CN106065268A - A kind of electrostatic spraying unsaturated polyester (UP) white primer and preparation method thereof - Google Patents
A kind of electrostatic spraying unsaturated polyester (UP) white primer and preparation method thereof Download PDFInfo
- Publication number
- CN106065268A CN106065268A CN201610581040.9A CN201610581040A CN106065268A CN 106065268 A CN106065268 A CN 106065268A CN 201610581040 A CN201610581040 A CN 201610581040A CN 106065268 A CN106065268 A CN 106065268A
- Authority
- CN
- China
- Prior art keywords
- agent
- unsaturated polyester
- electrostatic spraying
- white primer
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electrostatic spraying unsaturated polyester (UP) white primer and preparation method thereof, including main paint, diluent, initiator, accelerator；Described main enamel-cover includes unsaturated polyester resin 40%～55%, defoamer 0.3%～0.4%, dispersant 0.3%～0.6%, anti-settling agent 0.5%～0.8%, levelling agent 0.4%～0.6%, polymerization inhibitor 0.1%～0.3%, conductive agent 0.3%～0.6%, agent 2%～4% of polishing, titanium dioxide 10%～15%, filler 20%～40%, active solvent 3%～5%；Described diluent includes butyl acetate 20%, styrene 30%, dimethylbenzene 50%.The white primer of the present invention uses the alkylol ammonium salt solution of unsaturated acidic carboxy-late to reduce resistance of coating, improves coating conductivity, can realize electrostatic spraying, improves work efficiency, have preferable sag resistance, covering property, and film is plentiful smooth.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of electrostatic spraying unsaturated polyester (UP) white primer and preparation side thereof
Method.
Background technology
Unsaturated polyester (UP) white primer has the fillibility of excellence, and hardness is high, richness is good, be difficult to advantages such as subsiding, extensively
General be applied to white furniture application in, mainly take conventional air spraying method to construct, when complex part is constructed, deposit
Big in difficulty of construction, ineffective problem, spraying process is easily caused coating cloud simultaneously and splashes, coating painting rate is low, is coated with
Material waste is serious, and painting environment is poor, and workpiece smooth coating degree is the best, and polishing workload is big, and dust is many, pollutes environment, and harm is strong
Health, can not meet furniture enterprise to energy-conservation, environmental protection, the demand efficiently produced.
Electrostatic spraying is to utilize high-pressure electrostatic electric field to make electronegative paint particles transport along the direction orientation that electric field is contrary
Dynamic, and by paint particles absorption at a kind of spraying method of surface of the work, can facilitate and complex part is sprayed, due to not
Saturated polyester resin is nonpolar macromolecular compound, poorly conductive, it is difficult to meet the requirement of electrostatic spraying, common unsaturated polyester
Ester white primer is carried out cannot be by paint-absorbable on workpiece when electrostatic spraying is constructed, and particularly workpiece back edge is more difficult to
Absorption coating, does not reaches and is satisfied with painting effect.
Summary of the invention
The technical problem to be solved is to provide for unsaturated polyester (UP) white primer existence in prior art
Not enough, it is provided that a kind of electrostatic spraying unsaturated polyester (UP) white primer and preparation method thereof, conveniently complex part is constructed,
Reducing difficulty of construction, improve work efficiency, smooth coating is smooth, and painting effect is good.
The technical solution adopted for the present invention to solve the technical problems is: at the bottom of a kind of electrostatic spraying unsaturated polyester (UP) white
Paint, including main paint, diluent, initiator, accelerator；
Described main enamel-cover includes the component of following mass percent: unsaturated polyester resin 40%～55%, defoamer 0.3%～0.4%,
Dispersant 0.3%～0.6%, anti-settling agent 0.5%～0.8%, levelling agent 0.4%～0.6%, polymerization inhibitor 0.1%～0.3%, conductive agent
0.3%～0.6%, agent 2%～4% of polishing, titanium dioxide 10%～15%, filler 20%～40%, active solvent 3%～5%, said components
Percentage ratio sum is 100%；
Described diluent includes the component of following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；
Described main paint, diluent, initiator, the weight ratio of accelerator be: 100:40:1～2:1～2.
