CN105949665A - Cold-resistant low-temperature-resistant wire and cable material - Google Patents
Cold-resistant low-temperature-resistant wire and cable material Download PDFInfo
- Publication number
- CN105949665A CN105949665A CN201610436957.XA CN201610436957A CN105949665A CN 105949665 A CN105949665 A CN 105949665A CN 201610436957 A CN201610436957 A CN 201610436957A CN 105949665 A CN105949665 A CN 105949665A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- cold
- electric wire
- low temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a cold-resistant low-temperature-resistant wire and cable material. The material is prepared from, by weight, 70-80 parts of PVC resin, 2-4 parts of bisphenol A, 3-7 parts of polystyrene, 1-3 parts of polyamide, 5-8 parts of nano alumina, 2-4 parts of tribasic lead sulfate, 3-5 parts of dibasic lead phosphite, 2-4 parts of calcium carbonate, 20-25 parts of polyethylene glycol, 10-15 parts of polyvinyl alcohol, 12-15 parts of sodium borate, 8-12 parts of magnesium chloride and 12-16 parts of titanium dioxide. SG-4 polyvinyl chloride resin manufactured through the suspension polymerization method is adopted as the PVC resin. The material has good cold resistance, low temperature resistance, mechanical properties, electric insulation performance and processability, and also has excellent flame retardancy, waterproof performance and moisture resistance.
Description
Technical field
The present invention relates to technical field of electric wires and cables, specifically a kind of cold-resistant low temperature resistant electric wire and cable material.
Background technology
Electric wire in order to transmit electricity (magnetic) can, information and realize electromagnetic energy conversion wire product, the electric wire of broad sense
Being also referred to simply as cable, the cable of narrow sense refers to insulated cable, and it may be defined as: the aggregation being made up of following part；One
Or many insulated wire cores, and the clad that each of which is likely to be of, total protective layer and outer jacket.
Electric wire description is various, has wide range of applications, use voltage at 1kV and following more, in the face of special occasions
The most derivative new product, such as fire-resistant cable, flame-retardant cable, low smoke and zero halogen, low-smoke low-halogen cable, mouse termite-proof, anti-
The wear-resisting cable of cable, oil resistant, medical cable, agricultural cable, mining cable, thin-walled electric wire etc..
Electric wire is widely used in industry-by-industry, must develop along with the most information-based, and the effect of electric wire is the most prominent
Go out, in industry and people are lived, all play very important role.In consideration of it, the present invention proposes a kind of cold-resistant resistance to low
Temperature electric wire and cable material.
Summary of the invention
The technical problem to be solved is to provide a kind of cold-resistant low temperature resistant electric wire and cable material.To be solved by this invention
Technical problem realizes by the following technical solutions:
A kind of cold-resistant low temperature resistant electric wire and cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 70-80 part, double
Phenol A2-4 part, polystyrene 3-7 part, polyamide 1-3 part, nano aluminium oxide 5-8 part, tribasic lead sulfate 2-4 part,
Dibasic lead phosphite 3-5 part, calcium carbonate 2-4 part, Polyethylene Glycol 20-25 part, polyvinyl alcohol 10-15 part, sodium borate
12-15 part, magnesium chloride 8-12 part and titanium dioxide 12-16 part.
Further, currently preferred raw material components is: polyvinyl chloride resin 75 parts, bisphenol-A 3 parts, polystyrene 5 parts, poly-
Amide 1 part, nano aluminium oxide 6 parts, tribasic lead sulfate 3 parts, dibasic lead phosphite 4 parts, calcium carbonate 3 parts, poly-
Ethylene glycol 23 parts, polyvinyl alcohol 12 parts, sodium borate 13.5 parts, 10 parts of magnesium chloride and titanium dioxide 14 parts.
Further, described polyvinyl chloride resin uses the SG-4 model Corvic that suspension polymerization is manufactured.
