CN106079737A - 一种自粘型保温隔音棉 - Google Patents

一种自粘型保温隔音棉 Download PDF

Info

Publication number
CN106079737A
CN106079737A CN201610621220.5A CN201610621220A CN106079737A CN 106079737 A CN106079737 A CN 106079737A CN 201610621220 A CN201610621220 A CN 201610621220A CN 106079737 A CN106079737 A CN 106079737A
Authority
CN
China
Prior art keywords
proof material
self
adhering
cotton
heat preservation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610621220.5A
Other languages
English (en)
Inventor
顾子文
顾云昌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshou City Jia Dian Textile Co Ltd
Original Assignee
Changshou City Jia Dian Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshou City Jia Dian Textile Co Ltd filed Critical Changshou City Jia Dian Textile Co Ltd
Priority to CN201610621220.5A priority Critical patent/CN106079737A/zh
Publication of CN106079737A publication Critical patent/CN106079737A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种自粘型保温隔音棉，包括：铝箔层、橡塑保温板、玻璃纤维隔音毡、发泡聚酯隔音棉、不干胶层，所述铝箔层压合在所述橡塑保温板的上表面上，所述玻璃纤维隔音毡粘合在所述橡塑保温板的下表面上，所述发泡聚酯隔音棉与所述玻璃纤维隔音毡粘合在一起，所述发泡聚酯隔音棉包括光滑的上表面和锯齿形下表面，所述不干胶层附着在所述锯齿形下表面的锯齿顶上。通过上述方式，本发明具有较好的保温性能，同时具有自粘结性能，便于安装且安装后牢固度高。

Description

一种自粘型保温隔音棉
技术领域
本发明涉及隔音棉领域，特别是涉及一种自粘型保温隔音棉。
背景技术
建筑墙体的隔音性能较差，声音会通过墙体传送，特别是音乐厅、舞厅、工业厂房等噪音比较大的场所，墙体传播声音会严重影响到周围环境，形成噪声污染，因此在其墙体上一般都会安装隔音棉，但是现有的隔音棉安装时需要先打胶，安装麻烦且安装后牢固度差，同时现有的隔音棉保温性能也还存在缺陷。
发明内容
本发明主要解决的技术问题是提供一种自粘型保温隔音棉，能够解决现有隔音棉安装繁琐、保温性能差等缺陷。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种自粘型保温隔音棉，包括：铝箔层、橡塑保温板、玻璃纤维隔音毡、发泡聚酯隔音棉、不干胶层，所述铝箔层压合在所述橡塑保温板的上表面上，所述玻璃纤维隔音毡粘合在所述橡塑保温板的下表面上，所述发泡聚酯隔音棉与所述玻璃纤维隔音毡粘合在一起，所述发泡聚酯隔音棉包括光滑的上表面和锯齿形下表面，所述不干胶层附着在所述锯齿形下表面的锯齿顶上。
在本发明一个较佳实施例中，所述发泡聚酯隔音棉的厚度为3-8cm。
在本发明一个较佳实施例中，所述锯齿形下表面的齿高H为2-5cm。
在本发明一个较佳实施例中，所述铝箔层的外表面附着有透明纳米硅系薄膜。
本发明的有益效果是：本发明采用多层复合结构，使隔音棉具有较好的保温性能，同时在发泡聚酯隔音棉的锯齿形下表面的锯齿顶上附着有不干胶层，使隔音棉具有自粘结性能，便于安装且安装后牢固度高。
附图说明
图1是本发明自粘型保温隔音棉一较佳实施例的结构示意图；
附图中各部件的标记如下：1、铝箔层，2、橡塑保温板，3、玻璃纤维隔音毡，4、发泡聚酯隔音棉，5、不干胶层。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
请参阅图1，本发明实施例包括：
一种自粘型保温隔音棉，包括：铝箔层1、橡塑保温板2、玻璃纤维隔音毡3、发泡聚酯隔音棉4、不干胶层5，所述铝箔层1压合在所述橡塑保温板2的上表面上，所述玻璃纤维隔音毡3粘合在所述橡塑保温板2的下表面上，所述发泡聚酯隔音棉4与所述玻璃纤维隔音毡3粘合在一起，所述发泡聚酯隔音棉4包括光滑的上表面和锯齿形下表面，所述不干胶层5附着在所述锯齿形下表面的锯齿顶上。
其中，所述发泡聚酯隔音棉4的厚度为3-8cm。
所述锯齿形下表面的齿高H为2-5cm，采用锯齿形表面结构，能够提高发泡聚酯隔音棉4的吸音效果。
所述铝箔层1的外表面附着有透明纳米硅系薄膜，所述透明纳米硅系薄膜具有优异的阻水性能，同时具有良好的自清洁性能，能够避免隔音棉表面受污而影响其外观性能及使用性能。
本发明揭示了一种自粘型保温隔音棉，采用多层复合结构，使隔音棉具有较好的保温性能，同时在发泡聚酯隔音棉的锯齿形下表面的锯齿顶上附着有不干胶层，使隔音棉具有自粘结性能，便于安装且安装后牢固度高。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种自粘型保温隔音棉，其特征在于，包括：铝箔层、橡塑保温板、玻璃纤维隔音毡、发泡聚酯隔音棉、不干胶层，所述铝箔层压合在所述橡塑保温板的上表面上，所述玻璃纤维隔音毡粘合在所述橡塑保温板的下表面上，所述发泡聚酯隔音棉与所述玻璃纤维隔音毡粘合在一起，所述发泡聚酯隔音棉包括光滑的上表面和锯齿形下表面，所述不干胶层附着在所述锯齿形下表面的锯齿顶上。
2.根据权利要求1所述的自粘型保温隔音棉，其特征在于，所述发泡聚酯隔音棉的厚度为3-8cm。
3.根据权利要求1所述的自粘型保温隔音棉，其特征在于，所述锯齿形下表面的齿高H为2-5cm。
4.根据权利要求1所述的自粘型保温隔音棉，其特征在于，所述铝箔层的外表面附着有透明纳米硅系薄膜。
CN201610621220.5A 2016-08-02 2016-08-02 一种自粘型保温隔音棉 Pending CN106079737A (zh)