CN105949829A - Coating for electric power fittings and preparation method thereof - Google Patents
Coating for electric power fittings and preparation method thereof Download PDFInfo
- Publication number
- CN105949829A CN105949829A CN201610418364.0A CN201610418364A CN105949829A CN 105949829 A CN105949829 A CN 105949829A CN 201610418364 A CN201610418364 A CN 201610418364A CN 105949829 A CN105949829 A CN 105949829A
- Authority
- CN
- China
- Prior art keywords
- parts
- full dose
- coating
- consumption
- armour clamp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a coating for electric power fittings and a preparation method thereof. The coating for the electric power fittings is composed of, by mass, 60-80 parts of a silica solution, 15-30 parts of epoxy resin, 15-25 parts of polyester resin, 10-16 parts of SHP-50 polysiloxane powder, 15-20 parts of polyimide resin, 7-12 parts of acetylene black, 6-15 parts of nanometer titania, 8-10 parts of water glass, 4-8 parts of petroleum asphalt, 8-15 parts of guar gum WP-05, 6-10 parts of SER-AD FA 179, 3-5 parts of diethylenetriamine, 2-4 parts of antioxygen 1076, 5-8 parts of phosphate aluminum-chromium and 1-3 parts of a sodium hydroxide solution. The coating is prepared through the steps of mixed smelting, crushing, mixing, stirring, aging and the like. The coating has the advantages that the coating has excellent corrosion resistance and corona resistance, gathering of electric charges can be reduced, the probability of partial discharge breakdown is lowered, the corona-resistant protective effect is achieved, and the problems of aging, corrosion and the like in the use process of the electric power fittings are effectively prevented.
Description
Technical field
The present invention relates to gold utensil protective coating field, be specifically related to a kind of electric armour clamp coating and
Its preparation method.
Background technology
Electric armour clamp, is to connect and all kinds of devices in combinational electric system, plays transmission machinery
The metal-ware of load, electrical load and certain protective action, rises emphatically in project of transmitting and converting electricity
The effect wanted.Product quality is not only related to electric power netting safe running, is also relate to person property peace
Entirely, thus it is guaranteed that the properties of product of electric armour clamp and service life are very important tasks.
Electric armour clamp is mainly metal cast iron class, easily occurs that burn into is aging etc. and ask during life-time service
Topic.At present, the method for conventional protection metal material is external coating overcoat.
Patent application CN102604537A disclosed in China asks for metal is corrosion-prone
Topic proposes a kind of waterborne metal anti-corrosive paint and preparation method thereof, its by Ludox emulsion,
GH-26XB silicon the third anticorrosion emulsion, rutile titanium white R-930, alcohol ester 12, extra fine talc
Powder, ultrafine mica powder, superfine silicon dioxide powder, GH5050 dispersant, DA dispersant,
PE-100 wetting agent, GHP101 thickening agent, preservative 981, SN-345 defoamer, water
Composition, the waterborne metal anti-corrosive paint of this invention is nontoxic, environmental protection, has splendid water-tight corrosion-proof
The advantages such as erosion property, high temperature resistant, alkali resistance, weatherability, scrub resistance and artificial ageing resistance, be
More satisfactory novel aqueous metal anti-corrosive paint.
Although prior art achieves certain effect to anti-corrosion of metal aspect, but in raw material
Ultra-fine composition is too much, it is difficult to controls dispersibility, easily assembles agglomerating, cause coating surface out-of-flatness,
The phenomenons such as crackle, affect performance.And electric armour clamp is except existing as corrosion of metal problem,
Also have the corona phenomenon that causes after energising, discharge under conditions of high field intensity cause high temperature, portion
The phenomenons such as part is aging, burning remain unsolved.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of electric armour clamp coating and system thereof
Preparation Method, efficiently solves the problem that gold utensil burn into is aging, and has excellent corona resistance,
Coating is uniformly dispersed, flat smooth, and combination property is stable, has the service life of gold utensil significantly
Lifting.
In order to realize above-mentioned purpose, the present invention uses following technical scheme:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 60-80 part, ring
Epoxy resins 15-30 part, polyester resin 15-25 part, SHP-50 polysiloxanes powder 10-16 part,
Polyimide resin 15-20 part, acetylene carbon black 7-12 part, nano titanium oxide 6-15 part,
Waterglass 8-10 part, asphalt 4-8 part, guar gum WP-05 8-15 part, SER-AD
FA179 6-10 part, diethylentriamine 3-5 part, antioxidant 1076 2-4 part, aluminum phosphate
Chromium 5-8 part, sodium hydroxide solution 1-3 part.
