CN106398403A - Smart home furniture coating - Google Patents
Smart home furniture coating Download PDFInfo
- Publication number
- CN106398403A CN106398403A CN201611118305.8A CN201611118305A CN106398403A CN 106398403 A CN106398403 A CN 106398403A CN 201611118305 A CN201611118305 A CN 201611118305A CN 106398403 A CN106398403 A CN 106398403A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- smart home
- home furniture
- furniture coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a smart home furniture coating. The smart home furniture coating consists of the following components: hydrogenated butadiene-acrylonitrile rubber, fluorosilicone rubber, ethylene propylene rubber, isobutyltriethoxy silane, epoxy chloropropane, butyl acetate, hydrogenated castor oil, citronellyl formate, zinc pyrithione, hexadecyl trimethyl ammonium bromide, allylthiourea, butylparaben, diboron trioxide powder, molybdenum trioxide powder, asbestos fiber, quartz powder, titanium dioxide, calcium carbide powder, boron carbide powder, potassium carbonate powder, pyromellitic dianhydride, hexahydrophthalic anhydride, triethylene glycol diisooctoate, aluminum stearate, sodium polystyrenesulfonate, sodium dodecyl benzene sulfonate, magnesium stearate, isophorone diisocyanate, ethylparaben and dibasic lead sulfate. The smart home furniture coating provided by the invention has relatively excellent flame retardance, acid-base resistance and anti-mildew and antibacterial properties; and the product performance is improved.
Description
Technical field
The present invention relates to a kind of smart home furniture coating, belong to smart home technical field of furniture.
Background technology
Smart home is with house as platform, using comprehensive wiring technology, the network communications technology, security precautions technology, from
Dynamic control technology, audio frequency and video technology will be integrated for facility relevant for life staying idle at home, build efficient housing facilities and family's schedule thing
The management system of business, lifting house security, convenience, comfortableness, artistry, and realize the living environment of environmental protection and energy saving.Intelligence
Furniture in energy household is necessary to suitable coating and is protected, preferably to improve using effect as needed.
Content of the invention
It is an object of the invention to provide a kind of smart home furniture coating, smart home furniture is better achieved to apply
The use function of layer, makes product have fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves product serviceability.
To achieve these goals, technical scheme is as follows.
A kind of smart home furniture coating, is grouped into by the group of following mass fraction：26～30 parts of hydrogenated nitrile-butadiene rubber, fluorine
24～28 parts of silicon rubber, 24～28 parts of EP rubbers, 22～26 parts of isobutyl triethoxy silane, epoxychloropropane 24～28
Part, 24～28 parts of butyl acetate, 22～26 parts of rilanit special, 24～28 parts of citronellyl formate, 24～28 parts of ZPT,
22～26 parts of cetyl trimethylammonium bromide, 22～26 parts of allylthiourea, 22～26 parts of butyl hydroxybenzoate, diboron trioxide
24～28 parts of powder, 22～26 parts of molybdenum trioxide powder, 20～24 parts of asbestos fibre, 24～28 parts of quartz powder, titanium dioxide 22
～26 parts, 20～24 parts of carbonization calcium powder, 22～26 parts of boron carbide powder, 20～24 parts of potassium carbonate powder, Pyromellitic Acid two
20～24 parts of acid anhydride, 20～24 parts of hexahydro phthalic anhydride, 18～22 parts of triethylene glycol two tricaprylate, aluminum stearate 14～18
Part, 12～16 parts of kayexalate, 12～16 parts of neopelex, 12～16 parts of magnesium stearate, isophorone
12～16 parts of diisocyanate, 12～16 parts of ethylparaben, 12～16 parts of second base lead sulfate.
Further, above-mentioned smart home furniture coating, is grouped into by the group of following mass fraction：Hydrogenated nitrile-butadiene rubber 26
Part, 24 parts of fluorosioloxane rubber, 24 parts of EP rubbers, 22 parts of isobutyl triethoxy silane, 24 parts of epoxychloropropane, butyl acetate 24
Part, 22 parts of rilanit special, 24 parts of citronellyl formate, 24 parts of ZPT, 22 parts of cetyl trimethylammonium bromide, allyl
22 parts of base thiocarbamide, 22 parts of butyl hydroxybenzoate, 24 parts of diboron trioxide powder, 22 parts of molybdenum trioxide powder, 20 parts of asbestos fibre, stone
24 parts of English powder, 22 parts of titanium dioxide, 20 parts of carbonization calcium powder, 22 parts of boron carbide powder, 20 parts of potassium carbonate powder, Pyromellitic Acid
20 parts of dianhydride, 20 parts of hexahydro phthalic anhydride, 18 parts of triethylene glycol two tricaprylate, 14 parts of aluminum stearate, polystyrene sulphur
12 parts of sour sodium, 12 parts of neopelex, 12 parts of magnesium stearate, 12 parts of IPDI, ethylparaben
12 parts, 12 parts of second base lead sulfate.
