CN106084829A - A kind of warm mix waste rubber powder modified asphalt compound and preparation method thereof - Google Patents
A kind of warm mix waste rubber powder modified asphalt compound and preparation method thereof Download PDFInfo
- Publication number
- CN106084829A CN106084829A CN201610546687.8A CN201610546687A CN106084829A CN 106084829 A CN106084829 A CN 106084829A CN 201610546687 A CN201610546687 A CN 201610546687A CN 106084829 A CN106084829 A CN 106084829A
- Authority
- CN
- China
- Prior art keywords
- warm
- parts
- modified asphalt
- rubber powder
- waste rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of warm mix waste rubber powder modified asphalt compound, belongs to modified asphalt material technical field.It is characterized in that, including the component of following parts by weight: 10 30 parts of shoddies, 60 80 parts of matrix pitches, 20 40 parts of styrene butadiene styrene block copolymers, 10 20 parts of warm-mixing agents, 10 20 parts of wood fibers, 30 50 parts of other fillers;Described warm-mixing agent is made up of the raw material of following weight portion: sulfonate type anion surfactant 50 80 parts, sulfate type anion surfactant 50 80 parts, soaps anion surfactant 30 50 parts, 60 100 parts of paraffin.Warm mix waste rubber powder modified asphalt compound that the present invention provides and preparation method thereof, by warm-mixing agent and each component are reasonably compounded, waste rubber powder modified asphalt viscosity is made to be greatly reduced, so that mixing and stirring temperature to reduce 30 40 DEG C, save the energy, meanwhile, modified pitch is made to have good low-temperature ductility, softening point and needle penetration.
Description
Technical field
The present invention relates to a kind of asphalt, particularly relate to a kind of warm mix waste rubber powder modified asphalt compound and preparation thereof
Method, belongs to modified asphalt material technical field.
Background technology
Waste old is the internationally recognized solid waste affecting environment and must process.Automobile tire is typically using
Scrap in rear 2-3, therefore, want the waste rubber tire that production quantity is surprising the most every year.Rubber for tire is at over cure
Reason, has special cross-linked structure, and recycling is the most difficult.Damaged tire is different from refuse and the rubbish of other kind
Rubbish, it is impossible to process with landfill method, but, if can not get processing in time, stack for a long time, by the health to natural environment and the mankind
Cause and have a strong impact on.Therefore, the discarded of rubber tyre has become a kind of public hazards.In order to protect environment and turn waste into wealth, discarded rubber
The utilization of rubber tire tire is put on agenda by each Main Developed Countries in the world already.Except retread, reclaimed rubber and diarrhea of heat type
With processing outside a part of waste and used rubber tyre, be applied among the construction of asphalt roads, be big batch processing waste old relatively
Good selection.
Rubber modified mixes has decrease of noise functions, and can improve cryogenic property, the paving of current rubber asphalt
If major part still uses high temperature mix, temperature is more than 180 DEG C, and higher than the temperature of mixing and stirring of plain asphalt, high temperature process not only needs
Consuming the substantial amounts of energy, and in work progress, can produce a lot of flue dust and waste gas, the health of harm workmen is good for
Health, the carbon dioxide given off can produce again greenhouse effect, and environmental pollution is serious, thus rubber modified mixes only produces
It is limited to 1000t every day.The employing of warm mix technology will assist in the large scale application of modified asphalt mixture.The most permissible
Promote the exploitation of warm-mixed asphalt concrete road surface decrease of noise functions.
Although warm mix technology is applied to the example of waste rubber powder modified asphalt, such as, Application No. by prior artCN201110262504.7Patent, and Application No.CN201310736778.4Patent, but, the application and prior art
Relatively big difference is all there is at the aspect such as material choice or implementation result.
Summary of the invention
The present invention provides a kind of warm mix waste rubber powder modified asphalt compound and preparation method thereof, by by warm-mixing agent and each group
Divide the most compounding, making waste rubber powder modified asphalt viscosity be greatly reduced, so that mixing and stirring temperature to reduce 30-40 DEG C, saving
The energy, meanwhile, makes modified pitch have good low-temperature ductility, softening point and needle penetration.
What the present invention used the specific scheme is that
A kind of warm mix waste rubber powder modified asphalt compound, including the component of following parts by weight:
10-30 part shoddy, 60-80 part matrix pitch, 20-40 part styrene butadiene styrene block copolymer (SBS),
10-20 part warm-mixing agent, 10-20 part wood fiber, other fillers of 30-50 part.
