CN105778398A - 3D printing material with function of multiply trapping and killing insects and preparation method thereof - Google Patents
3D printing material with function of multiply trapping and killing insects and preparation method thereof Download PDFInfo
- Publication number
- CN105778398A CN105778398A CN201610343098.XA CN201610343098A CN105778398A CN 105778398 A CN105778398 A CN 105778398A CN 201610343098 A CN201610343098 A CN 201610343098A CN 105778398 A CN105778398 A CN 105778398A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- weight
- agent
- luring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a 3D printing material with the function of multiply trapping and killing insects and a preparation method thereof. The 3D printing material is prepared from the following components in parts by weight: 120-140 parts of ABS (acrylonitrile butadiene styrene copolymers), 2-8 parts of light dispersing agent, 2-8 parts of initiator, 10-20 parts of cross-linking agent, 10-20 parts of coupling agent, 10-30 parts of clam shell powder, 2-8 parts of elemental sulfur, 1-4 parts of medical stone powder, 1-4 parts of walnut shell ultrafine powder, 1-6 parts of limonene, 4-20 parts of toosendainin, 2-8 parts of sweet stevia extract, 2-8 parts of photochromic toner and 0.2-0.4 part of additive. The 3D printing material new variety is provided for users to selectively use as required and the application and development space of the 3D printing material with ABS as the main raw material is greatly expanded from the aspect of the 3D printing material, so the significance is outstanding.
Description
Technical field
The invention belongs to 3D and print field, be specifically related to a kind of 3D printing material and preparation method thereof.
Background technology
Along with the development that 3D printing technique makes rapid progress, the concept that 3D prints is known by the public gradually.FDM technology is to utilize ABS, polycarbonate (PC), polyphenylsulfone (PPSF), PLA and the heated extruding of other thermoplastic become the filament of semi-molten state, by the mode being deposited on storehouse basis layer by layer, from the direct construction prototype of 3DCAD data.This technology is commonly used to plastotype, assembling, functional test and conceptual design.Additionally, FDM technology can apply to draw a design and quick manufacture.
ABS material, ABS, original name is acrylonitrile-butadiene-styrene copolymer, is the essential core of domestic fusion sediment (FDM) formula wire rod.From the properties of material, from the angle in hot junction, the relatively easy printing of ABS plastic.No matter use which type of extruder, all can extruded material relatively glidingly.ABS resilient enough, is suitable for making furnishings or ornament, as long as printing with suitable temperature, allows material layer by layer firmly stick, and the intensity of ABS will become at a relatively high.ABS has flexibility, also only can bend even if bearing pressure, will not fracture.
But this material has the characteristic of contract on cooling on the one hand, from local shedding hot plate, unsettled, can throw into question.If it addition, the object height printed is significantly high, sometimes also can flood peel off.Therefore, ABS prints and can not lack hot plate.It is uncomfortable that abnormal smells from the patient when printing on the other hand allows people have very much.
Along with development in science and technology and social progress, 3D printed product starts to be not limited only to industrial design, building, engineering and construction (AEC), automobile, Aero-Space, dentistry and medical industries, education, GIS-Geographic Information System, civil engineering, the fields such as gun, also begin to come into daily life, in order to make some living utensils or ornament, but the application in life is still embodied in the purposes that the shape of the product printed is brought at present, and the Art Design etc. that its color and shape are formed, the 3D application and development printed be there is also very big space, simultaneously in degradable rate, toughness and intensity all need to be further improved.
Summary of the invention
Goal of the invention: for prior art Problems existing, first technical problem to be solved by this invention is to provide has the multiple 3D printed material luring disinsection efficiency.Second to be solved by this invention technical problem is that this preparation method with the multiple 3D printed material luring disinsection efficiency.
Technical scheme: for solving above-mentioned technical problem, the invention provides and a kind of have the multiple 3D printed material luring disinsection efficiency, include following components according to parts by weight and make: ABS120~140 part;Light diffusing agent 2~8 parts;Initiator 2~8 parts;Cross-linking agent 10~20 parts;Coupling agent 10~20 parts;Concha Meretricis Seu Cyclinae powder 10~30 parts;Elemental sulfur 2~8 parts;Medical stone powder 1~4 part;Walnut shell ultrafine powder 1~4 part;Limonene 1~6 part;Plant toosedarin 4~20 parts;Stevia rebaudiana (Bertoni) Hemsl extract 2~8 parts;Sensitization discoloration toner 2~8 parts;Auxiliary agent 0.2~0.4 part.
