CN106087302A - A kind of dyeing and finishing processing method of frivolous ventilative polyester-cotton blend anti-plumage fabric - Google Patents
A kind of dyeing and finishing processing method of frivolous ventilative polyester-cotton blend anti-plumage fabric Download PDFInfo
- Publication number
- CN106087302A CN106087302A CN201610551669.9A CN201610551669A CN106087302A CN 106087302 A CN106087302 A CN 106087302A CN 201610551669 A CN201610551669 A CN 201610551669A CN 106087302 A CN106087302 A CN 106087302A
- Authority
- CN
- China
- Prior art keywords
- fabric
- polyester
- dyeing
- cotton blend
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the dyeing and finishing processing method of a kind of frivolous ventilative polyester-cotton blend anti-plumage fabric, be to sequentially pass through grey cloth to move back to boil drift, soft sizing, press polish and sanding operation.This states frivolous ventilative polyester-cotton blend anti-plumage fabric is to be formed by warp thread and weft yarns, warp thread be 50D～75D ultra-fine denier polyester filament yarn, weft yarn be 40S～60S polyester cotton blended yarns.The advantage that the fabric that dyeing and finishing processing method of the present invention produces has soft plumage function admirable fine and smooth, anti-.
Description
Technical field
The invention belongs to shell-fabric dyeing and finishing processing technique field, be specifically related to the dyeing and finishing of a kind of frivolous ventilative polyester-cotton blend anti-plumage fabric
Processing method.
Background technology
The continuous pursuit lived high-quality along with socioeconomic development and people, eiderdown quilt is more and more
Selected by consumer, become a kind of indispensable resisting cold product.Due to the self-characteristic of eider down, eiderdown quilt inevitably results from
The scene of " race floss ", not only impact sleep is experienced, and the most also can affect the health of consumer.
Anti-plumage fabric the most on the market interweaves with cotton and polyester-cotton blend or the product of blending is in the majority, and it has respective short
Plate.Wherein cotton class anti-plumage fabric comfortable ventilating, but it is faced with roving count, and fabric is the most thick and heavy, with the feature of eiderdown quilt is
Unmatch；And high yarn count fabric is big with the presence of fabric sound, the problem of anti-chiseling down difference.In addition cotton class anti-plumage fabric is inhaled
Moist by force, not only make fabric thick and heavy, be also easy to breed bacteria acarid, have a strong impact on the health of consumer.And in the market
Polyester-cotton blend anti-plumage fabric presents inferior quality, the phenomenon that class sense is low more so that the likability of eiderdown quilt is reduced, wherein by consumer
Poor quality is mainly manifested in that feel is poor, sound big, to run floss phenomenon serious.
The patent of patent CN 105177810A discloses the production method of a kind of polyester-cotton blend sanding anti-plumage fabric, and fabric uses
Be warp-wise be polyester filament broadwise be the method that polyester cotton blended yarn interweaves, the advantage of this fabric is that fabric is frivolous, good permeability,
Overcome cotton fabric simultaneously and easily grow the shortcoming of acarid antibacterial, but the dyeing and finishing processing mode of this fabric is that long vehicle boils drift, with
Time take is the technique of press polish after first sanding, the sound causing fabric is bigger than normal, and fabric is easily generated aurora phenomenon；In addition this fabric
Have employed again singeing, fabric gap can be caused to become big, anti-floss performance reduces.
Summary of the invention
Solve the technical problem that: it is an object of the invention to overcome the deficiencies in the prior art to provide a kind of frivolous ventilative polyester-cotton blend
The dyeing and finishing processing method of anti-plumage fabric, the advantage that the method processing fabric has soft plumage function admirable fine and smooth, anti-.
Technical scheme: the dyeing and finishing processing method of a kind of frivolous ventilative polyester-cotton blend anti-plumage fabric, grey cloth is sequentially passed through move back boil drift,
Soft sizing, press polish and sanding operation, to obtain final product.
Further, described frivolous ventilative polyester-cotton blend anti-plumage fabric is to be formed by warp thread and weft yarns, warp thread be 50D～
75D ultra-fine denier polyester filament yarn, weft yarn are 40S～60S polyester cotton blended yarns.
Further, the one side press polish of described frivolous ventilative polyester-cotton blend anti-plumage fabric, another side sanding,
Further, described in move back and boil drift for one-bath DSB method, and take pine formula processing.
Further, described in move back that to boil the consumption of Caustic soda in drift operation be 10～20g/L, the consumption of refining agent is 3～5g/L,
The consumption of hydrogen peroxide is 3～5g/L, and the process time is 40～60min, and treatment temperature is 110～130 DEG C.
Further, in described soft shaping process, setting temperature is 160～180 DEG C, and speed is 40～50m/min.
Further, can also add Radix Saposhnikoviae finishing agent in described soft shaping process, the consumption of Radix Saposhnikoviae finishing agent is 40
～60g/L.
Further, can also add raising agent in described soft shaping process, the consumption of raising agent is 30～50g/L.
Further, described sanding operation employing rubber roller is combined with carbon element roller and carries out sanding.
