CN105994404A - Insect trapping and killing 3D printed product with micropore structure and preparation method thereof - Google Patents
Insect trapping and killing 3D printed product with micropore structure and preparation method thereof Download PDFInfo
- Publication number
- CN105994404A CN105994404A CN201610351827.6A CN201610351827A CN105994404A CN 105994404 A CN105994404 A CN 105994404A CN 201610351827 A CN201610351827 A CN 201610351827A CN 105994404 A CN105994404 A CN 105994404A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- printed product
- weight
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an insect trapping and killing 3D printed product with a micropore structure and a preparation method thereof. The 3D printed material is prepared from the following components in parts by weight: 120-140 parts of ABS (acrylonitrile butadiene styrene copolymers), 2-8 parts of light diffusant, 2-8 parts of initiator, 10-20 parts of a crosslinking agent, 10-20 parts of a coupling agent, 10-30 parts of oyster shell powder, 2-8 parts of bentonite, 1-4 parts of walnut shell superfine powder, 1-6 parts of limonene, 4-20 parts of an antibacterial agent, 2-8 parts of sweet stevia extract, 2-8 parts of noctilucent powder and 0.2-0.4 part of an auxiliary. The new variety of the 3D printed product provided by the invention is selected and used by users as required, has the effect of greatly expanding the application and development space of the 3D printed product with ABS as the main raw material from the aspect of 3D printing and has outstanding significance.
Description
Technical field
The invention belongs to 3D and print field, be specifically related to a kind of 3D printed product and preparation method thereof.
Background technology
The development maked rapid progress along with 3D printing technique, the concept that 3D prints gradually is known by the public.FDM technology is profit
With ABS, polycarbonate (PC), polyphenylsulfone (PPSF), PLA and other thermoplastic are subject to
To adding the filament being hot extruded into as semi-molten state, by the mode being deposited on the basis of storehouse layer by layer, from 3D CAD data
Directly construction prototype.This technology is commonly used to plastotype, assembling, functional test and conceptual design.Additionally, FDM
Technology can apply to draw a design and quickly manufacture.
ABS material, ABS, original name is acrylonitrile-butadiene-styrene copolymer, is domestic fusion sediment (FDM) formula
The essential core of wire rod.From the properties of material, from the perspective of hot junction, the relatively easy printing of ABS plastic.Nothing
Which type of extruder is opinion use, all can extruded material the most glidingly.ABS resilient enough, be suitable for making furnishings or
Ornament, as long as printing with suitable temperature, allows material layer by layer firmly stick, and the intensity of ABS will become at a relatively high.
ABS has flexibility, also only can bend even if bearing pressure, will not fracture.But during this material on the one hand printing
It is uncomfortable that abnormal smells from the patient allows people have very much, and the product variety function on the other hand printed is limited, it is impossible to meet market many
Sample demand.
Along with development in science and technology and social progress, 3D printed product starts to be not limited only to industrial design, building, engineering and construction
(AEC), automobile, Aero-Space, dentistry and medical industries, education, GIS-Geographic Information System, civil engineering, gun etc.
Field, also begins to come into daily life, in order to make some living utensils or ornament, but at present in life
Application be still embodied in the purposes that the shape of printed product is brought, and the art that its color and shape are formed
Designs etc., the application and development printing 3D there is also the biggest space, simultaneously intensity in degradable rate, toughness and all
Need to be further improved.
Summary of the invention
Goal of the invention: the problem existed for prior art, first technical problem to be solved by this invention is to provide tool
There is the trapping worm type 3D printed product of microcellular structure.Second to be solved by this invention technical problem is that this has micropore
The preparation method of the trapping worm type 3D printed product of structure.3rd technical problem to be solved by this invention is to provide institute
State the application of the trapping worm type 3D printed product with microcellular structure.
Technical scheme: for solving above-mentioned technical problem, the invention provides a kind of trapping worm type 3D with microcellular structure
According to parts by weight, printed product, includes that following components is made: ABS 120～140 parts；Light diffusing agent 2～8 parts；Draw
Send out agent 2～8 parts；Cross-linking agent 10～20 parts；Coupling agent 10～20 parts；Oyster shell powder 10～30 parts；Bentonite 2～8
Part；Walnut shell ultrafine powder 1～4 parts；Limonene 1～6 parts；Antibacterial 4～20 parts；Stevia rebaudiana (Bertoni) Hemsl extract 2～8 parts；
Luminescent powder 2～8 parts；Auxiliary agent 0.2～0.4 part.