It is further preferred that also include feather powder 2~8 parts according to parts by weight.
Preferably, described light diffusing agent is organosilicon light diffusing agent.
Preferably, described initiator is thermal initiator.
Preferably, described initiator is the mixture of light trigger and thermal initiator.
Preferably, described initiator includes following components according to parts by weight and makes: light trigger 1~3 part;Thermal initiator 1~5 part.
Preferably, described coupling agent is one or both the mixture in titanate coupling agent or silane coupler.
Preferably, described plant toosedarin is Parmelia tinctorum Despr. extract.
Preferably, described plant toosedarin is orcin.
Preferably, described auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.1~0.2 part;Toughener 0.1~0.2 part.
Invention also provides for the above-mentioned preparation method with the multiple 3D printed material luring disinsection efficiency, comprise the steps:
1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;
2) it is cooled to 20 DEG C~30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;
3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;
4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;
5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;
6) while ultra violet lamp 30~60min, stirring is put in extruder, is added hot-extrudable after being cooled to 50 DEG C~55 DEG C, and vacuum drying prepares target product.
As preferably, described step 3) be: by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, feather powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform.
Beneficial effect: provided by the invention have the multiple 3D printed material luring disinsection efficiency, significantly enhances the network structure of material, the 3D printed product good toughness made with this material on the one hand, and degradable rate is high;On the other hand by the synergism of initiator, Concha Meretricis Seu Cyclinae powder and elemental sulfur, alleviate the characteristic of ABS material contract on cooling, effectively reduce flood that may be present when ABS material prints and peel off the problem brought, promote plastotype quality;When in component, increase has feather powder further, initiator and elemental sulfur and feather powder synergism, incidental local shedding when can effectively overcome ABS material to print, unsettled or flood peel off the problem brought, further the printing plastotype quality of effective improving product.
nullUse the product that 3D printed material provided by the invention prints simultaneously,There is moulding own and on the basis of basic function that shape is brought,Photosensitive meeting variable color on the one hand,Namely under sunlight or ultraviolet irradiation change,Produce the change of molecular structure and absorbing wavelength,Thus producing the change of color or being reduced into original color,Increase interest,Available corresponding color and color change attract different types of fly worm near (yellow etc. that such as more winged insect is liked) targetedly on the other hand,Its component limonene of the third aspect and Stevia rebaudiana (Bertoni) Hemsl extract synergism,Make the product odour virtue sweet increase allure to fly worm printed,And limonene and plant toosedarin、Medical stone powder synergism makes the present invention have excellent antimicrobial and anti-inflammation efficacy concurrently,And fly worm sperm can be killed effectively suppress the breeding of worm's ovum,Therefore at abnormal smells from the patient、Under the multiple action of light color, the present invention has and well lures disinsection efficiency,Cleannes are high,Good scavenging free radicals effect and anti-radiation effect can be played simultaneously.Simultaneously limonene can also be effectively improved with the ABS 3D printed material the being raw material abnormal smells from the patient when carrying out high temperature print job, improves working environment;And with medical stone powder, plant toosedarin synergism, there is antioxidation, significantly improve antioxygenic property and the stability of 3D printed material provided by the invention further;Plus overall composition synergism so that the 3D printed product made with this material is homogeneous, and stress is uniform, it is easy to cutting plastotype, on the product that printing prepares, artificial microscopic carvings, cutting, plastotype provide better ease for use further.
The preparation method with the multiple 3D printed material luring disinsection efficiency provided by the invention simultaneously, limonene, Stevia rebaudiana (Bertoni) Hemsl extract and plant toosedarin is added by atomization in the process of high-speed stirred, and under ultra violet lamp, it is stirred cooling, improve stability and the non-oxidizability of obtained 3D printing consumables further.
Entirety extends service life, it is provided that a kind of 3D printed material new varieties select as required for user, from 3D printed material aspect, are greatly enlarged with the application development space of the ABS 3D printed material being primary raw material, and meaning is notable.
Detailed description of the invention
Embodiment 1: a kind of have the multiple 3D printed material luring disinsection efficiency, includes following components according to parts by weight and makes: ABS120 part;Light diffusing agent 2 parts;Initiator 2 parts;Cross-linking agent 10 parts;Coupling agent 10 parts;Concha Meretricis Seu Cyclinae powder 10 parts;Elemental sulfur 2 parts;Medical stone powder 1 part;Walnut shell ultrafine powder 1 part;Limonene 1 part;Plant toosedarin 4 parts;Stevia rebaudiana (Bertoni) Hemsl extract 2 parts;Sensitization discoloration toner 2 parts;Auxiliary agent 0.2 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein initiator includes following components according to parts by weight and makes: light trigger 1 part;Thermal initiator 1 part.
