CN103603112A - Semi-worsted color spinning knitting yarn and production process thereof - Google Patents
Semi-worsted color spinning knitting yarn and production process thereof Download PDFInfo
- Publication number
- CN103603112A CN103603112A CN201310668778.5A CN201310668778A CN103603112A CN 103603112 A CN103603112 A CN 103603112A CN 201310668778 A CN201310668778 A CN 201310668778A CN 103603112 A CN103603112 A CN 103603112A
- Authority
- CN
- China
- Prior art keywords
- spinning
- parts
- knitting yarn
- dyed
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a semi-worsted color spinning knitting yarn which comprises the following components in parts by weight: 30-36 parts of mucilage glues, 20-26 parts of chinlon, 15-21 parts of cotton, 15-21 parts of wool, 3-7 parts of cashmere and 3-7 parts of rabbit hair. The production process of the semi-worsted color spinning knitting yarn comprises the following steps of (1) dyeing; (2) mixing hairs; (3) carding cotton; (4) drawing; (5) spinning a rough yarn; (6) spinning a fine yarn; (7) spooling; (8) doubling; (9) carrying out double twisting. The semi-worsted color spinning knitting yarn disclosed by the invention is formed by blending six raw materials and has the advantages of smoothness, good moisture absorption property and heat-retention property, good tensile property, good lustrousness and soft hand feeling. According to the production process of the semi-worsted color spinning knitting yarn, the fore spinning process is a wool spinning process, and the rear spinning process is a cotton spinning process.
Description
Technical field
The present invention relates to a kind of yarn and production technology, be specifically related to a kind of half spinning dyed-spinning and knitting yarn and production technology thereof.
Background technology
The dry strength of viscose is lower than cotton, and it wets and only has by force dry 50% strong left and right, and elastic resilience is poor, not wear-resisting, and sun-proof, alkaline-resisting not acidproof; But viscose good hygroscopicity, is easy to dyeing, and fabric is comfortable and easy to wear.With it and synthetic fiber blending, the wearability that can promote fabric.
Polyamide fibre has good resilience under lower fusing point, and fatigue resistance and heat endurance also have preferably stretching property by force.
The spun yarn of combed cotton is thin and quality is better, and the cloth that combed cotton is made has higher quality level in texture, washable and durability.
Wool is the important source material of textile industry, and it has the advantages such as good springiness, hygroscopicity is strong, warmth retention property is good.But because price is high, concerning the production of non-weaving cloth, use seldom, and 70 public Sheep Cashmere prices are relatively cheap, and the contained staple fibre in the inside is many.
White goat cashmere time is convenient to the look of eating of raw material in dyeing, if use purple suede or blue or green suede, that when dyeing, will cause that color distortion is equivalent to be mingled with has different hair color the same.
Exempt from suede fiber finer, strong, the surperficial scale of velvet neatly bright and clean, the concentrated softness of knitting wool and the advantage of the glutinous cunning of real silk, the pulp cavity layer with cellular structure, thereby 2 times of the warmth retention property knitting wool that is wool, sucting wet air permeability is also better than the knitting wool (knitting wool) of other natural fabrics, and has the health properties of maintaining skin.
In existing knitting blended yarn technique, be generally three, four kind of raw material carry out blending, for blending finished product and the production technology thereof of six kinds of raw materials, also needs to carry out deep research.
Summary of the invention
Goal of the invention: the invention provides a kind of half spinning dyed-spinning and knitting yarn and production technology thereof being formed by six kinds of raw material blending, can reach according to people's requirement the quality of required product.
Technical scheme: a kind of half spinning dyed-spinning and knitting yarn, described half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: viscose glue 30-36 part, polyamide fibre 20-26 part, cotton 15-21 part, wool 15-21 part, goat cashmere 3-7 part, rabbit suede 3-7 part.
As optimization, described half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: 33 parts of viscose glues, 23 parts, polyamide fibre, cotton 18 parts, 18 parts of wools, 4 parts, goat cashmere, 4 parts of rabbit suedes.
As optimization, described viscose glue is viscose staple fibre, and specification is 1.67D*38mm.
As optimization, described polyamide fibre specification is 1.67D*38mm.
As optimization, described cotton is combed cotton, and the length of combed cotton is 28 mm.
As optimization, described wool is 70 public Sheep Cashmeres, and length is 45-60 mm.
As optimization, described goat cashmere is white goat cashmere, and length is 28-30 mm.
As optimization, described rabbit suede length is 28-30 mm.
The production technology of half spinning dyed-spinning and knitting yarn, comprises the steps: 1) dyeing; 2) and hair; 3) comb and parallel cotton fibers prior to spinning, weight of card sliver is 21.00g/5m; 4) drafting, sliver exporting speed is 340r/min; 5) rove, ingot speed is 1000r/min; 6) spun yarn, ingot speed is 15000 r/min; 7) winder; 8) doubling; 9) double twisting.
As optimization, described step 2) and in hair, the vexed hair time is 12 hours, and mixing number of times is 2 times, and hacking number of times is 3 times, and crude oil is 1:3 with the ratio of profit.
Beneficial effect: the present invention is the half spinning dyed-spinning and knitting yarn being formed by six kinds of raw material blending, and yarn is smooth, has good moisture pick-up properties and thermal property, there is good stretching property by force, good luster, soft, before its production technology, spin as wool spinning technology, after spin as cotton spinning.
The specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail.
