CN105968979A - Outdoor communication cabinet coating - Google Patents
Outdoor communication cabinet coating Download PDFInfo
- Publication number
- CN105968979A CN105968979A CN201610486354.0A CN201610486354A CN105968979A CN 105968979 A CN105968979 A CN 105968979A CN 201610486354 A CN201610486354 A CN 201610486354A CN 105968979 A CN105968979 A CN 105968979A
- Authority
- CN
- China
- Prior art keywords
- parts
- communication cabinet
- outdoor communication
- powder
- cabinet coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an outdoor communication cabinet coating. The outdoor communication cabinet coating comprises PVC (polyvinyl chloride) resin, tricresyl phosphate, aluminum hydroxide powder, trioctyl trimellitate, zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, dibasic lead phthalate, polyamide-imide, potassium sorbate, styrene-acrylic emulsion, cogon elements, diatomaceous earth, melamine cyanurate, styrenated phenol, oxadixyl mancozeb, vancomycin, sodium diacetate, isophthalic acid alkyd resin, cyclohexanone, lumisterol, aluminum stearate, stearin, nitrocotton, citronellyl formate, epoxidized soybean oil, montmorillonite, polycarbonate, lead phosphite, triethyl citrate, fluorine ether rubber, sodium allysulfonate, wollastonite powder and tri-beta-chloroethyl phosphate. The outdoor communication cabinet coating has the advantages that the outdoor communication cabinet coating is excellent in flame-retardant, acid-resistant, alkali-resistant, anti-mildew and antibacterial performance, and the performance of the outdoor communication cabinet coating can be improved.
Description
Technical field
The present invention relates to a kind of outdoor communication cabinet coating, belong to communication cabinet technical field.
Background technology
Outdoor communication cabinet is the one of outdoor cabinet, under the influence of referring to be directly in natural climate, it is made up of metal or nonmetallic materials, do not allow lack of competence operator to enter the cabinet of operation, provide outdoor physical working environment and the equipment of security system for radio communication website or cable network site works station.Outdoor communication cabinet needs to use suitable coating material to be protected, in order to use the most out of doors.
Summary of the invention
It is an object of the invention to provide a kind of outdoor communication cabinet coating, in order to the function of outdoor communication cabinet coating is better achieved.
To achieve these goals, technical scheme is as follows.
nullA kind of outdoor communication cabinet coating,It is made up of the component of following mass fraction: polyvinyl chloride resin 16~20 parts、Tricresyl phosphate 18~22 parts、Aluminium-hydroxide powder 14~18 parts、Trioctyl trimellitate (TOTM) 12~16 parts、Zinc oxide powder 18~22 parts、Parachlorometaxylenol 14~18 parts、Hydroxypropyl starch ether 12~16 parts、Dythal 18~22 parts、Polyamidoimide 14~18 parts、Potassium sorbate 12~16 parts、Styrene-acrylic emulsion 18~22 parts、Cylindrin 14~18 parts、Kieselguhr 14~18 parts、Melamine cyanurate 12~16 parts、Styrenated phenol 18~22 parts、Sandofan 14~18 parts、Vancomycin 12~16 parts、Sodium diacetate 18~22 parts、Isophthalic alkyd resin 14~18 parts、Ketohexamethylene 12~16 parts、Lumisterol 18~22 parts、Aluminium stearate 14~18 parts、Tristerin 12~16 parts、Nitrocotton 18~22 parts、Citronellyl formate 14~18 parts、Epoxy soybean oil 14~18 parts、Montmorillonite 14~18 parts、Merlon 14~18 parts、Dibasic lead phosphite 14~18 parts、Triethyl citrate 14~18 parts、Fluoroether rubber 14~18 parts、Sodium allylsulfonate 14~18 parts、Wollastonite in powder 14~18 parts、Trichloroethyl phosphate 14~18 parts.