Further, described initiator is the methyl ethyl ketone peroxide solution of 10% concentration.
Further, described accelerator is cobalt iso-octoate.
Further, described unsaturated polyester resin is Pneumoperitoneum pressure resin, and described defoamer is broken bubble
Polysiloxane liquid；Described dispersant is the high molecular unsaturated polyester carboxylic acid solution of organic modified polyorganosiloxane.
Further, described anti-settling agent is gas-phase silica；Described levelling agent is polyacrylate flow agent, described resistance
Poly-agent is the quinol solution of 5% concentration；Described polishing agent is zinc stearate.
Further, described titanium dioxide is Rutile type titanium dioxide, and described filler is Pulvis Talci and ground calcium carbonate；
Described active solvent is styrene, and described conductive agent is the alkylol ammonium salt solution of unsaturated acidic carboxy-late.
Further, described main enamel-cover includes the component of following mass percent: unsaturated polyester resin 40%, defoamer
0.3%, dispersant 0.6%, anti-settling agent 0.8%, levelling agent 0.4%, polymerization inhibitor 0.1%, conductive agent 0.3%, agent 3% of polishing, titanium dioxide
10%, filler 40%, active solvent 4.5%.
Further, described main enamel-cover includes the component of following mass percent: unsaturated polyester resin 48%, defoamer
0.4%, dispersant 0.4%, anti-settling agent 0.6%, levelling agent 0.4%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide
13%, filler 28%, active solvent 4.6%.
Further, described main enamel-cover includes the component of following mass percent: unsaturated polyester resin 55%, defoamer
0.4%, dispersant 0.4%, anti-settling agent 0.5%, levelling agent 0.6%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide
15%, filler 20%, active solvent 3.5%.
The preparation method of a kind of electrostatic spraying unsaturated polyester (UP) white primer, comprises the following steps:
(A) main paint is prepared: weigh raw material by following mass percent: unsaturated polyester resin 40%-55%, defoamer 0.3%-
0.4%, dispersant 0.3%-0.6%, anti-settling agent 0.5%-0.8%, levelling agent 0.4%-0.6%, polymerization inhibitor 0.1%-0.3%, conductive agent
0.3%-0.6%, polish agent 2%-4%, titanium dioxide 10%-15%, filler 20%-40%, active solvent 3%-5%；Again by unsaturated polyester (UP)
It is uniform that container for stirring put into by resin and defoamer, is then respectively adding dispersant, anti-settling agent, levelling agent, conductive agent, inhibition
Agent, polishing agent and titanium dioxide and filler mix homogeneously, be uniformly dispersed until fineness reaches 40um, with active solvent regulation to required
Viscosity, filters and packages winner and paints component；
(B) diluent is prepared: weigh raw material by following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Will
Three kinds of raw materials are mixed to get diluent；
(C) by main paint: diluent: initiator: the weight proportion of accelerator=100:40:1～2:1～2 weighs said components, and
Mix homogeneously, i.e. obtains a kind of electrostatic spraying unsaturated polyester (UP) white primer.
The beneficial effect of the invention is: the electrostatic spraying unsaturated polyester (UP) white primer of the present invention is addition insatiable hunger in coating
With the alkylol ammonium salt solution of acidic carboxy-late, reduce resistance of coating, meet electrostatic spraying requirement, such that it is able to carry out electrostatic
Being coated with, by using electrostatic absorption principle, during construction, white primer is easily absorbing on the surface of the workpiece, without waste, pollution-free, fall
Low VOC emission, overcomes conventional air spraying seriously polluted, and utilization efficiency of coatings is low, and the comprehensive application to complex part exists substantially
Dead angle, the shortcomings such as coating efficiency is low, so that furniture enterprise thoroughly takes leave of individual workship's operation that traditional-handwork spraying is dirty, random, poor,
Mechanization automatic job can be carried out, reduce labor strength, there is working environment good, save the advantages such as coating, significantly carry
High efficiency of construction and construction quality.
