CN106010411A - Glitter powder sequin membrane and preparation method thereof - Google Patents
Glitter powder sequin membrane and preparation method thereof Download PDFInfo
- Publication number
- CN106010411A CN106010411A CN201610354449.7A CN201610354449A CN106010411A CN 106010411 A CN106010411 A CN 106010411A CN 201610354449 A CN201610354449 A CN 201610354449A CN 106010411 A CN106010411 A CN 106010411A
- Authority
- CN
- China
- Prior art keywords
- glitter powder
- powder
- sequin
- glitter
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a glitter powder sequin membrane and a preparation method thereof. The glitter powder sequin membrane comprises a PET base material layer, a first water glue layer and a glitter powder layer, wherein the water glue of the first water glue layer is obtained by processing the following raw materials in parts by weight: 20-28 parts of ethylene vinyl acetate, 30-45 parts of PU resin copolymer emulsion, 15-23 parts of isooctoate and 15-25 parts of water. The preparation method of the glitter powder sequin membrane comprises the following steps: (I) preparation of glitter powder: selecting a PET base material, aluminizing and coloring, and slitting and powdering to obtain the glitter powder; and (II) preparation of the glitter powder sequin membrane: selecting a PET base material, uniformly coating the PET base material with appropriate water glue, uniformly spreading appropriate glitter powder, and performing extrusion, powder absorption, drying, rolling and slitting processes to obtain the glitter powder sequin membrane. In the invention, oily glue is replaced by waterborne glue; the glitter powder sequin membrane is obtained by gluing, automatic powder spreading, extrusion, powder absorption, protection layer coating and drying; the defect that the oily glue is not environment-friendly is overcome; and the product has the advantages of brightness, beauty, easiness in powdering without tool penetration, boiling resistance, scratch resistance and no falling.
Description
Technical field
The present invention relates to a kind of membrane material and preparation method thereof, more particularly to a kind of glitter powder sequin film and preparation method thereof.
Background technology
Sequin film is mainly used in the making of sequin, and sequin is the most common a kind of ornaments, is widely used in clothing, evening dress, footwear, cap, handbag, headwear, wool manufacturing, pearl embroidery, lamp decoration, artware etc..
The glitter powder sequin film occurred in the market; it is to be formed by painting factice, artificial dusting, baking, again airing, up-protective layer; its defect is that factice contains poisonous composition, not environmentally, additionally; the artificial dusting uniformity is poor; product specification is low, and production efficiency is low, and product not resistant to cook, easy dry linting; present invention seek to address that above-mentioned technical problem, it is provided that a kind of use glitter powder sequin film that glue processes, that product specification is high and preparation method thereof.
Summary of the invention
It is an object of the invention to solve the deficiencies in the prior art, it is provided that a kind of glitter powder sequin film and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of glitter powder sequin film, including PET base material layer, the first gelatine layer, glitter powder layer, glue used by described first gelatine layer is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 20-28 part, PU resin copolymer emulsion 30-45 part, tricaprylate 15-23 part, water 15-25 part；
The preparation method of described glitter powder sequin film is as follows:
The first step, prepared by glitter powder:
Choose PET base material, aluminize and paint, then prepare glitter powder through cutting, rush powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, inhale powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
The present invention uses glue, and the feature of environmental protection is good, and more firm to the adhesion of glitter powder, difficult drop-off in punching course, non-stick knife, and wear-resisting, resistant to cook saves cutter version, and quality is high.
Preferably, used by described gelatine layer, glue is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 22 parts, PU resin copolymer emulsion 38 parts, tricaprylate 20 parts
Preferably, described glitter powder sequin film also includes the second gelatine layer being positioned at the anti-dry linting that shields on glitter powder layer surface, after having extruded, inhales powder the most again, coats the second gelatine layer in second step, dries, rolling and cut operation.
Preferably, second step spread fertilizer over the fields glitter powder use vibration screening mechanism automatically spread fertilizer over the fields.
Glitter powder sequin film to be realized automated production; after the most important thing is gluing, high efficient and reliable is wanted in dusting; existing using manual dusting, the present invention chooses vibration screening mechanism, by vibration; glitter powder uniformly falls from screening mechanism and spreads fertilizer over the fields the surface in gelatine layer; it addition, after up-protective layer, change baking, dry two procedures for disposable drying; operation shortens, and production efficiency is high.
A kind of preparation method of glitter powder sequin film:
The first step, prepared by glitter powder:
Choose PET base material, aluminize and paint, then prepare glitter powder through cutting, rush powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, inhale powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
Preferably, the thickness of PET base material is 60-150 μm, and the coated weight of the first gelatine layer is 5-7g/, and the amount of spreading fertilizer over the fields of glitter powder is 65-75g/, and the coated weight of the second gelatine layer is 2-4g/.
Preferably, drying temperature in second step is 100 DEG C-110 DEG C, and drying time is 45s-60s.
The invention has the beneficial effects as follows: the present invention changes oily gum into water-base cement; by gluing, automatic dusting, extrude, inhale powder, up-protective layer and drying obtain glitter powder sequin film; overcoming factice defect not environmentally, product has punching " not penetration of a cutting tool " vivid, attractive in appearance, easy, resistant to cook, scratch resistance, adeciduate advantage.
Detailed description of the invention
Below by specific embodiment, technical scheme is described in further detail.