nullFurther,Above-mentioned outdoor communication cabinet coating,It is made up of the component of following mass fraction: polyvinyl chloride resin 16 parts、Tricresyl phosphate 18 parts、Aluminium-hydroxide powder 14 parts、Trioctyl trimellitate (TOTM) 12 parts、Zinc oxide powder 18 parts、Parachlorometaxylenol 14 parts、Hydroxypropyl starch ether 12 parts、Dythal 18 parts、Polyamidoimide 14 parts、Potassium sorbate 12 parts、Styrene-acrylic emulsion 18 parts、Cylindrin 14 parts、14 parts of kieselguhr、Melamine cyanurate 12 parts、Styrenated phenol 18 parts、Sandofan 14 parts、Vancomycin 12 parts、Sodium diacetate 18 parts、Isophthalic alkyd resin 14 parts、Ketohexamethylene 12 parts、Lumisterol 18 parts、Aluminium stearate 14 parts、Tristerin 12 parts、Nitrocotton 18 parts、Citronellyl formate 14 parts、Epoxy soybean oil 14 parts、Montmorillonite 14 parts、Merlon 14 parts、Dibasic lead phosphite 14 parts、Triethyl citrate 14 parts、Fluoroether rubber 14 parts、Sodium allylsulfonate 14 parts、Wollastonite in powder 14 parts、Trichloroethyl phosphate 14 parts.
nullFurther,Above-mentioned outdoor communication cabinet coating,It is made up of the component of following mass fraction: polyvinyl chloride resin 18 parts、Tricresyl phosphate 20 parts、Aluminium-hydroxide powder 16 parts、Trioctyl trimellitate (TOTM) 14 parts、Zinc oxide powder 20 parts、Parachlorometaxylenol 16 parts、Hydroxypropyl starch ether 14 parts、Dythal 20 parts、Polyamidoimide 16 parts、Potassium sorbate 14 parts、Styrene-acrylic emulsion 20 parts、Cylindrin 16 parts、16 parts of kieselguhr、Melamine cyanurate 14 parts、Styrenated phenol 20 parts、Sandofan 16 parts、Vancomycin 14 parts、Sodium diacetate 20 parts、Isophthalic alkyd resin 16 parts、Ketohexamethylene 14 parts、Lumisterol 20 parts、Aluminium stearate 16 parts、Tristerin 14 parts、Nitrocotton 20 parts、Citronellyl formate 16 parts、Epoxy soybean oil 16 parts、Montmorillonite 16 parts、Merlon 16 parts、Dibasic lead phosphite 16 parts、Triethyl citrate 16 parts、Fluoroether rubber 16 parts、Sodium allylsulfonate 16 parts、Wollastonite in powder 16 parts、Trichloroethyl phosphate 16 parts.
nullFurther,Above-mentioned outdoor communication cabinet coating,It is made up of the component of following mass fraction: polyvinyl chloride resin 20 parts、Tricresyl phosphate 22 parts、Aluminium-hydroxide powder 18 parts、Trioctyl trimellitate (TOTM) 16 parts、Zinc oxide powder 22 parts、Parachlorometaxylenol 18 parts、Hydroxypropyl starch ether 16 parts、Dythal 22 parts、Polyamidoimide 18 parts、Potassium sorbate 16 parts、Styrene-acrylic emulsion 22 parts、Cylindrin 18 parts、18 parts of kieselguhr、Melamine cyanurate 16 parts、Styrenated phenol 22 parts、Sandofan 18 parts、Vancomycin 16 parts、Sodium diacetate 22 parts、Isophthalic alkyd resin 18 parts、Ketohexamethylene 16 parts、Lumisterol 22 parts、Aluminium stearate 18 parts、Tristerin 16 parts、Nitrocotton 22 parts、Citronellyl formate 18 parts、Epoxy soybean oil 18 parts、Montmorillonite 18 parts、Merlon 18 parts、Dibasic lead phosphite 18 parts、Triethyl citrate 18 parts、Fluoroether rubber 18 parts、Sodium allylsulfonate 18 parts、Wollastonite in powder 18 parts、Trichloroethyl phosphate 18 parts.
Further, above-mentioned outdoor communication cabinet coating production step is as follows:
(1) by the polyvinyl chloride resin of described mass fraction, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20~40KHz, rate of dispersion 5000~about 5400r/min, jitter time is 30~60min;
(2) melamine cyanurate of described mass fraction, styrenated phenol, Sandofan, vancomycin, sodium diacetate are added, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, rate of dispersion 4800~about 5200r/min, and jitter time is 30~50min;
(3) adding the kieselguhr of described mass fraction, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, rate of dispersion 4600~about 4800r/min, and jitter time is 20~40min;This product is prepared after mix homogeneously.