The electrostatic spraying unsaturated polyester (UP) white primer of the present invention has preferable atomizing effect, good to the parcel of workpiece
Good, it is difficult to sagging, is greatly improved the coating effect of workpiece, owing to film coated surface thickness is uniform, is easy to polish flat, significantly saves
Saving polishing workload, dust reduces, and site environment is clean, is obviously improved work situation, reduces labor strength, contributes to protecting
Barrier workers ' health, meets national energy-saving and reduces discharging requirement.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1
A kind of electrostatic spraying unsaturated polyester (UP) white primer of the present invention, including main paint, diluent, initiator, accelerator；Described
Main enamel-cover includes the component of following mass percent: unsaturated polyester resin 40%, defoamer 0.3%, dispersant 0.6%, anti-settling agent
0.8%, levelling agent 0.4%, polymerization inhibitor 0.1%, conductive agent 0.3%, agent 3% of polishing, titanium dioxide 10%, filler 40%, active solvent
4.5%；Described diluent includes the component of following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Described
Main paint, diluent, initiator, the weight ratio of accelerator be: 100:40:1:1.Wherein said initiator is the peroxide of 10% concentration
Changing methyl ethyl ketone solution, described accelerator is cobalt iso-octoate, and described unsaturated polyester resin is Pneumoperitoneum pressure resin, institute
State defoamer for broken bubble polysiloxane liquid；Described dispersant is that the high molecular unsaturated polyester carboxylic acid of organic modified polyorganosiloxane is molten
Liquid, described anti-settling agent is gas-phase silica；Described levelling agent is polyacrylate flow agent, and described polymerization inhibitor is the right of 5% concentration
Resorcinol solution；Described polishing agent is zinc stearate, and described titanium dioxide is Rutile type titanium dioxide, and described filler is Pulvis Talci
And ground calcium carbonate；Described active solvent is styrene, and described conductive agent is that the alkylol ammonium salt of unsaturated acidic carboxy-late is molten
Liquid.
Unsaturated polyester resin and the defoamer of above-mentioned mass percent are put into container for stirring uniformly, adds the most respectively
Enter dispersant, anti-settling agent, levelling agent, conductive agent, polymerization inhibitor, polishing agent, titanium dioxide and filler mix homogeneously, be uniformly dispersed until
Fineness reaches 40um, with active solvent regulation to required viscosity, filters and packages winner and paints component；Weigh by following mass percent
Raw material: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Three kinds of raw materials are mixed to get diluent；Finally by main paint: dilution
Agent: initiator: after the weight proportion of accelerator=100:40:1:1 takes said components mix homogeneously, obtains a kind of electrostatic spraying not
Saturated polyester white primer, can carry out electrostatic spraying.
After cold spraying construction, the surface drying time of film is less than 30 minutes, and the time of doing solid work is 10 hours, when 25 degree during polishing
Between be 8 hours, hardness be more than 2H, adhesive force be less than 1 grade.
Embodiment 2
A kind of electrostatic spraying unsaturated polyester (UP) white primer of the present invention, including main paint, diluent, initiator, accelerator；Described
Main enamel-cover includes the component of following mass percent: unsaturated polyester resin 48%, defoamer 0.4%, dispersant 0.4%, anti-settling agent
0.6%, levelling agent 0.4%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide 13%, filler 28%, active solvent
4.6%；Described diluent includes the component of following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Described
Main paint, diluent, initiator, the weight ratio of accelerator be: 100:40:1.5:1.5.Wherein said initiator is 10% concentration
Methyl ethyl ketone peroxide solution, described accelerator is cobalt iso-octoate, and described unsaturated polyester resin is Pneumoperitoneum pressure tree
Fat, described defoamer is broken bubble polysiloxane liquid；Described dispersant is the high molecular unsaturated polyester of organic modified polyorganosiloxane
Carboxylic acid solution, described anti-settling agent is gas-phase silica；Described levelling agent is polyacrylate flow agent, and described polymerization inhibitor is 5% dense
The quinol solution of degree；Described polishing agent is zinc stearate, and described titanium dioxide is Rutile type titanium dioxide, and described filler is
Pulvis Talci and ground calcium carbonate；Described active solvent is styrene, and described conductive agent is the alkylol of unsaturated acidic carboxy-late
Ammonium salt solution.