It is further preferred that also include nano-silver ionic 2～8 parts according to parts by weight.
Preferably, described initiator is thermal initiator.
Preferably, described light diffusing agent is organosilicon light diffusing agent.
Preferably, according to parts by weight, described antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 1～6 parts；Thin
Lotus flavone extract 1～4 parts；Luan Shu extract 1～6 parts, medical stone powder 1～4 parts.
Preferably, described initiator is the mixture of light trigger and thermal initiator.
Preferably, according to parts by weight, described initiator includes that following components is made: light trigger 1～3 parts；Thermal initiation
Agent 1～5 parts.
Preferably, one or both the mixture during described coupling agent is titanate coupling agent or silane coupler.
Preferably, according to parts by weight, described auxiliary agent includes that following components is made: plasticizer 0.1～0.2 part；Toughener 0.1～
0.2 part.
Invention also provides the preparation method for the above-mentioned trapping worm type 3D printed product with microcellular structure, bag
Include following steps:
1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting；
2) it is cooled to 20 DEG C～30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize to obtain preparing being grafted and hand over
The ABS powder of connection agent；
3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite, walnut shell ultra micro
Powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；
4) by step 3) gains are while continue to be mixed and stirred for uniform, and mixing adds the anti-of corresponding parts by weight successively
Microbial inoculum, Stevia rebaudiana (Bertoni) Hemsl extract and limonene；
5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；
6) while ultra violet lamp 30～60min, after stirring is cooled to 50 DEG C～55 DEG C, three-dimensional fast shaping is passed through
Technology, adds hot-extrudable moulding, vacuum drying, prepares target product.
Preferably, described step 4) be: by step 3) gains are while continue to be mixed and stirred for uniform, mix successively
Close and add the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract, limonene and nano-silver ionic.
Invention also provides the above-mentioned trapping worm type 3D printed product with microcellular structure and there is microcellular structure making
Ornament in application.
Beneficial effect: the trapping worm type 3D printed product with microcellular structure that the present invention provides, on the one hand significantly strengthens
The network structure of product, is effectively improved the toughness of product, and degradable rate is high；On the other hand by thermal initiator, swollen
Profit soil and walnut shell ultrafine powder, the synergism of oyster shell powder so that product itself has certain microcellular structure.
Use the 3D printed product that the present invention provides simultaneously, there is moulding own and the base of basic function that shape is brought
On plinth, on the one hand at night or dark, luminescence can play floor light and identification effect, on the other hand effectively utilize light
Line attracts fly worm close, its component limonene of the third aspect and Stevia rebaudiana (Bertoni) Hemsl extract synergism, is not only effectively improved ABS
Abnormal smells from the patient when material at high temperature melts, improves working environment, and makes the product odour sweet increase of virtue prepared by the present invention to fly
The allure of worm；And limonene makes with the Parmelia tinctorum Despr. extract in antibacterial, Luan Shu extract and medical stone powder synergism
Obtain one aspect of the present invention and there is antioxidation, on the other hand have excellent purifying functions concurrently, have and preferably remove freedom
Base effect and certain anti-radiation effect, third aspect antibacterial and limonene synergism have excellent anti-inflammation merit concurrently
Effect, and fly worm sperm can be killed effectively suppress the breeding of worm's ovum, therefore present invention tool under the dual function of abnormal smells from the patient and light
Having and well lure disinsection efficiency, cleannes are high, significantly improve the antioxygenic property of the present invention, biocidal property the most further
And stability, have excellent anticorrosion concurrently herein in connection with its microcellular structure and de-taste fresh-keeping and purifying effect；When component increases further
When having nano-silver ionic, can further play lasting antibacterial merit on the microcellular structure of the present invention and purifying functions
Effect.Under the synergism of microcellular structure and said components, advantages of good adsorption effect of the present invention so that it can be as functional product
Product are extensively applied, and are particluarly suitable in last step of overall modelling making various interest, dicoration and the killing pests and suppressing bacteria of having concurrently and adsorb
The ornament of purifying functions or functional product, practicality interest has concurrently, in terms of 3D printed product, is greatly enlarged
The application development space of 3D printed product, meaning is notable.