Wherein coupling agent is titanate coupling agent.
Wherein plant toosedarin is Parmelia tinctorum Despr. extract.
Wherein auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.1 part;Toughener 0.1 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;2) it is cooled to 20 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;6) while ultra violet lamp 30, stirring is put in extruder, is added hot-extrudable after being cooled to 50 DEG C, and vacuum drying prepares target product.After testing, the flexility of material reaches 82.2Mpa, notch impact strength reaches 47.8MJ/m2。
Embodiment 2: a kind of have the multiple 3D printed material luring disinsection efficiency, includes following components according to parts by weight and makes: ABS140 part;Light diffusing agent 8 parts;Initiator 8 parts;Cross-linking agent 20 parts;Coupling agent 20 parts;Concha Meretricis Seu Cyclinae powder 30 parts;Elemental sulfur 8 parts;Medical stone powder 4 parts;Walnut shell ultrafine powder 4 parts;Limonene 6 parts;Plant toosedarin 20 parts;Stevia rebaudiana (Bertoni) Hemsl extract 8 parts;Sensitization discoloration toner 8 parts;Auxiliary agent 0.4 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein initiator includes following components according to parts by weight and makes: light trigger 3 parts;Thermal initiator 5 parts.
Wherein coupling agent is silane coupler.
Wherein plant toosedarin is orcin.
Wherein auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.2 part;Toughener 0.2 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;2) it is cooled to 30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;6) while ultra violet lamp 60min, stirring is put in extruder, is added hot-extrudable after being cooled to 55 DEG C, and vacuum drying prepares target product.After testing, the flexility of material reaches 82.4Mpa, notch impact strength reaches 47.9MJ/m2。
Embodiment 3: a kind of have the multiple 3D printed material luring disinsection efficiency, includes following components according to parts by weight and makes: ABS130 part;Light diffusing agent 5 parts;Initiator 5 parts;Cross-linking agent 15 parts;Coupling agent 15 parts;Concha Meretricis Seu Cyclinae powder 20 parts;Elemental sulfur 5 parts;Medical stone powder 3 parts;Walnut shell ultrafine powder 2 parts;Feather powder 5 parts;Limonene 4 parts;Plant toosedarin 12 parts;Stevia rebaudiana (Bertoni) Hemsl extract 5 parts;Sensitization discoloration toner 5 parts;Auxiliary agent 0.3 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein initiator includes following components according to parts by weight and makes: thermal initiator 5 parts.
Wherein coupling agent is the mixture of titanate coupling agent and silane coupler, and ratio is 2:3.
Wherein plant toosedarin is Parmelia tinctorum Despr. extract.
Wherein auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.15 part;Toughener 0.15 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, feather powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;6) while ultra violet lamp 45min, stirring is put in extruder, is added hot-extrudable after being cooled to 52 DEG C, and vacuum drying prepares target product.After testing, the flexility of material reaches 83.8Mpa, notch impact strength reaches 48.8MJ/m2。
Embodiment 4: a kind of have the multiple 3D printed material luring disinsection efficiency, includes following components according to parts by weight and makes: ABS125 part;Light diffusing agent 3 parts;Initiator 3 parts;Cross-linking agent 12 parts;Coupling agent 12 parts;Concha Meretricis Seu Cyclinae powder 15 parts;Elemental sulfur 4 parts;Medical stone powder 2 parts;Walnut shell ultrafine powder 2 parts;Feather powder 4 parts;Limonene 2 parts;Plant toosedarin 8 parts;Stevia rebaudiana (Bertoni) Hemsl extract 4 parts;Sensitization discoloration toner 4 parts;Auxiliary agent 0.2 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein initiator includes following components according to parts by weight and makes: thermal initiator 3 parts.
Wherein coupling agent is titanate coupling agent.
Wherein plant toosedarin is Parmelia tinctorum Despr. extract.
Wherein auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.1 part;Toughener 0.1 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, feather powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;6) while ultra violet lamp 40min, stirring is put in extruder, is added hot-extrudable after being cooled to 50 DEG C, and vacuum drying prepares target product.
