
Embodiments of the invention by having corrosion-resistant composite membrane at the inner surface of described power transformation box casing and outer surface,
The Corrosion Protection making this power transformation box significantly improves, and in combination with the exhaust fan on casing, can mention protection against the tide, anticorrosion effect
Really.
Preferably, described composite coating is with epoxy resin as film forming matter, and polyaniline/Al nanoparticle is as filler, plating
The composite fibre of copper carbon fiber and polyaniline fiber composition is as Internet.
In the composite coating of the application, the composite fibre formed using copper carbon fiber and polyaniline fiber as Internet,
On the one hand, copper carbon fiber has the transmission of excellent pliability and electric conductivity, beneficially conductive ion；Simultaneously copper carbon fiber with
Polyaniline fiber is used in mixed way, and both form network structure alternately so that the application composite coating, in mechanical properties, strengthens
The suppleness of coating, impact resistance, this composite network structure enhances the wearability of composite coating simultaneously, increases and uses the longevity
Life；In terms of electrochemistry, corynebacterium copper carbon fiber mutually splices, and forms conductive network, for conducting electricity in corrosion electrolytic solution
Ion possesses electric screening action, strengthens the corrosion resistance of coating；On the other hand, in the application composite coating Internet effectively every
From matrix and contacting of corroding electrolyte, there is physical shielding effect, hinder the corrosive ion diffusion to matrix, improve matrix
Corrosion resistance.
Preferably, described composite coating is using normal propyl alcohol as antifreeze.
In the application composite coating, add normal propyl alcohol as antifreeze so that at low temperatures, this composite coating thin film still has
There are suitable corrosion resistance, meanwhile, frost resistance and composite fibre synergism, the at low temperatures mechanical performance of composite coating thin film
Decline relatively low, create good effect.
It is further preferred that the preparation process of described composite coating is as follows:
Step one, prepares copper carbon fiber:
Taking carbon fiber, a diameter of 50～100 μm, carbon fiber, as electrode, uses electrochemical method its plated surface one layer
Copper film, copper film thickness is 5 μm, is then cut to 1～5mm length；
Step 2, prepares polyaniline fiber:
Take aniline and distilled water that volume ratio is 1:60, under the effect of mineral acid, aniline is dissolved in distilled water, super
Under sound, mix homogeneously, form solution A, then take FeCl3 6H2O and distilled water that mass ratio is 1:50, by FeCl3 6H2O
Being dissolved in distilled water, form solution B, then by A, B mix homogeneously, wherein A, B volume ratio is 2:3, is existed by A, B mixed solution
Standing and reacting 10h under the conditions of ice-water bath, obtains bottle green product, is filtered by reaction gained solution, be first washed with deionized water in
Property, then it is colourless to be washed till filtrate with ethanol, by product dried 30h in drying baker, obtains polyaniline fiber；
Then, take copper carbon fiber and polyaniline fiber, mass ratio 1:1, put it in dilute hydrochloric acid solution, constantly stir
Mix, simultaneously acidification 2h, be then washed with deionized water to neutrality, dried 5h in drying baker, obtain composite fibre；
Step 3, prepares polyaniline/Al nanoparticle:
First the dodecylbenzene sodium sulfonate taking 3g is dissolved in 200ml deionized water, is added by the aniline of 3ml, at water
In bath, 78 DEG C process 30min, are subsequently adding 0.5g Al nanoparticle, magnetic agitation 1h, obtain the homogeneous suspension of Al particle；
The Ammonium persulfate. of 10g is dissolved in 100ml hydrochloric acid solution, magnetic agitation 1h, then utilizes separatory funnel by ammonium persulfate solution
It is added drop-wise in aniline solution, is stirred continuously and makes it react 4h, then stand filtration, filtrate washing is pulverized after drying
End, obtains polyaniline/Al nanoparticle powder body；
Step 4, prepares composite coating:
The application composite coating with epoxy resin as film forming matter, polyaniline/Al nanoparticle as filler, zinc phosphate,
