CN105949664A - Anti-abrasion high-strength insulating wire and cable material - Google Patents
Anti-abrasion high-strength insulating wire and cable material Download PDFInfo
- Publication number
- CN105949664A CN105949664A CN201610436884.4A CN201610436884A CN105949664A CN 105949664 A CN105949664 A CN 105949664A CN 201610436884 A CN201610436884 A CN 201610436884A CN 105949664 A CN105949664 A CN 105949664A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable material
- wear
- insulated wire
- polyacrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-abrasion high-strength insulating wire and cable material. The material is prepared from, by weight, 110-130 parts of PVC resin, 2-4 parts of calcium carbonate, 20-25 parts of polyethylene glycol, 10-15 parts of polyvinyl alcohol, 12-15 parts of sodium borate, 8-12 parts of magnesium chloride, 12-16 parts of titanium dioxide, 50-60 parts of chlorinated polyethylene, 10-15 parts of silicon rubber, 2-4 parts of polyacrylate, 1-2 parts of anti-ageing agent MB, 7-13 parts of antimonous oxide, 5-10 parts of decabrominated dipheny ethane, 15-20 parts of fumed silica, 5-10 parts of nano zeolite, 10-15 parts of precipitated barium sulphate and 3-6 parts of composite filler. The material has good abrasion resistance, pressure resistance, mechanical properties, electric insulating performance and processability, is high in strength and hardness and good in insulation performance, and has excellent flame retardancy, waterproof performance and moisture resistance.
Description
Technical field
The present invention relates to technical field of electric wires and cables, specifically a kind of wear-resisting high-strength degree insulated wire cable material.
Background technology
Electric wire in order to transmit electricity (magnetic) can, information and realize electromagnetic energy conversion wire product, the electric wire of broad sense
Being also referred to simply as cable, the cable of narrow sense refers to insulated cable, and it may be defined as: the aggregation being made up of following part;One
Or many insulated wire cores, and the clad that each of which is likely to be of, total protective layer and outer jacket.
Electric wire description is various, has wide range of applications, use voltage at 1kV and following more, in the face of special occasions
The most derivative new product, such as fire-resistant cable, flame-retardant cable, low smoke and zero halogen, low-smoke low-halogen cable, mouse termite-proof, anti-
The wear-resisting cable of cable, oil resistant, medical cable, agricultural cable, mining cable, thin-walled electric wire etc..
Electric wire is widely used in industry-by-industry, must develop along with the most information-based, and the effect of electric wire is the most prominent
Go out, in industry and people are lived, all play very important role.In consideration of it, the present invention proposes a kind of wear-resisting high-strength
Degree insulated wire cable material.
Summary of the invention
The technical problem to be solved is to provide a kind of wear-resisting high-strength degree insulated wire cable material.The present invention to solve
Technical problem certainly realizes by the following technical solutions:
A kind of wear-resisting high-strength degree insulated wire cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 110-130
Part, calcium carbonate 2-4 part, Polyethylene Glycol 20-25 part, polyvinyl alcohol 10-15 part, sodium borate 12-15 part, magnesium chloride
8-12 part, titanium dioxide 12-16 part, chlorinated polyethylene 50-60 part, silicone rubber 10-15 part, polyacrylate 2-4 part,
Antioxidant MB 1-2 part, zinc stearate 2-4 part, stearic acid monoglyceride 3-5 part, modified aluminium hydroxide 20-30 part, phosphorus
Acid 2-methyl-2-phenylpropane diphenyl ester 5-10 part, antimony oxide 7-13 part, TDE 5-10 part, gas-phase silica 15-20
Part, nano zeolite 5-10 part, blanc fixe 10-15 part, compounded mix 3-6 part.
Further, currently preferred raw material components is: polyvinyl chloride resin 120 parts, calcium carbonate 3 parts, Polyethylene Glycol 22 parts,
Polyvinyl alcohol 12 parts, sodium borate 13.5 parts, 10 parts of magnesium chloride, titanium dioxide 14 parts, chlorinated polyethylene 55 parts, silicon rubber
12 parts of glue, polyacrylate 3 parts, antioxidant MB 1.5 parts, zinc stearate 3 parts, stearic acid monoglyceride 4 parts, change
Property aluminium hydroxide 25 parts, phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 8 parts, antimony oxide 10 parts, TDE 8 parts, gas phase
White carbon 17 parts, nano zeolite 7 parts, blanc fixe 12 parts, compounded mix 4 parts.
Further, described polyvinyl chloride resin uses the SG-5 model Corvic that suspension polymerization is manufactured.
Compared with prior art, the present invention has good wear-resisting pressure performance, mechanical performance, electrical insulation properties and processing
Performance, and intensity is high, hardness is big and good insulating, also has the anti-flammability of excellence and waterproof and dampproof property simultaneously.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below to this
Invention is expanded on further.
