CN106085191A - A kind of construction method of wood product surface paint - Google Patents
A kind of construction method of wood product surface paint Download PDFInfo
- Publication number
- CN106085191A CN106085191A CN201610395318.3A CN201610395318A CN106085191A CN 106085191 A CN106085191 A CN 106085191A CN 201610395318 A CN201610395318 A CN 201610395318A CN 106085191 A CN106085191 A CN 106085191A
- Authority
- CN
- China
- Prior art keywords
- paint
- wood
- dried
- parts
- middle level
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides the construction method of a kind of wood product surface paint, comprise the steps: that (1) sanding surface is processed, (2) prime treatment is dried with UV, (3) colouring is processed and (6) finish paint process with drying, (4) sanding, dedusting, (5) middle level.In wherein said step (2), UV wood crude oil paint is by weight, including following components: six official's polyurethane acrylic resins 10 15 parts, two official's polyurethane acrylic resin 20 25 parts, the modified UV monomer 30 35 parts of double official, sensitising agent 35 parts, levelling agent 0.1 0.2 parts, defoamer 0.3 0.5 parts, wetting agent 0.3 0.5 parts, nano silicon dispersion liquid 15 20 parts, 10 15 parts of gas phase nano silica dumb light powder.By embodiment of the present invention, also obtain one at wood surface and have compared with thin protective layer, waterproof antiwear excellent performance, save again texture and the texture of timber essence simultaneously.
Description
Technical field
The present invention relates to painted surface and process technology field, be specifically related to the construction method of a kind of wood product surface paint,
It is mainly used in the construction processing of the surface paint of timber floor, can be also used for the construction of the wood product surface such as furniture, timber paint
Process.
Background technology
Raising with national consumption level with to environmental requirement, people select woodwork when had more select and
Higher requirement, as required woodwork closer to the essential color of timber and texture texture etc..
The weatherability of traditional wood products, solid wooden floor board or solid wooden compound floor is poor, changes relatively in humidity and temperature
It during the medium-term and long-term use of big environment, is easily deformed and ftractures, poor dimensional stability.Especially timber floor, it is in humidity relatively
When high environment uses, easily produce variable color, rotten, poor stability.Thus, Traditional Wood floor all can cover one layer enough
The painting layer of thickness, to reach to prevent timber floor to be easily generated variable color, deformation, rotten when using in the higher environment of humidity ratio
Generation, improve timber floor dimensional stability.
Although current process technique ensure that the waterproof corrosion resisting property of timber floor, but, also cover at wood floor surface
One layer of thicker diaphragm, it is impossible to the textural aesthetic of timber essence and sense of touch.It and consumer is when choosing timber floor, is more desirable to
Wood surface is selected to have compared with thin protective layer, its texture that can embody timber essence and sense of touch.For this problem, have one on the market
Product after a little improvement, as the dry vegetable oils such as employing wood wax oil form protective layer, but is plant component due to it, firmly
The performance requirement of traditional paint is not reached on degree, wear-resisting and high temperature resistant, resistance to acids and bases.
Therefore, increasing wooden product enterprises is highly desirable can have a kind of product can solve the problems referred to above.
Content of the invention
For the problems referred to above, the invention provides the construction method of a kind of wood product surface paint, it is thus achieved that one has
Compared with thin protective layer, waterproof antiwear excellent performance, save again the texture of timber essence and the wooden floor of texture simultaneously.
A kind of UV wood crude oil paint, including the component of following weight portion:
The present invention with the addition of nano silicon dispersion liquid, and the anti-ultraviolet aging experimental performance of UV micro-coating paint is permissible
Being brought up to more than 600h by original 250h, scrub resistance improves more than 10 times, and the drying time of coating is greatly lowered, anti-soil
Performance is greatly improved, and has excellent self-cleaning property and adhesive force.If without nano silicon dispersion liquid, coating
Resistant and ultraviolet-resistant performance will reduce.
The present invention with the addition of gas phase nano silica dumb light powder, can be substantially reduced the glossiness of coating, make coat side table
Face glossiness is below 5 degree.If using normal dull powder, do not reach effect below 5 degree for the surface gloss.
