CN106116259A - A kind of colored Self-leveling porous footpath face material and preparation method - Google Patents
A kind of colored Self-leveling porous footpath face material and preparation method Download PDFInfo
- Publication number
- CN106116259A CN106116259A CN201610462251.0A CN201610462251A CN106116259A CN 106116259 A CN106116259 A CN 106116259A CN 201610462251 A CN201610462251 A CN 201610462251A CN 106116259 A CN106116259 A CN 106116259A
- Authority
- CN
- China
- Prior art keywords
- leveling
- colored self
- porous
- footpath face
- cementitious matter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of colored Self-leveling porous footpath face material and preparation method, belong to asphalt pavement material field, including cementitious matter with gather materials, it is characterized in that: described cementitious matter is made up of the component of following mass percent: epoxy resin 25 ~ 50%, diluent 2 ~ 5%, firming agent 30 ~ 50%, strengthens spike 15 ~ 40%；Described gathering materials joins limestone or gravel for single-stage.Relative to prior art, the invention have the benefit that the present invention uses single-stage to join to gather materials and prepare compound, cementitious matter consumption can be greatly reduced, thus reduce cost.It addition, the present invention has big air gap characteristics, be combined with storage-type basic unit for footpath face, the storage of precipitation can be realized, alleviate urban heat land effect.Material at high temperature good stability prepared by the present invention, low-temperature cracking-resistance is strong, caking property is strong, economic and environment-friendly, preparation is simple, good weatherability, porous water storage.
Description
Technical field
The present invention relates to colored Self-leveling porous footpath face material and the preparation method of a kind of municipal administration footpath, belong to
Asphalt pavement material field.
Background technology
Over nearly 20 years, China's economy and society quickly grows, and the living standard of the people rises year by year, in country's overall situation
Under guiding, town dweller is more and more higher to the requirement of living environment.Road is as the important component part in city, except meeting
Outside current primary demand, ought to undertake more function, such as colored road surface and beautify city, porous pavements water storage is to city
The control etc. of city's tropical island effect.
The existing Colorful Asphalt Pavement in market mainly includes three classes: a class is color asphalt concrete；One class is colored envelope
Layer；Another kind of is coloured coating.Owing to the consumption of three types of technology chromatic cementing agent is the highest, and the part that colored road surface is the most expensive
It is cementitious matter, so the cost of several colored road surface is the highest.It addition, a few class colored road surfaces are water shutoff layer, it is impossible to storage
Moisture, therefore not there is the effect alleviating urban heat island.Published colored road surface material Patents does not the most possess big space, thoroughly
Water, water storage function.
Summary of the invention
The present invention is directed to deficiencies of the prior art, it is provided that a kind of colored Self-leveling porous footpath face material and
Its preparation method, its major advantage is that high-temperature stability is good, low-temperature cracking-resistance is strong, caking property is strong, economic and environment-friendly, preparation is simple,
Good weatherability, porous water storage etc..
In order to realize above-mentioned target, the present invention adopts the following technical scheme that: a kind of colored Self-leveling porous footpath face
Material, including cementitious matter with gather materials, it is characterised in that: described cementitious matter is made up of the component of following mass percent: epoxy
Resin 25～50%, diluent 2～5%, firming agent 30～50%, strengthen spike 15～40%；Described gathering materials is joined for single-stage
Limestone or gravel.
Described spike of strengthening is made up of the component of following mass percent: bentonite 10～30%, Pulvis Talci 50～
80%, 600～800 mesh silica flour 10～30%, pigment 10～30%.
Described aggregate size is between 9mm～11mm.
The described mass ratio with cementitious matter that gathers materials is 2.5:1～3.5:1.
Described epoxy resin is oiliness epoxy resin, and firming agent is modified amine curing agent.Described diluent is diethylene glycol contracting
Water glycerin ether.Described modified amine curing agent is low molecule pa resin, molecular weight 650～1050.
The preparation method of a kind of colored Self-leveling porous footpath face material, it is characterised in that comprise the following steps:
(1) by bentonite 10～30%, Pulvis Talci 50～80%, 600～800 mesh silica flour 10～30%, pigment 10～
30% weighs by weight percentage, and as strengthening, spike is stand-by；
(2) by epoxy resin 25～50%, diluent 2～5%, strengthen spike 15～40% and join by weight percentage
System mixing, the most quickly stirring 45～60min is to mix homogeneously, obtains cementitious matter first product；
(3) single-stage is joined gather materials that to add the cementitious matter first product stirring 1～2min that agitator prepared with step (2) equal to mixing
Even, obtain compound；
(4) being added by firming agent in the compound of step (3), stirring 1～2min, to mix homogeneously, makes colored Self-leveling
Porous footpath face material.
Relative to prior art, the invention have the benefit that the present invention uses single-stage to join to gather materials and prepare compound, can be big
Width reduces cementitious matter consumption, thus reduces cost.It addition, the present invention has big air gap characteristics, be combined with storage-type basic unit and be used for
Footpath face, can realize the storage of precipitation, alleviates urban heat land effect.Material at high temperature good stability prepared by the present invention, low temperature
Crack resistance is strong, caking property is strong, economic and environment-friendly, preparation is simple, good weatherability, porous water storage.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention made concrete introduction.
One colour Self-leveling porous footpath face of the present invention material is mainly made up of with gathering materials cementitious matter.Cementitious matter quality
Percentage ratio composition as follows: epoxy resin 25～50%, diluent 10～30%, firming agent 30～50%, reinforcement spike 15～
40%.Strengthen spike mass percent composition as follows: bentonite 10～30%, Pulvis Talci 50～80%, 800 mesh silica flours 10～
30%, pigment 10～30%.Gathering materials and join limestone aggregates or gravel for single-stage, aggregate size is between 9mm～11mm.Single-stage is joined
The ratio with cementitious matter of gathering materials is 2.5:1～3.5:1.Described epoxy resin is oiliness epoxy resin, and firming agent is that modified amine is solid
Agent.Described diluent is diethylene glycol glycidyl ether.