Unsaturated polyester resin and the defoamer of above-mentioned mass percent are put into container for stirring uniformly, adds the most respectively
Enter dispersant, anti-settling agent, levelling agent, conductive agent, polymerization inhibitor, polishing agent, titanium dioxide and filler mix homogeneously, be uniformly dispersed until
Fineness reaches 40um, with active solvent regulation to required viscosity, filters and packages winner and paints component；Weigh by following mass percent
Raw material: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Three kinds of raw materials are mixed to get diluent；Finally by main paint: dilution
Agent: initiator: after the weight proportion of accelerator=100:40:1.5:1.5 takes said components mix homogeneously, obtains a kind of electrostatic
It is coated with unsaturated polyester (UP) white primer, electrostatic spraying can be carried out.
After cold spraying construction, the surface drying time of film is less than 30 minutes, and the time of doing solid work is 10 hours, when 25 degree during polishing
Between be 8 hours, hardness be more than 2H, adhesive force be less than 1 grade.
Embodiment 3
A kind of electrostatic spraying unsaturated polyester (UP) white primer of the present invention, including main paint, diluent, initiator, accelerator；Described
Main enamel-cover includes the component of following mass percent: unsaturated polyester resin 55%, defoamer 0.4%, dispersant 0.4%, anti-settling agent
0.5%, levelling agent 0.6%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide 15%, filler 20%, active solvent
3.5%；Described diluent includes the component of following mass percent: butyl acetate 20%, styrene 30%, and dimethylbenzene 50% is described
Main paint, diluent, initiator, the weight ratio of accelerator be: 100:40:2:2.Wherein said initiator is the peroxide of 10% concentration
Changing methyl ethyl ketone solution, described accelerator is cobalt iso-octoate, and described unsaturated polyester resin is Pneumoperitoneum pressure resin, institute
State defoamer for broken bubble polysiloxane liquid；Described dispersant is that the high molecular unsaturated polyester carboxylic acid of organic modified polyorganosiloxane is molten
Liquid, described anti-settling agent is gas-phase silica；Described levelling agent is polyacrylate flow agent, and described polymerization inhibitor is the right of 5% concentration
Resorcinol solution；Described polishing agent is zinc stearate, and described titanium dioxide is Rutile type titanium dioxide, and described filler is Pulvis Talci
And ground calcium carbonate；Described active solvent is styrene, and described conductive agent is that the alkylol ammonium salt of unsaturated acidic carboxy-late is molten
Liquid.
Unsaturated polyester resin and the defoamer of above-mentioned mass percent are put into container for stirring uniformly, adds the most respectively
Enter dispersant, anti-settling agent, levelling agent, conductive agent, polymerization inhibitor, polishing agent, titanium dioxide and filler mix homogeneously, be uniformly dispersed until
Fineness reaches 40um, with active solvent regulation to required viscosity, filters and packages winner and paints component；Weigh by following mass percent
Raw material: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；Three kinds of raw materials are mixed to get diluent；Finally by main paint: dilution
Agent: initiator: after the weight proportion of accelerator=100:40:2:2 takes said components mix homogeneously, obtains a kind of electrostatic spraying not
Saturated polyester white primer, can carry out electrostatic spraying.
After cold spraying construction, the surface drying time of film is less than 30 minutes, and the time of doing solid work is 10 hours, when 25 degree during polishing
Between be 8 hours, hardness be more than 2H, adhesive force be less than 1 grade.
By contrast, the electrostatic spraying unsaturated polyester (UP) white primer film performance in above three embodiment with use other
The film performance of construction method is compared, and richness is more preferable, and profile pattern improves, and is easier to polish flat bottom, significantly saves
Save polishing workload, reduce dust pollution, owing to mechanization automatic spraying operating can be carried out, without waste, pollution-free, reduce VOC
Discharge, reduces labor strength, has working environment good, saves the advantages such as coating, is greatly improved efficiency of construction and construction matter
Amount.