Preferably, described sensitising agent is cracking type sensitising agent.
Preferably, described levelling agent is fluorine richness carbonic ether acrylate.
Preferably, described defoamer is organosilicon defoamer.
Preferably, described wetting agent is polyether-modified poly-silica siloxane copolymers class wetting agent.
The preparation method of a kind of UV wood crude oil paint, comprises the following steps:
1) in dispersion cylinder, put into six official's polyurethane acrylic resins, two official polyurethane acroleic acid trees by weight successively
Fat, the modified UV monomer of double official, sensitising agent, levelling agent, defoamer, wetting agent, stirring makes to mix, and obtains the group of clear
Divide A；
2) stir component A, be added into nano silicon dispersion liquid, mix, obtain component B；
3) stir component B, be added into gas phase nano silica dumb light powder, mix, obtain described UV wood crude oil
Paint.
Preferably, in step 1) in, mixing speed is 2000RPM, and mixing time is 20 minutes.
Preferably, in step 2) in, mixing speed is 400RPM, and mixing time is 10 minutes.
Preferably, in step 3) in, mixing speed is 800RPM, and mixing time is 20 minutes.
The UV wood crude oil paint of the present invention may penetrate in lumber fibre, after irradiating through ultraviolet light, sends out with lumber fibre rapidly
Raw cross-linking reaction, reinforces lumber fibre, and forms one layer of very thin protective layer at wood surface, have wear-resisting, waterproof effect,
Remain again the texture texture of timber simultaneously；Add nano silicon dispersion liquid, improve the anti-ultraviolet aging of this coating
Performance and pollution resistance, be greatly lowered drying time；Add gas phase nano silica dumb light powder, reduce the gloss of coating
Degree；This paint is without formaldehyde, benzene and heavy metal etc., and safety and environmental protection, VOC content are low.
In order to realize the technical purpose of the present invention, the present invention adopts the following technical scheme that.
The construction method of a kind of wood product surface paint, comprises the steps:
(1) sanding surface process, it is ensured that element plate smooth surface impulse-free robustness；
(2) prime treatment and UV are dried: be dried with UV drying machine after the former paint of plain plate UV wood that will handle well；
(3) paint and be dried: former for dried element plate Waterborne wood paint is coated with colouring, making the former paint of Waterborne wood enter fiber
In pore, then element plate is placed in the long infrared levelling passage of 10-20 rice and is dried；
(4) sanding, dedusting: after dried element plate sanding in step (3) to Waterborne wood former paint smooth surface impulse-free robustness
Carry out dust removal process；
(5) middle level processes one: repeat step (2), and to smooth surface impulse-free robustness, gained element plate sanding is carried out dedusting
Process；
(6) middle level processes two: after the former paint of gained element plate UV wood in step (5), be dried with UV drying machine, sand
Light carries out dust removal process to smooth surface impulse-free robustness；
(7) finish paint process: repeat step (2), obtain finished product.
Preferably, described UV wood crude oil paint is by weight, including following components: six official's polyurethane acrylic resin: 10-
15 parts, two official's polyurethane acrylic resins: 20-25 part, the modified UV monomer of double official: 30-35 part, sensitising agent: 3-5 part, levelling agent:
0.1-0.2 part, defoamer: 0.3-0.5 part, wetting agent: 0.3-0.5 part, nano silicon dispersion liquid: 15-20 part, gas phase are received
Rice silica dumb light powder: 10-15 part.
Preferably, in described step (2), UV wood crude oil paint coating weight is 5-8g/m2, UV drying condition is 100-120mJ/
cm2。
Preferably, in described step (3), Waterborne wood former paint coating weight is 10-15g/m2, drying condition is dry at being 55-60 DEG C
Dry 1-2 minute.
