CN106084829B - A kind of warm mix waste rubber powder modified asphalt mixture and preparation method thereof - Google Patents
A kind of warm mix waste rubber powder modified asphalt mixture and preparation method thereof Download PDFInfo
- Publication number
- CN106084829B CN106084829B CN201610546687.8A CN201610546687A CN106084829B CN 106084829 B CN106084829 B CN 106084829B CN 201610546687 A CN201610546687 A CN 201610546687A CN 106084829 B CN106084829 B CN 106084829B
- Authority
- CN
- China
- Prior art keywords
- parts
- warm
- rubber powder
- modified asphalt
- waste rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of warm mix waste rubber powder modified asphalt mixture, belongs to modified asphalt material technical field.It is characterised in that it includes the component of following parts by weight: 10-30 parts of shoddies, 60-80 parts of matrix pitches, 20-40 parts of Styrene-Butadiene-Styrene Block Copolymer, 10-20 parts of warm-mixing agents, 10-20 parts of wood fibers, 30-50 parts of other fillers;The warm-mixing agent is made of the raw material of following parts by weight: 50-80 parts of sulfonate type anionic surfactant, 50-80 parts of sulfate type anionic surfactant, 30-50 parts of soaps anionic surfactant, 60-100 parts of paraffin.Warm mix waste rubber powder modified asphalt mixture provided by the invention and preparation method thereof, by the way that warm-mixing agent and each component are reasonably compounded, waste rubber powder modified asphalt viscosity is greatly reduced, 30-40 DEG C is reduced to make to mix and stir temperature, the energy is saved, meanwhile making modified pitch that there is good low-temperature ductility, softening point and needle penetration.
Description
Technical field
The present invention relates to a kind of asphalt more particularly to a kind of warm mix waste rubber powder modified asphalt mixture and its preparations
Method belongs to modified asphalt material technical field.
Background technique
Waste old is the internationally recognized solid waste that influences environment and must handle.Automobile tire is generally using
It is scrapped in 2-3 afterwards, therefore, wants the waste rubber tire that production quantity is surprising every year in the world.Rubber for tire through over cure at
Reason, has special cross-linked structure, and recycling and reusing is more difficult.Damaged tire is different from the waste and rubbish of other types
Rubbish cannot be handled with landfill method, still, long-term to stack if cannot handle in time, by the health to natural environment and the mankind
It causes to seriously affect.Therefore, the discarded of rubber tyre has become a kind of public hazards.In order to protect environment and turn waste into wealth, rubber is discarded
The utilization of rubber tire tire is put on agenda by each Main Developed Countries in the world already.In addition to retread, reclaimed rubber and Re Li
With can handle outside a part of waste and used rubber tyre, among the construction of asphalt roads, be big batch processing waste old compared with
Good selection.
Rubber modified mixes have decrease of noise functions, and can improve cryogenic property, at present the paving of rubber asphalt
If most of still use high temperature mix, temperature is more than 180 DEG C, and higher than the temperature of mixing and stirring of plain asphalt, high temperature process is not only needed
The a large amount of energy is consumed, and in the construction process, many flue dust and exhaust gas can be generated, the body for endangering construction personnel is strong
Health, the carbon dioxide given off can generate greenhouse effects again, and environmental pollution is serious, thus rubber modified mixes production is only
It is limited to daily 1000t.The use of warm mix technology will be helpful to the large scale application of modified asphalt mixture.It simultaneously again can be with
Push the exploitation of warm-mixed asphalt concrete road surface decrease of noise functions.
Although having the example that warm mix technology is applied to waste rubber powder modified asphalt in the prior art, for example, application No. isCN201110262504.7Patent, and application No. isCN201310736778.4Patent, still, the application and the prior art
No matter raw material selection or in terms of all there is relatively big differences.
Summary of the invention
The present invention provides a kind of warm mix waste rubber powder modified asphalt mixture and preparation method thereof, by by warm-mixing agent and each group
Point reasonable compounding, is greatly reduced waste rubber powder modified asphalt viscosity, so that making to mix and stir temperature reduces 30-40 DEG C, saves
The energy, meanwhile, make modified pitch that there is good low-temperature ductility, softening point and needle penetration.
It is that the present invention uses the specific scheme is that
A kind of warm mix waste rubber powder modified asphalt mixture, the component including following parts by weight:
10-30 parts of shoddies, 60-80 parts of matrix pitches, 20-40 parts of Styrene-Butadiene-Styrene Block Copolymer,
10-20 parts of warm-mixing agents, 10-20 parts of wood fibers, 30-50 parts of other fillers.