Preferably, electric armour clamp coating is made up of following mass fraction: Ludox 70-80 part,
Epoxy resin 23-30 part, polyester resin 20-25 part, SHP-50 polysiloxanes powder 13-16
Part, polyimide resin 17-20 part, acetylene carbon black 10-12 part, nano titanium oxide 10-15
Part, waterglass 9-10 part, asphalt 6-8 part, guar gum WP-05 12-15 part,
SER-AD FA179 8-10 part, diethylentriamine 4-5 part, antioxidant 1076 3-4 part,
Aluminum phosphate chromium 6-8 part, sodium hydroxide solution 2-3 part.
Preferably, the preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 130 DEG C-140 DEG C, and mixing 20-25min extrudes tabletting,
Pulverize after parking cooling, cross 400 mesh sieves, obtain mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 85 DEG C
-90 DEG C stir, and then freezing processing becomes solid, cross 800 mesh sieves, obtain mixing after pulverizing
Thing two, cryopreservation is standby;
3) polyimide resin of full dose is heated to 90 DEG C-105 DEG C, is subsequently adding full dose
Acetylene carbon black and the nano titanium oxide of full dose, be stirring evenly and then adding into the antioxidant of full dose
1076, continue stirring 10-15min, cool down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 36-48h, obtains final coating.
Preferably, preparation process 2) whipping process medium velocity be 60-80r/min, during stirring
Between be 20-25min.
Preferably, preparation process 3) in acetylene carbon black be divided into 5 additions, every 5min
Once feeding intake, mixing speed is 45-60r/min.
Preferably, preparation process 3) in rate of cooling be 5 DEG C/min.
Preferably, preparation process 4) in mix and blend be first to stir 5min with 150r/min,
Then 5min is stirred with 80r/min.
The present invention uses above-mentioned technical scheme can reach to provide the benefit that: the present invention is molten with silicon
Glue is matrix, adds various inserts and prepares gained.The resistance to water of Ludox, heat resistance are bright
Showing and be better than organic coating, film is fine and close and harder, does not produce electrostatic, and in air, various dust are difficult
Adhere to, there is the strongest contamination resistance.Acetylene carbon black is super-normal structure black, is easily formed space
Network channel, beneficially polymer are formed chain type conductive structure, and nano titanium oxide has
High electrical conductivity, the electric charge making surface gather spreads rapidly along surface, it is to avoid internal field
Too high and shelf depreciation occurs, meanwhile, nano titanium oxide also has the effect absorbing ultraviolet light,
And dissipate by the way of heat, therefore can play a protective role.Aluminum phosphate chromium can as adhesive
Plasticity is good, Heat stability is good, along with the rising intensity of temperature strengthens the most accordingly, and its contained three
Valency chromium will not be transformed into toxicity Cr VI, and safety is high.SHP-50 polysiloxanes powder hydrophobic,
After solidification good to water repellency, there is stronger hydrophobicity and durability.SER-AD FA179
The corrosion inhibitor that can be used as water soluble paint prevents from dodging the formation of erosion.Colophonium belongs to hydrophobicity
Material, but viscosity is very big has mobility, corrosion-resistant and have toughness.Guar gum WP-05
Uniformly dispersed for rheology modifier, beneficially coating, has resistance to water and has significantly
Price advantage.
In preparation process, first epoxy resin and polyester resin are mixed, at a certain temperature in
In mill mixing, make both dispersed by the levelability of guar gum, may advantageously facilitate poly-
In ester, the hydroxyl in carboxyl and epoxy resin, epoxy reaction, draw have both combination properties
Epoxy polyester, availability is higher.And Colophonium and epoxy resin also are able to reaction and generate epoxy drip
Green grass or young crops, it is strong that this Colophonium compares plain asphalt corrosion resistance, and has certain elasticity.Acetylene charcoal
Black and nano titanium oxide addition by several times is mixed with and the most fully reacts, the polymer space of formation
Structure is more stable, and the antioxidant being subsequently added makes living radical before macromolecular chain aoxidizes
Just lose activity, thus can effectively stop polymer oxidation, degraded, improve polymeric material
Inverter fed motor ability.
