CN104356661B - A kind of Compositional type SBS modified pitch steady heat storage agent - Google Patents
A kind of Compositional type SBS modified pitch steady heat storage agent Download PDFInfo
- Publication number
- CN104356661B CN104356661B CN201410665122.2A CN201410665122A CN104356661B CN 104356661 B CN104356661 B CN 104356661B CN 201410665122 A CN201410665122 A CN 201410665122A CN 104356661 B CN104356661 B CN 104356661B
- Authority
- CN
- China
- Prior art keywords
- modified pitch
- pitch
- heat storage
- sbs
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of Compositional type SBS modified pitch steady heat storage agent, its component and percentage composition thereof are as follows: the polyethylene polyamine salt 50~80% containing a chain alkyl and one or more thiazolinyl and aryl, antioxidant 5~20%, accelerator 10~30%.Beneficial effects of the present invention is as follows: make matrix pitch and SBS organically combine by stabilizer, makes modified pitch have lasting hot storage stability.Chain alkyl and aryl in polyethylene polyamine salt improve the compatibility between matrix pitch and SBS;The matrix pitch that arene content is different had good adaptability;Be conducive to the formation of modified asphalt cross-linking structure;Reduce the aging and degraded during the preparation of modified pitch and thermmal storage;Improve the serviceability of modified pitch;Improve modified pitch and mix and stir the Adhesion property between material or between modified pitch and roadbed.
Description
Technical field
The present invention relates to a kind of Compositional type SBS modified pitch steady heat storage agent, belong to Fine Organic Chemical product field.
Technical background
Colophonium is the raw material that road traffic, buildings waterproof and industrial antisepsis are conventional.Along with road traffic is to Colophonium serviceability
Requirement improves constantly, and the inherent defect of matrix pitch restricts its development and application, and asphalt modification technology is arisen at the historic moment.Colophonium at present
The kind of modifying agent and method of modifying are a lot, the most especially with the application of SBS modified pitch and with the fastest developing speed, account for whole world Colophonium
The 60% more than of usage amount.
SBS is a kind of non-polar polymeric material, and relative density is less than 0.9, and Colophonium is the mixture that a kind of composition is extremely complex,
Containing polar component, relative density is more than 0.9;Both cause segregation phenomenon occur when thermmal storage at qualitative difference, have impact on
The serviceability of SBS modified pitch.In order to obtain the modification that hot storage stability is good, can meet road traffic serviceability needs
Colophonium, it is necessary to add modified pitch compatibility stabilizer.
The modified asphalt stabilizer of reported in literature mainly has mediation type and the big class of chemical reaction type two at present.Mediation type stabilizer is usual
The polarity difference between SBS and matrix pitch and relative density difference can only be changed, and obtain the storage stability of short-term, be in harmonious proportion in a large number
The membership that adds of agent affects the original serviceability of modified pitch.Chemical reaction type stabilizer is to send out between matrix pitch and modifying agent
Biochemical reaction, makes matrix pitch and modifying agent organically combine, and then obtains permanent hot storage stability.Chemistry is anti-
The type stabilizer of answering can be divided into again sulphur-containing stabilizer and without sulfur stabilizer, and what current reported in literature was more is sulphur-containing stabilizer.Sulfur-bearing is steady
The host determining agent is Cosan, by the crosslinking between sulfur and rubber, it is achieved the network interpenetrating between matrix pitch and modifying agent,
And then the hot storage stability of acquisition modified pitch, but sulphur-containing stabilizer is difficult to solve modified pitch usability during thermmal storage
The problem of adhesion difference between loss of energy, and modified pitch and mix.
Summary of the invention
The present invention provides a kind of compound SBS modified pitch steady heat storage agent, uses this stabilizer, can not only prevent SBS from changing
Segregation phenomenon is there is in property Colophonium during thermmal storage, and modified pitch usability loss of energy during thermmal storage can be reduced,
Improve the Adhesion property between SBS modified pitch and mix.
