CN105983327B - 一种甲醛清除剂的制备方法 - Google Patents
一种甲醛清除剂的制备方法 Download PDFInfo
- Publication number
- CN105983327B CN105983327B CN201610574948.7A CN201610574948A CN105983327B CN 105983327 B CN105983327 B CN 105983327B CN 201610574948 A CN201610574948 A CN 201610574948A CN 105983327 B CN105983327 B CN 105983327B
- Authority
- CN
- China
- Prior art keywords
- solution
- water
- formaldehyde
- butyl titanate
- certain amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种甲醛清除剂的制备方法，其技术方案包括：首先，在一定量浓硝酸中依次加入有机钛酸盐、硝酸锌以及氯化锡，剧烈搅拌，得到溶液A；其次，在一定量水中，加入表面活性剂萘磺酸钠、助剂聚乙二醇以及氧化石墨烯，水浴升温、搅拌，得到溶液B；然后，将溶液B倒入溶液A中，水浴控温，混合静置一段时间后，得到溶液C；再次，将溶液C自然冷却至室温，滴加液碱溶液调节溶液pH值至中性，经过滤、去离子水洗涤得到滤饼D；最后，将滤饼D溶于一定量水中，加入尿素和茶多酚，搅拌一段时间后，超声分散，制得甲醛去除剂溶液E。该甲醛去除剂综合催化分解、氧化还原、封闭封堵等机理，能有效去除甲醛。
Description
技术领域
本发明涉及环保净化剂技术领域，具体涉及一种甲醛清除剂的制备方法。
背景技术
甲醛，是一种无色气体，有特殊刺激性气味，对人体具有严重的危害性，例如：刺激人的皮肤、呼吸道、致突变性、致癌变等。目前已经引起了人类广泛的重视，但是在日常生活中，甲醛普遍存在于装修、装饰材料中，与人们生活密切相关，去除材料中的甲醛已成为一种必然趋势。
甲醛清除剂的作用原理通常包括中和反应类、催化分解类、氧化还原类、封闭封堵类。大多数专利通常是采用其中的一种机理，例如：CN 105727494A以聚葵二酸葵二胺、聚丙烯酰胺、植物提取液为有效成份，制备了甲醛清除剂；CN 101274281 A报道了一种室温去除空气中甲醛催化剂及其制备方法，将甲醛氧化为H2O和CO2。
因此，寻找一种绿色、环保、高效的甲醛清除剂，已成为环保材料领域的一种迫切需求。
发明内容
本发明的目的在于：提供一种甲醛去除剂及其制备方法，结合无机材料的优良性质及有机化学改性技术，快速批量制备复合二氧化钛、氧化锌、氧化锡、氧化石墨烯、表面活性剂萘磺酸钠、聚乙二醇、茶多酚、聚乙烯醇以及尿素的甲醛去除剂。
本发明的技术方案：首先，在一定量浓硝酸中依次加入有机钛酸盐、硝酸锌以及氯化锡，剧烈搅拌，得到溶液A；其次，在一定量水中，加入表面活性剂萘磺酸钠、助剂聚乙二醇以及氧化石墨烯，水浴升温、搅拌，得到溶液B；然后，将溶液B倒入溶液A中，水浴控温，混合静置一段时间后，得到溶液C；再次，将溶液C自然冷却至室温，滴加液碱溶液调节溶液pH值至中性，经过滤、去离子水洗涤得到滤饼D；最后，将滤饼D溶于一定量水中，加入尿素和茶多酚，搅拌一段时间后，超声分散，制得甲醛去除剂溶液E。
本发明与现有技术相比，具有显著优点：其一、该甲醛去除剂以氧化石墨烯为吸附剂，对甲醛具有较强吸附能力；其二、该甲醛去除剂复合了氧化钛、氧化锌、氧化锡，尿素和茶多酚，能有效去除甲醛；其三、该甲醛去除剂使用便携，应用范围广泛。
具体实施方式
下面结合具体实施例说明本发明的技术解决方案，这些实施例不能理解为对技术方案的限制。