Preferably, in described step (6), UV wood crude oil paint coating weight is 3-5g/m2, UV drying condition is 100-120mJ/
cm2。
The invention has the beneficial effects as follows: the invention provides the construction method of a kind of wood product surface paint, and by this
The UV wood crude oil paint providing in invention is used in combination, and further embodies advantages of the present invention, compared with prior art, has
Advantages below:
1st, guarantee this texture of timber that existing woodwork or timber floor enterprise frustrate and sense of touch and timber paint film are solved
The problem that can not have both of waterproof antiwear performance；
2nd, timber floor good stability, the water resistance of the present invention are excellent, and anti-wear performance is good；
3rd, surface paint used by the present invention is without the harmful substances such as formaldehyde, benzene, heavy metal, Environmental Safety；
4th, production technology is simple, and equipment requirement is low, is suitable for large-scale promotion and uses, can be widely used in timber floor, timber,
The surface paint such as furniture, woodwork workpiece process technique.
Detailed description of the invention
In order to be better understood from the present invention, below in conjunction with specific embodiment, invention is described in detail, as without saying especially
Bright, in following example, the component of UV wood crude oil paint is, by weight, including following components: six official polyurethane acroleic acid trees
Fat: 10-15 part, two official's polyurethane acrylic resins: 20-25 part, the modified UV monomer of double official: 30-35 part, sensitising agent: 3-5 part,
Levelling agent: 0.1-0.2 part, defoamer: 0.3-0.5 part, wetting agent: 0.3-0.5 part, nano silicon dispersion liquid: 15-20
Part, gas phase nano silica dumb light powder: 10-15 part.
Six official's polyurethane acrylic resins of the present invention can be selected for the 6145-100 of Changxing company；
Two official's polyurethane acrylic resins of the present invention can be selected for the EB-264 of Qing Te company；
Double official's UV monomers of the present invention can be selected for the EM222 in Changxing；
The sensitising agent of the present invention can use the cracking type sensitising agent 1173 that Hua Tai macromolecular material company produces；
The levelling agent of the present invention can be selected for the BYK-3510 of Bi Ke company；
The defoamer of the present invention can be selected for the BYK-055 of Bi Ke company；
The wetting agent agent of the present invention can be selected for the BYK-306 of Bi Ke company；
The nano silicon dispersion liquid of the present invention can be selected for the VK-S01A of Jing Rui company；
The gas phase nano silica dumb light powder of the present invention can be selected for the R972 of goldschmidt chemical corporation.
Embodiment 1:
A kind of UV wood crude oil paint, including the component of following weight portion:
UV wood crude oil paint preparation method: (1) puts into 15 part of six official's polyurethane acroleic acid by weight in dispersion cylinder successively
Resin, 25 part of two official's polyurethane acrylic resin, the modified UV monomers of 30 parts of double officials, 4 parts of sensitising agents, 0.2 part of levelling agent, 0.3 part
Defoamer, 0.5 part of wetting agent, under mixer rotating speed is 2000RPM, stirs 20 minutes, make to mix, obtain clear
Component A；(2) under mixer rotating speed is 400RPM, stir component A, be added into 15 parts of nano silicon dispersion liquids simultaneously,
Stir 10 minutes, mix, obtain component B；(3) it is transferred under 800PRM at mixer rotating speed, stir component B, add simultaneously
Enter 10 parts of gas phase nano silica dumb light powder, stir 20 minutes, mix, i.e. obtain the UV wood crude oil paint of the present invention.
The construction method of a kind of wood product surface paint, comprises the steps:
(1) sanding surface process, it is ensured that element plate smooth surface impulse-free robustness；
(2) prime treatment and UV are dried: the former paint of plain plate UV wood that will handle well, it is ensured that coating weight is 8g/m2,
Then being dried with UV drying machine, drying energy is 120mJ/cm2；
(3) paint and be dried: former for dried element plate Waterborne wood paint being coated with colouring, it is ensured that coating weight is 15g/m2,
Making the former paint of Waterborne wood enter in fiber pore, then element plate being placed in the long levelling passage of 10-20 rice and be dried, drying condition is
It is dried 1-2 minute at 55-60 DEG C；
(4) sanding, dedusting: after dried element plate sanding in step (3) to Waterborne wood former paint smooth surface impulse-free robustness
Carry out dust removal process；
(5) middle level processes one: repeat step (2), and to smooth surface impulse-free robustness, gained element plate sanding is carried out dedusting
Process；
(6) middle level processes two: by the former paint of gained element plate UV wood in step (5), it is ensured that coating weight is 5g/m2,
Then being dried with UV drying machine, drying energy is 120mJ/cm2；Sanding again carries out dust removal process to smooth surface impulse-free robustness；
(7) finish paint process: repeat step (2), obtain finished product.