In order to achieve the above object, the present invention by the following technical solutions: a kind of Compositional type SBS modified pitch steady heat storage agent,
Its component and percentage composition thereof are as follows: the polyethylene polyamine salt 50~80 containing a chain alkyl and one or more thiazolinyl and aryl
%, antioxidant 5~20%, accelerator 10~30%.
By such scheme, described chain alkyl is C12~C20Alkyl.
By such scheme, described thiazolinyl is any one in vinyl, acrylic and pi-allyl, described aryl be phenyl,
Any one in benzyl and p-methoxyphenyl.
By such scheme, described polyethylene polyamine salt is ethylenediamine, diethylenetriamine, triethylene tetramine, TEPA
Any one in hydrochlorate, phosphate and sulfate.
By such scheme, described antioxidant is any one in antioxidant 264,1010 and 1076, fineness >=
300 mesh.
By such scheme, described accelerator is any one or the combination of two kinds in sierozem power, montmorillonite powder and flyash.
The concrete preparation method of above-mentioned Compositional type SBS modified pitch steady heat storage agent a: chain alkyl and one or many will be contained
The polyethylene polyamine salt of individual thiazolinyl and aryl is heated to flowable state, then antioxidant and accelerator is added thereto, stirring mixing
Uniformly, pulverize after being cooled to room temperature, i.e. obtain product more than 300 mesh.
Beneficial effects of the present invention is as follows:
1. the present invention employing polyethylene polyamine salt containing a chain alkyl and one or more thiazolinyl and aryl is as host, many
Amido in amine at high temperature reacts with the oxygen-content active point of polar compound in Colophonium, it is achieved stabilizer and the change of matrix pitch
Learning and combine, the carbon-carbon double bond in thiazolinyl crosslinks with the carbon-carbon double bond in SBS, it is achieved the chemistry knot between stabilizer and SBS
Close.Make matrix pitch and SBS organically combine by stabilizer, make modified pitch have lasting hot storage stability.
Chain alkyl and aryl in polyethylene polyamine salt improve the compatibility between matrix pitch and SBS;
2. change length or the content of aryl of polyethylene polyamine salt chain alkyl, make the substrate drip that stabilizer is different to arene content
Green grass or young crops has good adaptability;
3. the addition of accelerator accelerates stabilizer and SBS and the interaction of matrix pitch, beneficially modified asphalt cross-linking structure
Formation;
4. the formation of cross-linked structure and the addition of antioxidant, during significantly reducing preparation and the thermmal storage of modified pitch
Aging and degraded;
5. the formation of cross-linked structure improves the homogeneity of modified pitch, improves the serviceability of modified pitch;
6. between polar group and the metal-oxide of absorption and the mix in amine salt more than, there is good affinity, improve and change
Property Colophonium and mix and stir the Adhesion property between material or between modified pitch and roadbed.
Detailed description of the invention
Embodiment described below is the particular content in order to further illustrate the present invention, and the scope of application of the present invention is not by concrete real
Executing the impact of example, specific embodiment can determine according to concrete condition when technical scheme and use.
Embodiment 1
The preparation of stabilizer
By 3.5kg octadecyl vinyl base benzyl diethylenetriamine hydrochloride salt to flowable state, then by 0.5kg antioxidant
1010 and 1.0kg flyash are added thereto, and are cooled to room temperature after being uniformly mixed, finely ground to i.e. being compounded more than 300 mesh
The modified pitch steady heat storage agent of type SBS.
The 500.0g trade mark is SK-70 by the preparation of modified pitch#Asphalt be heated to 160 DEG C, add 20.0g star-shaped sbs
With 5.0g aforementioned stable agent, it is warming up to 180 DEG C after low velocity shear 30min at this temperature, and high speed shear at this temperature
40min, is then cooled to 160 DEG C, and 240min is grown at the uniform velocity stirring, i.e. obtains SBS modified bitumen product.
SBS modified bitumen product performance test
By the measurement of test method modification of " standard specification for construction and acceptance of highway asphalt pavement " (JTG F40-2004) that Ministry of Communications issues
The performance of Colophonium, the results are shown in Table 1 and table 2.