In summary, electric armour clamp coating even compact of the present invention, have excellent corrosion-resistant
Property and corona resistance, can be effectively ensured the practicality of electric armour clamp, be obviously improved electric armour clamp
Service life, and waterproof, antifouling capacity is strong, has certain elasticity, can be used for vibration-absorptive material
Protection.
Detailed description of the invention
For making the purpose of the embodiment of the present invention, technical scheme and advantage clearer, below will knot
Close the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely retouched
State, it is clear that described embodiment is a part of embodiment of the present invention rather than whole realities
Execute example.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creation
The every other embodiment obtained under property work premise, broadly falls into the scope of protection of the invention.
Embodiment 1:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 65 parts, epoxy
Resin 15 parts, 25 parts of polyester resin, 12 parts of SHP-50 polysiloxanes powder, polyimides
Resin 17 parts, acetylene carbon black 12 parts, nano titanium oxide 12 parts, waterglass 8.5 parts,
5 parts of asphalt, guar gum WP-05 10 parts, SER-AD FA179 7 parts, diethyl
Support triamine 4 parts, antioxidant 1076 2.3 parts, aluminum phosphate chromium 7 parts, sodium hydroxide solution 1.5
Part.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 130 DEG C, and mixing 20min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 85 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 90 DEG C, is subsequently adding the acetylene charcoal of full dose
The black nano titanium oxide with full dose, is stirring evenly and then adding into the antioxidant 1076 of full dose, continues
Continuous stirring 10min, cools down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 36h, obtains final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 80r/min, mixing time is
20min.Preparation process 3) in mixing speed be 60r/min.
Embodiment 2:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 70 parts, epoxy
Resin 30 parts, 20 parts of polyester resin, 13 parts of SHP-50 polysiloxanes powder, polyimides
Resin 15 parts, acetylene carbon black 10 parts, nano titanium oxide 10 parts, waterglass 9 parts, stone
Oil asphalt 4 parts, guar gum WP-05 12 parts, SER-AD FA179 8 parts, diethylene
Triamine 4.5 parts, antioxidant 1076 4 parts, aluminum phosphate chromium 8 parts, sodium hydroxide solution 2.5
Part.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 135 DEG C, and mixing 22min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 88 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 105 DEG C, is subsequently adding the acetylene of full dose
White carbon black and the nano titanium oxide of full dose, be stirring evenly and then adding into the antioxidant 1076 of full dose,
Continue stirring 12min, cool down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 40h, obtains final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 65r/min, mixing time is
25min.Preparation process 3) in mixing speed be 45r/min.
Embodiment 3:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 78 parts, epoxy
Resin 20 parts, 23 parts of polyester resin, 10 parts of SHP-50 polysiloxanes powder, polyimides
Resin 20 parts, acetylene carbon black 8 parts, nano titanium oxide 8 parts, waterglass 9.5 parts, stone
Oil asphalt 8 parts, guar gum WP-05 8 parts, SER-AD FA179 10 parts, diethylene
Triamine 5 parts, antioxidant 1076 3.5 parts, aluminum phosphate chromium 6 parts, sodium hydroxide solution 2.8
Part.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 140 DEG C, and mixing 25min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 86 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 100 DEG C, is subsequently adding the acetylene of full dose
The nano titanium oxide of white carbon black full dose, is stirring evenly and then adding into the antioxidant 1076 of full dose, continues
Continuous stirring 14min, cools down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
FA179, the guar gum WP-05 of 3/4 consumption and the aluminum phosphate chromium of 3/4 consumption and addition, mixed
Close stirring, be aged 45h, obtain final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 70r/min, mixing time is
22min.Preparation process 3) in mixing speed be 50r/min.