Aluminium triphosphate, Pulvis Talci and barium sulfate are as color stuffing, copper carbon fiber and the composite fibre conduct of polyaniline fiber composition
Internet, n-butyl alcohol and N-Methyl pyrrolidone are as mixed solvent, and silane coupler is as auxiliary agent, and polyamide 6 50 is as solid
Agent, normal propyl alcohol is as antifreeze；
Take 5 parts of polyanilines/Al nanoparticle and 9 parts of composite fibre be placed in beaker, add 60 parts of N-Methyl pyrrolidone,
Magnetic agitation 30min, is then sonicated 2h；
Then putting in another beaker by 10 parts of epoxy resin and 6 parts of n-butyl alcohol, magnetic agitation 1h, by solution in two beakers
Mixing, stirs 2h, is sequentially added into normal propyl alcohol 4 parts, zinc phosphate 1 part, aluminium triphosphate 2 parts, Pulvis Talci 1 part and 3 parts of barium sulfate, then
Add 2 parts of polyamide 6 50 firming agent after stirring 1h, after mechanical agitation 2h, obtain the composite coating of the application；
Described composite coating is coated in target object surface, solidifies 12h after drying, after solidification, coating layer thickness be 200～
400μm。
Preferably, the experiment effect aspect of the application composite coating, the corrosion resistance of the application composite coating: anticorrosive
Performance is evaluated by electrochemical means, by molten for the Na2S that the matrix coating different-thickness composite coating of the present invention is placed on 4wt%
In liquid, stand 300h, test resistance rate of change, it is found that the corrosion of the application composite coating is less from electric current, it is possible to effectively prevent corruption
The erosion electrolyte corrosion to matrix, and the anti-freezing property of described composite coating is good.
Application scenarios four:
Fig. 1 shows a kind of based on composite coating the corrosion-resistant power transformation box that embodiments herein relates to, by Fig. 1, institute
State power transformation box to include:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
Preferably, it is additionally provided with illuminator in described casing.
Preferably, described illuminator is sound control lighting device.
Preferably, described interior and outer surface are provided with corrosion-resistant composite membrane, and described corrosion-resistant composite film thickness is
400～600 μm.
Preferably, described corrosion-resistant composite membrane is coated in described interior and outer surface through being dried by composite coating
Rear solidification 12h is formed.
Embodiments of the invention by having corrosion-resistant composite membrane at the inner surface of described power transformation box casing and outer surface,
The Corrosion Protection making this power transformation box significantly improves, and in combination with the exhaust fan on casing, can mention protection against the tide, anticorrosion effect
Really.
Preferably, described composite coating is with epoxy resin as film forming matter, and polyaniline/Al nanoparticle is as filler, plating
The composite fibre of copper carbon fiber and polyaniline fiber composition is as Internet.
In the composite coating of the application, the composite fibre formed using copper carbon fiber and polyaniline fiber as Internet,
On the one hand, copper carbon fiber has the transmission of excellent pliability and electric conductivity, beneficially conductive ion；Simultaneously copper carbon fiber with
Polyaniline fiber is used in mixed way, and both form network structure alternately so that the application composite coating, in mechanical properties, strengthens
The suppleness of coating, impact resistance, this composite network structure enhances the wearability of composite coating simultaneously, increases and uses the longevity
Life；In terms of electrochemistry, corynebacterium copper carbon fiber mutually splices, and forms conductive network, for conducting electricity in corrosion electrolytic solution
Ion possesses electric screening action, strengthens the corrosion resistance of coating；On the other hand, in the application composite coating Internet effectively every
From matrix and contacting of corroding electrolyte, there is physical shielding effect, hinder the corrosive ion diffusion to matrix, improve matrix
Corrosion resistance.
