CN106118304A - A kind of young-generating machine internal layer modification antirust paint - Google Patents

A kind of young-generating machine internal layer modification antirust paint Download PDF

Info

Publication number
CN106118304A
CN106118304A CN201610613089.8A CN201610613089A CN106118304A CN 106118304 A CN106118304 A CN 106118304A CN 201610613089 A CN201610613089 A CN 201610613089A CN 106118304 A CN106118304 A CN 106118304A
Authority
CN
China
Prior art keywords
parts
antirust paint
young
internal layer
generating machine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610613089.8A
Other languages
Chinese (zh)
Inventor
刘玉洁
汤建
缪农
汤雨晴
缪岩和
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Jia Ai Electronics Co Ltd
Original Assignee
Bengbu Jia Ai Electronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Jia Ai Electronics Co Ltd filed Critical Bengbu Jia Ai Electronics Co Ltd
Priority to CN201610613089.8A priority Critical patent/CN106118304A/en
Publication of CN106118304A publication Critical patent/CN106118304A/en
Pending legal-status Critical Current

Abstract

The present invention relates to antirust paint field, it is specifically related to the modified antirust paint of a kind of young-generating machine internal layer, is made up of the raw material of following weight portion: acrylic emulsion 30 35 parts, epoxy resin latex 30 35 parts, sepiolite powder 47 parts, Magnetitum powder 47 parts, octadecyldimethyl tertiary amine 0.5 1 parts, N N-Hydroxysuccinimide 0.5 1 parts, castor oil polyoxyethylene ether 0.5 1 parts, polypropylene glycerol aether 0.5 1 parts, silane coupler 12 parts, acetyl tributyl citrate three (2 ethyls are) ester 24 parts, modified nano-alumina 56 parts.Antirust paint good thermal shock of the present invention, corrosion resistance is very strong, has certain killing effect to antibacterial, antirust paint environmental protection, nontoxic, does not allows after drying the Yishui River, to ftracture, peel off under long Elevated temperature irradiation.