实施例1：依以下具体步骤制备一种甲醛清除剂。
步骤1、在100mL60%浓度硝酸中，依次加入90g钛酸丁酯、4.8g六水合硝酸锌以及0.15g氯化锡，剧烈搅拌2h，得到溶液A；
步骤2、在100mL水中，加入2.8g表面活性剂α-萘磺酸钠、0.9g助剂聚乙二醇以及0.5g氧化石墨烯，水浴升温至60oC、搅拌1h，得到溶液B；
步骤3、将溶液B倒入溶液A中，水浴控温60oC，混合静置24h，得到溶液C；
步骤4、将溶液C自然冷却至室温，滴加质量浓度30%的液碱溶液，调节溶液pH值至中性，经过滤、去离子水洗涤两遍，得到滤饼D；
步骤5、将50g滤饼D溶于1000mL水中，加入5g尿素和10g茶多酚，搅拌1h后，超声分散3h，制得甲醛去除剂溶液E。
实施例2：依以下具体步骤制备一种甲醛清除剂。
步骤1、在100mL60%浓度硝酸中，依次加入90g钛酸丁酯、9.6g六水合硝酸锌以及0.3g氯化锡，剧烈搅拌4h，得到溶液A；
步骤2、在100mL水中，加入4.6g表面活性剂β-萘磺酸钠、2.8g助剂聚乙二醇以及1.5g氧化石墨烯，水浴升温至80oC、搅拌2h，得到溶液B；
步骤3、将溶液B倒入溶液A中，水浴控温80oC，混合静置48h，得到溶液C；
步骤4、将溶液C自然冷却至室温，滴加质量浓度30%的液碱溶液，调节溶液pH值至中性，经过滤、去离子水洗涤两遍，得到滤饼D；
步骤5、将80g滤饼D溶于1000mL水中，加入10g尿素和20g茶多酚，搅拌2h后，超声分散6h，制得甲醛去除剂溶液E。
实施例3：依以下具体步骤制备一种甲醛清除剂。
步骤1、在100mL60%浓度硝酸中，依次加入90g钛酸丁酯、6g六水合硝酸锌以及0.2g氯化锡，剧烈搅拌3h，得到溶液A；
步骤2、在100mL水中，加入3.5g表面活性剂β-萘磺酸钠、2.0g助剂聚乙二醇以及1.2g氧化石墨烯，水浴升温至70oC、搅拌1.5h，得到溶液B；
步骤3、将溶液B倒入溶液A中，水浴控温70oC，混合静置36h，得到溶液C；
步骤4、将溶液C自然冷却至室温，滴加质量浓度30%的液碱溶液，调节溶液pH值至中性，经过滤、去离子水洗涤两遍，得到滤饼D；
步骤5、将60g滤饼D溶于1000mL水中，加入7g尿素和20g茶多酚，搅拌1.5h后，超声分散4h，制得甲醛去除剂溶液E。
Claims (4)
1.一种甲醛清除剂的制备方法，其特征在于包含以下步骤：
第一步、在一定量质量浓度为60%的浓度硝酸中，依次加入钛酸丁酯、六水合硝酸锌以及氯化锡，剧烈搅拌2h-4h，得到溶液A；
第二步、在一定量水中，加入表面活性剂萘磺酸钠、助剂聚乙二醇以及氧化石墨烯，水浴升温至60oC-80oC、搅拌1h-2h，得到溶液B；
第三步、将溶液B倒入溶液A中，水浴控温60oC-80oC，混合静置24h-48h，得到溶液C；
第四步、将溶液C自然冷却至室温，滴加质量浓度30%的液碱溶液，调节溶液pH值至中性，经过滤、去离子水洗涤两遍，得到滤饼D；
第五步、将滤饼D溶于一定量水中，加入尿素和茶多酚，搅拌1h-2h后，超声分散3h-6h，制得甲醛去除剂溶液E。
2.根据权利要求1所述的一种甲醛清除剂的制备方法，其特征在于：溶液A中，钛酸丁酯占浓硝酸的摩尔比为20%，六水合硝酸锌占钛酸丁酯的摩尔比为3%-6%，氯化锡占钛酸丁酯的摩尔比为1.5%-3%。
3.根据权利要求1所述的一种甲醛清除剂的制备方法，其特征在于：溶液B中，萘磺酸钠任选α-萘磺酸钠或β-萘磺酸钠，其占钛酸丁酯的质量比为3%-5%，聚乙二醇占钛酸丁酯的质量比为1%-3%，氧化石墨烯占钛酸丁酯的质量比为0.5%-1.5%。
4.根据权利要求1所述的一种甲醛清除剂的制备方法，其特征在于：溶液E中，滤饼D占水的质量比为5%-8%，尿素和茶多酚分别占水的质量比为0.5%-1%和1%-3%。