The warm-mixing agent is made of the raw material of following parts by weight:
50-80 portions of sulfonate type anionic surfactants, 50-80 parts of sulfate type anionic surfactants, 30-50
Part soaps anionic surfactant, 60-100 parts of paraffin.
The shoddy grain fineness is 47-200 mesh, and water content is less than 5%.Wherein, shoddy grain fineness is 60-
120 mesh are preferred embodiment of the invention.
Other described fillers are one or more of coarse aggregate, fine aggregate, mineral aggregate.
The preferred 70# pitch of the matrix pitch or 90# pitch.
The sulfonate type anionic surfactant is preferably dioctyl succinate disulfonate acid or detergent alkylate sulphur
Sour sodium.
The sulfate type anionic surfactant is preferably lauryl sodium sulfate, sodium hexadecyl sulfate, ten
One or more of octadecyl sodium sulfate.
The soaps anionic surfactant is preferably one or more of stearic acid, oleic acid, lauric acid.
The preparation method of warm mix waste rubber powder modified asphalt mixture, which comprises the steps of:
(1) warm-mixing agent is prepared, in proportion by sulfonate type anionic surfactant, sulfate type anion surface active
Agent, soaps anionic surfactant and paraffin are uniformly mixed, and said mixture is added in reaction kettle, at 100-120 DEG C,
Stirring 20-30 minutes, is cooled back to room temperature, obtains warm-mixing agent.
(2) proportioned shoddy, Styrene-Butadiene-Styrene Block Copolymer, matrix pitch are put into reaction kettle
Middle 170-180 DEG C of high-speed stirred, stirring obtain modified pitch in 90 minutes.
(3) by temperature obtained in modified pitch obtained in step (2), wood fiber and other fillers and step (1)
It mixes agent to be uniformly mixed, is heated to 120-130 DEG C to get waste rubber powder modified asphalt mixture is arrived.
Advantages of the present invention:
1, the present invention is greatly reduced waste rubber powder modified asphalt viscosity by reasonably compounding warm-mixing agent and each component,
30-40 DEG C is reduced to make to mix and stir temperature, has saved the energy.
2, preparation method provided by the invention is simple and convenient.
3, the present invention in warm-mixing agent reached reduce mix and stir temperature requirement while, there is modified asphalt mixture
Good low-temperature ductility, softening point and needle penetration.
Specific embodiment
Embodiment 1
10 parts of shoddies, 80 parts of 70# pitches, 20 parts of Styrene-Butadiene-Styrene Block Copolymer, 10 parts of warm-mixing agents,
10 parts of wood fibers, 30 parts of other fillers.
Warm-mixing agent are as follows: 50 parts of dioctyl succinate disulfonate acids, 50 parts of lauryl sodium sulfate, 30 parts of stearic acid, 60 parts of stones
Wax.
(1) prepare warm-mixing agent, by 50 parts of dioctyl succinate disulfonate acids, 50 parts of lauryl sodium sulfate, 30 parts of stearic acid,
60 parts of paraffin are uniformly mixed, and said mixture is added in reaction kettle, at 100-120 DEG C, are stirred 20-30 minutes, then cool down
To room temperature, warm-mixing agent is obtained.
(2) proportioned shoddy, Styrene-Butadiene-Styrene Block Copolymer, 70# pitch are put into reaction kettle
Middle 170-180 DEG C of high-speed stirred, stirring obtain modified pitch in 90 minutes.
(3) by temperature obtained in modified pitch obtained in step (2), wood fiber and other fillers and step (1)
It mixes agent to be uniformly mixed, is heated to 120-130 DEG C to get waste rubber powder modified asphalt mixture is arrived.
Embodiment 2
15 parts of shoddies, 80 parts of 70# pitches, 20 parts of Styrene-Butadiene-Styrene Block Copolymer, 15 parts of warm-mixing agents,
15 parts of wood fibers, 40 parts of other fillers.
Warm-mixing agent are as follows: 60 parts of dioctyl succinate disulfonate acids, 60 parts of lauryl sodium sulfate, 40 parts of stearic acid, 80 parts of stones
Wax.
(1) prepare warm-mixing agent, by 60 parts of dioctyl succinate disulfonate acids, 60 parts of lauryl sodium sulfate, 40 parts of stearic acid,
80 parts of paraffin are uniformly mixed, and said mixture is added in reaction kettle, at 100-120 DEG C, are stirred 20-30 minutes, then cool down
To room temperature, warm-mixing agent is obtained.