This beneficial effect of the invention is: the present invention relates to a kind of outdoor communication cabinet coating, composed of the following components: polyvinyl chloride resin, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, kieselguhr, melamine cyanurate, styrenated phenol, Sandofan, vancomycin, sodium diacetate, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate.This outdoor communication cabinet preparation technology of coating method is simple, and prepared product has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment
1
nullOutdoor communication cabinet coating in the present embodiment,It is made up of the component of following mass fraction: polyvinyl chloride resin 16 parts、Tricresyl phosphate 18 parts、Aluminium-hydroxide powder 14 parts、Trioctyl trimellitate (TOTM) 12 parts、Zinc oxide powder 18 parts、Parachlorometaxylenol 14 parts、Hydroxypropyl starch ether 12 parts、Dythal 18 parts、Polyamidoimide 14 parts、Potassium sorbate 12 parts、Styrene-acrylic emulsion 18 parts、Cylindrin 14 parts、14 parts of kieselguhr、Melamine cyanurate 12 parts、Styrenated phenol 18 parts、Sandofan 14 parts、Vancomycin 12 parts、Sodium diacetate 18 parts、Isophthalic alkyd resin 14 parts、Ketohexamethylene 12 parts、Lumisterol 18 parts、Aluminium stearate 14 parts、Tristerin 12 parts、Nitrocotton 18 parts、Citronellyl formate 14 parts、Epoxy soybean oil 14 parts、Montmorillonite 14 parts、Merlon 14 parts、Dibasic lead phosphite 14 parts、Triethyl citrate 14 parts、Fluoroether rubber 14 parts、Sodium allylsulfonate 14 parts、Wollastonite in powder 14 parts、Trichloroethyl phosphate 14 parts.
Above-mentioned outdoor communication cabinet coating production step is as follows:
(1) by the polyvinyl chloride resin of described mass fraction, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) adding the melamine cyanurate of described mass fraction, styrenated phenol, Sandofan, vancomycin, sodium diacetate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) adding the kieselguhr of described mass fraction, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min;This product is prepared after mix homogeneously.
Embodiment
2
nullOutdoor communication cabinet coating in the present embodiment,It is made up of the component of following mass fraction: polyvinyl chloride resin 18 parts、Tricresyl phosphate 20 parts、Aluminium-hydroxide powder 16 parts、Trioctyl trimellitate (TOTM) 14 parts、Zinc oxide powder 20 parts、Parachlorometaxylenol 16 parts、Hydroxypropyl starch ether 14 parts、Dythal 20 parts、Polyamidoimide 16 parts、Potassium sorbate 14 parts、Styrene-acrylic emulsion 20 parts、Cylindrin 16 parts、16 parts of kieselguhr、Melamine cyanurate 14 parts、Styrenated phenol 20 parts、Sandofan 16 parts、Vancomycin 14 parts、Sodium diacetate 20 parts、Isophthalic alkyd resin 16 parts、Ketohexamethylene 14 parts、Lumisterol 20 parts、Aluminium stearate 16 parts、Tristerin 14 parts、Nitrocotton 20 parts、Citronellyl formate 16 parts、Epoxy soybean oil 16 parts、Montmorillonite 16 parts、Merlon 16 parts、Dibasic lead phosphite 16 parts、Triethyl citrate 16 parts、Fluoroether rubber 16 parts、Sodium allylsulfonate 16 parts、Wollastonite in powder 16 parts、Trichloroethyl phosphate 16 parts.
Above-mentioned outdoor communication cabinet coating production step is as follows:
(1) by the polyvinyl chloride resin of described mass fraction, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) adding the melamine cyanurate of described mass fraction, styrenated phenol, Sandofan, vancomycin, sodium diacetate, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) adding the kieselguhr of described mass fraction, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min;This product is prepared after mix homogeneously.