What the present invention provided simultaneously has the preparation method of the trapping worm type 3D printed product of microcellular structure, by a high speed
Add during stirring and be stirred cooling under antibacterial, Stevia rebaudiana (Bertoni) Hemsl extract and limonene, and ultra violet lamp, enter
One step improves stability and the non-oxidizability of obtained 3D printed product.
Entirety extends service life, it is provided that the new varieties of a kind of 3D printed product select as required for user,
In terms of 3D printing, it is greatly enlarged the application development space of 3D printed product with ABS as primary raw material, meaning
Significantly.
Detailed description of the invention
Embodiment 1: a kind of trapping worm type 3D printed product with microcellular structure, includes following components according to parts by weight
Make: ABS 120 parts；Light diffusing agent 2 parts；Initiator 2 parts；Cross-linking agent 10 parts；Coupling agent 10 parts；Concha Ostreae
10 parts of powder；Bentonite 2 parts；Walnut shell ultrafine powder 1 part；Limonene 1 part；Antibacterial 4 parts；Stevia rebaudiana (Bertoni) Hemsl extract 2
Part；Luminescent powder 2 parts；Auxiliary agent 0.2 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein according to parts by weight, antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 1 part；Mint flavone extract
1 part；Luan Shu extract 1 part, medical stone powder 1 part.
Wherein according to parts by weight, initiator includes that following components is made: light trigger 1 part；Thermal initiator 1 part.
Wherein coupling agent is titanate coupling agent.
Wherein according to parts by weight, auxiliary agent includes that following components is made: plasticizer 0.1 part；Toughener 0.1 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes,
Grafting；2) it is cooled to 20 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing graft crosslinking
The ABS powder of agent；3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite,
Walnut shell ultrafine powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；4) by step 3) gains continue mixed
Merging while stirring, mixing adds the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and limonene successively；
5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；6) shine at uviol lamp
While penetrating 30, after stirring is cooled to 50 DEG C, by three-dimensional fast shaping technology, add hot-extrudable moulding, vacuum drying,
Prepare target product.After testing, the flexility of material reaches 82.4Mpa, notch impact strength reaches
47.5MJ/m2。
Embodiment 2: a kind of trapping worm type 3D printed product with microcellular structure, includes following components according to parts by weight
Make: ABS 140 parts；Light diffusing agent 8 parts；Initiator 8 parts；Cross-linking agent 20 parts；Coupling agent 20 parts；Concha Ostreae
30 parts of powder；Bentonite 8 parts；Walnut shell ultrafine powder 4 parts；Limonene 6 parts；Antibacterial 20 parts；Stevia rebaudiana (Bertoni) Hemsl extract
8 parts；Luminescent powder 8 parts；Auxiliary agent 0.4 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein according to parts by weight, antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 6 parts；Mint flavone extract
4 parts；Luan Shu extract 6 parts, medical stone powder 4 parts.
Wherein according to parts by weight, initiator includes that following components is made: light trigger 3 parts；Thermal initiator 5 parts.
Wherein coupling agent is silane coupler.
Wherein according to parts by weight, auxiliary agent includes that following components is made: plasticizer 0.2 part；Toughener 0.2 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes,
Grafting；2) it is cooled to 30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing graft crosslinking
The ABS powder of agent；3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite,
Walnut shell ultrafine powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；4) by step 3) gains continue mixed
Merging while stirring, mixing adds the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and limonene successively；
5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；6) shine at uviol lamp
While penetrating 60min, after stirring is cooled to 55 DEG C, by three-dimensional fast shaping technology, add hot-extrudable moulding, vacuum
It is dried, prepares target product.After testing, the flexility of material reaches 82.7Mpa, notch impact strength
Reach 47.8MJ/m2。
Embodiment 3: a kind of trapping worm type 3D printed product with microcellular structure, includes following components according to parts by weight
Make: ABS 130 parts；Light diffusing agent 5 parts；Initiator 5 parts；Cross-linking agent 15 parts；Coupling agent 15 parts；Concha Ostreae
20 parts of powder；Bentonite 5 parts；Walnut shell ultrafine powder 2 parts；Nano-silver ionic 5 parts；Limonene 4 parts；Antibacterial 12
Part；Stevia rebaudiana (Bertoni) Hemsl extract 5 parts；Luminescent powder 5 parts；Auxiliary agent 0.3 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein according to parts by weight, antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 4 parts；Mint flavone extract
2 parts；Luan Shu extract 4 parts, medical stone powder 2 parts.
