CN105400044A - Halogen-free flame-retardant cable material - Google Patents
Halogen-free flame-retardant cable material Download PDFInfo
- Publication number
- CN105400044A CN105400044A CN201510936379.1A CN201510936379A CN105400044A CN 105400044 A CN105400044 A CN 105400044A CN 201510936379 A CN201510936379 A CN 201510936379A CN 105400044 A CN105400044 A CN 105400044A
- Authority
- CN
- China
- Prior art keywords
- parts
- halogen
- cable material
- free flame
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The ingredients discloses a halogen-free flame-retardant cable material composed of the following raw materials in parts by weight: 80-90 parts of low density polyethylene, 20-25 parts of EVA resin, 6-10 parts of epoxidized natural rubber, 20-30 parts of a silane coupling agent modified magnesium hydroxide flame retardant, 13-18 parts of nano calcium carbonate, 2-7 parts of nano silica, 0.5-1 part of pentaerythritol, 6-12 parts of aluminum hydroxide, 4-8 parts of a talcum powder, 3-6 parts of a silicone powder, 3-5 parts of maleic anhydride graft, 3-5 parts of zinc oxide, 1-5 parts of stearic acid, and 2-5 parts of an antioxidant. The halogen-free flame-retardant cable material has the advantages of good flame retardant effect, excellent heat resistance, high tear strength, resilience performance improvement, and good comprehensive performance.
Description
Technical field
The invention belongs to field of cables, be specifically related to a kind of Halogen-free flame-retardant cable material.
Background technology
Cable is normally made up of the conductor outsourcing insulation of one or more mutually insulated and protective layer; along with the frequent generation of electrical fire accident; the fire-retardant problem of electric wire draws attention gradually; add fire retardant in cable material and effectively can improve flame retardant properties; the classification of fire retardant can be divided into halogen system, organophosphorus system, silicon system, high purity alumina-magnesia, molybdenum system, boron system etc. according to element kind; and containing multiple carcinogenic substance in the product that the burning of halogen system produces; harm environment and healthy, needs the halogen-free flame retardants researching and developing superior performance.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of Halogen-free flame-retardant cable material.
Technical scheme of the present invention is: a kind of Halogen-free flame-retardant cable material, be made up of the raw material of following parts by weight: Low Density Polyethylene 80-90 part, EVA resin 20-25 part, epoxy natural rubber 6-10 part, silane coupler modified flame retardant of magnesium hydroxide 20-30 part, nano-calcium carbonate 13-18 part, nano silicon 2-7 part, tetramethylolmethane 0.5-1 part, aluminium hydroxide 6-12 part, talcum powder 4-8 part, silicone powder 3-6 part, maleic anhydride graft 3-5 part, zinc oxide 3-5 part, stearic acid 1-5 part, oxidation inhibitor 2-5 part.
Compared with prior art, the invention has the advantages that: good flame retardation effect, excellent heat resistance, tearing toughness and screen resilience performance improve, good combination property.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of Halogen-free flame-retardant cable material, be made up of the raw material of following parts by weight: Low Density Polyethylene 80 parts, EVA resin 20 parts, epoxy natural rubber 6 parts, silane coupler modified flame retardant of magnesium hydroxide 20 parts, nano-calcium carbonate 13 parts, nano silicon 2 parts, tetramethylolmethane 0.5 part, 6 parts, aluminium hydroxide, talcum powder 4 parts, silicone powder 3 parts, maleic anhydride graft 3 parts, 3 parts, zinc oxide, stearic acid 1 part, 2 parts, oxidation inhibitor.
Embodiment 2
A kind of Halogen-free flame-retardant cable material, be made up of the raw material of following parts by weight: Low Density Polyethylene 85 parts, EVA resin 23 parts, epoxy natural rubber 8 parts, silane coupler modified flame retardant of magnesium hydroxide 25 parts, nano-calcium carbonate 15 parts, nano silicon 5 parts, tetramethylolmethane 0.7 part, 10 parts, aluminium hydroxide, talcum powder 6 parts, silicone powder 5 parts, maleic anhydride graft 4 parts, 4 parts, zinc oxide, stearic acid 3 parts, 3 parts, oxidation inhibitor.
Embodiment 3
A kind of Halogen-free flame-retardant cable material, be made up of the raw material of following parts by weight: Low Density Polyethylene 90 parts, EVA resin 25 parts, epoxy natural rubber 10 parts, silane coupler modified flame retardant of magnesium hydroxide 30 parts, nano-calcium carbonate 18 parts, nano silicon 7 parts, tetramethylolmethane 1 part, 12 parts, aluminium hydroxide, talcum powder 8 parts, silicone powder 6 parts, maleic anhydride graft 5 parts, 5 parts, zinc oxide, stearic acid 5 parts, 5 parts, oxidation inhibitor.
Describe the present invention by way of example above, but the invention is not restricted to above-mentioned specific embodiment, all any changes of doing based on the present invention or modification all belong to the scope of protection of present invention.
Claims (1)
1. a Halogen-free flame-retardant cable material, it is characterized in that: be made up of the raw material of following parts by weight: Low Density Polyethylene 80-90 part, EVA resin 20-25 part, epoxy natural rubber 6-10 part, silane coupler modified flame retardant of magnesium hydroxide 20-30 part, nano-calcium carbonate 13-18 part, nano silicon 2-7 part, tetramethylolmethane 0.5-1 part, aluminium hydroxide 6-12 part, talcum powder 4-8 part, silicone powder 3-6 part, maleic anhydride graft 3-5 part, zinc oxide 3-5 part, stearic acid 1-5 part, oxidation inhibitor 2-5 part.