CN101922058A - Wormwood fiber capable of releasing negative ions and manufacturing method thereof - Google Patents
Wormwood fiber capable of releasing negative ions and manufacturing method thereof Download PDFInfo
- Publication number
- CN101922058A CN101922058A CN2009101478626A CN200910147862A CN101922058A CN 101922058 A CN101922058 A CN 101922058A CN 2009101478626 A CN2009101478626 A CN 2009101478626A CN 200910147862 A CN200910147862 A CN 200910147862A CN 101922058 A CN101922058 A CN 101922058A
- Authority
- CN
- China
- Prior art keywords
- wormwood
- resin
- anion
- anna
- understand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wormwood fiber capable of releasing negative ions, which comprises the following components in the formula: 1-20 of wormwood raw fiber powder, 0.1-20 of Annaao negative ion additive, 60-90 of resin, 0-10 of assistant and 0-10 of colorant. The manufacturing process comprises the following steps: adding the wormwood raw fiber powder, the Annaao negative ion additive, the resin, the assistant and the colorant into a double-screw extruder, blending, extruding, cooling, and pelletizing to obtain the master batch; and drying the master batch, then adding the dried master batch and the resin slices into the double-screw extruder, extruding and spraying filaments at the set temperature, and winding to obtain the wormwood fiber capable of releasing more than 1000 negative ions per cubic centimeter. The obtained fiber simultaneously has the advantages of wormwood and the function of releasing negative ions, and the Annaao negative ion additive can release negative ions for a long time, thereby greatly optimizing the air quality, being beneficial to the human health and improving the applicability of the fiber. The invention is widely applied to the fields of textiles, garments and health care products.
Description
Technical field:
The invention belongs to weaving, clothes and field of health care products.The Wormwood fiber capable scope of application that the present invention discharges anion is extremely extensive, products obtained therefrom had both had wormwood health care, health and medicinal function, can discharge anion, emitting far-infrared, sterilization, the flavor of sterilizing, dispel again, the gained fiber has the good health care function, can be widely used in weaving, clothes and field of health care products.
Background of invention:
Wormwood is a herbaceos perennial, and wormwood and Chinese life have confidential relation, and whenever when the Dragon Boat Festival, people always place Chinese mugwort man with " avoiding evil spirits ", and the strain body after stalk is withered is soaked stifling reaching disinfectant antipruritic, and the puerpera is many to have a bath or stifling with Ai Shui.Wormwood nature and flavor hardship, suffering, temperature are gone into spleen, liver, kidney.Compendium of Material Medica record: Ai Yiye is used as medicine, and warm in nature, bitter, the property of nontoxic, pure sun, logical 12 warp, tool Hui Yang, the blood of regulating the flow of vital energy, pursues effect such as raw, arresting bleeding and miscarriage prevention, also is usually used in acupuncture.So be otherwise known as " doctor's grass ", just popular " herb bath " in Taiwan is exactly to select wormwood for use mostly now.Also can be used as in the acupuncture " moxibustion " and as dyestuff.
Medical research shows that the anion number of keeping health of people is: 1000-2000/cm
3The anion number at countryside, beach is: 5000-50000/cm
3, can strengthen body immunity and antimicrbial power; And the anion number of dwelling house enclosed area, city only is: 40-50/cm
3, under this environment, can bring out physiological barrier such as headache, insomnia, neurasthenia, burnout etc. for a long time; Indoor anion number at the dress air-conditioning can be reduced to: 0-25/cm
3It is vital setting up and having the environment that can keep health, therefore people just constantly develop, develop the functional material with release anion, and the fiber, fabric, the textile product that discharge anion are extensively more and more paid attention to by people because of its Application Areas.
The Wormwood fiber capable that discharges anion is selected the additive and the wormwood that can discharge anion for use, is ground into nano level powder then, again powder is managed to sneak in the fiber.So, fiber has the advantage of wormwood simultaneously and discharges the function of anion, with its lining that is made into, ready-made clothes or indoor ornament, Anna's serial anionic additive difficult to understand can discharge anion muchly, optimize air quality greatly, be of value to health, increased the health-care effect of textiles, improved the application of fiber, made it be widely used in weaving, clothes and field of health care products.