Embodiment 2
The preparation of stabilizer
3.5kg cetyl allyl phenyl ethylenediamine-hydrochloride is heated to flowable state, then by 0.5kg antioxidant 264
It is added thereto with 1.0kg sierozem power, after being uniformly mixed, is cooled to room temperature, finely ground to i.e. obtaining Compositional type SBS more than 300 mesh
Modified pitch steady heat storage agent.
The preparation preparation method of modified pitch is with embodiment 1
Performance of modified bitumen is tested
Method of testing, with embodiment 1, the results are shown in Table 2.
Embodiment 3
The preparation of stabilizer
3.0kg myristyl vinyl benzyl triethylene tetramine phosphate is heated to flowable state, then by 0.6kg antioxidant
1076 and 1.4kg flyash are added thereto, and are cooled to room temperature after being uniformly mixed, and are crushed to i.e. be compounded more than 300 mesh
The modified pitch steady heat storage agent of type SBS.
The preparation preparation method of modified pitch is with embodiment 1
Performance of modified bitumen is tested
Method of testing, with embodiment 1, the results are shown in Table 2.
Embodiment 4
The preparation of stabilizer
By 3.0kg sodium dodecyl allyl base phenyl TEPA hydrochloride salt to flowable state, then by 0.7kg antioxidant
1010 and 1.3kg sierozem power are added thereto, and after being uniformly mixed, are cooled to room temperature, are crushed to, more than 300 mesh, i.e. obtain
Compositional type SBS modified pitch steady heat storage agent.
The preparation preparation method of modified pitch is with embodiment 1
Performance of modified bitumen is tested
Method of testing, with embodiment 1, the results are shown in Table 2.
Embodiment 5
The preparation of stabilizer
By 3.0kg sodium dodecyl allyl base benzyl diethylenetriamine hydrochloride salt to flowable state, then by 0.5kg antioxidant
1076 and 1.0kg flyash and 0.5kg sierozem power are added thereto, and after being uniformly mixed, are cooled to room temperature, are crushed to be more than
300 mesh, i.e. obtain Compositional type SBS modified pitch steady heat storage agent.
The preparation preparation method of modified pitch is with embodiment 1
Performance of modified bitumen is tested
Method of testing, with embodiment 1, the results are shown in Table 2.
Embodiment 6
The preparation of stabilizer
By 3.0kg sodium dodecyl allyl base p-methoxyphenyl TEPA hydrochloride salt to flowable state, then 0.5kg is resisted
Oxidant 1010 and 1.5kg montmorillonite powder is added thereto, and after being uniformly mixed, is cooled to room temperature, is crushed to more than 300 mesh,
I.e. obtain Compositional type SBS modified pitch steady heat storage agent.
The preparation preparation method of modified pitch is with embodiment 1
Performance of modified bitumen is tested
Method of testing, with embodiment 1, the results are shown in Table 2.
Table 1 does not adds the SBS performance of modified bitumen of stabilizer
Table 2 adds the SBS performance of modified bitumen of stabilizer
Claims (4)
1. a Compositional type SBS modified pitch steady heat storage agent, its component and percentage composition thereof are as follows: containing a chain alkyl and the polyethylene polyamine salt 50 ~ 80% of one or more thiazolinyl and aryl, antioxidant 5 ~ 20%, accelerator 10 ~ 30%;Described chain alkyl is C12~C20Alkyl.
2. the Compositional type SBS modified pitch steady heat storage agent as described in claim 1, it is characterised in that described thiazolinyl is any one in vinyl, acrylic and pi-allyl, and described aryl is any one in phenyl, benzyl and p-methoxyphenyl.
3. the Compositional type SBS modified pitch steady heat storage agent as described in claim 1, it is characterised in that described antioxidant is any one in antioxidant 264, antioxidant 1010 and antioxidant 1076.
4. the Compositional type SBS modified pitch steady heat storage agent as described in claim 1, it is characterised in that described accelerator is any one or the combination of two kinds in sierozem power, montmorillonite powder and flyash.