Description

A kind of young-generating machine internal layer modification antirust paint
Technical field
The present invention relates to antirust paint field, be specifically related to the modified antirust paint of a kind of young-generating machine internal layer.
Background technology
Young-generating machine, has another name called generation machine, production machine or goes out shell machine.Young-generating machine is exactly that germ cell egg is fixed through hatch machine one section Time grow, in eggshell, development growth becomes the blank of life, artificial uses electricity to be carried out under other conditioning, broken Shell produces the machine of poult.The simplest understanding of young-generating machine is that still life (ovum egg) becomes being (animal), it appearance big Improve greatly the incubation rate of hatching egg, be the guarantee in hatching later stage.Owing to there will be being blank in later stage young-generating machine, so hatching Antirust paint in machine must assure that the safety of being blank, and in young-generating machine humiture change greatly, amount of bacteria many, it is necessary to energy Corrosion-resistant.
Summary of the invention
The technical problem to be solved is to provide a kind of young-generating machine internal layer modified antirust paint.
The technical problem to be solved realizes by the following technical solutions:
A kind of young-generating machine internal layer modification antirust paint, is made up of the raw material of following weight portion: acrylic emulsion 30-35 part, Epoxy resin latex 30-35 part, sepiolite powder 4-7 part, Magnetitum powder 4-7 part, octadecyldimethyl tertiary amine 0.5-1 part, N-hydroxyl Base butanimide 0.5-1 part, castor oil polyoxyethylene ether 0.5-1 part, polypropylene glycerol aether 0.5-1 part, silane coupler 1-2 part, tri(2-ethylhexyl)acetocitrate 2-4 part, modified nano-alumina 5-6 part.
Described modified nano graphite alkene is made up of the raw material of following weight portion: nano aluminium oxide 9 parts, rosmarinic acid 1 part, first Base silicone oil 1 part, tea polyphenols 0.5 part, resveratrol 0.5 part, erythrose 4-phosphatase 11 part；Its preparation method is, is mixed by each raw material Close, stir, then with malic acid regulation compound pH value to 6.8-6.9, then compound is warming up to 45-50 DEG C, so Rear standing prepared after 20 hours.
Preferably, a kind of young-generating machine internal layer, with modified antirust paint, is made up of the raw material of following weight portion: acrylic emulsion 32 Part, epoxy resin latex 32 parts, sepiolite powder 5 parts, Magnetitum powder 5 parts, octadecyldimethyl tertiary amine 0.8 part, N-hydroxysuccinimidyl Acid imide 0.8 part, castor oil polyoxyethylene ether 0.8 part, polypropylene glycerol aether 0.8 part, silane coupler 1.5 parts, acetyl lemon Lemon acid three (2-ethyl is) ester 3 parts, modified nano-alumina 5.5 parts.
The preparation method of the modified antirust paint of a kind of young-generating machine internal layer, step is as follows: by each raw material mix homogeneously, then exist High speed dispersion 20-25 minute under 1500-1600 rev/min of rotating speed, obtains finished product.
The invention has the beneficial effects as follows: antirust paint good thermal shock of the present invention, corrosion resistance is very strong, has antibacterial necessarily Killing effect, antirust paint environmental protection, nontoxic, do not allow after drying the Yishui River, to ftracture under long Elevated temperature irradiation, peel off.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot Close specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of young-generating machine internal layer, with modified antirust paint, is made up of the raw material of following weight portion: acrylic emulsion 32 parts, epoxy Resin emulsion 32 parts, sepiolite powder 5 parts, Magnetitum powder 5 parts, octadecyldimethyl tertiary amine 0.8 part, N-hydroxy-succinamide 0.8 part, castor oil polyoxyethylene ether 0.8 part, polypropylene glycerol aether 0.8 part, silane coupler 1.5 parts, acetyl tributyl citrate three (2-ethyl is) ester 3 parts, modified nano-alumina 5.5 parts.
Described modified nano graphite alkene is made up of the raw material of following weight portion: nano aluminium oxide 9 parts, rosmarinic acid 1 part, first Base silicone oil 1 part, tea polyphenols 0.5 part, resveratrol 0.5 part, erythrose 4-phosphatase 11 part；Its preparation method is, is mixed by each raw material Close, stir, then with malic acid regulation compound pH value to 6.8-6.9, then compound is warming up to 45-50 DEG C, so Rear standing prepared after 20 hours.
The preparation method of the modified antirust paint of a kind of young-generating machine internal layer, step is as follows: by each raw material mix homogeneously, then exist High speed dispersion 20-25 minute under 1500-1600 rev/min of rotating speed, obtains finished product.
Embodiment 2
A kind of young-generating machine internal layer, with modified antirust paint, is made up of the raw material of following weight portion: acrylic emulsion 30 parts, epoxy Resin emulsion 30 parts, sepiolite powder 4 parts, Magnetitum powder 4 parts, octadecyldimethyl tertiary amine 0.5 part, N-hydroxy-succinamide 0.5 part, castor oil polyoxyethylene ether 0.5 part, polypropylene glycerol aether 0.5 part, silane coupler 1 part, acetyl tributyl citrate three (2- Ethyl is) ester 2 parts, modified nano-alumina 5 parts.
Described modified nano graphite alkene is made up of the raw material of following weight portion: nano aluminium oxide 9 parts, rosmarinic acid 1 part, first Base silicone oil 1 part, tea polyphenols 0.5 part, resveratrol 0.5 part, erythrose 4-phosphatase 11 part；Its preparation method is, is mixed by each raw material Close, stir, then with malic acid regulation compound pH value to 6.8-6.9, then compound is warming up to 45-50 DEG C, so Rear standing prepared after 20 hours.
The preparation method of the modified antirust paint of a kind of young-generating machine internal layer, step is as follows: by each raw material mix homogeneously, then exist High speed dispersion 20-25 minute under 1500-1600 rev/min of rotating speed, obtains finished product.
Embodiment 3
A kind of young-generating machine internal layer, with modified antirust paint, is made up of the raw material of following weight portion: acrylic emulsion 35 parts, epoxy Resin emulsion 35 parts, sepiolite powder 7 parts, Magnetitum powder 7 parts, octadecyldimethyl tertiary amine 1 part, N-hydroxy-succinamide 1 part, Castor oil polyoxyethylene ether 1 part, polypropylene glycerol aether 1 part, silane coupler 2 parts, tri(2-ethylhexyl)acetocitrate 4 Part, modified nano-alumina 6 parts.
Described modified nano graphite alkene is made up of the raw material of following weight portion: nano aluminium oxide 9 parts, rosmarinic acid 1 part, first Base silicone oil 1 part, tea polyphenols 0.5 part, resveratrol 0.5 part, erythrose 4-phosphatase 11 part；Its preparation method is, is mixed by each raw material Close, stir, then with malic acid regulation compound pH value to 6.8-6.9, then compound is warming up to 45-50 DEG C, so Rear standing prepared after 20 hours.
The preparation method of the modified antirust paint of a kind of young-generating machine internal layer, step is as follows: by each raw material mix homogeneously, then exist High speed dispersion 20-25 minute under 1500-1600 rev/min of rotating speed, obtains finished product.
The metallic anti-rust paint using embodiment 1 carries out technology for detection, and result is as follows: 1, adhesive force/level≤1 grade；2, pliable and tough Property/level: 1 grade；3, thermostability: 200 DEG C stand intact；4, alkali resistance: 40% sodium hydroxide 50 days stands intact；5, acid resistance: 40% sulphuric acid 50 days stands intact；6, thermal shock resistance: 20 DEG C-50 DEG C interval continuous warming pull-down tests 7 days is excellent.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and Equivalent defines.