Wherein according to parts by weight, initiator includes that following components is made: thermal initiator 5 parts.
Wherein coupling agent is the mixture of titanate coupling agent and silane coupler, and ratio is 3:2.
Wherein according to parts by weight, auxiliary agent includes that following components is made: plasticizer 0.15 part；Toughener 0.15 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes,
Grafting；2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing graft crosslinking
The ABS powder of agent；3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite,
Walnut shell ultrafine powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；4) by step 3) gains continue mixed
Merge stir while, successively mixing add the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract, limonene and
Nano-silver ionic；5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；6)
While ultra violet lamp 45min, after stirring is cooled to 52 DEG C, by three-dimensional fast shaping technology, add hot-extrudable
Moulding, vacuum drying, prepare target product.After testing, the flexility of material reaches 83.9Mpa, lacks
Mouth impact strength reaches 49.0MJ/m2。
Embodiment 4: a kind of trapping worm type 3D printed product with microcellular structure, includes following components according to parts by weight
Make: ABS 125 parts；Light diffusing agent 3 parts；Initiator 3 parts；Cross-linking agent 12 parts；Coupling agent 12 parts；Concha Ostreae
15 parts of powder；Bentonite 4 parts；Walnut shell ultrafine powder 2 parts；Nano-silver ionic 4 parts；Limonene 2 parts；Antibacterial 8
Part；Stevia rebaudiana (Bertoni) Hemsl extract 4 parts；Luminescent powder 4 parts；Auxiliary agent 0.2 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein according to parts by weight, antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 2 parts；Mint flavone extract
2 parts；Luan Shu extract 2 parts, medical stone powder 2 parts.
Wherein according to parts by weight, initiator includes that following components is made: thermal initiator 3 parts.
Wherein coupling agent is titanate coupling agent.
Wherein according to parts by weight, auxiliary agent includes that following components is made: plasticizer 0.1 part；Toughener 0.1 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes,
Grafting；2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing graft crosslinking
The ABS powder of agent；3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite,
Walnut shell ultrafine powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；4) by step 3) gains continue mixed
Merge stir while, successively mixing add the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract, limonene and
Nano-silver ionic；5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；6)
While ultra violet lamp 40min, after stirring is cooled to 50 DEG C, by three-dimensional fast shaping technology, add hot-extrudable
Moulding, vacuum drying, prepare target product.After testing, the flexility of material reaches 83.3Mpa, lacks
Mouth impact strength reaches 47.9MJ/m2。
Embodiment 5: a kind of trapping worm type 3D printed product with microcellular structure, includes following components according to parts by weight
Make: ABS 135 parts；Light diffusing agent 6 parts；Initiator 6 parts；Cross-linking agent 18 parts；Coupling agent 18 parts；Concha Ostreae
25 parts of powder；Bentonite 6 parts；Walnut shell ultrafine powder 3 parts；Nano-silver ionic 6 parts；Limonene 4 parts；Antibacterial 16
Part；Stevia rebaudiana (Bertoni) Hemsl extract 6 parts；Luminescent powder 6 parts；Auxiliary agent 0.4 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein according to parts by weight, antibacterial includes that following components is made: Parmelia tinctorum Despr. extract 5 parts；Mint flavone extract
3 parts；Luan Shu extract 5 parts, medical stone powder 3 parts.
Wherein according to parts by weight, initiator includes that following components is made: light trigger 2 parts；Thermal initiator 4 parts.