Embodiment 1:
A kind of glitter powder sequin film, including PET base material layer, the first gelatine layer, glitter powder layer and the second gelatine layer, used by described first and second gelatine layer, glue is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 20 parts, PU resin copolymer emulsion 30 parts, tricaprylate 15 parts；
The preparation method of described glitter powder sequin film is as follows:
The first step, prepared by glitter powder:
Choosing PET base material, technique is aluminized and is painted routinely, then cuts through routine, rushes powder craft and prepare glitter powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, coat the second gelatine layer, suction powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
The thickness of PET base material is 60 μm, and the coated weight of the first gelatine layer is 5g/, and the amount of spreading fertilizer over the fields of glitter powder is 65g/, and the coated weight of the second gelatine layer is 2g/, and drying temperature in second step is 100 DEG C, and drying time is 60s.
Embodiment 2:
A kind of glitter powder sequin film, including PET base material layer, the first gelatine layer, glitter powder layer and the second gelatine layer, used by described first and second gelatine layer, glue is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 28 parts, PU resin copolymer emulsion 45 parts, tricaprylate 23 parts；
The preparation method of described glitter powder sequin film is as follows:
The first step, prepared by glitter powder:
Choosing PET base material, technique is aluminized and is painted routinely, then cuts through routine, rushes powder craft and prepare glitter powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, coat the second gelatine layer, suction powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
The thickness of PET base material is 150 μm, and the coated weight of the first gelatine layer is 7g/, and the amount of spreading fertilizer over the fields of glitter powder is 75g/, and the coated weight of the second gelatine layer is 4g/, and drying temperature in second step is 110 DEG C, and drying time is 45s.
Embodiment 3:
A kind of glitter powder sequin film, including PET base material layer, the first gelatine layer, glitter powder layer and the second gelatine layer, used by described first and second gelatine layer, glue is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 22 parts, PU resin copolymer emulsion 38 parts, tricaprylate 20 parts；
The preparation method of described glitter powder sequin film is as follows:
The first step, prepared by glitter powder:
Choosing PET base material, technique is aluminized and is painted routinely, then cuts through routine, rushes powder craft and prepare glitter powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, coat the second gelatine layer, suction powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
The thickness of PET base material is 100 μm, and the coated weight of the first gelatine layer is 6g/, and the amount of spreading fertilizer over the fields of glitter powder is 70g/, and the coated weight of the second gelatine layer is 3g/, and drying temperature in second step is 105 DEG C, and drying time is 50s.
The glitter powder sequin film that the present embodiment 1-3 prepares, its technical specification is as follows:
1, tensile strength (mpa) is longitudinally >=120, laterally >=120；
2, elongation at break (%) is longitudinally≤120, laterally≤120；
3, water boiling resistance: 100 DEG C of high temperature decocting in water 30min do not fall glue, not dry linting；
4, appearance index: scratch width≤0.3mm, at cut≤5 of length≤100mm, 500m every cigarette head≤1；
5, bisque binding strength (%) >=98%.
Embodiment described above is the one preferably scheme of the present invention, and the present invention not makees any pro forma restriction, also has other variant and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (7)
1. a glitter powder sequin film, including PET base material layer, the first gelatine layer, glitter powder layer, it is characterized in that: glue used by described first gelatine layer is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 20-28 part, PU resin copolymer emulsion 30-45 part, tricaprylate 15-23 part, water 15-25 part；The preparation method of described glitter powder sequin film is as follows:
The first step, prepared by glitter powder:
Choose PET base material, aluminize and paint, then prepare glitter powder through cutting, rush powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, inhale powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
Glitter powder sequin film the most according to claim 1, it is characterised in that: used by described gelatine layer, glue is formed by the Raw material processing of following weight portion: ethylene-vinyl acetate 22 parts, PU resin copolymer emulsion 38 parts, tricaprylate 20 parts, 20 parts of water.
Glitter powder sequin film the most according to claim 1; it is characterized in that: described glitter powder sequin film also includes being positioned at the second gelatine layer of the anti-dry linting that shields on glitter powder layer surface; after second step has extruded; inhale powder the most again, coat the second gelatine layer, dry, rolling and cut operation.
4. according to the glitter powder sequin film described in claim 1 or 2 or 3, it is characterised in that: second step spreads fertilizer over the fields glitter powder and uses vibration screening mechanism automatically to spread fertilizer over the fields.
5. the preparation method of the glitter powder sequin film described in a claim 1-4 any one, it is characterised in that:
The first step, prepared by glitter powder:
Choose PET base material, aluminize and paint, then prepare glitter powder through cutting, rush powder；
Second step, glitter powder sequin film preparation:
Choose PET base material, uniformly coat appropriate glue, more uniformly spread fertilizer over the fields appropriate glitter powder, be then passed through extruding, inhale powder, drying, rolling and cut operation, it is thus achieved that glitter powder sequin film.
The preparation method of glitter powder sequin film the most according to claim 5, it is characterised in that: the thickness of PET base material is 60-150 μm, and the coated weight of the first gelatine layer is 5-7g/, and the amount of spreading fertilizer over the fields of glitter powder is 65-75g/, and the coated weight of the second gelatine layer is 2-4g/.
The preparation method of glitter powder sequin film the most according to claim 1, it is characterised in that: drying temperature in second step is 100 DEG C-110 DEG C, and drying time is 45s-60s.