Claims (4)

1. a young-generating machine internal layer modification antirust paint, it is characterised in that be made up of the raw material of following weight portion: acrylic emulsion 30-35 part, epoxy resin latex 30-35 part, sepiolite powder 4-7 part, Magnetitum powder 4-7 part, octadecyldimethyl tertiary amine 0.5-1 Part, N-hydroxy-succinamide 0.5-1 part, castor oil polyoxyethylene ether 0.5-1 part, polypropylene glycerol aether 0.5-1 part, silane Coupling agent 1-2 part, tri(2-ethylhexyl)acetocitrate 2-4 part, modified nano-alumina 5-6 part.
2. a kind of young-generating machine internal layer modification antirust paint as claimed in claim 1, it is characterised in that described modified nano graphite Alkene is made up of the raw material of following weight portion: nano aluminium oxide 9 parts, rosmarinic acid 1 part, methyl-silicone oil 1 part, tea polyphenols 0.5 part, white Veratryl alcohol 0.5 part, erythrose 4-phosphatase 11 part；Its preparation method is, is mixed by each raw material, stirs, and then adjusts with malic acid Joint compound pH value, to 6.8-6.9, is then warming up to 45-50 DEG C to compound, prepares after then standing 20 hours.
3. young-generating machine internal layer as claimed in claim 1 a kind of is with modified antirust paint, it is characterised in that former by following weight portion Material is made: acrylic emulsion 32 parts, epoxy resin latex 32 parts, sepiolite powder 5 parts, Magnetitum powder 5 parts, octadecyldimethyl uncle Amine 0.8 part, N-hydroxy-succinamide 0.8 part, castor oil polyoxyethylene ether 0.8 part, polypropylene glycerol aether 0.8 part, silane Coupling agent 1.5 parts, tri(2-ethylhexyl)acetocitrate 3 parts, modified nano-alumina 5.5 parts.
4. the preparation method of the modified antirust paint of young-generating machine internal layer as claimed in claim 1, it is characterised in that step is such as Under: by each raw material mix homogeneously, then high speed dispersion 20-25 minute under 1500-1600 rev/min of rotating speed, obtains finished product.
CN201610613089.8A 2016-07-29 2016-07-29 A kind of young-generating machine internal layer modification antirust paint Pending CN106118304A (en)