CN106064912A - A kind of dry powder art cement - Google Patents
A kind of dry powder art cement Download PDFInfo
- Publication number
- CN106064912A CN106064912A CN201610353254.0A CN201610353254A CN106064912A CN 106064912 A CN106064912 A CN 106064912A CN 201610353254 A CN201610353254 A CN 201610353254A CN 106064912 A CN106064912 A CN 106064912A
- Authority
- CN
- China
- Prior art keywords
- cement
- powder
- dry powder
- mesh
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cement technology field, being specifically related to a kind of dry powder art cement, it adopts the following technical scheme that: its formula composition is as follows: Portland cement 10% 63.5%, A Er Bobai cement 10% 63.5%, grey calcium 3 6%, attapulgite 3 6%, flyash 3 6%, hydroxymethyl-propyl cellulose 0.3 0.6%, redispersible powder 5 7%, water-soluble poval powder 1 3%, wax powder 0.5 2.5%, dispersant 0.5 1.5%, defoamer 0.2 0.7%；It has environmental-protecting performance and highlights, easily stores, easily transports, need not antifreeze long shelf-life, just stirs quantity by quantity when using, and will not form waste, and formula is simple, cost-effective and have the advantages such as natural colour.
Description
[technical field]
The present invention relates to cement technology field, be specifically related to a kind of dry powder art cement.
[background technology]
Art cement originates from the LOFT industry wind epoch, is a kind of Novel wall ground decoration new material of American-European countries.Skill
Art cement slowly introduces Chinese market from these countries in recent years, and Current Domestic Ye You minority producer imitates and produces.But because of state
Main material (cement) material fineness relatively rough (80-120 mesh) in the art cement product of interior market, can only imitate production part art
The skin texture that cement veneers is more rough, it is impossible to development & production surface is fine and smooth, bright, smooth, penetrating and has the art of stereovision
Cement products.
The defect of existing art cement (dry powder or paste):
First be existing dry powder art cement be pure white powdery or cement monochrome goods, client needs color, construction
Mill base, toner are added in order to annotate in Shi Bixu scene.Because secondary adds pigment there may be not environmentally problem.Second is market
Upper band coloured finished product art cement is generally paste, is that producer adds mill base or iron oxide according to customer demand at factory
The stirring of row pigment is made.3rd is to carry coloured paste art cement product on market, mostly multiple with pigment by emulsion, powder
Conjunction forms, and environmental issue is a query.4th is existing paste art cement product, needs to do in storage, transportation
Anticorrosion, mildew-resistant, antifreeze process, and it is provided with certain quality guarantee period, cause cost of transportation to increase, be difficult to store.It addition, anticorrosion
Agent, antifungus agent are substantially and exist with Organic substance state, add preservative and the paste art cement of antifungus agent, and environmental issue is
Individual query.5th is existing paste art cement product, and general employing metal bucket or Plastic Drum hold, and are easily generated during use
Waste, thus in a disguised form add trimming cost.
[summary of the invention]
Present invention aims to defect and the deficiency of prior art, it is provided that a kind of simple in construction, reasonable in design, make
With a kind of dry powder art cement, it uses domestic Portland cement (color is essentially grey black) and A Er Bobai
Build natural colour by the allotment of adding proportion between cement (white), have that environmental-protecting performance is prominent, easily store, easily transport,
Need not just stir quantity by quantity when antifreeze long shelf-life, use, will not form waste, formula is simple, cost-effective
And there is the advantages such as natural colour.
A kind of dry powder art cement of the present invention, it adopts the following technical scheme that: its formula composition is as follows: commonly
Portland cement 10%-63.5%, A Er Bobai cement 10%-63.5%, ash calcium 3-6%, attapulgite 3-6%, flyash
3-6%, hydroxymethyl-propyl cellulose 0.3-0.6%, redispersible powder 5-7%, water-soluble poval powder 1-3%, wax
Powder 0.5-2.5%, dispersant 0.5-1.5%, defoamer 0.2-0.7%；
It uses following preparation method:
Step one: ash concrete (800 mesh after grinding) 43.5%, white cement (800 mesh after grinding) 30%, ash calcium: 5%, recessed
Convex rod soil: 5%, flyash: 5%, hydroxymethyl-propyl cellulose: 0.5%, redispersible powder: 6%, water-soluble poval
Powder: 2%, wax powder: 1.5%, dispersant: 1%, defoamer: 0.5%；
Step 2: by each formula constitutive material in step one, be added in order in dry powder blender；
Step 3: the dry powder blender in step 2 is used 60-80 rev/min, carries out uniform stirring 20-25 minute,
Open high speed pears cutter to carry out disperseing 5 minutes simultaneously, prepare finished product.
