CN104498160A - Concrete releasing agent prepared from rosin and preparation method thereof - Google Patents
Concrete releasing agent prepared from rosin and preparation method thereof Download PDFInfo
- Publication number
- CN104498160A CN104498160A CN201410785664.3A CN201410785664A CN104498160A CN 104498160 A CN104498160 A CN 104498160A CN 201410785664 A CN201410785664 A CN 201410785664A CN 104498160 A CN104498160 A CN 104498160A
- Authority
- CN
- China
- Prior art keywords
- rosin
- concrete
- parts
- preparation
- releasing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a concrete releasing agent prepared from rosin and a preparation method thereof. The concrete releasing agent is prepared from the following raw materials in parts by weight: 25-40 parts of modified rosin, 20-25 parts of olive oil, 0.6-0.8 part of triethylene diamine, 8-10 parts of a calcium-zinc stabilizer, 2-3 parts of alkenyl succinate, 1.5-2.0 parts of diphenylamine, 1.4-1.5 parts of stearin, 4-5 parts of stearic acid, 0.1-0.3 part of lithium carbonate, 0.5-0.6 part of sodium fluosilicate and 150-200 parts of deionized water. The concrete releasing agent disclosed by the invention has a good releasing effect. By modifying rosin, the releasing smoothness is good, so that the concrete and a mould are quickly released. The concrete released is smooth and level in surface and free of defects and the mould is few in concrete amount and free of rust on the template. The concrete releasing agent disclosed by the invention is green, environment-friendly, economic and suitable for wide application.
Description
Technical field
The invention provides a kind of concrete parting agent, particularly a kind of concrete parting agent made with rosin and preparation method thereof.
Background technology
Concrete parting agent is also known as concrete isolation agent or demoulding lubricant; Be one be applied to template inwall rise lubrication and buffer action, make concrete can depart from template smoothly when form removal, keep the intact material of concrete shape, traditional release materials adds diesel oil with machine oil or used oil, find in the engineering constructions such as long-term water conservancy and hydropower, highway, railway, use used oil brushing template, concrete surface is produced and pollutes, pollution in various degree is also caused to environment simultaneously; But existing releasing agent exist stripping result not good, be difficult to remove in template, and ineffective to template maintenance, operating efficiency etc. is affected also increases construction cost.
Summary of the invention
The object of the present invention is to provide a kind of concrete parting agent made with rosin and preparation method thereof.
The present invention adopts following technical scheme to achieve these goals:
With the concrete parting agent that rosin is made, the weight part of its constitutive material is: modified rosin 25-40, sweet oil 20-25, triethylene diamine 0.6-0.8, calcium zinc stabilizer 8-10, alkenyl succinic acid ester 2-3, pentanoic 1.5-2.0, stearin 1.4-1.5, stearic acid 4-5, Quilonum Retard 0.1-0.3, Sodium Silicofluoride 0.5-0.6 and deionized water 150-200.
With the concrete parting agent that rosin is made, the weight part of its constitutive material is: modified rosin 35, sweet oil 22, triethylene diamine 0.7, calcium zinc stabilizer 9, alkenyl succinic acid ester 2.5, pentanoic 1.8, stearin 1.5, stearic acid 4.5, Quilonum Retard 0.2, Sodium Silicofluoride 0.5 and deionized water 180.
The preparation method of the concrete parting agent made with rosin, comprises following content:
(1) preparation of modified rosin: first by rosin heating to 50-60 DEG C; Then the 3.5-4.0% ferrous sulfate of rosin quality, 8-10% carbon fiber, 10-15% bamboo fibers is added wherein; Be uniformly mixed and place 2-3 hour, and then add the potassium humate powder of rosin 4-5%, be warming up to uniform stirring 1-2 hour under the condition of 80-90 DEG C, naturally cool to room temperature, regulator solution pH value is to 2-3; Again with deionized water in mass ratio 1:5 mix, stir 30-40 minute, centrifugation obtains filtrate;
(2) take each raw material by the weight part of constitutive material, the modified rosin of step (1) is put into reactor, is heated to 100-120 DEG C, in heat-processed, spills minor amount of water; Then sweet oil, triethylene diamine and calcium zinc stabilizer is added; Continue heat and stir 40-50 minute, temperature controls in the scope of 140 DEG C-150 DEG C; Finally add other residue constitutive material, continue to be stirred to moisture and evaporate completely, to obtain final product.