Described warm-mixing agent is made up of the raw material of following weight portion:
50-80 part sulfonate type anion surfactant, 50-80 part sulfate type anion surfactant, 30-50
Part soaps anion surfactant, 60-100 part paraffin.
Described shoddy fineness of the particles is 47-200 mesh, and water content is less than 5%.Wherein, shoddy fineness of the particles is 60-
120 mesh, for the preferred version of the present invention.
Other described fillers are one or more in coarse aggregate, fine aggregate, mineral aggregate.
Described matrix pitch preferred 70# Colophonium or 90# Colophonium.
Described sulfonate type anion surfactant is preferably dioctyl succinate disulfonate acid or detergent alkylate sulphur
Acid sodium.
Described sulfate type anion surfactant be preferably sodium lauryl sulphate, sodium hexadecyl sulfate, ten
One or more in SOS.
Described soaps anion surfactant is preferably one or more in stearic acid, oleic acid, lauric acid.
The preparation method of warm mix waste rubber powder modified asphalt compound, it is characterised in that comprise the steps:
(1) warm-mixing agent is prepared, in proportion by sulfonate type anion surfactant, sulfate type anion surface active
Agent, soaps anion surfactant and paraffin mix homogeneously, join said mixture in reactor, at 100-120 DEG C,
Stir 20-30 minute, be cooled back to room temperature, obtain warm-mixing agent.
(2) shoddy good for proportioning, styrene butadiene styrene block copolymer (SBS), matrix pitch are put into reactor
Middle 170-180 DEG C of high-speed stirred, stirs and obtains modified pitch in 90 minutes.
(3) temperature that will obtain in the modified pitch obtained in step (2), wood fiber and other fillers and step (1)
Mix agent mix homogeneously, be heated to 120-130 DEG C, i.e. obtain waste rubber powder modified asphalt compound.
Advantages of the present invention:
1, the present invention is by reasonably compounding warm-mixing agent and each component, makes waste rubber powder modified asphalt viscosity be greatly reduced,
So that mixing and stirring temperature to reduce 30-40 DEG C, save the energy.
2, the preparation method that the present invention provides is simple and convenient.
3, the warm-mixing agent in the present invention reached reduce mix and stir temperature requirement while, make modified asphalt mixture have
Well low-temperature ductility, softening point and needle penetration.
Detailed description of the invention
Embodiment 1
10 parts of shoddies, 80 parts of 70# Colophonium, 20 parts of styrene butadiene styrene block copolymer (SBS), 10 parts of warm-mixing agents,
10 parts of wood fibers, 30 parts of other fillers.
Warm-mixing agent is: 50 parts of dioctyl succinate disulfonate acids, 50 parts of sodium lauryl sulphates, 30 parts of stearic acid, 60 parts of stones
Wax.
(1) prepare warm-mixing agent, by 50 parts of dioctyl succinate disulfonate acids, 50 parts of sodium lauryl sulphates, 30 parts of stearic acid,
60 parts of paraffin mix homogeneously, join said mixture in reactor, at 100-120 DEG C, stir 20-30 minute, then cool down
To room temperature, obtain warm-mixing agent.
(2) shoddy good for proportioning, styrene butadiene styrene block copolymer (SBS), 70# Colophonium are put into reactor
Middle 170-180 DEG C of high-speed stirred, stirs and obtains modified pitch in 90 minutes.
(3) temperature that will obtain in the modified pitch obtained in step (2), wood fiber and other fillers and step (1)
Mix agent mix homogeneously, be heated to 120-130 DEG C, i.e. obtain waste rubber powder modified asphalt compound.
Embodiment 2
15 parts of shoddies, 80 parts of 70# Colophonium, 20 parts of styrene butadiene styrene block copolymer (SBS), 15 parts of warm-mixing agents,
15 parts of wood fibers, 40 parts of other fillers.
Warm-mixing agent is: 60 parts of dioctyl succinate disulfonate acids, 60 parts of sodium lauryl sulphates, 40 parts of stearic acid, 80 parts of stones
Wax.
(1) prepare warm-mixing agent, by 60 parts of dioctyl succinate disulfonate acids, 60 parts of sodium lauryl sulphates, 40 parts of stearic acid,
80 parts of paraffin mix homogeneously, join said mixture in reactor, at 100-120 DEG C, stir 20-30 minute, then cool down
To room temperature, obtain warm-mixing agent.