Further, above-mentioned smart home furniture coating, is grouped into by the group of following mass fraction：Hydrogenated nitrile-butadiene rubber 28
Part, 26 parts of fluorosioloxane rubber, 26 parts of EP rubbers, 24 parts of isobutyl triethoxy silane, 26 parts of epoxychloropropane, butyl acetate 26
Part, 24 parts of rilanit special, 26 parts of citronellyl formate, 26 parts of ZPT, 24 parts of cetyl trimethylammonium bromide, allyl
24 parts of base thiocarbamide, 24 parts of butyl hydroxybenzoate, 26 parts of diboron trioxide powder, 24 parts of molybdenum trioxide powder, 22 parts of asbestos fibre, stone
26 parts of English powder, 24 parts of titanium dioxide, 22 parts of carbonization calcium powder, 24 parts of boron carbide powder, 22 parts of potassium carbonate powder, Pyromellitic Acid
22 parts of dianhydride, 22 parts of hexahydro phthalic anhydride, 20 parts of triethylene glycol two tricaprylate, 16 parts of aluminum stearate, polystyrene sulphur
14 parts of sour sodium, 14 parts of neopelex, 14 parts of magnesium stearate, 14 parts of IPDI, ethylparaben
14 parts, 14 parts of second base lead sulfate.
Further, above-mentioned smart home furniture coating, is grouped into by the group of following mass fraction：Hydrogenated nitrile-butadiene rubber 30
Part, 28 parts of fluorosioloxane rubber, 28 parts of EP rubbers, 26 parts of isobutyl triethoxy silane, 28 parts of epoxychloropropane, butyl acetate 28
Part, 26 parts of rilanit special, 28 parts of citronellyl formate, 28 parts of ZPT, 26 parts of cetyl trimethylammonium bromide, allyl
26 parts of base thiocarbamide, 26 parts of butyl hydroxybenzoate, 28 parts of diboron trioxide powder, 26 parts of molybdenum trioxide powder, 24 parts of asbestos fibre, stone
28 parts of English powder, 26 parts of titanium dioxide, 24 parts of carbonization calcium powder, 26 parts of boron carbide powder, 24 parts of potassium carbonate powder, Pyromellitic Acid
24 parts of dianhydride, 24 parts of hexahydro phthalic anhydride, 22 parts of triethylene glycol two tricaprylate, 18 parts of aluminum stearate, polystyrene sulphur
16 parts of sour sodium, 16 parts of neopelex, 16 parts of magnesium stearate, 16 parts of IPDI, ethylparaben
16 parts, 16 parts of second base lead sulfate.
Further, above-mentioned smart home furniture coating production step is as follows：
（1）By the hydrogenated nitrile-butadiene rubber of described mass fraction, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxy
Chloropropane, butyl acetate, rilanit special, citronellyl formate, ZPT, cetyl trimethylammonium bromide, pi-allyl
Thiocarbamide, butyl hydroxybenzoate, diboron trioxide powder, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder
End, boron carbide powder, potassium carbonate powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion
5000～5400r/min about, jitter time is 30～60min；
（2）Add the pyromellitic acid anhydride of described mass fraction, hexahydro phthalic anhydride, triethylene glycol two tricaprylate,
Aluminum stearate, kayexalate, the dispersion of ultrasonic high speed, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～
5200r/min about, jitter time is 30～50min；
（3）Add the neopelex of described mass fraction, magnesium stearate, IPDI, nipalgin
Ethyl ester, second base lead sulfate, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～4800r/min
Left and right, jitter time is 20～40min；This product is obtained after mixing.
This beneficial effect of the invention is：Smart home furniture coating in the present invention, composed of the following components：Hydrogenation fourth
Nitrile rubber, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxychloropropane, butyl acetate, rilanit special, first
Sour citronellyl acrylate, ZPT, cetyl trimethylammonium bromide, allylthiourea, butyl hydroxybenzoate, diboron trioxide powder
End, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder, boron carbide powder, potassium carbonate powder, all
PMDA, hexahydro phthalic anhydride, triethylene glycol two tricaprylate, aluminum stearate, kayexalate, 12
Sodium alkyl benzene sulfonate, magnesium stearate, IPDI, ethylparaben, second base lead sulfate.Product tool of the present invention
There is more superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve properties of product.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is described, to be better understood from the present invention.
