CN105315751A - 一种腻子粉强度剂 - Google Patents

一种腻子粉强度剂 Download PDF

Info

Publication number
CN105315751A
CN105315751A CN201410341471.9A CN201410341471A CN105315751A CN 105315751 A CN105315751 A CN 105315751A CN 201410341471 A CN201410341471 A CN 201410341471A CN 105315751 A CN105315751 A CN 105315751A
Authority
CN
China
Prior art keywords
putty powder
parts
strengthening agent
putty
silica gel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410341471.9A
Other languages
English (en)
Inventor
张芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Angduo Environment Treatment Co Ltd
Original Assignee
Chongqing Angduo Environment Treatment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Angduo Environment Treatment Co Ltd filed Critical Chongqing Angduo Environment Treatment Co Ltd
Priority to CN201410341471.9A priority Critical patent/CN105315751A/zh
Publication of CN105315751A publication Critical patent/CN105315751A/zh
Pending legal-status Critical Current

Abstract

一种腻子粉强度剂,它由下列配料制作而成(重量比),腻子粉1000份,水240-270份,硅胶3-20份,腻子粉助剂10-100份,镧钵稀土0.05-5份;先将所述硅胶、带早强功能的腻子粉助剂和镧钵稀土加人水中搅拌均匀,再将腻子粉加人上述搅拌好的液体中,搅拌成腻子粉浆体,经硬化后将其破碎,即得成品。本发明能有效提高腻子粉强度,其添加量为腻子粉总量的2%,成本低,经济实用,适合腻子粉厂中推广使用。

Description

一种腻子粉强度剂
技术领域:本发明涉及一种建筑材料,具体涉及一种用于在腻子粉制作过程中添加的腻子粉强度剂及制作该剂的方法。
背景技术:腻子粉是一种极常用的建筑材料,出于节约能源和资源消耗的目的,如何提高腻子粉的强度,以及在保持强度的前提下减少腻子粉熟料的用量,受到全国各研究机构、大专院校的重视。目前,有多篇资料报道了在腻子粉熟料、石膏、混合材中加入某种添加材料共同粉磨,可以提高腻子粉强度,从而增加混合材的比例,这类添加材料可以称为腻子粉强度激发剂,如中国发明专利CN1059411C、中国发明专利公开CN1220977A,CN1241545A分别公开了不同成份的腻子粉强度激发剂,它们可以不同程度地提高腻子粉的强度,从而增加混合材的比例,减少腻子粉熟料的用量,起到节约能源和资源的作用,但是这些腻子粉强度激发剂本身成本较高,而添加量一般在5-10%之间,因而经济成本较高,难以用于大规模生产。
发明内容:本发明目的是提供一种成本低、添加量少,又能有效提高腻子粉强度的腻子粉强度剂,同时提供该腻子粉强度剂的制作方法。
为达到上述目的,本发明采用的技术方案是:一种腻子粉强度剂,它由下列配料制作而成(重量比),
腻子粉1000份,
水240-270份,
硅胶3-20份,
带早强功能的腻子粉助剂10-100份,
镧铈稀土0.05-5份。
制作本发明的腻子粉强度激发剂时,先将所述硅胶、带早强功能的腻子粉助剂和镧铈稀土加入水中搅拌均匀。再将腻子粉加入上述搅拌好的液体中,搅拌成腻子粉浆体,经硬化后将其破碎。即得成品;一般情况下,所述腻子粉浆体须经3天时间硬化,然后以机械方法将其破碎,其破碎后的成品为固体颗粒状物体即可,为提高效果,可将其磨成粗粉。
使用时,在腻子粉磨头添加腻子粉总质量2%的本发明的腻子粉强度激发剂,与腻子粉熟料、石膏、混合材同时粉磨即可,出磨腻子粉3天的抗压强度可提高2-3Mpa,28天的抗压强度可提高6-l0Mpa。
上述技术方案中,效果更好的配料重最比为,
腻子粉1000份,
水250份,
硅胶5-8份,
腻子粉助剂20-30份,
镧铈稀土0.5-1份。
本发明的机理来自于“腻子粉晶胚”理论,根据这一理论,可以用硬化了的腻子粉体经细磨成为腻子粉核,作为腻子粉强度激发剂,由于在腻子粉中掺有了腻子粉核,促使新拌腻子粉颗粒的快速生长,强度上升。但是这种方法对腻子粉强度的提高作用不够,本发明用掺入了硅胶、腻子粉助剂和镧铈稀土的腻子粉肺制成腻子粉核,对提高腻子粉的强度起到了明显的作用。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
1、由于本发明应用“腻子粉晶胚”理论制成,对腻子粉强度的提高有显著作用,在添加量为2%的情况下,出磨腻子粉3天的抗压强度可提高2-3Mpa。28天的抗压强度可提高6-10Mpa。
2、由于本发明的主要成份为腻子粉,且使用时所需添加量为2%。因而成本低,经济实用,适合腻子粉厂中推广使用。
实施案例:
实施例一:一种腻子粉强度剂。由下列配料制作而成,散装腻子粉1000公斤,水(自来水)250公斤,宜兴市国立助剂厂生产的国立牌硅胶5公斤,阜宁县白玉关水溶性树脂厂生产的白玉牌腻子粉助剂Xu25公斤,镧铈稀土0.5公斤。
先将所述硅胶、带早强功能的腻子粉助剂和镧铈稀土加入水中搅排均匀,再将腻子粉加入上述搅拌好的液体中,搅拌成腻子粉浆休,经3天硬化后将其破碎,即得成品,为增强效果,可将其预磨成粗粉。
使用时,添加占腻子粉总最2%的本品,与腻子粉熟料、石青、混合材一起粉磨即可。
上述材料的价格情况如下:
原材料名称数量(公斤)单价(元l公斤)总价(元)
散装腻子粉10000.14140
水250一一
国立牌硅胶54.845
白玉牌腻子粉助剂Xu254.8120
镧铈稀土0.5126
合计(成品)1128311
因此,本实施例的激发剂原材料成本约276元/吨,完全能符合腻子粉厂生的需要。

Claims (3)

1.一种腻子粉强度剂,其特征在于:它由下列配料制作而成(重量比),
腻子粉1000份,
水240-270份,
硅胶3-20份,
腻子粉助剂10-100份,
镧铈稀土0.05-5份。
2.如权利要求1所述的腻子粉强度剂,其特征在于:所述配料的重量比为,
腻子粉1000份,
水250份,
硅胶5-8份,
腻子粉助剂20-30份,
镧铈稀土0.5-1份。
3.制作如权利要求1所述的腻子粉强度剂的方法,其特征在于:先将所述硅胶、带早强功能的腻子粉助剂和镧铈稀土加入水中搅拌均匀,再将腻子粉加入上述搅拌好的液体中,搅拌成腻子粉浆体,经硬化后将其破碎,即得成品。
CN201410341471.9A 2014-07-18 2014-07-18 一种腻子粉强度剂 Pending CN105315751A (zh)