Embodiment 4:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 75 parts, epoxy
Resin 23 parts, 15 parts of polyester resin, 16 parts of SHP-50 polysiloxanes powder, polyimides
Resin 18 parts, acetylene carbon black 7 parts, nano titanium oxide 6 parts, waterglass 10 parts, oil
Colophonium 7 parts, guar gum WP-05 15 parts, SER-AD FA179 6 parts, diethylene three
Amine 3.5 parts, antioxidant 1076 2 parts, aluminum phosphate chromium 5 parts, sodium hydroxide solution 3 parts.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 135 DEG C, and mixing 23min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 87 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 95 DEG C, is subsequently adding the acetylene charcoal of full dose
The black nano titanium oxide with full dose, is stirring evenly and then adding into the antioxidant 1076 of full dose, continues
Continuous stirring 15min, cools down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 48h, obtains final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 75r/min, mixing time is
23min.Preparation process 3) in mixing speed be 55r/min.
Embodiment 5:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 80 parts, epoxy
Resin 18 parts, 18 parts of polyester resin, 15 parts of SHP-50 polysiloxanes powder, polyimides
Resin 16 parts, acetylene carbon black 11 parts, nano titanium oxide 15 parts, waterglass 8 parts, stone
Oil asphalt 6 parts, guar gum WP-05 13 parts, SER-AD FA179 8 parts, diethylene
Triamine 3 parts, antioxidant 1076 3 parts, aluminum phosphate chromium 6 parts, sodium hydroxide solution 2 parts.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 130 DEG C, and mixing 22min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 90 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 102 DEG C, is subsequently adding the acetylene of full dose
White carbon black and the nano titanium oxide of full dose, be stirring evenly and then adding into the antioxidant 1076 of full dose,
Continue stirring 12min, cool down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 42h, obtains final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 60r/min, mixing time is
20min.Preparation process 3) in mixing speed be 55r/min.
Embodiment 6:
A kind of electric armour clamp coating is made up of following mass fraction: Ludox 60 parts, epoxy
Resin 25 parts, 22 parts of polyester resin, 12 parts of SHP-50 polysiloxanes powder, polyimides
Resin 18 parts, acetylene carbon black 10 parts, nano titanium oxide 14 parts, waterglass 8.5 parts,
5 parts of asphalt, guar gum WP-05 10 parts, SER-AD FA179 6 parts, diethyl
Support triamine 3.8 parts, antioxidant 1076 3.8 parts, aluminum phosphate chromium 7 parts, sodium hydroxide solution
1 part.
A kind of preparation method of electric armour clamp coating, its preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 140 DEG C, and mixing 20min extrudes tabletting, parks cooling
Rear pulverizing, crosses 400 mesh sieves, obtains mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 88 DEG C
Stirring, then freezing processing becomes solid, crosses 800 mesh sieves, obtain mixture two after pulverizing,
Cryopreservation is standby;
3) polyimide resin of full dose is heated to 98 DEG C, is subsequently adding the acetylene charcoal of full dose
The black nano titanium oxide with full dose, is stirring evenly and then adding into the antioxidant 1076 of full dose, continues
Continuous stirring 10min, cools down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 45h, obtains final coating.
Above-mentioned preparation process 2) whipping process medium velocity be 70r/min, mixing time is
25min.Preparation process 3) in mixing speed be 50r/min.
Coating of the present invention and market are commonly used coating application on same metal part, carry out corrosion-resistant
Performance test (the rate of corrosion % caused in the identical time), data such as following table:
Salt fog | Sodium nitrite | Molybdic acid acid sodium | |
Embodiment 1 | 3.8 | 2.4 | 2.5 |
Embodiment 2 | 2.6 | 2.3 | 3.0 |
Embodiment 3 | 3.9 | 3.6 | 2.8 |
Embodiment 4 | 4.2 | 3.1 | 2.1 |
Embodiment 5 | 3.0 | 3.5 | 2.3 |
Embodiment 6 | 2.5 | 3.2 | 1.7 |
Embodiment meansigma methods | 3.33 | 3.0 | 2.4 |
Reference substance 1 | 6.7 | 5.4 | 2.2 |
Reference substance 2 | 5.4 | 6.0 | 3.6 |
Reference substance 3 | 5.8 | 5.7 | 4.3 |
Reference substance meansigma methods | 5.97 | 5.7 | 3.37 |
Understand electric armour clamp coating of the present invention from above table to have more compared with existing coating
Good anticorrosion effect.
It addition, the product embodiment of the present invention prepared and reference product carry out Inverter fed motor and test
Go out product of the present invention and occur that the starting voltage relatively matched group of corona phenomenon improves 6.8kV (averagely
Value), the corona resistance of product the most of the present invention is higher.
