CN105950922A - 一种抗氧化镍铝合金 - Google Patents

一种抗氧化镍铝合金 Download PDF

Info

Publication number
CN105950922A
CN105950922A CN201610396179.6A CN201610396179A CN105950922A CN 105950922 A CN105950922 A CN 105950922A CN 201610396179 A CN201610396179 A CN 201610396179A CN 105950922 A CN105950922 A CN 105950922A
Authority
CN
China
Prior art keywords
content
alloy
nickel
rare earth
aluminum alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610396179.6A
Other languages
English (en)
Inventor
翁华洁
周纯杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Chunjie Metal Products Co Ltd
Original Assignee
Taicang Chunjie Metal Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Chunjie Metal Products Co Ltd filed Critical Taicang Chunjie Metal Products Co Ltd
Priority to CN201610396179.6A priority Critical patent/CN105950922A/zh
Publication of CN105950922A publication Critical patent/CN105950922A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗氧化性镍铝合金，包括如下质量百分比含量的成分：镍占22.5‑26.5%，铜占3.6‑4.8%，硅0.8‑1.2%，钼0.5‑1.1%，钛0.4‑1.0%，铍0.2‑0.6%，稀土元素2.4‑3.2%，余量为铝和杂质，所述杂质的含量不超过0.05%；所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为56‑74%，所述镧的含量为26‑44%，通过上述方式，本发明能够具备有良好的抗氧化性能，从而使得镍铝合金在高温环境下不易被氧化，大幅提高了使用寿命。

Description

一种抗氧化镍铝合金
技术领域
本发明涉及一种铝合金材料，特别涉及一种抗氧化镍铝合金。
背景技术
铝合金是以铝为基体元素，然后加入一种或多种合金元素组成的合金，铝合金的密度低，但强度比较高，而且具有优良的导电性、导热性和抗蚀性等，使得铝合金材料在各行业中得到了较为广泛的应用。
随着对铝合金材料研究的深入，现有铝合金材料种类较多，各种铝合金材料的性能也存在较大差异，现阶段，铝合金种类多种多样，镍铝合金就是其中典型代表，但是现有的镍铝合金存在已被氧化的缺陷。
发明内容
本发明主要解决的技术问题是提供一种抗氧化镍铝合金，能够具备有良好的抗氧化性能，从而使得镍铝合金在高温环境下不易被氧化，大幅提高了使用寿命。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种抗氧化镍铝合金，包括如下质量百分比含量的成分：
镍占22.5-26.5%，铜占3.6-4.8%，硅0.8-1.2%，钼0.5-1.1%，钛0.4-1.0%，铍0.2-0.6%，稀土元素2.4-3.2%，余量为铝和杂质，所述杂质的含量不超过0.05%；
所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为56-74%，所述镧的含量为26-44%。
在本发明一个较佳实施例中，所述杂质为硫、磷、碳的任意一种或多种混合。
在本发明一个较佳实施例中，所述钼和所述钛的含量总和为1.5%。
在本发明一个较佳实施例中，所述稀土元素中成分质量配比具体为：所述铈的含量为65%，所述镧的含量为35%。
本发明的有益效果是：本发明一种抗氧化镍铝合金能够具备有良好的抗氧化性能，从而使得镍铝合金在高温环境下不易被氧化，大幅提高了使用寿命。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1：
一种抗氧化镍铝合金，包括如下质量百分比含量的成分：
镍占22.5%，铜占4.8%，硅0.8%，钼1.1%，钛0.4%，铍0.6%，稀土元素2.4%，余量为铝和杂质，所述杂质的含量不超过0.05%；
所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为74%，所述镧的含量为26%。
实施例2：
一种抗氧化镍铝合金，包括如下质量百分比含量的成分：
镍占26.5%，铜占3.6%，硅1.2%，钼0.5%，钛1.0%，铍0.2%，稀土元素3.2%，余量为铝和杂质，所述杂质的含量不超过0.05%；
所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为56%，所述镧的含量为44%。
实施例3：
一种抗氧化镍铝合金，包括如下质量百分比含量的成分：
镍占24.5%，铜占4.2%，硅1.0%，钼0.8%，钛0.7%，铍0.4%，稀土元素2.8%，余量为铝和杂质，所述杂质的含量不超过0.05%；
所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为56-74%，所述镧的含量为26-44%。
其中，所述杂质为硫、磷、碳的任意一种或多种混合。
本发明一种抗氧化镍铝合金的制备方法如下：
（1）、按照上述比例称取相应的镍、铜、硅、钼、钛、铍以及铝，放入高温熔炉内，加温至1400-1500℃，得到混合初液；
（2）、待混合液自然冷却至800-900℃之间时，向内投入稀土元素，再加热至1100-1200℃，得到混合终液；
（3）、将上述混合终液浇注入指定的模具内，冷却成型后得到抗氧化镍铝合金。
区别于现有技术，本发明一种抗氧化镍铝合金通过添加由铈和镧混合的稀土元素，同时优化成分配比，从而能够具备有良好的抗氧化性能，从而使得镍铝合金在高温环境下不易被氧化，大幅提高了使用寿命。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (4)

1.一种抗氧化性镍铝合金，其特征在于，包括如下质量百分比含量的成分：
镍占22.5-26.5%，铜占3.6-4.8%，硅0.8-1.2%，钼0.5-1.1%，钛0.4-1.0%，铍0.2-0.6%，稀土元素2.4-3.2%，余量为铝和杂质，所述杂质的含量不超过0.05%；
所述稀土元素由铈和镧混合构成，按照质量百分比配比，所述铈的含量为56-74%，所述镧的含量为26-44%。
2.根据权利要求1所述的抗氧化性镍铝合金，其特征在于，所述杂质为硫、磷、碳的任意一种或多种混合。
3.根据权利要求1所述的抗氧化性镍铝合金，其特征在于，所述钼和所述钛的含量总和为1.5%。
4.根据权利要求1所述的抗氧化性镍铝合金，其特征在于，所述稀土元素中成分质量配比具体为：所述铈的含量为65%，所述镧的含量为35%。
CN201610396179.6A 2016-06-07 2016-06-07 一种抗氧化镍铝合金 Pending CN105950922A (zh)