After using said structure, present invention have the beneficial effect that a kind of dry powder art cement of the present invention, it uses state
By the allotment of adding proportion between interior Portland cement (color is essentially grey black) and A Er Bobai cement (white)
Build natural colour, there is environmental-protecting performance and highlight, easily store, easily transport, need not quantity when antifreeze long shelf-life, use
Just stirring quantity, will not form waste, formula is simple, cost-effective and have the advantages such as natural colour.
[detailed description of the invention]
Describe the present invention, illustrative examples therein and explanation in detail with specific embodiment below to be only used for explaining
The present invention, but not as a limitation of the invention.
A kind of dry powder art cement described in this detailed description of the invention, it adopts the following technical scheme that: its formula forms
As follows: Portland cement 10%-63.5%, A Er Bobai cement 10%-63.5%, ash calcium 5%, attapulgite 5%, powder
Coal ash 5%, hydroxymethyl-propyl cellulose 0.5%, redispersible powder 6%, water-soluble poval powder 2%, wax powder
1.5%, dispersant 1%, defoamer 0.5%；
It uses following preparation method:
Step one: ash concrete (800 mesh after grinding) 43.5%, white cement (800 mesh after grinding) 30%, ash calcium: 5%, recessed
Convex rod soil: 5%, flyash: 5%, hydroxymethyl-propyl cellulose: 0.5%, redispersible powder: 6%, water-soluble poval
Powder: 2%, wax powder: 1.5%, dispersant: 1%, defoamer: 0.5%；
Step 2: by each formula constitutive material in step one, be added in order in dry powder blender；
Step 3: the dry powder blender in step 2 is used 60-80 rev/min, carries out uniform stirring 20-25 minute,
Open high speed pears cutter to carry out disperseing 5 minutes simultaneously, prepare finished product.
The raw material of dry powder art cement of the present invention employing and range of application:
1) Portland cement: 10%-63.5% function: by Portland clinker, the mixing material of 5%-20%
And the levigate hydraulic cementing materials made of proper amount of gypsum.
80-120 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 200 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 300 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 400 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 500 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 600 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 700 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
About 800 mesh: adjust in the range of carrying out 10-63.5% according to needs and the white cement of skin texture and color.
2) A Er Bobai cement: 10%-63.5% function: full name white portland cement, burns with the raw material of proper composition
To partial melting, be able to calcium silicates is main component, and the poor grog of irony adds appropriate Gypsum Fibrosum, levigate make white
Color hydraulic cementing materials.
80-120 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 200 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 300 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 400 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 500 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 600 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 700 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
About 800 mesh: adjust in the range of carrying out 10-63.5% according to needs and the ash concrete of skin texture and color.
3) ash calcium: 5%.Function: sierozem power is a kind of air hardening cementitious materials, and being applied to can in building coating or mortar
The intensity of raising system, resistance to water, abrasion resistance etc..
4) attapulgite: 5%.Function；Filler, levelling agent, thickening agent and stabilizer as dry powder art cement.Its
Feature is: to moisture content acceptance, discharge performance by force, not expanding indeformable, bonding can be good, and light weight toughness is big, has heat-insulation warm keeping, suction
The effect of sound, can Anti-moth-eating, anti-sag is strong, adapts to the change of air themperature, and indeformable.
5) flyash: 5%.Function: flyash is the primary solids refuse that coal-burning power plant discharges.The comprehensive utilization of flyash
With, turn waste into wealth, turn bane into boon, it has also become an important techno-economic policy in China's economic construction, be to solve China's electricity
Power production environment is polluted, the important means of contradiction between resource shortage, is also one of the task of the faced solution of power generation.Warp
Crossing exploitation, flyash is widely used in all departments such as building work, building materials, water conservancy
6) hydroxymethyl-propyl cellulose: 0.5%.Function: have water conservation, thickening controls the open hour and improves the merit of application property
Can property additive.
7) redispersible powder: 6%.Function；There is the functional additive increasing product system adhesion strength.
8) water-soluble poval powder: 2%.Function；There is the functional additive improving product system adhesion strength.
9) wax powder: 1.5%.Function: wax powder, name of chemical substance, is commonly applied to, among chemical technology production, can be used for carrying
High anti-scratch, wearability and levelling adhesive force.Also have splendid anti scuffing and excellent extinction, the transparency and feel.
10) dispersant: 1%.Function: dispersant (Dispersant) is that one has lipophile and parent in intramolecular simultaneously
The interfacial agent of two kinds of opposite nature of aqueous.Can homogeneous dispersion those be poorly soluble in liquid inorganic, consolidating of organic pigment
Body granule, also can prevent sedimentation and the cohesion of solid particle simultaneously, forms the medicament needed for stable suspension.