Embodiment
3
nullOutdoor communication cabinet coating in the present embodiment,It is made up of the component of following mass fraction: polyvinyl chloride resin 20 parts、Tricresyl phosphate 22 parts、Aluminium-hydroxide powder 18 parts、Trioctyl trimellitate (TOTM) 16 parts、Zinc oxide powder 22 parts、Parachlorometaxylenol 18 parts、Hydroxypropyl starch ether 16 parts、Dythal 22 parts、Polyamidoimide 18 parts、Potassium sorbate 16 parts、Styrene-acrylic emulsion 22 parts、Cylindrin 18 parts、18 parts of kieselguhr、Melamine cyanurate 16 parts、Styrenated phenol 22 parts、Sandofan 18 parts、Vancomycin 16 parts、Sodium diacetate 22 parts、Isophthalic alkyd resin 18 parts、Ketohexamethylene 16 parts、Lumisterol 22 parts、Aluminium stearate 18 parts、Tristerin 16 parts、Nitrocotton 22 parts、Citronellyl formate 18 parts、Epoxy soybean oil 18 parts、Montmorillonite 18 parts、Merlon 18 parts、Dibasic lead phosphite 18 parts、Triethyl citrate 18 parts、Fluoroether rubber 18 parts、Sodium allylsulfonate 18 parts、Wollastonite in powder 18 parts、Trichloroethyl phosphate 18 parts.
Above-mentioned outdoor communication cabinet coating production step is as follows:
(1) by the polyvinyl chloride resin of described mass fraction, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) adding the melamine cyanurate of described mass fraction, styrenated phenol, Sandofan, vancomycin, sodium diacetate, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) adding the kieselguhr of described mass fraction, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min;This product is prepared after mix homogeneously.
Carrying out performance measurement for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
- null1. an outdoor communication cabinet coating,It is characterized in that: be made up of the component of following mass fraction: polyvinyl chloride resin 16~20 parts、Tricresyl phosphate 18~22 parts、Aluminium-hydroxide powder 14~18 parts、Trioctyl trimellitate (TOTM) 12~16 parts、Zinc oxide powder 18~22 parts、Parachlorometaxylenol 14~18 parts、Hydroxypropyl starch ether 12~16 parts、Dythal 18~22 parts、Polyamidoimide 14~18 parts、Potassium sorbate 12~16 parts、Styrene-acrylic emulsion 18~22 parts、Cylindrin 14~18 parts、Kieselguhr 14~18 parts、Melamine cyanurate 12~16 parts、Styrenated phenol 18~22 parts、Sandofan 14~18 parts、Vancomycin 12~16 parts、Sodium diacetate 18~22 parts、Isophthalic alkyd resin 14~18 parts、Ketohexamethylene 12~16 parts、Lumisterol 18~22 parts、Aluminium stearate 14~18 parts、Tristerin 12~16 parts、Nitrocotton 18~22 parts、Citronellyl formate 14~18 parts、Epoxy soybean oil 14~18 parts、Montmorillonite 14~18 parts、Merlon 14~18 parts、Dibasic lead phosphite 14~18 parts、Triethyl citrate 14~18 parts、Fluoroether rubber 14~18 parts、Sodium allylsulfonate 14~18 parts、Wollastonite in powder 14~18 parts、Trichloroethyl phosphate 14~18 parts.
- nullOutdoor communication cabinet coating the most according to claim 1,It is characterized in that: described outdoor communication cabinet coating is made up of the component of following mass fraction: polyvinyl chloride resin 16 parts、Tricresyl phosphate 18 parts、Aluminium-hydroxide powder 14 parts、Trioctyl trimellitate (TOTM) 12 parts、Zinc oxide powder 18 parts、Parachlorometaxylenol 14 parts、Hydroxypropyl starch ether 12 parts、Dythal 18 parts、Polyamidoimide 14 parts、Potassium sorbate 12 parts、Styrene-acrylic emulsion 18 parts、Cylindrin 14 parts、14 parts of kieselguhr、Melamine cyanurate 12 parts、Styrenated phenol 18 parts、Sandofan 14 parts、Vancomycin 12 parts、Sodium diacetate 18 parts、Isophthalic alkyd resin 14 parts、Ketohexamethylene 12 parts、Lumisterol 18 parts、Aluminium stearate 14 parts、Tristerin 12 parts、Nitrocotton 18 parts、Citronellyl formate 14 parts、Epoxy soybean oil 14 parts、Montmorillonite 14 parts、Merlon 14 parts、Dibasic lead phosphite 14 parts、Triethyl citrate 14 parts、Fluoroether rubber 14 parts、Sodium allylsulfonate 14 parts、Wollastonite in powder 14 parts、Trichloroethyl phosphate 14 parts.