Specific embodiment 1:
A half spinning dyed-spinning and knitting yarn, half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: 34 parts of viscose glues, 23 parts, polyamide fibre, cotton 20 parts, 15 parts of wools, 3 parts, goat cashmere, 5 parts of rabbit suedes.
Wherein, viscose glue is viscose staple fibre, and specification is 1.67D*38mm, and polyamide fibre specification is 1.67D*38mm, cotton is combed cotton, and the length of combed cotton is 28mm, and wool is 70 public Sheep Cashmeres, and length is 45mm, goat cashmere is white goat cashmere, and length is 28mm, and rabbit suede length is 28mm.
The production technology of half spinning dyed-spinning and knitting yarn, comprises the steps: 1) dyeing; 2) and hair; 3) comb and parallel cotton fibers prior to spinning, weight of card sliver is 21.00g/5m; 4) drafting, sliver exporting speed is 340r/min; 5) rove, ingot speed is 1000r/min; 6) spun yarn, ingot speed is 15000 r/min; 7) winder; 8) doubling; 9) double twisting.
Wherein, step 2) and in hair, the vexed hair time is 12 hours, and mixing number of times is 2 times, and hacking number of times is 3 times, and crude oil is 1:3 with the ratio of profit.
Specific embodiment 2:
A half spinning dyed-spinning and knitting yarn, half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: 32 parts of viscose glues, 26 parts, polyamide fibre, cotton 15 parts, 15 parts of wools, 5 parts, goat cashmere, 7 parts of rabbit suedes.
Wherein, viscose glue is viscose staple fibre, and specification is 1.67D*38mm, and polyamide fibre specification is 1.67D*38mm, cotton is combed cotton, and the length of combed cotton is 28mm, and wool is 70 public Sheep Cashmeres, and length is 50mm, goat cashmere is white goat cashmere, and length is 30mm, and rabbit suede length is 30mm.
The production technology of half spinning dyed-spinning and knitting yarn, comprises the steps: 1) dyeing; 2) and hair; 3) comb and parallel cotton fibers prior to spinning, weight of card sliver is 21.00g/5m; 4) drafting, sliver exporting speed is 340r/min; 5) rove, ingot speed is 1000r/min; 6) spun yarn, ingot speed is 15000 r/min; 7) winder; 8) doubling; 9) double twisting.
Wherein, step 2) and in hair, the vexed hair time is 12 hours, and mixing number of times is 2 times, and hacking number of times is 3 times, and crude oil is 1:3 with the ratio of profit.
Specific embodiment 3:
A half spinning dyed-spinning and knitting yarn, half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: 33 parts of viscose glues, 20 parts, polyamide fibre, cotton 18 parts, 18 parts of wools, 7 parts, goat cashmere, 4 parts of rabbit suedes.
Wherein, viscose glue is viscose staple fibre, and specification is 1.67D*38mm, and polyamide fibre specification is 1.67D*38mm, cotton is combed cotton, and the length of combed cotton is 28mcm, and wool is 70 public Sheep Cashmeres, and length is 54mm, goat cashmere is white goat cashmere, and length is 29mm, and rabbit suede length is 29mm.
The production technology of half spinning dyed-spinning and knitting yarn, comprises the steps: 1) dyeing; 2) and hair; 3) comb and parallel cotton fibers prior to spinning, weight of card sliver is 21.00g/5m; 4) drafting, sliver exporting speed is 340r/min; 5) rove, ingot speed is 1000r/min; 6) spun yarn, ingot speed is 15000 r/min; 7) winder; 8) doubling; 9) double twisting.
Wherein, step 2) and in hair, the vexed hair time is 12 hours, and mixing number of times is 2 times, and hacking number of times is 3 times, and crude oil is 1:3 with the ratio of profit.
Claims (10)
1. a half spinning dyed-spinning and knitting yarn, is characterized in that: described half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: viscose glue 30-36 part, polyamide fibre 20-26 part, cotton 15-21 part, wool 15-21 part, goat cashmere 3-7 part, rabbit suede 3-7 part.
2. half spinning dyed-spinning and knitting yarn according to claim 1, is characterized in that: as optimization, described half spinning dyed-spinning and knitting yarn is comprised of according to parts by weight following component: 33 parts of viscose glues, 23 parts, polyamide fibre, cotton 18 parts, 18 parts of wools, 4 parts, goat cashmere, 4 parts of rabbit suedes.
3. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described viscose glue is viscose staple fibre, and specification is 1.67D*38mm.
4. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described polyamide fibre specification is 1.67D*38mm.
5. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described cotton is combed cotton, and the length of combed cotton is 28 mm.
6. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described wool is 70 public Sheep Cashmeres, and length is 45-60 mm.
7. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described goat cashmere is white goat cashmere, and length is 28-30 mm.
8. half spinning dyed-spinning and knitting yarn according to claim 1 and 2, is characterized in that: described rabbit suede length is 28-30 mm.
9. the production technology of half spinning dyed-spinning and knitting yarn according to claim 1, is characterized in that: comprise the steps: 1) dyeing; 2) and hair; 3) comb and parallel cotton fibers prior to spinning, weight of card sliver is 21.00g/5m; 4) drafting, sliver exporting speed is 340r/min; 5) rove, ingot speed is 1000r/min; 6) spun yarn, ingot speed is 15000 r/min; 7) winder; 8) doubling; 9) double twisting.
10. the production technology of half spinning dyed-spinning and knitting yarn according to claim 9, is characterized in that: described step 2) and in hair, the vexed hair time is 12 hours, and mixing number of times is 2 times, and hacking number of times is 3 times, and crude oil is 1:3 with the ratio of profit.