CN109666396A - Novel water-based low-gloss ultraviolet curing coating and preparation and use methods thereof - Google Patents
Novel water-based low-gloss ultraviolet curing coating and preparation and use methods thereof Download PDFInfo
- Publication number
- CN109666396A CN109666396A CN201910036463.6A CN201910036463A CN109666396A CN 109666396 A CN109666396 A CN 109666396A CN 201910036463 A CN201910036463 A CN 201910036463A CN 109666396 A CN109666396 A CN 109666396A
- Authority
- CN
- China
- Prior art keywords
- parts
- low gloss
- curing paint
- novel aqueous
- gloss ultraviolet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel water-based low-gloss ultraviolet curing coating and a preparation and use method thereof, and the key points of the technical scheme are as follows: the composition consists of the following substances in parts by weight: 3-5 parts of water-based polyurethane acrylate A, 15-20 parts of water-based polyurethane acrylate B, 10-15 parts of water-based polyurethane acrylate C, 30-41 parts of mixed water-based reactive diluent, 3-10 parts of matting powder A, 5-10 parts of matting powder B, 2-3 parts of wax powder, 2-3 parts of wax slurry, 0.3-1 part of dispersing agent, 0.3-0.5 part of defoaming agent, 0.3-0.5 part of flatting agent, 2-4 parts of assistant initiator, 2-4 parts of photoinitiator A and 2-4 parts of photoinitiator B. The invention provides a novel water-based low-gloss ultraviolet curing coating, a preparation method and a use method thereof, after a product is dried, the luminosity can reach a matte effect of 5 degrees, the surface luminosity is uniform, the hand feeling is fine and smooth, the ultra-clear effect is realized, the ultra-coin scratch resistance is high, and the coating is suitable for ultra-low matte products.
Description
[technical field]
The invention belongs to high-molecular coating technical fields, and in particular to a kind of novel aqueous low gloss ultraviolet-curing paint
And its preparation and application.
[background technique]
The ultraviolet-curing paint of existing market, is substantially oiliness ultraviolet-curing paint, and ultraviolet-curing paint exists
Under action of ultraviolet light, the photoactive substance in system can generate active particle or group by photochemical reaction, thus primosome
Reactive resin in system carries out cross-linked polymeric, and then the paint film hardened, and most of product odour is big on existing market, paint film
Shrinkage is big, paint film is crisp and the features such as being not easy delustring, wherein ultralow dumb light product viscosity is excessively high, easy after-thickening is recycled, does not flow
It puts down, be not easy that dry, lingering taste is big, be not able to satisfy the market demand still, rare UV-curable waterborne coatings, are also deposited in the market
Admittedly containing the problems such as low, filling is poor, paint film easily returns white, not resistant to water, easy to crack, easy depainting, not anti-scratch.
[summary of the invention]
The purpose of the invention is to overcome the defect of existing coating, a kind of novel aqueous low gloss ultraviolet light solidification is provided
Coating.
Of the invention also provides a kind of preparation method of novel aqueous low gloss ultraviolet-curing paint.
Of the invention also provides a kind of application method of novel aqueous low gloss ultraviolet-curing paint.
A kind of novel aqueous low gloss ultraviolet-curing paint, by the material composition of following components by weight percent:
Preferably, the aqueous polyurethane acrylate A is 6 function low viscosity aliphatic urethane acrylates, Gu containing being
40%, aqueous polyurethane acrylate B are 3 functional aliphatic's urethane acrylates, Gu containing being 80%, watersoluble polyurethane acrylic acid
Ester C is 2 functional aliphatic's urethane acrylates, Gu containing the clear viscous shape liquid for 100%.Various functional polyurethane propylene
The flexibility that can improve system is combined in acid constituents, promotes paint film mobility.
Preferably, the hybrid reaction type diluent is ethoxyquin trimethylolpropane triacrylate and polyethylene glycol two
Acrylate, after being tested respectively in 7:3,6:4,5:5 ratio, the ratio of preferably 6:4 is prepared optimal.Ethoxyquin trihydroxy methyl
Three acrylate of propane and polyethylene glycol diacrylate rouge, belong to high-strength structure component, are bicomponent epoxy resin, no
Containing solvent, there is preferable shear strength and hardness.
Preferably, the flatting silica A is preferential to select that oil absorption is low, permeability is good and surface through processed fineness is 3-
6 microns of aerosil micro mist.
Preferably, more micropores and the distribution of particles of variation form the premise of its outstanding matte effect, are ideal
Spherical particle, do not influence the rheological property of coating completely, except with outstanding matte effect, enhance paint film elastic force (toughness)
Other than being influenced with hardness, low rheology, also has and improve scratch resistance, enhancing adhesive force, improve the soft degree in surface, weatherability
With gloss holding capacity.
Preferably, the photoinitiator A is 2- hydroxy-2-methyl -1- phenylacetone or 2- hydroxy-2-methyl -1- phenyl -
1- acetone, the photoinitiator b are 1- hydroxyl ring ethylphenyl ketone or 2,4, the oxidation of 6- trimethylbenzoy-dipheny
Phosphine.Particularly preferred photoinitiator is 2,4,6- trimethylbenzoy-dipheny phosphorous oxides (TPO), in low luster coating, because of powder
Expect more, paint film is thicker, need efficient ultraviolet initiator to reach solidification thoroughly, thus particularly preferably TPO do it is light-initiated
Agent.