Embodiment 2:
A kind of UV wood crude oil paint, including the component of following weight portion:
Raw material uses above weight, uses embodiment 1 method to prepare UV wood crude oil paint.
The construction method of a kind of wood product surface paint, comprises the steps:
(1) sanding surface process, it is ensured that element plate smooth surface impulse-free robustness；
(2) prime treatment and UV are dried: the former paint of plain plate UV wood that will handle well, it is ensured that coating weight is 6g/m2,
Then being dried with UV drying machine, drying energy is 110mJ/cm2；
(3) paint and be dried: former for dried element plate Waterborne wood paint being coated with colouring, it is ensured that coating weight is 12g/m2,
Make the former paint of Waterborne wood enter in fiber pore, then element plate is placed in the long infrared levelling passage of 10-20 rice and is dried, drying condition
It is dried 1-2 minute at 55-60 DEG C；
(4) sanding, dedusting: after dried element plate sanding in step (3) to Waterborne wood former paint smooth surface impulse-free robustness
Carry out dust removal process；
(5) middle level processes one: repeat step (2), and to smooth surface impulse-free robustness, gained element plate sanding is carried out dedusting
Process；
(6) middle level processes two: by the former paint of gained element plate UV wood in step (5), it is ensured that coating weight is 4g/m2,
Then being dried with UV drying machine, drying energy is 110mJ/cm2；Sanding again carries out dust removal process to smooth surface impulse-free robustness；
(7) finish paint process: repeat step (2), obtain finished product.
Embodiment 3:
A kind of UV wood crude oil paint, including the component of following weight portion:
Raw material uses above weight, uses the method for embodiment 1 to prepare UV wood crude oil paint.
The construction method of a kind of wood product surface paint, comprises the steps:
(1) sanding surface process, it is ensured that element plate smooth surface impulse-free robustness；
(2) prime treatment and UV are dried: the former paint of plain plate UV wood that will handle well, it is ensured that coating weight is 5g/m2,
Then being dried with UV drying machine, drying energy is 100mJ/cm2；
(3) paint and be dried: former for dried element plate Waterborne wood paint being coated with colouring, it is ensured that coating weight is 10g/m2,
Make the former paint of Waterborne wood enter in fiber pore, then element plate is placed in the long infrared levelling passage of 10-20 rice and is dried, drying condition
It is dried 1-2 minute at 55-60 DEG C；
(4) sanding, dedusting: after dried element plate sanding in step (3) to Waterborne wood former paint smooth surface impulse-free robustness
Carry out dust removal process；
(5) middle level processes one: repeat step (2), and to smooth surface impulse-free robustness, gained element plate sanding is carried out dedusting
Process；
(6) middle level processes two: by the former paint of gained element plate UV wood in step (5), it is ensured that coating weight is 3g/m2,
Then being dried with UV drying machine, drying energy is 100mJ/cm2；Sanding again carries out dust removal process to smooth surface impulse-free robustness；
(7) finish paint process: repeat step (2), obtain finished product.
Embodiment 4
A kind of UV wood crude oil paint, including the component of following weight portion:
Raw material uses above weight, uses the method for embodiment 1 to prepare UV wood crude oil paint, uses embodiment 1
Method be coated in the UV of preparation wood crude oil paint on wood product surface.