Embodiment 1
Smart home furniture coating in the present embodiment, is grouped into by the group of following mass fraction：26 parts of hydrogenated nitrile-butadiene rubber, fluorine
24 parts of silicon rubber, 24 parts of EP rubbers, 22 parts of isobutyl triethoxy silane, 24 parts of epoxychloropropane, 24 parts of butyl acetate, hydrogen
Change 22 parts of castor oil, 24 parts of citronellyl formate, 24 parts of ZPT, 22 parts of cetyl trimethylammonium bromide, allyl sulfide
22 parts of urea, 22 parts of butyl hydroxybenzoate, 24 parts of diboron trioxide powder, 22 parts of molybdenum trioxide powder, 20 parts of asbestos fibre, silica flour
24 parts of end, 22 parts of titanium dioxide, 20 parts of carbonization calcium powder, 22 parts of boron carbide powder, 20 parts of potassium carbonate powder, pyromellitic acid anhydride
20 parts, 20 parts of hexahydro phthalic anhydride, 18 parts of triethylene glycol two tricaprylate, 14 parts of aluminum stearate, kayexalate
12 parts, 12 parts of neopelex, 12 parts of magnesium stearate, 12 parts of IPDI, 12 parts of ethylparaben,
12 parts of second base lead sulfate.
Above-mentioned smart home furniture coating production step is as follows：
（1）By the hydrogenated nitrile-butadiene rubber of described mass fraction, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxy
Chloropropane, butyl acetate, rilanit special, citronellyl formate, ZPT, cetyl trimethylammonium bromide, pi-allyl
Thiocarbamide, butyl hydroxybenzoate, diboron trioxide powder, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder
End, boron carbide powder, potassium carbonate powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, rate of dispersion
5400r/min about, jitter time is 60min；
（2）Add the pyromellitic acid anhydride of described mass fraction, hexahydro phthalic anhydride, triethylene glycol two tricaprylate,
Aluminum stearate, kayexalate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 5200r/min about,
Jitter time is 50min；
（3）Add the neopelex of described mass fraction, magnesium stearate, IPDI, nipalgin
Ethyl ester, second base lead sulfate, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion 4800r/min about, during dispersion
Between be 40min；This product is obtained after mixing.
Embodiment 2
Smart home furniture coating in the present embodiment, is grouped into by the group of following mass fraction：28 parts of hydrogenated nitrile-butadiene rubber, fluorine
26 parts of silicon rubber, 26 parts of EP rubbers, 24 parts of isobutyl triethoxy silane, 26 parts of epoxychloropropane, 26 parts of butyl acetate, hydrogen
Change 24 parts of castor oil, 26 parts of citronellyl formate, 26 parts of ZPT, 24 parts of cetyl trimethylammonium bromide, allyl sulfide
24 parts of urea, 24 parts of butyl hydroxybenzoate, 26 parts of diboron trioxide powder, 24 parts of molybdenum trioxide powder, 22 parts of asbestos fibre, silica flour
26 parts of end, 24 parts of titanium dioxide, 22 parts of carbonization calcium powder, 24 parts of boron carbide powder, 22 parts of potassium carbonate powder, pyromellitic acid anhydride
22 parts, 22 parts of hexahydro phthalic anhydride, 20 parts of triethylene glycol two tricaprylate, 16 parts of aluminum stearate, kayexalate
14 parts, 14 parts of neopelex, 14 parts of magnesium stearate, 14 parts of IPDI, 14 parts of ethylparaben,
14 parts of second base lead sulfate.
Above-mentioned smart home furniture coating production step is as follows：
（1）By the hydrogenated nitrile-butadiene rubber of described mass fraction, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxy
Chloropropane, butyl acetate, rilanit special, citronellyl formate, ZPT, cetyl trimethylammonium bromide, pi-allyl
Thiocarbamide, butyl hydroxybenzoate, diboron trioxide powder, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder
End, boron carbide powder, potassium carbonate powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, rate of dispersion
5200r/min about, jitter time is 45min；
（2）Add the pyromellitic acid anhydride of described mass fraction, hexahydro phthalic anhydride, triethylene glycol two tricaprylate,
Aluminum stearate, kayexalate, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion 5000r/min about,
Jitter time is 40min；
（3）Add the neopelex of described mass fraction, magnesium stearate, IPDI, nipalgin
Ethyl ester, second base lead sulfate, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion 4700r/min about, during dispersion
Between be 30min；This product is obtained after mixing.