(2) proportioned shoddy, Styrene-Butadiene-Styrene Block Copolymer, 70# pitch are put into reaction kettle
Middle 170-180 DEG C of high-speed stirred, stirring obtain modified pitch in 90 minutes.
(3) by temperature obtained in modified pitch obtained in step (2), wood fiber and other fillers and step (1)
It mixes agent to be uniformly mixed, is heated to 120-130 DEG C to get waste rubber powder modified asphalt mixture is arrived.
Embodiment 3
30 parts of shoddies, 80 parts of 70# pitches, 40 parts of Styrene-Butadiene-Styrene Block Copolymer, 20 parts of warm-mixing agents,
20 parts of wood fibers, 50 parts of other fillers.
Warm-mixing agent are as follows: 80 parts of dioctyl succinate disulfonate acids, 80 parts of lauryl sodium sulfate, 50 parts of stearic acid, 100 parts of stones
Wax.
(1) prepare warm-mixing agent, by 80 parts of dioctyl succinate disulfonate acids, 80 parts of lauryl sodium sulfate, 50 parts of stearic acid,
100 parts of paraffin are uniformly mixed, and said mixture is added in reaction kettle, at 100-120 DEG C, are stirred 20-30 minutes, then cool down
To room temperature, warm-mixing agent is obtained.
(2) proportioned shoddy, Styrene-Butadiene-Styrene Block Copolymer, 70# pitch are put into reaction kettle
Middle 170-180 DEG C of high-speed stirred, stirring obtain modified pitch in 90 minutes.
(3) by temperature obtained in modified pitch obtained in step (2), wood fiber and other fillers and step (1)
It mixes agent to be uniformly mixed, is heated to 120-130 DEG C to get waste rubber powder modified asphalt mixture is arrived.
Table one is that the performance indicator of each embodiment compares
Embodiment 1 | Embodiment 2 | Embodiment 3 | |
5 DEG C of ductilities (cm) | 11.5 | 11.8 | 13.2 |
Softness number (DEG C) | 65.4 | 65 | 64 |
Needle penetration (0.1mm) | 46 | 46.3 | 47 |
Table one.
Claims (5)
1. a kind of warm mix waste rubber powder modified asphalt mixture, which is characterized in that the component including following parts by weight:
10-30 parts of shoddies, 60-80 parts of matrix pitches, 20-40 parts of Styrene-Butadiene-Styrene Block Copolymer, 10-20
Part warm-mixing agent, 10-20 parts of wood fibers, 30-50 parts of other fillers;The warm-mixing agent is made of the raw material of following parts by weight:
50-80 portions of sulfonate type anionic surfactants, 50-80 portions of sulfate type anionic surfactants, 30-50 parts of soaps
Analog anion surfactants, 60-100 part paraffin;
Other described fillers are one or more of coarse aggregate, fine aggregate, mineral aggregate;The sulfonate type anionic surface
Activating agent is dioctyl succinate disulfonate acid or neopelex;The sulfate type anionic surfactant is
One or more of lauryl sodium sulfate, sodium hexadecyl sulfate, sodium stearyl sulfate;The soaps anion table
Face activating agent is one or more of stearic acid, oleic acid, lauric acid.
2. warm mix waste rubber powder modified asphalt mixture according to claim 1, which is characterized in that the scrap rubber powder particles
Fineness is 47-200 mesh, and water content is less than 5%.
3. warm mix waste rubber powder modified asphalt mixture according to claim 1 or 2, which is characterized in that the shoddy
Grain fineness is 60-120 mesh.
4. warm mix waste rubber powder modified asphalt mixture according to claim 1, which is characterized in that the matrix pitch is
70# pitch or 90# pitch.
5. the preparation method of warm mix waste rubber powder modified asphalt mixture according to claim 1, which is characterized in that including such as
Lower step:
(1) prepare warm-mixing agent, in proportion by sulfonate type anionic surfactant, sulfate type anionic surfactant,
Soaps anionic surfactant and paraffin are uniformly mixed, and said mixture is added in reaction kettle, at 100-120 DEG C, is stirred
It mixes 20-30 minutes, is cooled back to room temperature, obtains warm-mixing agent;
It (2) will be in proportioned shoddy, Styrene-Butadiene-Styrene Block Copolymer, matrix pitch investment reaction kettle
170-180 DEG C of high-speed stirred, stirring obtain modified pitch in 90 minutes;
(3) by warm-mixing agent obtained in modified pitch obtained in step (2), wood fiber and other fillers and step (1)
It is uniformly mixed, is heated to 120-130 DEG C to get waste rubber powder modified asphalt mixture is arrived.