CN106118200A - 一种用于化工泵泵体的隔热腻子胶粉 - Google Patents
一种用于化工泵泵体的隔热腻子胶粉 Download PDFInfo
- Publication number
- CN106118200A CN106118200A CN201610457381.5A CN201610457381A CN106118200A CN 106118200 A CN106118200 A CN 106118200A CN 201610457381 A CN201610457381 A CN 201610457381A CN 106118200 A CN106118200 A CN 106118200A
- Authority
- CN
- China
- Prior art keywords
- parts
- pump
- heat insulation
- pump housing
- rubber powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用于化工泵泵体的隔热腻子胶粉,涉及泵阀制备技术领域,包括以下原料制备而成:石英沙粉10‑20份、水60‑80份、钛白粉3‑5份、膨胀珍珠岩2‑4份、海泡石1‑3份、滑石粉2‑4份、木纤维2‑4份、空心陶瓷微珠2‑4份、玻璃中空微珠2‑4份、塑料中空微珠3‑5份、粉煤灰漂珠2‑4份、蛭石粉6‑8份、明矾5‑7份、水玻璃6‑8份、增强剂15‑25份。本发明的有益效果是:本发明工艺流程简洁,原料配比合理,原料价廉且易得,制备的找平腻子胶粉作为泵体外壁隔热,不仅附着力强,并且有效的将泵体内部的热量阻隔,避免传热至泵壳,导致泵壳发热温度过高,且防止高温导致油漆脱落造成泵体表面的生锈腐蚀,安全简单,经久耐用。
Description
技术领域
本发明涉及泵阀制备技术领域,具体涉及一种用于化工泵泵体的隔热腻子胶粉。
背景技术
化工泵是全国联合设计的节能泵,泵的性能,技术要求,根据国际标准所规定的性能和尺寸设计的,其优点:全系列水利性能布局合理,用户选择范围宽,“后开式”结构,检修方便、效率和吸程达到国际先进水平,广泛用于工业、城市给水、排水、亦可用于农田、果园排灌,供输送清水或物理及化学性质类似清水的其他液体之用,随着科技水平的不断提高,化工泵的使用领域也多种多样,化工泵在使用时,由于一些特殊的环境需求,如进行高热的流体输送时,由于流体温度高,大量的热量会通过泵体传送至泵壳外壁,这样,泵壳外壁温度很高,很容易造成烫伤,同时,长期的高热量存在,会使得涂覆在泵壳表面的油漆受热过高,造成脱落,影响化工泵整体美观,且容易生锈腐蚀。
发明内容:
本发明所要解决的技术问题在于提供一种配比合理,制作工艺简单,效果显著的用于化工泵泵体的隔热腻子胶粉。
本发明所要解决的技术问题采用以下技术方案来实现:
一种用于化工泵泵体的隔热腻子胶粉,其特征在于,由以下重量份的原料制成:
石英沙粉10-20份、水60-80份、钛白粉3-5份、膨胀珍珠岩2-4份、海泡石1-3份、滑石粉2-4份、木纤维2-4份、空心陶瓷微珠2-4份、玻璃中空微珠2-4份、塑料中空微珠3-5份、粉煤灰漂珠2-4份、蛭石粉6-8份、明矾5-7份、水玻璃6-8份、增强剂15-25份。
各原料的优选重量为:石英沙粉15份、水70份、钛白粉4份、膨胀珍珠岩3份、海泡石2份、滑石粉3份、木纤维3份、空心陶瓷微珠3份、玻璃中空微珠3份、塑料中空微珠4份、粉煤灰漂珠3份、蛭石粉7份、明矾6份、水玻璃7份、增强剂20份。
所述的增强剂采用镧铈稀土8份、硅胶25份、水68份、早强剂7、碳酸钙15份通过先将所述硅胶、早强剂和镧铈稀土加入水中搅拌均匀,再将碳酸钙加入上述搅拌好的液体中,搅拌成浆体,经硬化后将其破碎,即得成品。
本申请中化工泵泵体的隔热腻子胶粉的制备方法为:
