CN106007622A - 一种β型半水脱硫石膏基面层自流平砂浆 - Google Patents

一种β型半水脱硫石膏基面层自流平砂浆 Download PDF

Info

Publication number
CN106007622A
CN106007622A CN201610348686.2A CN201610348686A CN106007622A CN 106007622 A CN106007622 A CN 106007622A CN 201610348686 A CN201610348686 A CN 201610348686A CN 106007622 A CN106007622 A CN 106007622A
Authority
CN
China
Prior art keywords
mortar
gypsum
water
sulfurized
hemihydrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610348686.2A
Other languages
English (en)
Other versions
CN106007622B (zh
Inventor
胡达明
单平平
陈定艺
黄福来
黄海波
鲁亮
林伟建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUJIAN CONSTRUCTION ENGINEERING AND CONSTRUCTION MATERIAL TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
FUJIAN CONSTRUCTION ENGINEERING AND CONSTRUCTION MATERIAL TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN CONSTRUCTION ENGINEERING AND CONSTRUCTION MATERIAL TECHNOLOGY DEVELOPMENT Co Ltd filed Critical FUJIAN CONSTRUCTION ENGINEERING AND CONSTRUCTION MATERIAL TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201610348686.2A priority Critical patent/CN106007622B/zh
Publication of CN106007622A publication Critical patent/CN106007622A/zh
Application granted granted Critical
Publication of CN106007622B publication Critical patent/CN106007622B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种β型半水脱硫石膏基面层自流平砂浆,该砂浆由以下质量百分比的组分组成:β半水脱硫石膏55%~60%;三聚氰胺减水剂0.2%~0.3%;聚羧酸减水剂0.1%~0.15%;有机酸缓凝剂0.1%~0.2%;羟丙基甲基纤维素醚0.05%~0.1%;淀粉醚0.05%~0.08%;轻质碳酸钙3%~5%;粉煤灰3%~5%;消泡剂0.05%~0.1%;余量为水。该砂浆在达到面层地坪材料要求的同时,不仅降低整个砂浆的成本,而且实现了工业固体废弃物即β半水脱硫石膏资源化循环利用。

