CN106032592A - Production technology for nylon hemp - Google Patents
Production technology for nylon hemp Download PDFInfo
- Publication number
- CN106032592A CN106032592A CN201510110723.1A CN201510110723A CN106032592A CN 106032592 A CN106032592 A CN 106032592A CN 201510110723 A CN201510110723 A CN 201510110723A CN 106032592 A CN106032592 A CN 106032592A
- Authority
- CN
- China
- Prior art keywords
- chinlon
- fiber crops
- relative humidity
- production technology
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of textile, and specifically relates to a production technology for nylon hemp. The production technology is characterized in that the technology breaks through use limitation of various conventional yarn spinning equipment, and reconfigures, transforms, and adjusts creatively, so that nylon and hemp are made into yarns in different styles. A drafting method is used to spin, and nylon and hemp are absorbed to uniformly mix. The surface of a yarn is smooth and clean, and a yarn is fluffy and soft in hand feeling. The technique is wide in adaptability of raw materials, spinning count can be high and low, and the technology is easy to popularize, equipment investment is low, and equipment occupies little workshop area.
Description
Technical field:
The present invention relates to textile technology field, be specifically related to the production technology of a kind of chinlon fiber crops.
Background technology:
Along with aesthetic degree and the demand of clothing are also varied from by people, people not only pursue its taking, more require taking, functional and dicoration in one;The most reheating is not loyal to the fabric that style is the most rough, starts to pursue U.S. of details.The thick mad yarn of traditional handicraft cannot meet high request for fancy yarn style instantly, and half spinning technology is arisen at the historic moment.Half spinning and conventional tradition wool worsted, the maximum difference of slubbing technique are, chinlon spinning technique is combined together by it with bast fibre spinning technology, defines a kind of novel spinning technique.Its front road be slubbing and hair equipment plus the comb and parallel cotton fibers prior to spinning of cotton spinning, drafting, rove, spinning frame etc., rear road is spinning winder, doubling, double twisting equipment, and equipment and the change of technique solve the indeterminable problem of original cotton spinning equipment.
Summary of the invention:
The present invention is in order to overcome the weak point of existing textile technology, it is provided that the production technology of a kind of chinlon fiber crops.
To achieve these goals, the concrete technical scheme of the present invention is as follows:
One, chinlon fiber crops pretreatment: in the ratio of chinlon fiber crops weight 2%, weighs oil preparation, loads aerosol apparatus, chinlon fiber crops are successively tiled on the ground, and successively uniformly oil spout, hides with plastic sheeting after completing, banking up 20 hours, oil formula is as follows: antistatic additive: 0.1 0.5%;And crude oil: 0.15 0.55%;Ludox: 0.03 0.15%;
Two, Blowing carding operation: eckling machine cylinder and doffer are improved to frequency control, main technologic parameters: quantitatively dry weight 25g/5m, licker-in speed 600r/min, cylinder speed 240 320 r/min, doffer speed 13 19 r/min, cylinder to cover plate is the hugest 0.305 every foot, 0.305,0.254,0.254,0.305mm;
Three, mixing in doubling step: take two strands of plying, drawing frame is improved to frequency control, main technologic parameters: twice plying uses terylene 60 150d, 30 60, cotton, quantitative dry weight 19.8g/5m of pooling capital;
Four, winding procedure: cylinder yarn is carried out yarn steaming sizing, yarn steaming temperature 90 100 degrees Celsius, 30 40 minutes time;
Five, critical process relative humidity controls: blowing relative humidity is 40 70%, and carding step 60 73 relative humidity is 55 65%, and unskilled workman's sequence relative humidity is 63 69%, and spinning process relative humidity is 65 75%.
The beneficial effects of the present invention is: a, the use boundary of all kinds of spinning equipments broken traditions, creative carrying out reconfigures, transforms and adjusts, so that slubbing class chinlon bast fibre spinning is made from a spining semi-worsted yarn.B, technological process are shorter, and cost ratio is relatively low.C, have employed the spinning of drawing-off method, and drawn that chinlon spins raw material mixing and combing and bast fibre spinning and closed drawing-off, so that the yarn uniform color spun out, chinlon fiber crops mix homogeneously, yam surface is bright and clean, and feel is fluffy, soft.D, this programme process wide to the adaptability ratio of raw material, spinning count can be high or low, and technology is easily popularized, and equipment investment is low, takies plant area few.
Specific implementation method:
Below in conjunction with embodiment, the invention will be further described:
One, the selection of raw material: according to product need select chinlon 60-150d respectively, fiber crops 30-60 prop up, quantitative dry weight 20.2g/5m of pooling capital.
Two, the pretreatment before spinning: when chinlon fiber crops produce on bast-fiber spinning apparatus, easily produce electrostatic through friction, have a strong impact on spinning process, particularly in comb and parallel cotton fibers prior to spinning, mixing in doubling step.So oil preparation is treated as fine or not crucial one procedure (including that oil preparation selects, oil formula selects, oil content analysis) of spinning.
1, the selection of oil preparation: Ludox, the colloid solution of a kind of micro-blue-opalescent, the biggest specific surface area, stronger adsorptivity, can adhere to fiber surface, and be not dissolved in water, clump and play strengthen chinlon fiber crops cohesive force effect.And crude oil, it is mainly used in chinlon and spins industry there is significantly infiltration, moistening and antistatic property, can obviously improve chinlon fiber crops breakage phenomena in spinning process.Antistatic additive, eliminates the electrostatic that chinlon fiber crops produce in friction process, improves spinnability.
2, oil formula: antistatic additive: 0.7%, and crude oil 0.4%, Ludox 0.15%.Anionic chinlon fiber crops antistatic additive selected by described antistatic additive.
Described and crude oil commodity in use and crude oil, be the liquid form product made of self emulsifying dispersion method.
Claims (3)
1. the production technology of chinlon fiber crops is characterized in that technique comprises the steps of
Chinlon fiber crops pretreatment: in the ratio of chinlon fiber crops weight 2%, weighs oil preparation, loads aerosol apparatus, and chinlon fiber crops are successively tiled on the ground, successively uniformly oil spout, hides with plastic sheeting, bank up 20 hours after completing, and oil formula is as follows: antistatic additive: 0.1 0.5%;And crude oil: 0.15 0.55%;Ludox: 0.03 0.15%;
Blowing carding operation: eckling machine cylinder and doffer are improved to frequency control, main technologic parameters: quantitatively dry weight 25g/5m, licker-in speed 600r/min, cylinder speed 240 320
R/min, doffer speed 13 19 r/min, cylinder to cover plate is the hugest 0.305 every foot, 0.305,0.254,0.254,0.305mm;
Mixing in doubling step: take two strands of plying, drawing frame is improved to frequency control, main technologic parameters: twice plying uses chinlon 60 150d, fiber crops 30 60, quantitative dry weight 19.8g/5m of pooling capital;
Winding procedure: cylinder yarn is carried out yarn steaming sizing, yarn steaming temperature 90 100 degrees Celsius, 30 40 minutes time;
Critical process relative humidity controls: blowing relative humidity is 40 70%, and rippling working procedure 60 73 relative humidity is 55 65%, and unskilled workman's sequence relative humidity is 63 69%, and spinning process relative humidity is 65 75%.
The production technology of a kind of chinlon the most as claimed in claim 1 fiber crops, it is characterised in that anionic terylene antistatic additive selected by described antistatic additive.
The production technology of a kind of chinlon the most as claimed in claim 1 fiber crops, it is characterised in that described and crude oil commodity in use and crude oil, is the liquid form product made of self emulsifying dispersion method.