Comparative example 1
A kind of UV wood crude oil paint, including the component of following weight portion:
This UV wood crude oil paint preparation method: (1) puts into 25 part of six official's polyurethane propylene by weight in dispersion cylinder successively
Acid resin, 32 part of two official's polyurethane acrylic resin, the modified UV monomers of 37 parts of double officials, 5 parts of sensitising agents, 0.2 part of levelling agent, 0.4
Part defoamer, 0.4 part of wetting agent, under mixer rotating speed is 2000RPM, stirs 20 minutes, make to mix, i.e. obtain this UV
Wood crude oil paint.
The method using embodiment 1 is coated on the UV wood crude oil paint of preparation on wood product surface.
Being measured the paint film property after the former paint application of UV wood prepared by embodiment 1-4 and comparative example 1, gained is tied
Fruit is as shown in table 1.
Table 1 embodiment 1-4 and comparative example 1 performance detection table
From upper table data it can be seen that UV wood crude oil paint prepared by the present invention is coated on wood product surface, gained wooden
Product all meet indices, and use the UV wood not containing nano silicon dispersion liquid and gas phase nano silicon dumb light powder
Crude oil paint is coated on wood product surface, and the woodwork rub resistance of gained and stain resistance are substantially reduced, and do not meet indices
Regulation.By the wood crude oil paint of coating UV on woodwork so that it is penetrate into lumber fibre, after irradiating through ultraviolet light, rapidly with
Lumber fibre crosslinks reaction, reinforces lumber fibre.On the other hand also obtain one at wood surface has relatively thin protection
Layer, waterproof antiwear excellent performance, save again texture and the texture of timber essence simultaneously.
General principle, principal character and the advantage of the present invention have more than been shown and described.The technical staff of the industry should
Understanding, above-described embodiment does not limit the present invention in any form, and the mode of all employing equivalents or equivalent transformation is obtained
Technical scheme, all falls within protection scope of the present invention.
Claims (6)
1. the construction method of a wood product surface paint, it is characterised in that comprise the steps:
(1) surface treatment, it is ensured that element plate smooth surface impulse-free robustness；
(2) prime treatment and UV are dried: be dried with UV drying machine after the former paint of plain plate UV wood that will handle well；
(3) paint and be dried: being dried after former for dried element plate Waterborne wood paint is coated with colouring；
(4) sanding, dedusting: dried element plate sanding in step (3) is carried out to Waterborne wood former paint smooth surface impulse-free robustness
Dust removal process；
(5) middle level process: be coated processing with UV wood crude oil paint；
(6) finish paint process: repeat step (2), obtain finished product.
2. the construction method of a kind of wood product surface according to claim 1 paint, it is characterised in that: the process of described middle level
Including middle level process one and middle level process two, wherein, middle level processes one and is: repeat step (2), and by gained element plate sanding to table
Carry out dust removal process after the Glabrous thorn of face；Middle level processes two: middle level processes the plain plate UV wood crude oil paint of gained after
It after being again coated with, is dried with UV drying machine, after sanding to smooth surface impulse-free robustness, carries out dust removal process.
3. the construction method of a kind of wood product surface according to claim 2 paint, it is characterised in that: the process of described middle level
In two, UV wood crude oil paint coating weight is 3-5g/m2, UV drying condition is 100-120mJ/cm2。
4. the construction method of a kind of wood product surface paint according to any one of claim 1-3, it is characterised in that: described
UV wood crude oil paint by weight, including following components: six official's polyurethane acrylic resins: 10-15 part, two official's polyurethane propylene
Acid resin: 20-25 part, the modified UV monomer of double official: 30-35 part, sensitising agent: 3-5 part, levelling agent: 0.1-0.2 part, defoamer:
0.3-0.5 part, wetting agent: 0.3-0.5 part, nano silicon dispersion liquid: 15-20 part, gas phase nano silica dumb light powder:
10-15 part.
5. the construction method of a kind of wood product surface according to claim 4 paint, it is characterised in that: described step (2)
Middle UV wood crude oil paint coating weight is 5-8g/m2, UV drying condition is 100-120mJ/cm2。
6. the construction method of a kind of wood product surface according to claim 4 paint, it is characterised in that: described step (3)
Middle Waterborne wood former paint coating weight is 10-15g/m2, drying condition is dried 1-2 minute at being 55-60 DEG C.