- null3. according to the outdoor communication cabinet coating described in claim 1 to 2,It is characterized in that: described outdoor communication cabinet coating is made up of the component of following mass fraction: polyvinyl chloride resin 18 parts、Tricresyl phosphate 20 parts、Aluminium-hydroxide powder 16 parts、Trioctyl trimellitate (TOTM) 14 parts、Zinc oxide powder 20 parts、Parachlorometaxylenol 16 parts、Hydroxypropyl starch ether 14 parts、Dythal 20 parts、Polyamidoimide 16 parts、Potassium sorbate 14 parts、Styrene-acrylic emulsion 20 parts、Cylindrin 16 parts、16 parts of kieselguhr、Melamine cyanurate 14 parts、Styrenated phenol 20 parts、Sandofan 16 parts、Vancomycin 14 parts、Sodium diacetate 20 parts、Isophthalic alkyd resin 16 parts、Ketohexamethylene 14 parts、Lumisterol 20 parts、Aluminium stearate 16 parts、Tristerin 14 parts、Nitrocotton 20 parts、Citronellyl formate 16 parts、Epoxy soybean oil 16 parts、Montmorillonite 16 parts、Merlon 16 parts、Dibasic lead phosphite 16 parts、Triethyl citrate 16 parts、Fluoroether rubber 16 parts、Sodium allylsulfonate 16 parts、Wollastonite in powder 16 parts、Trichloroethyl phosphate 16 parts.
- null4. according to the outdoor communication cabinet coating described in claims 1 to 3,It is characterized in that: described outdoor communication cabinet coating is made up of the component of following mass fraction: polyvinyl chloride resin 20 parts、Tricresyl phosphate 22 parts、Aluminium-hydroxide powder 18 parts、Trioctyl trimellitate (TOTM) 16 parts、Zinc oxide powder 22 parts、Parachlorometaxylenol 18 parts、Hydroxypropyl starch ether 16 parts、Dythal 22 parts、Polyamidoimide 18 parts、Potassium sorbate 16 parts、Styrene-acrylic emulsion 22 parts、Cylindrin 18 parts、18 parts of kieselguhr、Melamine cyanurate 16 parts、Styrenated phenol 22 parts、Sandofan 18 parts、Vancomycin 16 parts、Sodium diacetate 22 parts、Isophthalic alkyd resin 18 parts、Ketohexamethylene 16 parts、Lumisterol 22 parts、Aluminium stearate 18 parts、Tristerin 16 parts、Nitrocotton 22 parts、Citronellyl formate 18 parts、Epoxy soybean oil 18 parts、Montmorillonite 18 parts、Merlon 18 parts、Dibasic lead phosphite 18 parts、Triethyl citrate 18 parts、Fluoroether rubber 18 parts、Sodium allylsulfonate 18 parts、Wollastonite in powder 18 parts、Trichloroethyl phosphate 18 parts.
- Outdoor communication cabinet coating the most according to claim 1, it is characterised in that: described outdoor communication cabinet coating production step is as follows:(1) by the polyvinyl chloride resin of described mass fraction, tricresyl phosphate, aluminium-hydroxide powder, trioctyl trimellitate (TOTM), Zinc oxide powder, parachlorometaxylenol, hydroxypropyl starch ether, Dythal, polyamidoimide, potassium sorbate, styrene-acrylic emulsion, Cylindrin, tristerin, nitrocotton, citronellyl formate, epoxy soybean oil, montmorillonite, Merlon, dibasic lead phosphite, triethyl citrate, fluoroether rubber, sodium allylsulfonate, wollastonite in powder, trichloroethyl phosphate is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20~40KHz, rate of dispersion about 5000~5400r/min, jitter time is 30~about 60min;(2) melamine cyanurate of described mass fraction, styrenated phenol, Sandofan, vancomycin, sodium diacetate are added, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, and rate of dispersion is about 4800~5200r/min, and jitter time is 30~about 50min;(3) kieselguhr of described mass fraction, isophthalic alkyd resin, Ketohexamethylene, lumisterol, aluminium stearate are added, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, and rate of dispersion is about 4600~4800r/min, and jitter time is 20~about 40min;This product is prepared after mix homogeneously.