CN106048890A - 一种超细纤维面膜布的制造方法 - Google Patents
一种超细纤维面膜布的制造方法 Download PDFInfo
- Publication number
- CN106048890A CN106048890A CN201610532639.3A CN201610532639A CN106048890A CN 106048890 A CN106048890 A CN 106048890A CN 201610532639 A CN201610532639 A CN 201610532639A CN 106048890 A CN106048890 A CN 106048890A
- Authority
- CN
- China
- Prior art keywords
- silk
- superfine fibre
- fiber
- cloth
- pet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种超细纤维面膜布的制造方法,其特征在于包含以下步骤:(1)将PA‑6聚合物切片和PET聚合物切片得到橘瓣型的原生丝;(2)将原生丝进行狭缝气流牵伸纺丝,再将以上所制成的橘瓣型纤维组体震荡摆动铺成连续性纤维网;再将此连续性纤维网利用高压水针进行喷射,在高压水针作用下橘瓣型纤维组合体中的PA‑6、PET组合纤维丝分裂开,形成超细状连续性独立的PA‑6超细纤维丝和PET超细纤维丝;在高压水针分裂的同时,高水压将独立性的PA‑6超细纤维丝和PET超细纤维丝冲嵌到双层立体状的接收网帘中形成三维立体状结构的长丝超细纤维布。具有超柔软,细腻,贴肤性好的特点。
Description
技术领域
本发明涉及聚合物熔融纺丝成布技术和护肤品面膜用布制作技术领域,具体是一种超细纤维面膜布的制造方法
背景技术
聚合物熔融纺丝成布技术是一种常用的纺丝制造技术,即是利用高压气流将熔融状态的聚合物通过缝式牵伸出纤维丝,此聚合物可以是一种或几种;经过牵伸后的纤维丝经过机械、化学或热粘合加固形成连续性长丝布;由此制成的连续性长丝布强力高、成本低,但布面粗糙、手感硬挺、不吸水。
市场上的护肤品面膜用布基本上都是采用一种或几种已经制成好的短纤维经过开松、梳理、成网,再经过机械、化学或热粘合加固形成短纤维面膜用布;由此制成的短纤维面膜用布生产工艺简单、手感柔软、吸水,但强力低、布面粗糙。
如何制造出一种强力高、吸水性好、布面柔滑的面膜用布成为行业急需解决的问题。
发明内容
本发明的目的是:提供一种超细纤维面膜布的制造方法,它制成的超细纤维面膜布柔软、弹性好、高倍吸液、贴肤性好。
本发明是这样实现的:一种超细纤维面膜布的制造方法,它包含以下步骤:
(1)将PA-6聚合物切片和PET聚合物切片分别进行结晶预处理、热风干燥、加热熔融挤压、过滤所得到的熔融体,分别经过计量泵按照比例加压注射到橘瓣型纺丝孔中,在风淋状态下得到橘瓣型的原生丝;
(2)将原生丝进行狭缝气流牵伸纺丝,再将以上所制成的橘瓣型纤维组体震荡摆动铺成连续性纤维网;再将此连续性纤维网利用高压水针进行喷射,在高压水针作用下橘瓣型纤维组合体中的PA-6、PET组合纤维丝分裂开,形成超细状连续性独立的PA-6超细纤维丝和PET超细纤维丝;在高压水针分裂的同时,高水压将独立性的PA-6超细纤维丝和PET超细纤维丝冲嵌到双层立体状的接收网帘中形成三维立体状结构的长丝超细纤维布;
所述双层立体状的接收网帘分为上下层结构,上层为粗尼龙丝与不锈钢丝立体交织而成,下层为细尼龙丝立体交织而成;再将此长丝超细纤维布烘干后充分浸入到高温度、高浓度的氢氧化钠溶液中使其中的PET超细纤维丝部分或全部水解;再经过冷热水循环水洗,弱酸中和、再水洗后烘干定型,制造出一种超柔软、超细纤维面膜布。
所述的一种超细纤维面膜布的制造方法,其特殊之处在于:所述长丝超细纤维布中的PA-6、PET超细纤维之间存在不同大小的空隙腔体,这些腔体增加了长丝超细布弹性和悬垂性,使布面手感柔软和丰满度增加。