Summary of the invention:
Invention prescription: wormwood fibrillation powder 1-20; Anna serial anionic additive 0.1-20 difficult to understand; Resin 60-90; Auxiliary agent 0-10; Colouring agent 0-10.
Technology: wormwood fibrillation powder, Anna's serial anionic additive difficult to understand, resin, auxiliary agent and colouring agent are added in the double screw extruder, and blend is extruded, cooling, and pelletizing makes masterbatch.To add in the double screw extruder with resin slicer after the masterbatch drying, extrude the spray silk under the temperature that configures, coiling can make the Wormwood fiber capable that discharges anion.
Embodiment 1: prescription: wormwood fibrillation powder 10; Anna's serial anionic additive 0 difficult to understand; Resin 70; Auxiliary agent 10; Colouring agent 10.Make 500/cm of release anion by above-mentioned technology
3Following Wormwood fiber capable.
Embodiment 2: prescription: wormwood fibrillation powder 10; Anna's serial anionic additive 5 difficult to understand; Resin 65; Auxiliary agent 10; Colouring agent 10.Make 1000/cm of release anion by above-mentioned technology
3Above Wormwood fiber capable.
Embodiment 3: prescription: wormwood fibrillation powder 5; Anna's serial anionic additive 10 difficult to understand; Resin 65; Auxiliary agent 10; Colouring agent 10.Make 1000/cm of release anion by above-mentioned technology
3Above Wormwood fiber capable.
Embodiment 4: prescription: wormwood fibrillation powder 5; Anna's serial anionic additive 3 difficult to understand; Resin 77; Auxiliary agent 5; Colouring agent 10.Make 1000/cm of release anion by above-mentioned technology
3Above Wormwood fiber capable.
Embodiment 5: prescription: wormwood fibrillation powder 5; Anna's serial anionic additive 1 difficult to understand; Resin 84; Auxiliary agent 5; Colouring agent 5.Make 1 000/cm of release anion by above-mentioned technology
3Above Wormwood fiber capable.
Claims (7)
1. discharge the Wormwood fiber capable and the manufacture method thereof of anion, it is characterized in that the invention prescription of making by the raw material of following mass ratio: wormwood fibrillation powder 1-20; Anna serial anionic additive 0.1-20 difficult to understand; Resin 60-90; Auxiliary agent 0-10; Colouring agent 0-10.
2. made by natural wormwood according to claims 1 described wormwood fibrillation powder, meet the raw material of national standard, Anna's serial anionic additive difficult to understand can mix with it.
3. be Anna's serial anionic additive difficult to understand according to claims 1 described release anionic additive, wherein Anna's serial anionic additive difficult to understand is the natural minerals that contains nano-pore, adds in the fibrous material or adhere to discharge anion on the textiles at 1000/cm
3More than.
4. comprise according to claims 1 described auxiliary agent: surfactant, adhesive, coupling agent, promoter and other textile auxiliaries.
5. be dyestuff and the pigment of preparing by national standard according to claims 1 described colouring agent.
6. comprise polyethylene (PE), polypropylene (PP), polystyrene (PS), polyethylene terephthalate (PET), polyamide (PA), the acrylonitrile-butadiene-styrene copolymer (ABS) that can be used for melt spinning according to claims 1 described resin.
7. according to the Wormwood fiber capable technology of claims 1 described release anion: wormwood fibrillation powder, Anna's serial anionic additive difficult to understand, resin, auxiliary agent and colouring agent are added in the double screw extruder, and blend is extruded, cooling, and pelletizing makes masterbatch.To add in the double screw extruder with resin slicer after the masterbatch drying, extrude the spray silk under the temperature that configures, coiling can make and discharge anion at 1000/cm
3Above Wormwood fiber capable.The gained fiber has the advantage of wormwood simultaneously and discharges the function of anion, and Anna's serial anionic additive difficult to understand can discharge anion muchly, optimizes air quality, and useful health has improved the application of fiber greatly.