It is further preferred that the preparation process of described composite coating is as follows:
Step one, prepares copper carbon fiber:
Taking carbon fiber, a diameter of 50～100 μm, carbon fiber, as electrode, uses electrochemical method its plated surface one layer
Copper film, copper film thickness is 5 μm, is then cut to 1～5mm length；
Step 2, prepares polyaniline fiber:
Take aniline and distilled water that volume ratio is 1:60, under the effect of mineral acid, aniline is dissolved in distilled water, super
Under sound, mix homogeneously, form solution A, then take FeCl3 6H2O and distilled water that mass ratio is 1:50, by FeCl3 6H2O
Being dissolved in distilled water, form solution B, then by A, B mix homogeneously, wherein A, B volume ratio is 2:3, is existed by A, B mixed solution
Standing and reacting 10h under the conditions of ice-water bath, obtains bottle green product, is filtered by reaction gained solution, be first washed with deionized water in
Property, then it is colourless to be washed till filtrate with ethanol, by product dried 30h in drying baker, obtains polyaniline fiber；
Then, take copper carbon fiber and polyaniline fiber, mass ratio 1:1, put it in dilute hydrochloric acid solution, constantly stir
Mix, simultaneously acidification 2h, be then washed with deionized water to neutrality, dried 5h in drying baker, obtain composite fibre；
Step 3, prepares polyaniline/Al nanoparticle:
First the dodecylbenzene sodium sulfonate taking 3g is dissolved in 200ml deionized water, is added by the aniline of 3ml, at water
In bath, 78 DEG C process 30min, are subsequently adding 0.5g Al nanoparticle, magnetic agitation 1h, obtain the homogeneous suspension of Al particle；
The Ammonium persulfate. of 10g is dissolved in 100ml hydrochloric acid solution, magnetic agitation 1h, then utilizes separatory funnel by ammonium persulfate solution
It is added drop-wise in aniline solution, is stirred continuously and makes it react 4h, then stand filtration, filtrate washing is pulverized after drying
End, obtains polyaniline/Al nanoparticle powder body；
Step 4, prepares composite coating:
The application composite coating with epoxy resin as film forming matter, polyaniline/Al nanoparticle as filler, zinc phosphate,
Aluminium triphosphate, Pulvis Talci and barium sulfate are as color stuffing, copper carbon fiber and the composite fibre conduct of polyaniline fiber composition
Internet, n-butyl alcohol and N-Methyl pyrrolidone are as mixed solvent, and silane coupler is as auxiliary agent, and polyamide 6 50 is as solid
Agent；
Take 5 parts of polyanilines/Al nanoparticle and 9 parts of composite fibre be placed in beaker, add 60 parts of N-Methyl pyrrolidone,
Magnetic agitation 30min, is then sonicated 2h；
Then putting in another beaker by 10 parts of epoxy resin and 6 parts of n-butyl alcohol, magnetic agitation 1h, by solution in two beakers
Mixing, stirs 2h, is sequentially added into zinc phosphate 1 part, aluminium triphosphate 2 parts, Pulvis Talci 1 part and 3 parts of barium sulfate, adds after being stirred for 1h
Enter 2 parts of polyamide 6 50 firming agent, after mechanical agitation 2h, obtain the composite coating of the application；
Described composite coating is coated in target object surface, solidifies 12h after drying, after solidification, coating layer thickness be 400～
600μm。
Preferably, the experiment effect aspect of the application composite coating, the corrosion resistance of the application composite coating: anticorrosive
Performance is evaluated by electrochemical means, by molten for the Na2S that the matrix coating different-thickness composite coating of the present invention is placed on 4wt%
In liquid, stand 300h, test resistance rate of change, it is found that the corrosion of the application composite coating is less from electric current, it is possible to effectively prevent corruption
The erosion electrolyte corrosion to matrix.
Application scenarios five:
Fig. 1 shows a kind of based on composite coating the corrosion-resistant power transformation box that embodiments herein relates to, by Fig. 1, institute
State power transformation box to include:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device include temperature inductor and with
The relay that temperature inductor is connected, described relay is also connected with described exhaust fan.