Preferably, the dispersing agent is the acidic-group copolymer for containing 100% admittedly, what the defoaming agent contained admittedly for 100%
Polyetherpolysilicone transparency liquid, the levelling agent are the polyether-modified dimethyl silicone polymer for containing 100% admittedly.
Preferably, the aided initiating is tertiary amine acrylate, alkyl hydroxy amine, one in dimethylaminobenzoic acid ester
Kind.Can photoinitiator be preferably tertiary amine acrylate, oligomer and dispersing agent can be turned by liquid rapidly in promotion system
Solid-state is turned to, optical active group interaction can be improved the absorption to luminous energy, increase activity, while to a certain extent
Overcome the xanthochromia of product.
A kind of preparation method of novel aqueous low gloss ultraviolet-curing paint, comprising the following steps:
1) turning one's coat property of mixing, is answered into type diluent, dispersing agent, defoaming agent, levelling agent, flatting silica A, flatting silica B, light-initiated
Agent A, photoinitiator b, aided initiating sequentially add mixing under 300~450 revs/min of revolving speed stirrings, then with revolving speed 700~
900 revs/min obtain just stage mixture in stirring 15~25 minutes;
2) aqueous polyurethane acrylate A, B, C, are sequentially added to above-mentioned elementary section of mixing species, then with revolving speed 700~
After 900 revs/min are stirred 15~25 minutes, after filtering removal impurity, novel aqueous low gloss ultraviolet-curing paint is obtained.
A kind of application method of novel aqueous low gloss ultraviolet-curing paint, comprising the following steps:
After each component substep is mixed evenly, after thermal barrel is added after filtering, bucket inside courtyard temperature is added to 55~
After 60 DEG C, make coating material temperature uniformly and facilitate defoaming complete, can roller coating operation, the UV-curable waterborne bottom of timber floor
Paint is applied and is installed, and fills and leads up pore, straight and even smooth with the polishing of No. 320 sand paper, can roller coating in the plate face polished, by coating 9~
10g/ ㎡ coating weight thickness, it is solid into uv cure machine 3-5 seconds through 80 degree of excess temperature Infrared Channel levelling 15~20 seconds
Change dry complete.
The present invention compared with the existing technology, has the advantage that
A kind of novel aqueous low gloss ultraviolet-curing paint of the invention, selects each degree of functionality in specific ratio range
Activated monomer combination do main body, improve the flexibility of system, promote paint film mobility, simultaneous selection is easy to the modified gas of delustring
Aerosil micro mist etc. is used as filler to obtain preferable matte effect, while cooperating diluent, dispersing agent and levelling agent etc.
Auxiliary agent improves the high oil-absorbing of conventional gas-phase SiO2 flatting silica, and coating is avoided to generate g., jelly-like phenomenon, in roller coating in use, stream
Phenomena such as the phenomenon that levelling is good, and feel is fine and smooth, silk is sliding, without cissing, uniform drying, white without returning in the drying process, cracking, in roller
Apply it is dry after, luminosity is up to the matte effect of 5-20 degree, and luminosity is uniform, and ultralow dumb light product is suitble to use, and surface has super
High oil absorption characteristic of the effect based on conventional gas-phase SiO2 flatting silica of sliding, super clear, the superhard coin scraping of silk, can make coating generate fruit
Freeze shape phenomenon, mobility is made to go wrong;
A kind of preparation method of novel aqueous low gloss ultraviolet-curing paint of the invention, process warm and, process is without dirt
Dye discharge, is suitble to industrialized production;
A kind of application method of novel aqueous low gloss ultraviolet-curing paint of the invention, not only can roller coating, can also add
Deionized water spraying, and will not block machine pipes by after-thickening in use, not have volatility penetrating odor, heating 50~
It will not be pungent during 60 degree, not stimulate eyes good to construction personnel's safeguard protection performance;Especially used on wood-based product surface,
Luminosity is up to 5 degree of matte effect, and surface luminous intensity is uniform, feel is fine and smooth, super clear, super anti-coin scrapes, and is suitble to ultralow mute
Light product uses.
[specific embodiment]
1-4 is to novel aqueous low gloss ultraviolet-curing paint of the invention and its preparation side combined with specific embodiments below
Method is further described.
A kind of preparation method of novel aqueous low gloss ultraviolet-curing paint, comprising the following steps:
1) turning one's coat property of mixing, is answered into type diluent, dispersing agent, defoaming agent, levelling agent, flatting silica A, it is flatting silica B, light-initiated
Agent A, photoinitiator b, aided initiating sequentially add mixing under 300~450 revs/min of revolving speed stirrings, then with revolving speed 700-900
Rev/min stirring 15~25 minutes just the stage mixture;
2) aqueous polyurethane acrylate A, B, C, are sequentially added to above-mentioned elementary section of mixing species, then with revolving speed 700~
After 900 revs/min are stirred 15~25 minutes, after filtering removal impurity, novel aqueous low gloss ultraviolet-curing paint is obtained.