Embodiment 3
Smart home furniture coating in the present embodiment, is grouped into by the group of following mass fraction：30 parts of hydrogenated nitrile-butadiene rubber, fluorine
28 parts of silicon rubber, 28 parts of EP rubbers, 26 parts of isobutyl triethoxy silane, 28 parts of epoxychloropropane, 28 parts of butyl acetate, hydrogen
Change 26 parts of castor oil, 28 parts of citronellyl formate, 28 parts of ZPT, 26 parts of cetyl trimethylammonium bromide, allyl sulfide
26 parts of urea, 26 parts of butyl hydroxybenzoate, 28 parts of diboron trioxide powder, 26 parts of molybdenum trioxide powder, 24 parts of asbestos fibre, silica flour
28 parts of end, 26 parts of titanium dioxide, 24 parts of carbonization calcium powder, 26 parts of boron carbide powder, 24 parts of potassium carbonate powder, pyromellitic acid anhydride
24 parts, 24 parts of hexahydro phthalic anhydride, 22 parts of triethylene glycol two tricaprylate, 18 parts of aluminum stearate, kayexalate
16 parts, 16 parts of neopelex, 16 parts of magnesium stearate, 16 parts of IPDI, 16 parts of ethylparaben,
16 parts of second base lead sulfate.
Above-mentioned smart home furniture coating production step is as follows：
（1）By the hydrogenated nitrile-butadiene rubber of described mass fraction, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxy
Chloropropane, butyl acetate, rilanit special, citronellyl formate, ZPT, cetyl trimethylammonium bromide, pi-allyl
Thiocarbamide, butyl hydroxybenzoate, diboron trioxide powder, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder
End, boron carbide powder, potassium carbonate powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, rate of dispersion
5000r/min, jitter time is 30min；
（2）Add the pyromellitic acid anhydride of described mass fraction, hexahydro phthalic anhydride, triethylene glycol two tricaprylate,
Aluminum stearate, kayexalate, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, dispersion
Time is 30min；
（3）Add the neopelex of described mass fraction, magnesium stearate, IPDI, nipalgin
Ethyl ester, second base lead sulfate, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion 4600r/min about, during dispersion
Between be 20min；This product is obtained after mixing.
Carry out performance measurement for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured
Data is as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
It can be seen that, product of the present invention has preferably corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a kind of smart home furniture coating it is characterised in that：It is grouped into by the group of following mass fraction：Hydrogenated nitrile-butadiene rubber 26
～30 parts, 24～28 parts of fluorosioloxane rubber, 24～28 parts of EP rubbers, 22～26 parts of isobutyl triethoxy silane, epoxy chloropropionate
24～28 parts of alkane, 24～28 parts of butyl acetate, 22～26 parts of rilanit special, 24～28 parts of citronellyl formate, ZPT
24～28 parts, 22～26 parts of cetyl trimethylammonium bromide, 22～26 parts of allylthiourea, 22～26 parts of butyl hydroxybenzoate,
24～28 parts of diboron trioxide powder, 22～26 parts of molybdenum trioxide powder, 20～24 parts of asbestos fibre, quartz powder 24～28
Part, 22～26 parts of titanium dioxide, 20～24 parts of carbonization calcium powder, 22～26 parts of boron carbide powder, 20～24 parts of potassium carbonate powder, all
20～24 parts of PMDA, 20～24 parts of hexahydro phthalic anhydride, 18～22 parts of triethylene glycol two tricaprylate, tristearin
14～18 parts of sour aluminium, 12～16 parts of kayexalate, 12～16 parts of neopelex, magnesium stearate 12～16
Part, 12～16 parts of IPDI, 12～16 parts of ethylparaben, 12～16 parts of second base lead sulfate.
2. smart home furniture coating according to claim 1 it is characterised in that：Described smart home furniture coating by with
The group of lower mass fraction is grouped into：26 parts of hydrogenated nitrile-butadiene rubber, 24 parts of fluorosioloxane rubber, 24 parts of EP rubbers, isobutyl group three ethoxy
22 parts of base silane, 24 parts of epoxychloropropane, 24 parts of butyl acetate, 22 parts of rilanit special, 24 parts of citronellyl formate, pyrithione
24 parts of zinc, 22 parts of cetyl trimethylammonium bromide, 22 parts of allylthiourea, 22 parts of butyl hydroxybenzoate, diboron trioxide powder
24 parts, 22 parts of molybdenum trioxide powder, 20 parts of asbestos fibre, 24 parts of quartz powder, 22 parts of titanium dioxide, 20 parts of carbonization calcium powder, carbon
Change 22 parts of boron powder, 20 parts of potassium carbonate powder, 20 parts of pyromellitic acid anhydride, 20 parts of hexahydro phthalic anhydride, triethylene glycol
Two 18 parts of tricaprylates, 14 parts of aluminum stearate, 12 parts of kayexalate, 12 parts of neopelex, magnesium stearate
12 parts, 12 parts of IPDI, 12 parts of ethylparaben, 12 parts of second base lead sulfate.