所述的一种超细纤维面膜布的制造方法,其特殊之处在于:所述步骤2中,在高温和较浓的烧碱溶液中对双组分中的PET超细纤维丝进行处理,使聚酯高分子物与氢氧化钠间进行多相水解反应;聚酯纤维在氢氧化钠水溶液中,纤维表面聚酯分子链的酯键水解断裂,并不断形成不同的聚合度的水解产物,最终形成水溶性的对苯二甲酸钠和乙二醇;同时,PET超细纤维丝表面被碱腐蚀后,其质量减轻,纤维直径变细,纤维的剪切刚度也下降,增加了超细纤维丝的细度,致使使布面更加细腻,贴肤性好。
所述的一种超细纤维面膜布的制造方法,其特殊之处在于:所述三维立体状结构的长丝超细纤维布制成超细纤维面膜布具有三维立体网状结构,连续长丝超细纤维丝之间形成不同大小的空隙腔体,使得制成的超细纤维面膜布的弹性和悬垂性优良,面膜布的吸液性也由原来的4倍增加到10倍,可使面膜成品能储存更多倍数的精华液;同时,由此方法制成的纤维直细度达到为2-6um,纤维的剪切刚度也随之下降,使得制成的超细纤维面膜布的手感柔软和丰满度增加。。
具体实施方式
下面结合实施例对本发明作进一步描述。这些实例仅用于说明本发明,而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明做各种修改或改动,这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例1
一种超细纤维面膜布的制造方法,它包含以下步骤:
(1)将PA-6聚合物切片和PET聚合物切片按照重量百分比为50%:50%比例分别熔融,即热风干燥、加热熔融挤压、过滤所得到的熔融体,加压注射到橘瓣型纺丝孔中,在风淋状态下,得到橘瓣型的原生丝;
(2)将原生丝进行狭缝气流牵伸纺丝,再将以上所制成的橘瓣型纤维组体震荡摆动铺成连续性纤维网;
再将此连续性纤维网利用150KG压力的高压水针进行喷射,形成三维立体状结构的的长丝超细纤维布;
再将此长丝超细纤维布烘干后即制成140克\平方米的长丝超细纤维布半成品,
再将140克\平方米的长丝超细纤维布半成品充分浸入到温度为95度、浓度为15克\升的氢氧化钠溶液中作用50分钟使PET超细纤维丝全部水解;再经过冷热水循环水洗,弱酸中和、再水洗后烘干定型,即制造出制造出一种70克\平方米的超柔软、超细纤维面膜布。
实施例2
(1)将PA-6聚合物切片和PET聚合物切片按照50%比例分别熔融,加压注射到橘瓣型纺丝孔中,在风淋状态下,得到橘瓣型的原生丝,
(2)将原生丝进行狭缝气流牵伸纺丝,再将以上所制成的橘瓣型纤维组体震荡摆动铺成连续性纤维网;将此连续性纤维网利用100KG压力的高压水针进行喷射,形成三维立体状结构的的长丝超细纤维布;再将此长丝超细纤维布烘干后即制成80克\平方米的长丝超细纤维布半成品,再将80克\平方米的长丝超细纤维布半成品充分浸入到温度为95度、浓度为15克\升的氢氧化钠溶液中作用50分钟,使PET超细纤维丝部分水解;再经过冷热水循环水洗,弱酸中和、再水洗后烘干定型,即制造出制造出一种50克\平方米的超柔软、超细纤维面膜布。
在高压水针分裂的同时,将独立性的PA-6超细纤维丝和PET超细纤维丝冲嵌到双层立体状的接收网帘中形成三维立体状结构的长丝超细纤维布,该双层立体状的接收网帘分为上下层结构,上层为粗尼龙丝与不锈钢丝立体交织而成,下层为细尼龙丝立体交织而成。具有三维立体状结构的长丝超细纤维布中的PA-6、PET超细纤维之间存在不同大小的空隙腔体,这些腔体增加了长丝超细布弹性和悬垂性,使布面手感柔软和丰满度增加。
将此长丝超细纤维布烘干后充分浸入高温度、高浓度的氢氧化钠溶液中使其中的PET超细纤维丝部分或全部水解;再经过冷热水循环水洗,弱酸中和、再水洗后烘干定型,制造出一种超柔软、超细纤维面膜布。工艺特点在于在高温和较浓的烧碱溶液中对双组分中的PET超细纤维丝进行处理,使聚酯高分子物与氢氧化钠间进行多相水解反应;聚酯纤维在氢氧化钠水溶液中,纤维表面聚酯分子链的酯键水解断裂,并不断形成不同的聚合度的水解产物,最终形成水溶性的对苯二甲酸钠和乙二醇;同时,PET超细纤维丝表面被碱腐蚀后,其质量减轻,纤维直径变细,纤维的剪切刚度也下降,增加了超细纤维丝的细度,致使使布面更加细腻,贴肤性好。