1)将石英沙粉、钛白粉、膨胀珍珠岩、海泡石、滑石粉、空心陶瓷微珠、玻璃中空微珠、塑料中空微珠、粉煤灰漂珠、蛭石粉、明矾、投入合成釜中,搅拌转速为300-400r/min,搅拌15-25分钟后,投入球磨机中,球磨至颗粒细度为25-35um;
2)将原料中的木纤维和水玻璃和步骤1得到的产物,再次放入合成釜中,转速为500-600r/min,搅拌10-20分钟后,再将水和增强剂加入其中,搅拌转速提高为为800-1000r/min,搅拌30-40分钟即可。
本发明的有益效果是:本发明工艺流程简洁,原料配比合理,原料价廉且易得,制备的找平腻子胶粉作为泵体外壁隔热,不仅附着力强,并且有效的将泵体内部的热量阻隔,避免传热至泵壳,导致泵壳发热温度过高,且防止高温导致油漆脱落造成泵体表面的生锈腐蚀,安全简单,经久耐用。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
称取:石英沙粉10kg、水60kg、钛白粉3kg、膨胀珍珠岩2kg、海泡石1kg、滑石粉2kg、木纤维2kg、空心陶瓷微珠2kg、玻璃中空微珠2kg、塑料中空微珠3kg、粉煤灰漂珠2kg、蛭石粉6kg、明矾5kg、水玻璃6kg、增强剂15kg。
实施例2
称取:石英沙粉15kg、水70kg、钛白粉4kg、膨胀珍珠岩3kg、海泡石2kg、滑石粉3kg、木纤维3kg、空心陶瓷微珠3kg、玻璃中空微珠3kg、塑料中空微珠4kg、粉煤灰漂珠3kg、蛭石粉7kg、明矾6kg、水玻璃7kg、增强剂20kg。
制备上述实施例1-2的方法为:
1)将石英沙粉、钛白粉、膨胀珍珠岩、海泡石、滑石粉、空心陶瓷微珠、玻璃中空微珠、塑料中空微珠、粉煤灰漂珠、蛭石粉、明矾、投入合成釜中,搅拌转速为300-400r/min,搅拌15-25分钟后,投入球磨机中,球磨至颗粒细度为25-35um;
2)将原料中的木纤维和水玻璃和步骤1得到的产物,再次放入合成釜中,转速为500-600r/min,搅拌10-20分钟后,再将水和增强剂加入其中,搅拌转速提高为为800-1000r/min,搅拌30-40分钟即可。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种用于化工泵泵体的隔热腻子胶粉,其特征在于,由以下重量份的原料制成:
石英沙粉10-20份、水60-80份、钛白粉3-5份、膨胀珍珠岩2-4份、海泡石1-3份、滑石粉2-4份、木纤维2-4份、空心陶瓷微珠2-4份、玻璃中空微珠2-4份、塑料中空微珠3-5份、粉煤灰漂珠2-4份、蛭石粉6-8份、明矾5-7份、水玻璃6-8份、增强剂15-25份。
2.根据权利要求1所述的一种用于化工泵泵体的隔热腻子胶粉,其特征在于:各原料的优选重量为:石英沙粉15份、水70份、钛白粉4份、膨胀珍珠岩3份、海泡石2份、滑石粉3份、木纤维3份、空心陶瓷微珠3份、玻璃中空微珠3份、塑料中空微珠4份、粉煤灰漂珠3份、蛭石粉7份、明矾6份、水玻璃7份、增强剂20份。
3.根据权利要求1所述的一种用于化工泵泵体的隔热腻子胶粉,其特征在于:所述的增强剂采用镧铈稀土8份、硅胶25份、水68份、早强剂7、碳酸钙15份通过先将所述硅胶、早强剂和镧铈稀土加入水中搅拌均匀,再将碳酸钙加入上述搅拌好的液体中,搅拌成浆体,经硬化后将其破碎,即得成品。
4.制备权利要求1或2中一种用于化工泵泵体的隔热腻子胶粉的方法,其特征在于:
1)将石英沙粉、钛白粉、膨胀珍珠岩、海泡石、滑石粉、空心陶瓷微珠、玻璃中空微珠、塑料中空微珠、粉煤灰漂珠、蛭石粉、明矾、投入合成釜中,搅拌转速为300-400r/min,搅拌15-25分钟后,投入球磨机中,球磨至颗粒细度为25-35um;
2)将原料中的木纤维和水玻璃和步骤1得到的产物,再次放入合成釜中,转速为500-600r/min,搅拌10-20分钟后,再将水和增强剂加入其中,搅拌转速提高为为800-1000r/min,搅拌30-40分钟即可。