Electric armour clamp coating the most of the present invention has excellent corrosion resistance and Inverter fed motor
Property, the practicality of electric armour clamp can be effectively ensured, be obviously improved the service life of electric armour clamp,
It is worthy to be popularized.
Above example only in order to technical scheme to be described, is not intended to limit;Although
With reference to previous embodiment, the present invention is described in detail, those of ordinary skill in the art
It is understood that the technical scheme described in foregoing embodiments still can be modified by it,
Or wherein portion of techniques feature is carried out equivalent;And these amendments or replacement, not
The essence making appropriate technical solution departs from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. an electric armour clamp coating, it is characterised in that described electric armour clamp coating by
Following mass fraction forms: Ludox 60-80 part, epoxy resin 15-30 part, polyester resin
15-25 part, SHP-50 polysiloxanes powder 10-16 part, polyimide resin 15-20 part,
Acetylene carbon black 7-12 part, nano titanium oxide 6-15 part, waterglass 8-10 part, asphalt
4-8 part, guar gum WP-05 8-15 part, SER-AD FA179 6-10 part, diethylene
Triamine 3-5 part, antioxidant 1076 2-4 part, aluminum phosphate chromium 5-8 part, sodium hydroxide solution
1-3 part.
Electric armour clamp coating the most according to claim 1, it is characterised in that described
Electric armour clamp coating is made up of following mass fraction: Ludox 70-80 part, epoxy resin
23-30 part, polyester resin 20-25 part, SHP-50 polysiloxanes powder 13-16 part, polyamides
Imide resin 17-20 part, acetylene carbon black 10-12 part, nano titanium oxide 10-15 part, water
Glass 9-10 part, asphalt 6-8 part, guar gum WP-05 12-15 part, SER-AD
FA179 8-10 part, diethylentriamine 4-5 part, antioxidant 1076 3-4 part, aluminum phosphate
Chromium 6-8 part, sodium hydroxide solution 2-3 part.
The preparation method of electric armour clamp coating the most according to claim 1 and 2, its
Being characterised by, preparation process is as follows:
1) by the epoxy resin of 4/5 consumption, the polyester resin of full dose, the aluminum phosphate of 1/4 consumption
The diethylentriamine of chromium, the guar gum WP-05 of 1/4 consumption and 4/5 consumption is put after uniformly mixing
Entering in mill, regulation temperature is 130 DEG C-140 DEG C, and mixing 20-25min extrudes tabletting,
Pulverize after parking cooling, cross 400 mesh sieves, obtain mixture one standby;
2) by the asphalt of full dose, the diethylentriamine of 1/5 consumption and the sodium hydroxide of full dose
Add in mixture one together with remaining 1/5 epoxy resin after solution mix homogeneously, at 85 DEG C
-90 DEG C stir, and then freezing processing becomes solid, cross 800 mesh sieves, obtain mixing after pulverizing
Thing two, cryopreservation is standby;
3) polyimide resin of full dose is heated to 90 DEG C-105 DEG C, is subsequently adding full dose
Acetylene carbon black and the nano titanium oxide of full dose, be stirring evenly and then adding into the antioxidant 1076 of full dose,
Continue stirring 10-15min, cool down to obtain mixture three;
4) by step 2) and step 3) in mixture add in Ludox, mix homogeneously,
Then by the SHP-50 polysiloxanes powder of full dose, the waterglass of full dose, the SER-AD of full dose
The aluminum phosphate chromium of FA179, the guar gum WP-05 of 3/4 consumption and 3/4 consumption adds, mixing
Stirring, is aged 36-48h, obtains final coating.
The preparation method of electric armour clamp coating the most according to claim 3, its feature
Be: described preparation process 2) whipping process medium velocity be 60-80r/min, mixing time
For 20-25min.
The preparation method of electric armour clamp coating the most according to claim 3, its feature
Be: described preparation process 3) in acetylene carbon black be divided into 5 additions, enter every 5min
Row once feeds intake, and mixing speed is 45-60r/min.
The preparation method of electric armour clamp coating the most according to claim 3, its feature
Be: described preparation process 3) in rate of cooling be 5 DEG C/min.
The preparation method of electric armour clamp coating the most according to claim 3, its feature
Be: described preparation process 4) in mix and blend for first stirring 5min with 150r/min, so
After with 80r/min stir 5min.