Preferably, it is additionally provided with illuminator in described casing.
Preferably, described illuminator is sound control lighting device.
Preferably, described interior and outer surface are provided with corrosion-resistant composite membrane, and described corrosion-resistant composite film thickness is
600～800 μm.
Preferably, described corrosion-resistant composite membrane is coated in described interior and outer surface through being dried by composite coating
Rear solidification 12h is formed.
Embodiments of the invention by having corrosion-resistant composite membrane at the inner surface of described power transformation box casing and outer surface,
The Corrosion Protection making this power transformation box significantly improves, and in combination with the exhaust fan on casing, can mention protection against the tide, anticorrosion effect
Really.
Preferably, described composite coating is with epoxy resin as film forming matter, and polyaniline/Al nanoparticle is as filler, plating
The composite fibre of copper carbon fiber and polyaniline fiber composition is as Internet.
In the composite coating of the application, the composite fibre formed using copper carbon fiber and polyaniline fiber as Internet,
On the one hand, copper carbon fiber has the transmission of excellent pliability and electric conductivity, beneficially conductive ion；Simultaneously copper carbon fiber with
Polyaniline fiber is used in mixed way, and both form network structure alternately so that the application composite coating, in mechanical properties, strengthens
The suppleness of coating, impact resistance, this composite network structure enhances the wearability of composite coating simultaneously, increases and uses the longevity
Life；In terms of electrochemistry, corynebacterium copper carbon fiber mutually splices, and forms conductive network, for conducting electricity in corrosion electrolytic solution
Ion possesses electric screening action, strengthens the corrosion resistance of coating；On the other hand, in the application composite coating Internet effectively every
From matrix and contacting of corroding electrolyte, there is physical shielding effect, hinder the corrosive ion diffusion to matrix, improve matrix
Corrosion resistance.
Preferably, described composite coating is using normal propyl alcohol as antifreeze.
In the application composite coating, add normal propyl alcohol as antifreeze so that at low temperatures, this composite coating thin film still has
There are suitable corrosion resistance, meanwhile, frost resistance and composite fibre synergism, the at low temperatures mechanical performance of composite coating thin film
Decline relatively low, create good effect.
It is further preferred that the preparation process of described composite coating is as follows:
Step one, prepares copper carbon fiber:
Taking carbon fiber, a diameter of 50～100 μm, carbon fiber, as electrode, uses electrochemical method its plated surface one layer
Copper film, copper film thickness is 5 μm, is then cut to 1～5mm length；
Step 2, prepares polyaniline fiber:
Take aniline and distilled water that volume ratio is 1:60, under the effect of mineral acid, aniline is dissolved in distilled water, super
Under sound, mix homogeneously, form solution A, then take FeCl3 6H2O and distilled water that mass ratio is 1:50, by FeCl3 6H2O
Being dissolved in distilled water, form solution B, then by A, B mix homogeneously, wherein A, B volume ratio is 2:3, is existed by A, B mixed solution
Standing and reacting 10h under the conditions of ice-water bath, obtains bottle green product, is filtered by reaction gained solution, be first washed with deionized water in
Property, then it is colourless to be washed till filtrate with ethanol, by product dried 30h in drying baker, obtains polyaniline fiber；
Then, take copper carbon fiber and polyaniline fiber, mass ratio 1:1, put it in dilute hydrochloric acid solution, constantly stir
Mix, simultaneously acidification 2h, be then washed with deionized water to neutrality, dried 5h in drying baker, obtain composite fibre；
Step 3, prepares polyaniline/Al nanoparticle:
First the dodecylbenzene sodium sulfonate taking 3g is dissolved in 200ml deionized water, is added by the aniline of 3ml, at water
In bath, 78 DEG C process 30min, are subsequently adding 0.5g Al nanoparticle, magnetic agitation 1h, obtain the homogeneous suspension of Al particle；
The Ammonium persulfate. of 10g is dissolved in 100ml hydrochloric acid solution, magnetic agitation 1h, then utilizes separatory funnel by ammonium persulfate solution