11) defoamer: 0.5%.Function: defoamer, is also called anti-foaming agent, can produce many during commercial production
Unwanted bubbles, needs to add defoamer.It is widely used in removing latex, textile sizing, food fermentation, biological medicine, coating, stone
The unwanted bubbles produced during the industry production such as oiling work, papermaking, industry cleaning link.
The preparation method that art cement of the present invention uses:
1) present invention use Portland cement and A Er Bobai cement, according to product skin texture and the demand of color,
Utilize ball mill to carry out different time for Portland cement and A Er Bobai cement sufficiently to grind.For changing it
Original Portland cement and the physical property of A Er Bobai cement and fineness.
2) assume to prepare a kind of refinement to criticize and scrape the art cement product of skin texture and color (because utilizing ash concrete and white cement
Adding proportion change and thickness change can annotate a lot of colors and skin texture and require).Can so produce:
Take: ash concrete (800 mesh after grinding) 43.5%+ white cement (800 mesh after grinding) 30%+ ash calcium: 5%+ attapulgite
Soil: 5%+ flyash: 5%+ hydroxymethyl-propyl cellulose: 0.5%+ redispersible powder: 6%+ water-soluble poval powder:
2%+ wax powder: 1.5%+ dispersant: 1%+ defoamer: 0.5%=100 part.All above material is added into dry powder in order
In mixer, use 60-80 rev/min and carry out uniform stirring 20-25 minute, open high speed pears cutter simultaneously and carry out disperseing 5 minutes,
This series products can be produced.
The dry powder art cement of the present invention meets the environmental protection policies such as national development dry powder and mortar, part art cement liquid
Creamy product is transformed into dry powdered.The dry powder art cement of the present invention is that the adjustment utilizing ash concrete and white cement adding proportion is annotated
Release the natural colour of art cement, thus mix colours without mill base and toner, it is to avoid cause product that environmental issue occurs.The present invention's
Dry powder art cement key inventive point is that Portland cement and A Er Bobai cement have been carried out deep processing, namely to water
Mud material has carried out grinding refinement respectively, makes it to annotate out surface the finest and the smoothest, bright, smooth, penetrating and have stereovision
Art cement effect.
The difference of the present invention and existing product and advantage:
1) dry powder art cement, all uses the material benefit of domestic raw material low cost, price.
2) dry powder art cement is powdered.Meet the development dry powder and mortar policy of country's promotion, and environmental protection.
3) dry powder art cement, it is not necessary to antifreeze process.
4) dry powder art cement, is not required to do anticorrosion, mildew-resistant process, does not has the shelf-life to limit.
5) dry powder art cement, has the advantages such as easily storage, easy transport.
6) dry powder art cement, utilizes the Natural color adjusting annotation art cement of ash concrete and white cement adding proportion
Coloured silk, thus mix colours without mill base and toner, it is to avoid there is environmental issue in product.
7) dry powder art cement is to utilize ordinary cement to be ground refinement, makes it to annotate out that surface is the finest and the smoothest, light
Bright, smooth, penetrating and there is the art cement effect of stereovision.
A kind of dry powder art cement of the present invention, it uses domestic Portland cement, and (color is the most greyish black
Color) and A Er Bobai cement (white) between build natural colour by the allotment of adding proportion, there is environmental-protecting performance prominent, easily
Store, easily transport, need not just stir quantity by quantity when antifreeze long shelf-life, use, waste, formula letter will not be formed
Single, cost-effective and there is the advantages such as natural colour.
The above is only the better embodiment of the present invention, thus all according to the feature described in present patent application scope and
The equivalence that principle is done changes or modifies, in the range of being all included in present patent application.
Claims (1)
1. a dry powder art cement, it is characterised in that: it adopts the following technical scheme that: its formula composition is as follows: ordinary silicon
Acid salt cement 10%-63.5%, A Er Bobai cement 10%-63.5%, ash calcium 3-6%, attapulgite 3-6%, flyash 3-
6%, hydroxymethyl-propyl cellulose 0.3-0.6%, redispersible powder 5-7%, water-soluble poval powder 1-3%, wax powder
0.5-2.5%, dispersant 0.5-1.5%, defoamer 0.2-0.7%；
It uses following preparation method:
Step one: ash concrete (800 mesh after grinding) 43.5%, white cement (800 mesh after grinding) 30%, ash calcium: 5%, attapulgite
Soil: 5%, flyash: 5%, hydroxymethyl-propyl cellulose: 0.5%, redispersible powder: 6%, water-soluble poval powder:
2%, wax powder: 1.5%, dispersant: 1%, defoamer: 0.5%；
Step 2: by each formula constitutive material in step one, be added in order in dry powder blender；
Step 3: the dry powder blender in step 2 is used 60-80 rev/min, carries out uniform stirring 20-25 minute, simultaneously
Open high speed pears cutter to carry out disperseing 5 minutes, prepare finished product.