CN106047240A - 一种基于空气滤清器应用的耐高温热熔胶 - Google Patents
一种基于空气滤清器应用的耐高温热熔胶 Download PDFInfo
- Publication number
- CN106047240A CN106047240A CN201610393881.7A CN201610393881A CN106047240A CN 106047240 A CN106047240 A CN 106047240A CN 201610393881 A CN201610393881 A CN 201610393881A CN 106047240 A CN106047240 A CN 106047240A
- Authority
- CN
- China
- Prior art keywords
- melt adhesive
- air filter
- resistant hot
- temp
- diluent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开的一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:聚烯烃弹性体25‑36%,增粘树脂32‑55%,稀释剂12‑25%,添加剂0.2‑0.5%。采用高性能聚合物为主要原料,满足110℃耐高温需求,性能稳定,有效实现耐高温需求,便于大规模推广使用。
Description
技术领域
本发明涉及一种基于空气滤清器应用的耐高温热熔胶。
背景技术
空气过滤器(Air Filter)是指空气过滤装置,一般用于洁净车间,洁净厂房,洁净手术室、实验室及洁净室,或者用于电子机械通信设备等的防尘。
目前,市面上的空气过滤器耐高温只能在60℃以下,无法满足其在复杂或高温环境下的持续性使用,这样造成其使用范围狭窄。
发明内容
为了解决现有技术中的上述问题,本发明提供了一种基于空气滤清器应用的耐高温热熔胶。
本发明提供一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 25 - 36%
增粘树脂 32 - 55%
稀释剂 12 - 25%
添加剂 0.2 - 0.5%。
作为优选方案之一,按以下质量份数设置组分:
聚烯烃弹性体 25 - 35%
增粘树脂 35 - 50%
稀释剂 15 - 23%
添加剂 0.2 - 0.4%。
作为优选方案之一,按以下质量份数设置组分:
聚烯烃弹性体 21 - 34%
增粘树脂 33 - 55%
稀释剂 15 - 22%
添加剂 0.2 - 0.4%。
作为优选方案之一,按以下质量份数设置组分:
聚烯烃弹性体 25%
增粘树脂 45%
稀释剂 18%
添加剂 0.3%。
作为优选方案之一,所述聚烯烃弹性体为茂金属聚烯烃。
作为优选方案之一,所述增粘树脂为C5石油树脂。
作为优选方案之一,所述稀释剂为高温合成蜡。
作为优选方案之一,所述添加剂为抗氧剂。
本发明有益效果:本配方配制的基于空气滤清器应用的耐高温热熔胶,采用高性能聚合物为主要原料,满足110℃耐高温需求,性能稳定,有效实现耐高温需求,便于大规模推广使用。
具体实施方式
实施例1:
一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 25 - 36%
增粘树脂 32 - 55%
稀释剂 12 - 25%
添加剂 0.2 - 0.5%。
其中:
所述聚烯烃弹性体为茂金属聚烯烃。所述增粘树脂为C5石油树脂。所述稀释剂为高温合成蜡。所述添加剂为抗氧剂。
实施例2:
一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 25 - 35%
增粘树脂 35 - 50%
稀释剂 15 - 23%
添加剂 0.2 - 0.4%。
其中:
所述聚烯烃弹性体为茂金属聚烯烃。所述增粘树脂为C5石油树脂。所述稀释剂为高温合成蜡。所述添加剂为抗氧剂。
实施例3:
一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 21 - 34%
增粘树脂 33 - 55%
稀释剂 15 - 22%
添加剂 0.2 - 0.4%。
其中:
所述聚烯烃弹性体为茂金属聚烯烃。所述增粘树脂为C5石油树脂。所述稀释剂为高温合成蜡。所述添加剂为抗氧剂。
实施例4:
一种基于空气滤清器应用的耐高温热熔胶,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 25%
增粘树脂 45%
稀释剂 18%
添加剂 0.3%。
其中:
所述聚烯烃弹性体为茂金属聚烯烃。所述增粘树脂为C5石油树脂。所述稀释剂为高温合成蜡。所述添加剂为抗氧剂。
本发明相对于传统加工工艺的不同之处在于:本配方配制的基于空气滤清器应用的耐高温热熔胶,采用高性能聚合物为主要原料,满足110℃耐高温需求,性能稳定,有效实现耐高温需求,便于大规模推广使用。
本发明不限于上述实施,凡采用相同原理及其方法实现相同技术效果的多种实施方式均与本专利雷同。
Claims (8)
1.一种基于空气滤清器应用的耐高温热熔胶,其特征在于,包括聚烯烃弹性体、增粘树脂、稀释剂及添加剂,按以下质量份数设置组分:
聚烯烃弹性体 25 - 36%
增粘树脂 32 - 55%
稀释剂 12 - 25%
添加剂 0.2 - 0.5%。
2.如权利要求1所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,按以下质量份数设置组分:
聚烯烃弹性体 25 - 35%
增粘树脂 35 - 50%
稀释剂 15 - 23%
添加剂 0.2 - 0.4%。
3.如权利要求1-2所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,按以下质量份数设置组分:
聚烯烃弹性体 21 - 34%
增粘树脂 33 - 55%
稀释剂 15 - 22%
添加剂 0.2 - 0.4%。
4.如权利要求1-3所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,按以下质量份数设置组分:
聚烯烃弹性体 25%
增粘树脂 45%
稀释剂 18%
添加剂 0.3%。
5.如权利要求1-4所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,所述聚烯烃弹性体为茂金属聚烯烃。
6.如权利要求1-4所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,所述增粘树脂为C5石油树脂。
7.如权利要求1-4所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,所述稀释剂为高温合成蜡。
8.如权利要求1-4所述的基于空气滤清器应用的耐高温热熔胶,其特征在于,所述添加剂为抗氧剂。