After testing, the flexility of material reaches 82.9Mpa, notch impact strength reaches 48.4MJ/m2。
Embodiment 5: a kind of have the multiple 3D printed material luring disinsection efficiency, includes following components according to parts by weight and makes: ABS135 part;Light diffusing agent 6 parts;Initiator 6 parts;Cross-linking agent 18 parts;Coupling agent 18 parts;Concha Meretricis Seu Cyclinae powder 25 parts;Elemental sulfur 6 parts;Medical stone powder 3 parts;Walnut shell ultrafine powder 3 parts;Feather powder 6 parts;Limonene 4 parts;Plant toosedarin 16 parts;Stevia rebaudiana (Bertoni) Hemsl extract 6 parts;Sensitization discoloration toner 6 parts;Auxiliary agent 0.4 part.
Wherein light diffusing agent is organosilicon light diffusing agent.
Wherein initiator includes following components according to parts by weight and makes: light trigger 2 parts;Thermal initiator 4 parts.
Wherein coupling agent is the mixture of titanate coupling agent and silane coupler.
Wherein plant toosedarin is orcin.
Wherein auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.2 part;Toughener 0.2 part.
Preparation method comprises the steps: 1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;2) it is cooled to 25 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, feather powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;6) while ultra violet lamp 50min, stirring is put in extruder, is added hot-extrudable after being cooled to 55 DEG C, and vacuum drying prepares target product.After testing, the flexility of material reaches 82.6Mpa, notch impact strength reaches 48.2MJ/m2。
More than implementing row and the present invention does not constitute restriction, relevant staff is in the scope not necessarily departing from the technology of the present invention thought, and what carry out various changes and modifications, and all falls within protection scope of the present invention.
Claims (9)
1. one kind has the multiple 3D printed material luring disinsection efficiency, it is characterised in that includes following components according to parts by weight and makes: ABS120~140 part;Light diffusing agent 2~8 parts;Initiator 2~8 parts;Cross-linking agent 10~20 parts;Coupling agent 10~20 parts;Concha Meretricis Seu Cyclinae powder 10~30 parts;Elemental sulfur 2~8 parts;Medical stone powder 1~4 part;Walnut shell ultrafine powder 1~4 part;Limonene 1~6 part;Plant toosedarin 4~20 parts;Stevia rebaudiana (Bertoni) Hemsl extract 2~8 parts;Sensitization discoloration toner 2~8 parts;Auxiliary agent 0.2~0.4 part.
2. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that also include feather powder 2~8 parts according to parts by weight.
3. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that described light diffusing agent is organosilicon light diffusing agent.
4. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that described initiator includes following components according to parts by weight and makes: light trigger 1~3 part;Thermal initiator 1~5 part.
5. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that described plant toosedarin is Parmelia tinctorum Despr. extract.
6. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that described plant toosedarin is orcin.
7. according to claim 1 have the multiple 3D printed material luring disinsection efficiency, it is characterised in that described auxiliary agent includes following components according to parts by weight and makes: plasticizer 0.1~0.2 part;Toughener 0.1~0.2 part.
8. the preparation method with the multiple 3D printed material luring disinsection efficiency as described in claim 1~7, it is characterised in that comprise the steps:
1) ABS particle high-temperature is melted, add initiator and cross-linking agent mixes, grafting;
2) it is cooled to 20 DEG C~30 DEG C after stirring, puts into extruder, heating, extrusion, pulverize and obtain preparing the ABS powder of graft crosslinking agent;
3) by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform;
4) by step 3) gains are continue to be mixed and stirred for uniform while, and mixing adds the limonene of corresponding parts by weight, Stevia rebaudiana (Bertoni) Hemsl extract and the plant toosedarin that process through atomization successively;
5) then add sensitization discoloration toner and the light diffusing agent of corresponding parts by weight, continue to be mixed and stirred for uniformly;
6) while ultra violet lamp 30~60min, stirring is put in extruder, is added hot-extrudable after being cooled to 50 DEG C~55 DEG C, and vacuum drying prepares target product.
9. the preparation method with the multiple 3D printed material luring disinsection efficiency according to claim 8, it is characterized in that, described step 3) be: by step 2) the ABS powder that obtains and the Concha Meretricis Seu Cyclinae powder of corresponding parts by weight, elemental sulfur, walnut shell ultrafine powder, feather powder, medical stone powder, coupling agent and auxiliary agent, heating mixing high-speed stirred are uniform.