Claims (10)
1. an electrostatic spraying unsaturated polyester (UP) white primer, it is characterised in that include main paint, diluent, initiator, promotion
Agent；
Described main enamel-cover includes the component of following mass percent: unsaturated polyester resin 40%～55%, defoamer 0.3%～
0.4%, dispersant 0.3%～0.6%, anti-settling agent 0.5%～0.8%, levelling agent 0.4%～0.6%, polymerization inhibitor 0.1%～
0.3%, conductive agent 0.3%～0.6%, agent 2%～4% of polishing, titanium dioxide 10%～15%, filler 20%～40%, activity
Solvent 3%～5%, the percentage ratio sum of said components is 100%；
Described diluent includes the component of following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene 50%；
Described main paint, diluent, initiator, the weight ratio of accelerator be: 100:40:1～2:1～2.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 1, it is characterised in that described initiator
It it is the methyl ethyl ketone peroxide solution of 10% concentration.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 1 and 2, it is characterised in that described rush
Entering agent is cobalt iso-octoate.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 3, it is characterised in that described unsaturation
Polyester resin is Pneumoperitoneum pressure resin, and described defoamer is broken bubble polysiloxane liquid；Described dispersant is organic changing
The high molecular unsaturated polyester carboxylic acid solution of property polysiloxanes.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 4, it is characterised in that described anti-settling agent
For gas-phase silica；Described levelling agent is polyacrylate flow agent, and described polymerization inhibitor is the quinol solution of 5% concentration；
Described polishing agent is zinc stearate.
6. according to a kind of electrostatic spraying unsaturated polyester (UP) white primer described in claim 4 or 5, it is characterised in that described
Titanium dioxide is Rutile type titanium dioxide, and described filler is Pulvis Talci and ground calcium carbonate；Described active solvent is styrene, described
Conductive agent is the alkylol ammonium salt solution of unsaturated acidic carboxy-late.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 6, it is characterised in that described main enamel-cover
Include the component of following mass percent: unsaturated polyester resin 40%, defoamer 0.3%, dispersant 0.6%, anti-settling agent
0.8%, levelling agent 0.4%, polymerization inhibitor 0.1%, conductive agent 0.3%, agent 3% of polishing, titanium dioxide 10%, filler 40%, activity
Solvent 4.5%.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 6, it is characterised in that described main enamel-cover
Include the component of following mass percent: unsaturated polyester resin 48%, defoamer 0.4%, dispersant 0.4%, anti-settling agent
0.6%, levelling agent 0.4%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide 13%, filler 28%, activity
Solvent 4.6%.
A kind of electrostatic spraying unsaturated polyester (UP) white primer the most according to claim 6, it is characterised in that described main enamel-cover
Include the component of following mass percent: unsaturated polyester resin 55%, defoamer 0.4%, dispersant 0.4%, anti-settling agent
0.5%, levelling agent 0.6%, polymerization inhibitor 0.2%, conductive agent 0.4%, agent 4% of polishing, titanium dioxide 15%, filler 20%, activity
Solvent 3.5%.
10. right to go the preparation method of a kind of electrostatic spraying unsaturated polyester (UP) white primer described in 1 to 9, it is characterised in that
Comprise the following steps:
(A) main paint is prepared: weigh raw material by following mass percent: unsaturated polyester resin 40%-55%, defoamer 0.3%-
0.4%, dispersant 0.3%-0.6%, anti-settling agent 0.5%-0.8%, levelling agent 0.4%-0.6%, polymerization inhibitor 0.1%-
0.3%, conductive agent 0.3%-0.6%, polish agent 2%-4%, titanium dioxide 10%-15%, filler 20%-40%, active solvent
3%-5%；Unsaturated polyester resin and defoamer are put into container for stirring uniform again, be then respectively adding dispersant, anti-settling
Agent, levelling agent, conductive agent, polymerization inhibitor, polishing agent and titanium dioxide and filler mix homogeneously, it is uniformly dispersed until fineness reaches
40um, with active solvent regulation to required viscosity, filters and packages winner and paints component；
(B) diluent is prepared: weigh raw material by following mass percent: butyl acetate 20%, styrene 30%, dimethylbenzene
50%；Three kinds of raw materials are mixed to get diluent；
(C) by main paint: diluent: initiator: the weight proportion of accelerator=100:40:1～2:1～2 weighs said components, and
Mix homogeneously, i.e. obtains a kind of electrostatic spraying unsaturated polyester (UP) white primer.