Beneficial effect of the present invention:
The present invention has good stripping result; by the modification to rosin; make demoulding slip good; realize it to the fast demoulding between concrete and mould; the smooth zero defect of concrete surface after the demoulding, the sticky amount of mould concrete is few, to template non-corroding; the present invention's green, environmental protection, economy, be applicable to applying widely.
Embodiment
Embodiment 1: the concrete parting agent made with rosin, the weight part (kg) of its constitutive material is: modified rosin 35, sweet oil 22, triethylene diamine 0.7, calcium zinc stabilizer 9, alkenyl succinic acid ester 2.5, pentanoic 1.8, stearin 1.5, stearic acid 4.5, Quilonum Retard 0.2, Sodium Silicofluoride 0.5 and deionized water 180.
The preparation method of the concrete parting agent made with rosin, comprises following content:
(1) preparation of modified rosin: first by rosin heating to 55 DEG C; Then 3.8% ferrous sulfate of rosin quality, 8% carbon fiber, 12% bamboo fibers is added wherein; Be uniformly mixed and place 2-3 hour, and then add the potassium humate powder of rosin 4.5%, be warming up to uniform stirring 1-2 hour under the condition of 85 DEG C, naturally cool to room temperature, regulator solution pH value is to 2-3; Again with deionized water in mass ratio 1:5 mix, stir 35 minutes, centrifugation obtains filtrate;
(2) take each raw material by the weight part of constitutive material, the modified rosin of step (1) is put into reactor, is heated to 100-120 DEG C, in heat-processed, spills minor amount of water; Then sweet oil, triethylene diamine and calcium zinc stabilizer is added; Continue heat and stir 40-50 minute, temperature controls in the scope of 140 DEG C-150 DEG C; Finally add other residue constitutive material, continue to be stirred to moisture and evaporate completely, to obtain final product.
Above-mentioned obtained concrete parting agent solid content≤5.3%; To steel plate without any corrosion harmfulness, dry film time 25-30min; Concrete surface is smooth, and adhesive capacity is 3.2g/m
2, meet the service requirements of concrete parting agent.
Claims (3)
1., with the concrete parting agent that rosin is made, it is characterized in that the weight part of its constitutive material is: modified rosin 25-40, sweet oil 20-25, triethylene diamine 0.6-0.8, calcium zinc stabilizer 8-10, alkenyl succinic acid ester 2-3, pentanoic 1.5-2.0, stearin 1.4-1.5, stearic acid 4-5, Quilonum Retard 0.1-0.3, Sodium Silicofluoride 0.5-0.6 and deionized water 150-200.
2. the concrete parting agent made with rosin according to claim 1, is characterized in that the weight part of its constitutive material is: modified rosin 35, sweet oil 22, triethylene diamine 0.7, calcium zinc stabilizer 9, alkenyl succinic acid ester 2.5, pentanoic 1.8, stearin 1.5, stearic acid 4.5, Quilonum Retard 0.2, Sodium Silicofluoride 0.5 and deionized water 180.
3. a preparation method for the concrete parting agent made with rosin as claimed in claim 1, is characterized in that comprising following content:
(1) preparation of modified rosin: first by rosin heating to 50-60 DEG C; Then the 3.5-4.0% ferrous sulfate of rosin quality, 8-10% carbon fiber, 10-15% bamboo fibers is added wherein; Be uniformly mixed and place 2-3 hour, and then add the potassium humate powder of rosin 4-5%, be warming up to uniform stirring 1-2 hour under the condition of 80-90 DEG C, naturally cool to room temperature, regulator solution pH value is to 2-3; Again with deionized water in mass ratio 1:5 mix, stir 30-40 minute, centrifugation obtains filtrate;
(2) take each raw material by the weight part of constitutive material, the modified rosin of step (1) is put into reactor, is heated to 100-120 DEG C, in heat-processed, spills minor amount of water; Then sweet oil, triethylene diamine and calcium zinc stabilizer is added; Continue heat and stir 40-50 minute, temperature controls in the scope of 140 DEG C-150 DEG C; Finally add other residue constitutive material, continue to be stirred to moisture and evaporate completely, to obtain final product.