Compared with prior art, the present invention has good cold-resistant resistance to low temperature, mechanical performance, electrical insulation properties and adds
Work performance, also has the anti-flammability of excellence and waterproof and dampproof property simultaneously.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below to this
Invention is expanded on further.
Embodiment 1
A kind of cold-resistant low temperature resistant electric wire and cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 70 parts, bis-phenol
A2 part, polystyrene 3 parts, polyamide 1 part, nano aluminium oxide 5 parts, tribasic lead sulfate 2 parts, two alkali formula phosphorous acid
3 parts of lead, calcium carbonate 2 parts, Polyethylene Glycol 20 parts, polyvinyl alcohol 10 parts, sodium borate 12 parts, 8 parts of magnesium chloride and titanium
12 parts of white lead.
Further, described polyvinyl chloride resin uses the SG-4 model Corvic that suspension polymerization is manufactured.
Embodiment 2
A kind of cold-resistant low temperature resistant electric wire and cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 75 parts, bis-phenol
A3 part, polystyrene 5 parts, polyamide 1 part, nano aluminium oxide 6 parts, tribasic lead sulfate 3 parts, two alkali formula phosphorous acid
4 parts of lead, calcium carbonate 3 parts, Polyethylene Glycol 23 parts, polyvinyl alcohol 12 parts, sodium borate 13.5 parts, 10 parts of magnesium chloride
With titanium dioxide 14 parts.
Further, described polyvinyl chloride resin uses the SG-4 model Corvic that suspension polymerization is manufactured.
Embodiment 3
A kind of cold-resistant low temperature resistant electric wire and cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 80 parts, bis-phenol
A4 part, polystyrene 7 parts, kymene part, nano aluminium oxide 8 parts, tribasic lead sulfate 4 parts, two alkali formula phosphorous acid
5 parts of lead, calcium carbonate 4 parts, Polyethylene Glycol 25 parts, polyvinyl alcohol 15 parts, sodium borate 15 parts, 12 parts of magnesium chloride and
Titanium dioxide 16 parts.
Further, described polyvinyl chloride resin uses the SG-4 model Corvic that suspension polymerization is manufactured.
Compared with prior art, the present invention has good cold-resistant resistance to low temperature, mechanical performance, electrical insulation properties and adds
Work performance, also has the anti-flammability of excellence and waterproof and dampproof property simultaneously.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.The technical staff of the industry
It should be appreciated that the present invention is not limited by step embodiment, the simply present invention's described in step embodiment and description is former
Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these change and change
Enter to both fall within scope of the claimed invention.Claimed scope is by appending claims and equivalent thereof
Define.
Claims (3)
1. a cold-resistant low temperature resistant electric wire and cable material, it is characterised in that: include following raw material and parts by weight of component: polyvinyl chloride resin
70-80 part, bisphenol-A 2-4 part, polystyrene 3-7 part, polyamide 1-3 part, nano aluminium oxide 5-8 part, three alkali formula sulphuric acid
Lead 2-4 part, dibasic lead phosphite 3-5 part, calcium carbonate 2-4 part, Polyethylene Glycol 20-25 part, polyvinyl alcohol 10-15 part,
Sodium borate 12-15 part, magnesium chloride 8-12 part and titanium dioxide 12-16 part.
One the most according to claim 1 resists cold low temperature resistant electric wire and cable material, it is characterised in that: preferably raw material components
For: polyvinyl chloride resin 75 parts, bisphenol-A 3 parts, polystyrene 5 parts, polyamide 1 part, nano aluminium oxide 6 parts, three alkali formula sulfur
Lead plumbate 3 parts, dibasic lead phosphite 4 parts, calcium carbonate 3 parts, Polyethylene Glycol 23 parts, polyvinyl alcohol 12 parts, sodium borate 13.5
Part, 10 parts of magnesium chloride and titanium dioxide 14 parts.
One the most according to claim 1 resists cold low temperature resistant electric wire and cable material, it is characterised in that: described polyvinyl chloride resin
Use the SG-4 model Corvic that suspension polymerization is manufactured.