It is added drop-wise in aniline solution, is stirred continuously and makes it react 4h, then stand filtration, filtrate washing is pulverized after drying
End, obtains polyaniline/Al nanoparticle powder body；
Step 4, prepares composite coating:
The application composite coating with epoxy resin as film forming matter, polyaniline/Al nanoparticle as filler, zinc phosphate,
Aluminium triphosphate, Pulvis Talci and barium sulfate are as color stuffing, copper carbon fiber and the composite fibre conduct of polyaniline fiber composition
Internet, n-butyl alcohol and N-Methyl pyrrolidone are as mixed solvent, and silane coupler is as auxiliary agent, and polyamide 6 50 is as solid
Agent, normal propyl alcohol is as antifreeze；
Take 5 parts of polyanilines/Al nanoparticle and 9 parts of composite fibre be placed in beaker, add 60 parts of N-Methyl pyrrolidone,
Magnetic agitation 30min, is then sonicated 2h；
Then putting in another beaker by 10 parts of epoxy resin and 6 parts of n-butyl alcohol, magnetic agitation 1h, by solution in two beakers
Mixing, stirs 2h, is sequentially added into normal propyl alcohol 4 parts, zinc phosphate 1 part, aluminium triphosphate 2 parts, Pulvis Talci 1 part and 3 parts of barium sulfate, then
Add 2 parts of polyamide 6 50 firming agent after stirring 1h, after mechanical agitation 2h, obtain the composite coating of the application；
Described composite coating is coated in target object surface, solidifies 12h after drying, after solidification, coating layer thickness be 600～
800μm。
Preferably, the experiment effect aspect of the application composite coating, the corrosion resistance of the application composite coating: anticorrosive
Performance is evaluated by electrochemical means, by molten for the Na2S that the matrix coating different-thickness composite coating of the present invention is placed on 4wt%
In liquid, stand 300h, test resistance rate of change, it is found that the corrosion of the application composite coating is less from electric current, it is possible to effectively prevent corruption
The erosion electrolyte corrosion to matrix, and the anti-freezing property of described composite coating is good.
Those skilled in the art, after considering description and putting into practice invention disclosed herein, will readily occur to its of the present invention
Its embodiment.The application is intended to any modification, purposes or the adaptations of the present invention, these modification, purposes or
Person's adaptations is followed the general principle of the present invention and includes the undocumented common knowledge in the art of the application
Or conventional techniques means.Description and embodiments is considered only as exemplary, and true scope and spirit of the invention are by following
Claim is pointed out.
It should be appreciated that the invention is not limited in precision architecture described above and illustrated in the accompanying drawings, and
And various modifications and changes can carried out without departing from the scope.The scope of the present invention is only limited by appended claim.
Claims (5)
1. a corrosion-resistant power transformation box based on composite coating, it is characterised in that including:
One casing；
At least one is located at the exhaust fan on described casing, and described exhaust fan is located at the top of described casing；
And at least one control device being located on described casing, this described control device includes temperature inductor and and temperature
The relay that induction apparatus is connected, described relay is also connected with described exhaust fan.
Power transformation box the most according to claim 1, it is characterised in that be additionally provided with illuminator in described casing.
Power transformation box the most according to claim 2, it is characterised in that described illuminator is sound control lighting device.
Power transformation box the most according to claim 3, it is characterised in that described interior and outer surface are provided with corrosion-resistant multiple
Closing film, described corrosion-resistant composite film thickness is 400～600 μm.
Power transformation box the most according to claim 4, it is characterised in that described corrosion-resistant composite membrane is coated in institute by composite coating
State interior and outer surface to be formed through dried solidification 12h.