由此制造出的超细纤维面膜布具有三维立体网状结构,连续长丝超细纤维丝之间形成不同大小的空隙腔体,使得制成的超细纤维面膜布的弹性和悬垂性优良,面膜布的吸液性也由原来的4倍增加到10倍,可使面膜成品能储存更多倍数的精华液;同时,由此方法制成的纤维直细度达到为2-6um,纤维的剪切刚度也随之下降,使得制成的超细纤维面膜布的手感柔软和丰满度增加。
使用本方法生产出的超细纤维面膜布柔软、弹性好、高倍吸液、贴肤性好,是一种完美的无纺布面膜基布。
工艺流程如下:
(1)PA-6聚合物切片→结晶→热风干燥→热熔融挤压→过滤→计量泵计量→加压注射到橘瓣型纺丝孔中的PA-6腔体中;
(2)PET聚合物切片→→结晶→热风干燥→热熔融挤压→过滤→计量泵计量→加压注射到橘瓣型纺丝孔中的PET腔体中;
(3)将(1)、(2)步骤在风淋状态下得到的橘瓣型原生丝→狭缝气流牵伸纺丝→震荡摆动铺成连续性纤维网→水针喷射→烘干→浸入氢氧化钠溶液→冷热水循环水洗→弱酸中和→再水洗→烘干定型→卷取成布。
以上所述的仅是本发明的优先实施方式。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明原理的情况下,还可以作出若干改进和变型,这也视为本发明的保护范围。
Claims (4)
1.一种超细纤维面膜布的制造方法,其特征在于包含以下步骤:
(1)将PA-6聚合物切片和PET聚合物切片分别进行结晶预处理、热风干燥、加热熔融挤压、过滤所得到的熔融体,分别经过计量泵按照比例加压注射到橘瓣型纺丝孔中,在风淋状态下得到橘瓣型的原生丝;
(2)将原生丝进行狭缝气流牵伸纺丝,再将以上所制成的橘瓣型纤维组体震荡摆动铺成连续性纤维网;再将此连续性纤维网利用高压水针进行喷射,在高压水针作用下橘瓣型纤维组合体中的PA-6、PET组合纤维丝分裂开,形成超细状连续性独立的PA-6超细纤维丝和PET超细纤维丝;在高压水针分裂的同时,高水压将独立性的PA-6超细纤维丝和PET超细纤维丝冲嵌到双层立体状的接收网帘中形成三维立体状结构的长丝超细纤维布;
所述双层立体状的接收网帘分为上下层结构,上层为粗尼龙丝与不锈钢丝立体交织而成,下层为细尼龙丝立体交织而成;再将此长丝超细纤维布烘干后充分浸入到高温度、高浓度的氢氧化钠溶液中使其中的PET超细纤维丝部分或全部水解;再经过冷热水循环水洗,弱酸中和、再水洗后烘干定型,制造出一种超柔软、超细纤维面膜布。
2.根据权利要求1所述的一种超细纤维面膜布的制造方法,其特征在于:所述长丝超细纤维布中的PA-6、PET超细纤维之间存在不同大小的空隙腔体,这些腔体增加了长丝超细布弹性和悬垂性,使布面手感柔软和丰满度增加。
3.根据权利要求1所述的一种超细纤维面膜布的制造方法,其特征在于:所述步骤2中,在高温和较浓的烧碱溶液中对双组分中的PET超细纤维丝进行处理,使聚酯高分子物与氢氧化钠间进行多相水解反应;聚酯纤维在氢氧化钠水溶液中,纤维表面聚酯分子链的酯键水解断裂,并不断形成不同的聚合度的水解产物,最终形成水溶性的对苯二甲酸钠和乙二醇;同时,PET超细纤维丝表面被碱腐蚀后,其质量减轻,纤维直径变细,纤维的剪切刚度也下降,增加了超细纤维丝的细度,致使使布面更加细腻,贴肤性好。
4.根据权利要求1所述的一种超细纤维面膜布的制造方法,其特征在于:所述三维立体状结构的长丝超细纤维布制成超细纤维面膜布具有三维立体网状结构,连续长丝超细纤维丝之间形成不同大小的空隙腔体,使得制成的超细纤维面膜布的弹性和悬垂性优良,面膜布的吸液性也由原来的4倍增加到10倍,可使面膜成品能储存更多倍数的精华液;同时,由此方法制成的纤维直细度达到为2-6um,纤维的剪切刚度也随之下降,使得制成的超细纤维面膜布的手感柔软和丰满度增加。