Beneficial effect: the dyeing and finishing processing method that the present invention uses takes pine formula pre-treatment, relative to traditional long vehicle and volume
Cylinder technique, the fabric after the method processes is the softest comfortable, improves the shortcoming that plain fabric feel is the best, simultaneously at pine formula
Comprehending and make fabric more fluffy, yarn is more tight, and the anti-chiseling down of fabric is more preferable.Additionally, after the present invention also uses first press polish
The technique of sanding, special roughing process makes the more frivolous softness of fabric, sound little, the most also improves the class of fabric
Sense, for press polish after first sanding, the feel of wool of fabric is more preferable, and feel is finer and smoother.
Detailed description of the invention
Below by detailed description of the invention, the present invention is described in further detail.But those skilled in the art will manage
Solving, the following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.Unreceipted concrete skill in embodiment
Art or condition person, according to the technology described by the document in this area or condition (such as with reference to Zhao Tao write " dyeing and finishing technology with
Principle ", China Textiles Press, 2009；" fabric construction and design " written by Shen Lanping, China Textiles Press, 2005) or
Carry out according to product description.Agents useful for same or instrument unreceipted production firm person, be can by city available from routine
Product.
The dyeing and finishing processing method of flexible, breathable provided by the present invention anti-plumage fabric, be grey cloth is sequentially passed through move back boil drift,
Soft sizing, press polish and sanding operation, to obtain final product.Described frivolous ventilative polyester-cotton blend anti-plumage fabric is to be formed by warp thread and weft yarns,
Warp thread be 50D～75D ultra-fine denier polyester filament yarn, weft yarn be 40S～60S polyester cotton blended yarns.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend provided by the present invention anti-plumage fabric, wherein pretreatment procedure is used
Method be pine formula processing, specifically use overflow machine above-mentioned fabric is carried out pre-treatment.In the method, grey cloth is without burning
Hair operation, directly inserts grey cloth in overflow machine and carries out boiling drift.In fabric component involved in the present invention, polyester fiber content is relatively
Many, and fabric tissue use plain weave, fabric through weft yarn relative close, feel is harder, use pine formula single bath process before locate
The mode of reason can fully discharge the internal stress of fabric, makes yarn the most fluffy, also can promote while improving the feel of fabric
The anti-chiseling down performance of fabric.Additionally, the pretreatment mode of one-bath DSB method also has Simplified flowsheet, save the energy, ecological ring
The advantage protected.
In the shaping process of the present invention, in addition to obtaining the softening agent of excellent handle, also to add appropriate anti-drilling
Floss finishing agent, it is simple to form thin film at web surface, promotes the anti-chiseling down of fabric；The most also to add a certain amount of
Hair agent so that the sanding in rear road is more smooth, and the feel of wool is more preferable.
Using first calendaring technology, the fabric after press polish is smooth, and the velvet after sanding is finer and smoother, and damages the strength of fabric
Hinder less.And press polish after first sanding, although the feel of wool of fabric more preferably, but after press polish, its sanding effect can be substantially reduced, simultaneously
The local strength loss that also can cause because of fabric out-of-flatness is excessive.
In the press polish operation of the present invention, controlling calendering temperature and be not higher than 60 DEG C, prevent temperature too high, fabric is by " pressure
Extremely ", the feel causing fabric is poor, and the sound is big.Use reverse side press polish, i.e. reverse side to connect with the metallic roll of calender during press polish simultaneously
Touch, the nylon roller basis of front and calender, it is to avoid fabric front yarn be crushed and affect after road sanding operation.
In the sanding operation of the present invention, use front sanding operation, and be the mode that combines with carbon element rod of rubber roller,
Wherein 6 groups of rubber roller, 4 groups of carbon element rod, the number combinations of speed, pressure and two kinds of rollers during sanding according to the feel of fabric and
Feature adjusts, to obtain optimal feel.Additionally, for the anti-chiseling down ensureing fabric, it is ventilative that control sanding is expected below
Within 20mm/s.
Embodiment 1
Described fabric warp thread uses 50D-72F semi-dull polyester filament, and weft yarn uses 60S polyester cotton blended yarn, containing of polyester-cotton blend
Amount is 65:35.Fabric specification is 98 '/washs DTY 50D-72F half light and gently nets * combing RING SPINNING (polyester cotton 65/35) 60S/182*
112 plain weaves
Grey cloth is sequentially passed through concise, soft sizing, press polish and sanding operation.First grey cloth is carried out concise in overflow machine
Processing, its process technique is Caustic soda 15g/L, refining agent 5g/L, hydrogen peroxide 3g/L, and room temperature enters cloth, is warming up to 110 with 2 DEG C/min
DEG C, isothermal holding time 50min.By 70～80 DEG C of hot water wash 1h after concise end, after carry out expanding, dehydration, dry, cropping is beaten
Volume.Then semi-products after drying do upper soft heat treatment, and setting temperature is 160～180 DEG C, speed 40～50m/min, cropping
Clot.After will sizing after semi-products carry out press polish process, calendering temperature controls, in the range of 50～60 DEG C, suitably to adjust pressure
Power and speed, control the ventilative less than 15mm/s of cropping fabric.Last is sanding together, in sanding operation, uses 4 groups of sand
Roller and the process combination of 4 groups of carbon element rollers, adjust speed and pressure, controls fabric and breathes freely at 20mm/s, clot cropping.