Embodiment 1
A kind of wear-resisting high-strength degree insulated wire cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 110 parts,
Calcium carbonate 2 parts, Polyethylene Glycol 20 parts, polyvinyl alcohol 10 parts, sodium borate 12 parts, 8 parts of magnesium chloride, titanium dioxide 12
Part, chlorinated polyethylene 50 parts, 10 parts of silicone rubber, polyacrylate 2 parts, antioxidant MB 1 part, zinc stearate 2 parts,
Stearic acid monoglyceride 3 parts, modified aluminium hydroxide 20 parts, phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 5 parts, antimony oxide 7 parts,
TDE 5 parts, gas-phase silica 15 parts, nano zeolite 5 parts, blanc fixe 10 parts, compounded mix 3 parts.
Further, described polyvinyl chloride resin uses the SG-5 model Corvic that suspension polymerization is manufactured.
Embodiment 2
A kind of wear-resisting high-strength degree insulated wire cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 120 parts,
Calcium carbonate 3 parts, Polyethylene Glycol 22 parts, polyvinyl alcohol 12 parts, sodium borate 13.5 parts, 10 parts of magnesium chloride, titanium dioxide
14 parts, chlorinated polyethylene 55 parts, 12 parts of silicone rubber, polyacrylate 3 parts, antioxidant MB 1.5 parts, zinc stearate 3
Part, stearic acid monoglyceride 4 parts, modified aluminium hydroxide 25 parts, phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 8 parts, antimony oxide 10
Part, TDE 8 parts, gas-phase silica 17 parts, nano zeolite 7 parts, blanc fixe 12 parts, compounded mix
4 parts.
Further, described polyvinyl chloride resin uses the SG-5 model Corvic that suspension polymerization is manufactured.
Embodiment 3
A kind of wear-resisting high-strength degree insulated wire cable material, including following raw material and parts by weight of component: polyvinyl chloride resin 130 parts,
Calcium carbonate 4 parts, Polyethylene Glycol 25 parts, polyvinyl alcohol 15 parts, sodium borate 15 parts, 12 parts of magnesium chloride, titanium dioxide 16
Part, chlorinated polyethylene 60 parts, 15 parts of silicone rubber, polyacrylate 4 parts, antioxidant MB 2 parts, zinc stearate 4 parts,
Stearic acid monoglyceride 5 parts, modified aluminium hydroxide 30 parts, phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 10 parts, antimony oxide 13 parts,
TDE 10 parts, gas-phase silica 20 parts, nano zeolite 10 parts, blanc fixe 15 parts, compounded mix 6
Part.
Further, described polyvinyl chloride resin uses the SG-5 model Corvic that suspension polymerization is manufactured.
Compared with prior art, the present invention has good wear-resisting pressure performance, mechanical performance, electrical insulation properties and processing
Performance, and intensity is high, hardness is big and good insulating, also has the anti-flammability of excellence and waterproof and dampproof property simultaneously.
The ultimate principle of the present invention, principal character and advantages of the present invention have more than been shown and described.The technical staff of the industry
It should be appreciated that the present invention is not limited by step embodiment, the simply present invention's described in step embodiment and description is former
Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these change and change
Enter to both fall within scope of the claimed invention.Claimed scope is by appending claims and equivalent thereof
Define.
Claims (3)
1. a wear-resisting high-strength degree insulated wire cable material, it is characterised in that: include following raw material and parts by weight of component: PVC
Resin 110-130 part, calcium carbonate 2-4 part, Polyethylene Glycol 20-25 part, polyvinyl alcohol 10-15 part, sodium borate 12-15 part,
Magnesium chloride 8-12 part, titanium dioxide 12-16 part, chlorinated polyethylene 50-60 part, silicone rubber 10-15 part, polyacrylate 2-4
Part, antioxidant MB 1-2 part, zinc stearate 2-4 part, stearic acid monoglyceride 3-5 part, modified aluminium hydroxide 20-30 part,
Phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 5-10 part, antimony oxide 7-13 part, TDE 5-10 part, gas-phase silica 15-20
Part, nano zeolite 5-10 part, blanc fixe 10-15 part, compounded mix 3-6 part.
A kind of wear-resisting high-strength degree insulated wire cable material the most according to claim 1, it is characterised in that: preferably raw material
Component is: polyvinyl chloride resin 120 parts, calcium carbonate 3 parts, Polyethylene Glycol 22 parts, polyvinyl alcohol 12 parts, sodium borate 13.5 parts,
10 parts of magnesium chloride, titanium dioxide 14 parts, chlorinated polyethylene 55 parts, 12 parts of silicone rubber, polyacrylate 3 parts, antioxidant MB 1.5
Part, zinc stearate 3 parts, stearic acid monoglyceride 4 parts, modified aluminium hydroxide 25 parts, phosphoric acid 2-methyl-2-phenylpropane diphenyl ester 8 parts, three
Aoxidize 10 parts of two antimony, TDE 8 parts, gas-phase silica 17 parts, nano zeolite 7 parts, blanc fixe 12 parts,
Compounded mix 4 parts.
A kind of wear-resisting high-strength degree insulated wire cable material the most according to claim 1, it is characterised in that: described PVC
Resin uses the SG-5 model Corvic that suspension polymerization is manufactured.