Description

一种β型半水脱硫石膏基面层自流平砂浆
【技术领域】
本发明属于建筑施工材料领域,具体涉及一种β型半水脱硫石膏基面层自流平砂浆。
【背景技术】
传统的人工地坪施工是将混凝土地面凿毛,再进行人工找平施工。受原有地坪平整度影响,地面人工找平厚度往往在2cm以上,并经过较长时间的养护才可以进行下一道工序的施工。而自流平砂浆地坪是将自流平地坪砂浆泵送至楼板地面,借助液体流动的特点自动找平,并快速干燥。相比人工地面找平工艺节省了材料及人工,缩短了施工工期。
自流平砂浆分为水泥基和石膏基两种,水泥基的自流平砂浆配制技术相对比较成熟,成本比较低,硬性指标容易达标,但是经过一段时间容易开裂,存在难以大面积施工、周期长、效率低的缺陷。石膏基自流平具有尺寸稳定性好、干燥不开裂、吸潮等优点,但配制难度相对较大,目前主要是采用α石膏作为主材进行配制,这样成本较高,造成施工成本大幅提升,从而推广难度较大。
而工业副产石膏主要包括电厂烟气脱硫过程排放的固体废弃物脱硫石膏、湿法磷酸生产过程生产排放的磷石膏,我国这一固体废弃物年排放量在5000万吨以上,是亟待解决的污染物。如果能得到大规模利用,将成为一笔宝贵的资源。因此有必要研究采用工业副产β石膏制备石膏基自流平的相关技术。
【发明内容】
本发明所要解决的技术问题在于提供一种β型半水脱硫石膏基面层自流平砂浆,其在达到面层地坪材料要求的同时,不仅降低整个砂浆的成本,而且实现了工业固体废弃物即β半水脱硫石膏资源化循环利用。
本发明是通过以下技术方案解决上述技术问题的:一种β型半水脱硫石膏基面层自流平砂浆,该砂浆由以下质量百分比的组分组成:
本发明的有益效果在于:
提供一种β型半水脱硫石膏基面层自流平砂浆,且该砂浆具有效率高、养护时间短、强度和表面光硬度俱佳的特点,能够达到面层地坪材料要求,而β半水脱硫石膏的利用,不仅降低整个砂浆的成本,而且实现了工业固体废弃物即β半水脱硫石膏资源化循环利用,解决了工业固废所带来的环境污染问题。
【具体实施方式】
本发明一种β型半水脱硫石膏基面层自流平砂浆,该砂浆由以下质量百分比的组分组成:
其中,粉煤灰在本发明中所起到的作用:一方面,掺入上述量的粉煤灰可以提高自流平砂浆的流动度,这主要是因为粉煤灰颗粒大部分为空心微珠,适当的掺入可以有助于流动度的提高;另一方面,粉煤灰主要成分为玻璃体非晶态活性SiO2,这种SiO2能够与Ca(OH)2、粉煤灰中的Al2O3在石膏存在时形成稳定的钙矾石(3CaO·Al2O3·3CaSO4·32H2O),钙矾石的形成有利于补偿自流平砂浆大面积施工时的收缩问题;虽然石膏基自流平前期反应过程具有微膨胀性,但是后期的干燥过程中还是存在着少量的收缩,因此钙矾石的引入可以有效解决石膏基自流平砂浆的后期收缩问题,同时可以显著提高自流平砂浆的后期强度,表面硬度、耐磨性。
为了更好的对本发明进行阐述说明,申请人例举了如下实施例。
实施例1
向搅拌设备中加入33.85kg水,向水中添加0.3kg三聚氰胺减水剂、0.15kg聚羧酸减水剂、0.1kg有机酸缓凝剂、0.05kg羟丙基甲基纤维素醚、0.05kg淀粉醚、5kg粉煤灰、5kg轻质碳酸钙、0.05kg消泡剂、55kgβ半水脱硫石膏,接着搅拌均匀即得β型半水脱硫石膏基面层自流平砂浆,将所得砂浆用泵送施工。
实施例2
向搅拌设备中加入32.25kg水,向水中添加0.2kg三聚氰胺减水剂、0.1kg聚羧酸减水剂、0.2kg有机酸缓凝剂、0.1kg羟丙基甲基纤维素醚、0.05kg淀粉醚、粉煤灰3kg、4kg轻质碳酸钙、0.1kg消泡剂、60kgβ半水脱硫石膏,接着搅拌均匀即得β型半水脱硫石膏基面层自流平砂浆,将所得砂浆用泵送施工。
实施例3
向搅拌设备中加入34.22kg水,向水中添加0.25kg三聚氰胺减水剂、0.12kg聚羧酸减水剂、0.15kg有机酸缓凝剂、0.1kg羟丙基甲基纤维素醚、0.08kg淀粉醚、4kg粉煤灰、3kg轻质碳酸钙、0.08kg消泡剂、58kgβ半水脱硫石膏,接着搅拌均匀即得β型半水脱硫石膏基面层自流平砂浆,将所得砂浆用泵送施工。
为了验证本发明β型半水脱硫石膏基面层自流平砂浆是否符合建筑材料的相关标准,申请人对上述各实施例即实施例1至实施例3所得的β型半水脱硫石膏基面层自流平砂浆的主要性能指标进行检测,则各实施例的检测结果均如下表1所示。
表1主要性能指标及检测结果
由表1表明每个实施例所得的β型半水脱硫石膏基面层自流平砂浆均符合《石膏基自流平砂浆》(JC/T1023-2007)、国家标准《建筑石膏力学性能测定》(GB/T 17669.3-1999)、《建筑石膏净浆物理性能测定》(GB/T 17669.4-1999)的相关参数要求。
综上,本发明β型半水脱硫石膏基面层自流平砂浆具有效率高、养护时间短、强度和表面光硬度俱佳的特点,能够达到面层地坪材料要求,而β半水脱硫石膏的利用,不仅降低整个砂浆的成本,而且实现了工业固体废弃物即β半水脱硫石膏资源化循环利用,解决了工业固废所带来的环境污染问题。

Claims (1)

1.一种β型半水脱硫石膏基面层自流平砂浆,其特征在于:该砂浆由以下质量百分比的组分组成:
CN201610348686.2A 2016-05-24 2016-05-24 一种β型半水脱硫石膏基面层自流平砂浆 Active CN106007622B (zh)