3. the smart home furniture coating according to claim 1 to 2 it is characterised in that：Described smart home furniture coating
It is grouped into by the group of following mass fraction：28 parts of hydrogenated nitrile-butadiene rubber, 26 parts of fluorosioloxane rubber, 26 parts of EP rubbers, isobutyl group three
24 parts of Ethoxysilane, 26 parts of epoxychloropropane, 26 parts of butyl acetate, 24 parts of rilanit special, 26 parts of citronellyl formate, pyridine
26 parts of thioketones zinc, 24 parts of cetyl trimethylammonium bromide, 24 parts of allylthiourea, 24 parts of butyl hydroxybenzoate, diboron trioxide
26 parts of powder, 24 parts of molybdenum trioxide powder, 22 parts of asbestos fibre, 26 parts of quartz powder, 24 parts of titanium dioxide, carbonization calcium powder 22
Part, 24 parts of boron carbide powder, 22 parts of potassium carbonate powder, 22 parts of pyromellitic acid anhydride, 22 parts of hexahydro phthalic anhydride, three
20 parts of glycol two tricaprylate, 16 parts of aluminum stearate, 14 parts of kayexalate, 14 parts of neopelex, tristearin
14 parts of sour magnesium, 14 parts of IPDI, 14 parts of ethylparaben, 14 parts of second base lead sulfate.
4. the smart home furniture coating according to claims 1 to 3 it is characterised in that：Described smart home furniture coating
It is grouped into by the group of following mass fraction：30 parts of hydrogenated nitrile-butadiene rubber, 28 parts of fluorosioloxane rubber, 28 parts of EP rubbers, isobutyl group three
26 parts of Ethoxysilane, 28 parts of epoxychloropropane, 28 parts of butyl acetate, 26 parts of rilanit special, 28 parts of citronellyl formate, pyridine
28 parts of thioketones zinc, 26 parts of cetyl trimethylammonium bromide, 26 parts of allylthiourea, 26 parts of butyl hydroxybenzoate, diboron trioxide
28 parts of powder, 26 parts of molybdenum trioxide powder, 24 parts of asbestos fibre, 28 parts of quartz powder, 26 parts of titanium dioxide, carbonization calcium powder 24
Part, 26 parts of boron carbide powder, 24 parts of potassium carbonate powder, 24 parts of pyromellitic acid anhydride, 24 parts of hexahydro phthalic anhydride, three
22 parts of glycol two tricaprylate, 18 parts of aluminum stearate, 16 parts of kayexalate, 16 parts of neopelex, tristearin
16 parts of sour magnesium, 16 parts of IPDI, 16 parts of ethylparaben, 16 parts of second base lead sulfate.
5. smart home furniture coating according to claim 1 it is characterised in that：Described smart home furniture coating preparation
Method and step is as follows：
（1）By the hydrogenated nitrile-butadiene rubber of described mass fraction, fluorosioloxane rubber, EP rubbers, isobutyl triethoxy silane, epoxy
Chloropropane, butyl acetate, rilanit special, citronellyl formate, ZPT, cetyl trimethylammonium bromide, pi-allyl
Thiocarbamide, butyl hydroxybenzoate, diboron trioxide powder, molybdenum trioxide powder, asbestos fibre, quartz powder, titanium dioxide, carbonization calcium powder
End, boron carbide powder, potassium carbonate powder are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20～40KHz, rate of dispersion
About 5000～5400r/min, jitter time is 30～60min；
（2）Add the pyromellitic acid anhydride of described mass fraction, hexahydro phthalic anhydride, triethylene glycol two tricaprylate,
Aluminum stearate, kayexalate, the dispersion of ultrasonic high speed, ultrasonic frequency is 20～35KHz, rate of dispersion is about 4800～
5200r/min, jitter time is 30～50min；
（3）Add the neopelex of described mass fraction, magnesium stearate, IPDI, nipalgin
Ethyl ester, second base lead sulfate, ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/
Min, jitter time is 20～40min；This product is obtained after mixing.