Embodiment 2
Described fabric warp thread uses 75D-72F semi-dull polyester filament, and weft yarn uses 45S polyester cotton blended yarn, containing of polyester-cotton blend
Amount is 65:35.Fabric specification is 102/ to wash DTY half light and gently net 75D-72F* RING SPINNING 45S (polyester cotton 65/35)/152*88 plain weave
Grey cloth is sequentially passed through concise, soft sizing, press polish and sanding operation.First grey cloth is carried out concise in overflow machine
Processing, its process technique is Caustic soda 20g/L, refining agent 5g/L, hydrogen peroxide 4g/L, and room temperature enters cloth, is warming up to 120 with 2 DEG C/min
DEG C, isothermal holding time 60min.By 70～80 DEG C of hot water wash 1h after concise end, after carry out expanding, dehydration, dry, cropping is beaten
Volume.Then semi-products after drying do upper soft heat treatment, and setting temperature is 160～180 DEG C, speed 40～50m/min, cropping
Clot.After will sizing after semi-products carry out press polish process, calendering temperature controls, in the range of 50～60 DEG C, suitably to adjust pressure
Power and speed, control the ventilative less than 15mm/s of cropping fabric.Last is sanding together, in sanding operation, uses 6 groups of sand
Roller and the process combination of 4 groups of carbon element rollers, adjust speed and pressure, controls fabric and breathes freely at 20mm/s, clot cropping.
Reference examples 1
Difference with embodiment 1 is that in processing method, sanding operation is before press polish operation.
Reference examples 2
Difference with embodiment 1 is the pretreatment mode not taking one-bath DSB method and uses pine formula manufacturing procedure,
Use the mode of first singe desizing the most successively, kiering, bleaching.
Reference examples 3
Difference with embodiment 1 is that press polish and sanding are at the same face.
Table 1 fabric anti-chiseling down effect
| Project | Embodiment 1 | Embodiment 2 | Reference examples 1 | Reference examples 2 | Reference examples 3 |
| Run Rhizoma Imperatae number | 4 | 5 | 5 | 6 | 12 |
| Ventilative value | 25.51 | 28.17 | 15.12 | 17.85 | 40.89 |
By the data of table 1 it can be seen that pass through the fabric of pine formula pre-treatment, sanding after post processing is to use first press polish
Technique, the finished product anti-chiseling down effect finally given is very nearly the same with the fabric of other techniques, but the air permeable effect of fabric is more preferably,
Fabric is easier to retain more still air, and warming sense is higher.Reference examples 3 press polish and sanding are easily generated at the same face, fabric
Big space causes anti-plumage effect defective.
Table 2 fabric feel (AATCC Test Method 202-2012)
| Project | Resilience Socre | Softness Score | Smoothness Score |
| Embodiment 1 | 39.86 | 81.91 | 85.77 |
| Embodiment 2 | 37.92 | 82.65 | 86.16 |
| Reference examples 1 | 41.22 | 79.28 | 88.64 |
| Reference examples 2 | 41.12 | 76.65 | 89.23 |
| Reference examples 3 | 40.23 | 80.14 | 88.25 |
From table 2, every feel index of fabric is it can be seen that the pretreatment mode of single bath process obtains the pliability of fabric
More preferably, and using the technique of sanding after first press polish, the smooth degree of fabric can diminish.Summary data show: the present invention uses
Technique obtains fabric and has more preferable feel.
Claims (9)
1. the dyeing and finishing processing method of a frivolous ventilative polyester-cotton blend anti-plumage fabric, it is characterised in that: grey cloth is sequentially passed through move back boil drift,
Soft sizing, press polish and sanding operation, to obtain final product.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described gently
Thin ventilative polyester-cotton blend anti-plumage fabric is to be formed by warp thread and weft yarns, and warp thread is that 50D～75D ultra-fine denier polyester filament yarn, weft yarn are
40S～60S polyester cotton blended yarns.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described gently
The one side press polish of thin ventilative polyester-cotton blend anti-plumage fabric, another side sanding.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that move back described in:
Boil drift operation and use one-bath DSB method, and take pine formula processing.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that move back described in:
Boiling the consumption of Caustic soda in drift operation is 10～20g/L, and the consumption of refining agent is 3～5g/L, and the consumption of hydrogen peroxide is 3～5g/L,
The process time is 40～60min, and treatment temperature is 110～130 DEG C.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described soft
In soft shaping process, setting temperature is 160～180 DEG C, and speed is 40～50m/min.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described soft
Can also add Radix Saposhnikoviae finishing agent in soft shaping process, the consumption of Radix Saposhnikoviae finishing agent is 40～60g/L.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described soft
Can also add raising agent in soft shaping process, the consumption of raising agent is 30～50g/L.
The dyeing and finishing processing method of frivolous ventilative polyester-cotton blend the most according to claim 1 anti-plumage fabric, it is characterised in that: described mill
Hair operation employing rubber roller is combined with carbon element roller and carries out sanding.