Wherein coupling agent is the mixture of titanate coupling agent and silane coupler.
Wherein according to parts by weight, auxiliary agent includes that following components is made: plasticizer 0.2 part；Toughener 0.2 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes,
Grafting；2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing graft crosslinking
The ABS powder of agent；3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite,
Walnut shell ultrafine powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；4) by step 3) gains continue mixed
Merge stir while, successively mixing add the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract, limonene and
Nano-silver ionic；5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；6)
While ultra violet lamp 50min, after stirring is cooled to 55 DEG C, by three-dimensional fast shaping technology, add hot-extrudable
Moulding, vacuum drying, prepare target product.After testing, the flexility of material reaches 82.9Mpa, lacks
Mouth impact strength reaches 48.5MJ/m2。
The trapping worm type 3D printed product with microcellular structure that above-described embodiment provides, makes in last step of overall modelling
Various interest, dicoration and the ornament of killing pests and suppressing bacteria adsorption cleaning effect or the functional products of having concurrently, practicality is interesting
Having concurrently, in terms of 3D printed product, be greatly enlarged the application development space of 3D printed product, meaning is notable.
More than implementing row and the present invention is not constituted restriction, relevant staff is in the scope without departing from the technology of the present invention thought
In, carried out various changes and modifications, and all falls within protection scope of the present invention.
Claims (9)
1. a trapping worm type 3D printed product with microcellular structure, it is characterised in that according to parts by weight include with
Lower component is made: ABS 120～140 parts；Light diffusing agent 2～8 parts；Initiator 2～8 parts；Cross-linking agent 10～20 parts；
Coupling agent 10～20 parts；Oyster shell powder 10～30 parts；Bentonite 2～8 parts；Walnut shell ultrafine powder 1～4 parts；Fructus Citri Limoniae
Alkene 1～6 parts；Antibacterial 4～20 parts；Stevia rebaudiana (Bertoni) Hemsl extract 2～8 parts；Luminescent powder 2～8 parts；Auxiliary agent 0.2～0.4
Part.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that press
Nano-silver ionic 2～8 parts are also included according to parts by weight.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that institute
Stating light diffusing agent is organosilicon light diffusing agent.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that institute
State antibacterial and include that following components is made according to parts by weight: Parmelia tinctorum Despr. extract 1～6 parts；Mint flavone extract 1～
4 parts；Luan Shu extract 1～6 parts, medical stone powder 1～4 parts.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that institute
State initiator and include that following components is made according to parts by weight: light trigger 1～3 parts；Thermal initiator 1～5 parts.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that institute
Stating coupling agent is one or both the mixture in titanate coupling agent or silane coupler.
The trapping worm type 3D printed product with microcellular structure the most according to claim 1, it is characterised in that institute
State auxiliary agent and include that following components is made according to parts by weight: plasticizer 0.1～0.2 part；Toughener 0.1～0.2 part.
8. the preparation method of the trapping worm type 3D printed product with microcellular structure as described in claim 1～7, its
It is characterised by comprising the steps:
1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting；
2) it is cooled to 20 DEG C～30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize to obtain preparing being grafted and hand over
The ABS powder of connection agent；
3) by step 2) the ABS powder that obtains and the oyster shell powder of corresponding parts by weight, bentonite, walnut shell ultra micro
Powder, coupling agent and auxiliary agent, add hot mixing and high-speed stirred is uniform；
4) by step 3) gains are while continue to be mixed and stirred for uniform, and mixing adds the anti-of corresponding parts by weight successively
Microbial inoculum, Stevia rebaudiana (Bertoni) Hemsl extract and limonene；
5) then add luminescent powder and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly；
6) while ultra violet lamp 30～60min, after stirring is cooled to 50 DEG C～55 DEG C, three-dimensional fast shaping is passed through
Technology, adds hot-extrudable moulding, vacuum drying, prepares target product.
The preparation method of the trapping worm type 3D printed product with microcellular structure the most according to claim 8, it is special
Levy and be, described step 4) be: by step 3) gains are while continue to be mixed and stirred for uniform, and mixing adds successively
Enter the antibacterial of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract, limonene and nano-silver ionic.