Table 1: embodiment 1-4 each group distribution ratio
By Examples 1 to 4 products obtained therefrom, applied according to the application method of novel aqueous low gloss ultraviolet-curing paint
Dress test, comprising the following steps:
After each component substep is mixed evenly as required, after thermal barrel is added after filtering, bucket inside courtyard temperature is added to
After 55~60 DEG C, makes coating material temperature uniformly and facilitate defoaming completion, carry out roller coating operation, the aquosity ultraviolet light of timber floor is consolidated
It is good to change primer painting, fills and leads up pore, it is straight and even smooth with the polishing of No. 320 sand paper, can roller coating in the plate face polished, by coating
9~10g/ ㎡ coating weight thickness, through 80 degree of excess temperature Infrared Channel levelling 15~20 seconds, into uv cure machine 3-5
Second curing and drying is completed.
It is as shown in the table to carry out physicochemical property testing result for coated solidified product paint film obtained by Examples 1 to 4:
Table 2: coated solidified product paint film test result obtained by Examples 1 to 4
Novel aqueous low gloss ultraviolet-curing paint of the invention, can roller coating, nonwater-spraying is in timber floor, wooden blinds
Window on the woodworks such as furniture, shows the sliding coat of softer silk to woodwork, in roller coating in use, good leveling property, without roller
Trace, without cissing mirror cabinet the phenomenon that, phenomena such as uniform drying in the drying process is white without returning, cracking, after the drying, luminosity is up to 5
The matte effect of degree, and surface luminous intensity is uniform, feel is fine and smooth, super clear, super anti-coin scrapes, and ultralow dumb light product is suitble to make
With.
Claims (10)
1. a kind of novel aqueous low gloss ultraviolet-curing paint, it is characterised in that by the material composition of following components by weight percent:
2. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: described aqueous
Urethane acrylate A is 6 function low viscosity aliphatic urethane acrylates, Gu containing being 40%, aqueous polyurethane acrylate B
For 3 functional aliphatic's urethane acrylates, Gu containing is 80%, aqueous polyurethane acrylate C is 2 functional aliphatic's urethane propylene
Acid esters, Gu containing the clear viscous shape liquid for 100%.
3. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: the mixing
Response type diluent is ethoxyquin trimethylolpropane triacrylate and polyethylene glycol diacrylate rouge, respectively by 7:3,6:4,
After 5:5 ratio is tested, the ratio of preferably 6:4 is prepared optimal.
4. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: described to disappearLight Powder AFor 3-6 microns of aerosil micro mist of fineness.
5. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: described to disappearLight Powder BThe transparent spherical micro mist for being 3~6 microns for fineness.
6. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: the light draws
Hair agent A is 2- hydroxy-2-methyl -1- phenylacetone or 2- hydroxy-2-methyl -1- phenyl -1- acetone, the photoinitiator b are
1- hydroxyl ring ethylphenyl ketone or 2,4,6- trimethylbenzoy-dipheny phosphine oxide.
7. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: the dispersion
Agent is the acidic-group copolymer for containing 100% admittedly, and the defoaming agent is the 100% polyetherpolysilicone transparency liquid contained admittedly, institute
Stating levelling agent is admittedly containing 100%.
8. a kind of novel aqueous low gloss ultraviolet-curing paint according to claim 1, it is characterised in that: described help is drawn
Hair agent is one of tertiary amine acrylate, alkyl hydroxy amine, dimethylaminobenzoic acid ester.
9. a kind of preparation method of novel aqueous low gloss ultraviolet-curing paint, it is characterised in that the following steps are included:
1) turning one's coat property of mixing, is answered into type diluent, dispersing agent, defoaming agent, levelling agent, flatting silica A, flatting silica B, photoinitiator A,
Photoinitiator b, aided initiating sequentially add mixing under 300~450 revs/min of revolving speed stirrings, then with revolving speed 700-900 turns/
Minute stirring obtains just stage mixture for 15~25 minutes;
2) aqueous polyurethane acrylate A, B, C, are sequentially added to above-mentioned elementary section of mixing species, then with revolving speed 700~900
Rev/min stirring 15~25 minutes after, filtering removal impurity after, obtain novel aqueous low gloss ultraviolet-curing paint.
10. a kind of application method of novel aqueous low gloss ultraviolet-curing paint, it is characterised in that the following steps are included:
After each component substep is mixed evenly, after thermal barrel is added after filtering, bucket inside courtyard temperature is added to 55~60 DEG C
Afterwards, make coating material temperature uniformly and facilitate defoaming to complete, can roller coating operation, the UV-curable waterborne priming paint of timber floor is applied
Install, fill and lead up pore, it is straight and even smooth with the polishing of No. 320 sand paper, can roller coating in the plate face polished, by 9~10g/ of coating
㎡ coating weight thickness, it is dry into solidification in uv cure machine 3-5 seconds through 80 degree of excess temperature Infrared Channel levelling 15~20 seconds
Dry completion.