(2) shoddy good for proportioning, styrene butadiene styrene block copolymer (SBS), 70# Colophonium are put into reactor
Middle 170-180 DEG C of high-speed stirred, stirs and obtains modified pitch in 90 minutes.
(3) temperature that will obtain in the modified pitch obtained in step (2), wood fiber and other fillers and step (1)
Mix agent mix homogeneously, be heated to 120-130 DEG C, i.e. obtain waste rubber powder modified asphalt compound.
Embodiment 3
30 parts of shoddies, 80 parts of 70# Colophonium, 40 parts of styrene butadiene styrene block copolymer (SBS), 20 parts of warm-mixing agents,
20 parts of wood fibers, 50 parts of other fillers.
Warm-mixing agent is: 80 parts of dioctyl succinate disulfonate acids, 80 parts of sodium lauryl sulphates, 50 parts of stearic acid, 100 parts of stones
Wax.
(1) prepare warm-mixing agent, by 80 parts of dioctyl succinate disulfonate acids, 80 parts of sodium lauryl sulphates, 50 parts of stearic acid,
100 parts of paraffin mix homogeneously, join said mixture in reactor, at 100-120 DEG C, stir 20-30 minute, then cool down
To room temperature, obtain warm-mixing agent.
(2) shoddy good for proportioning, styrene butadiene styrene block copolymer (SBS), 70# Colophonium are put into reactor
Middle 170-180 DEG C of high-speed stirred, stirs and obtains modified pitch in 90 minutes.
(3) temperature that will obtain in the modified pitch obtained in step (2), wood fiber and other fillers and step (1)
Mix agent mix homogeneously, be heated to 120-130 DEG C, i.e. obtain waste rubber powder modified asphalt compound.
Table one is the performance indications contrast of each embodiment
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
5 DEG C of ductilities (cm) | 11.5 | 11.8 | 13.2 |
Softness number (DEG C) | 65.4 | 65 | 64 |
Needle penetration (0.1mm) | 46 | 46.3 | 47 |
Table one.
Claims (9)
1. a warm mix waste rubber powder modified asphalt compound, it is characterised in that include the component of following parts by weight:
10-30 part shoddy, 60-80 part matrix pitch, 20-40 part styrene butadiene styrene block copolymer (SBS), 10-20
Part warm-mixing agent, 10-20 part wood fiber, other fillers of 30-50 part;
Described warm-mixing agent is made up of the raw material of following weight portion:
50-80 part sulfonate type anion surfactant, 50-80 part sulfate type anion surfactant, 30-50 part soap
Analog anion surfactants, 60-100 part paraffin.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that described shoddy granule
Fineness is 47-200 mesh, and water content is less than 5%.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1 and 2, it is characterised in that described shoddy
Fineness of the particles is 60-120 mesh.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that other described fillers are
One or more in coarse aggregate, fine aggregate, mineral aggregate.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that described matrix pitch is
70# Colophonium or 90# Colophonium.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that described sulfonate type is cloudy
Ionic surface active agent is dioctyl succinate disulfonate acid or dodecylbenzene sodium sulfonate.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that described sulfate type is cloudy
Ionic surface active agent is one or more in sodium lauryl sulphate, sodium hexadecyl sulfate, sodium stearyl sulfate.
Warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that described soaps anion
Surfactant is one or more in stearic acid, oleic acid, lauric acid.
The preparation method of warm mix waste rubber powder modified asphalt compound the most according to claim 1, it is characterised in that include as
Lower step:
(1) prepare warm-mixing agent, in proportion by sulfonate type anion surfactant, sulfate type anion surfactant,
Soaps anion surfactant and paraffin mix homogeneously, join said mixture in reactor, at 100-120 DEG C, stirs
Mix 20-30 minute, be cooled back to room temperature, obtain warm-mixing agent;
(2) shoddy good for proportioning, styrene butadiene styrene block copolymer (SBS), matrix pitch are put in reactor
170-180 DEG C of high-speed stirred, stirs and obtains modified pitch in 90 minutes;
(3) warm-mixing agent that will obtain in the modified pitch obtained in step (2), wood fiber and other fillers and step (1)
Mix homogeneously, is heated to 120-130 DEG C, i.e. obtains waste rubber powder modified asphalt compound.