The preparation method of colored Self-leveling porous footpath face material, comprises the following steps:
(1) by bentonite 10～30%, Pulvis Talci 50～80%, 800 mesh silica flours 10～30%, pigment 10～30% is pressed
Ratio weighs, stand-by；
(2) by epoxy resin 25～50%, diluent 10～30%, strengthen spike 15～40% and carry out in proportion preparing mixing
Closing, the most quickly stirring 45～60min is to uniformly；
(3) join single-stage to gather materials and add cementitious matter prepared by action of forced stirring device and 1,2 steps and stir 1～2min to uniformly；
(4) being added by firming agent in the compound of the 3rd step, stirring 1～2min, to uniformly, makes colored Self-leveling porous people
Face, trade material.
The composition proposal of several concrete colored Self-leveling porous footpath face material is given below, and it is concrete to provide it
Preparation method.
Scheme one
Preparation method:
(1) by bentonite 15%, Pulvis Talci 54%, 800 mesh silica flours 16%, pigment 15% weighs in proportion, stand-by；
(2) by epoxy resin 30%, diluent 3%, strengthen spike 32% and carry out preparation mixing in proportion, the soonest
Speed stirring 45～60min is to uniformly；
(3) count firming agent ratio, according to gathering materials: cementitious matter mass ratio 3:1, list graded gravel is added action of forced stirring device
The cementitious matter prepared with 1,2 steps stirs 1～2min to uniformly；
(4) by firming agent 35%, adding in the compound of the 3rd step, stirring 1～2min, to uniformly, makes colored Self-leveling
Porous footpath face material.
Scheme two
Preparation method:
(1) by bentonite 10%, Pulvis Talci 70%, 800 mesh silica flours 10%, pigment 10% weighs in proportion, stand-by；
(2) by epoxy resin 35%, diluent 5%, strengthen spike 25% and carry out preparation mixing in proportion, the soonest
Speed stirring 45～60min is to uniformly；
(3) count firming agent ratio, according to gathering materials: cementitious matter mass ratio 3.1:1, single-stage is joined limestone gravel and adds strong
Cementitious matter stirring 1～2min prepared by agitator processed and 1,2 steps is to uniformly；
(4) by firming agent 35%, adding in the compound of the 3rd step, stirring 1～2min, to uniformly, makes colored Self-leveling
Porous footpath face material.
The performance indications of the typical proportion chromatic cementing agent of the present invention are as shown in table 1, colored Self-leveling porous footpath face
Material property is as shown in table 2.
Table 1 color resin properties of rubber index request
Table 2 colored Self-leveling porous footpath face material property
The above is only the preferred embodiment of the present invention, it should be pointed out that: for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make the replacement of some improvement and equivalents, these improve
The technical scheme obtained with equivalent also should belong to protection scope of the present invention.
Claims (8)
1. a colored Self-leveling porous footpath face material, including cementitious matter with gather materials, it is characterised in that: described cementitious matter
Be made up of the component of following mass percent: epoxy resin 25 ~ 50%, diluent 2 ~ 5%, firming agent 30 ~ 50%, strengthen spike 15 ~
40%；Described gathering materials joins limestone or gravel for single-stage.
Colored Self-leveling porous footpath face the most according to claim 1 material, it is characterised in that: described reinforcement spike
It is made up of the component of following mass percent: bentonite 10 ~ 30%, Pulvis Talci 50 ~ 80%, 600 ~ 800 mesh silica flours 10 ~ 30%, face
Material 10 ~ 30%.
Colored Self-leveling porous footpath face the most according to claim 2 material, it is characterised in that: described aggregate size
Between 9mm ~ 11mm.
Colored Self-leveling porous footpath face the most according to claim 1 material, it is characterised in that: described gathers materials and glue
The mass ratio of ramming material is 2.5:1 ~ 3.5:1.
Colored Self-leveling porous footpath face the most according to claim 2 material, it is characterised in that: described epoxy resin is
Oiliness epoxy resin, firming agent is modified amine curing agent.
Colored Self-leveling porous footpath face the most according to claim 5 material, it is characterised in that: described modified amine is solid
Agent is low molecule pa resin, molecular weight 650 ~ 1050.
Colored Self-leveling porous footpath face the most according to claim 2 material, it is characterised in that: described diluent is two
Glycol glycidyl ether.
8. the preparation method of a colored Self-leveling porous footpath face material, it is characterised in that comprise the following steps:
(1) by bentonite 10 ~ 30%, Pulvis Talci 50 ~ 80%, 600 ~ 800 mesh silica flours 10 ~ 30%, pigment 10 ~ 30% percentage by weight
Than weighing, as strengthening, spike is stand-by；
(2) by epoxy resin 25 ~ 50%, diluent 2 ~ 5%, strengthen spike 15 ~ 40% and carry out preparation mixing by weight percentage,
Under room temperature, quickly stirring 45 ~ 60min, to mix homogeneously, obtains cementitious matter first product；
(3) single-stage is joined gather materials add agitator prepare with step (2) cementitious matter first product stirring 1 ~ 2min to mixing homogeneously, must
To compound；
(4) being added by firming agent in the compound of step (3), 1 ~ 2min is to mix homogeneously in stirring, makes colored Self-leveling porous
Footpath face material.